Al-7graphite composite was processed using Al-7graphite mushy prepared by electromagnetic-mechanical stirring method, and the influence of solid fraction on the distributing of graphite particles in ingot was studied....Al-7graphite composite was processed using Al-7graphite mushy prepared by electromagnetic-mechanical stirring method, and the influence of solid fraction on the distributing of graphite particles in ingot was studied. The results shows that the relationship between solid fraction and stirring temperature of mushy is: f(s) = 591.5-0.897 t (where f(s) is the solid fraction, t is the stirring temperature). For Al-7graphite composite, with the increasing of solid fraction, the aggregation extent of graphite particles reduced gradually, and when solid fraction was larger than 30%, graphite particles could distribute evenly in ingot.展开更多
The bonding of steel plate to Al 7graphite slurry was studied for the first time. The relationship model about preheat temperature of steel plate,solid fraction of Al 7graphite slurry, rolling speed and interfacial ...The bonding of steel plate to Al 7graphite slurry was studied for the first time. The relationship model about preheat temperature of steel plate,solid fraction of Al 7graphite slurry, rolling speed and interfacial shear strength of bonding plate could be established by artificial neural networks perfectly.This model could be optimized with a genetic algorithm.The optimum bonding parameters are:516℃ for preheat temperature of steel plate,32.5% for solid fraction of Al 7graphite slurry and 12mm/s for rolling speed,and the largest interfacial shear strength of bonding plate is 70.6MPa.展开更多
基金China and Tsinghua-Zhongda Postdoctoral Science Foundation.]
文摘Al-7graphite composite was processed using Al-7graphite mushy prepared by electromagnetic-mechanical stirring method, and the influence of solid fraction on the distributing of graphite particles in ingot was studied. The results shows that the relationship between solid fraction and stirring temperature of mushy is: f(s) = 591.5-0.897 t (where f(s) is the solid fraction, t is the stirring temperature). For Al-7graphite composite, with the increasing of solid fraction, the aggregation extent of graphite particles reduced gradually, and when solid fraction was larger than 30%, graphite particles could distribute evenly in ingot.
文摘The bonding of steel plate to Al 7graphite slurry was studied for the first time. The relationship model about preheat temperature of steel plate,solid fraction of Al 7graphite slurry, rolling speed and interfacial shear strength of bonding plate could be established by artificial neural networks perfectly.This model could be optimized with a genetic algorithm.The optimum bonding parameters are:516℃ for preheat temperature of steel plate,32.5% for solid fraction of Al 7graphite slurry and 12mm/s for rolling speed,and the largest interfacial shear strength of bonding plate is 70.6MPa.