Quenching and partitioning(Q&P)which provides a balance between toughness and strength is a promising heat treatment in iron and steel industry.However,there are three parameters(quenching temperature,partitioning...Quenching and partitioning(Q&P)which provides a balance between toughness and strength is a promising heat treatment in iron and steel industry.However,there are three parameters(quenching temperature,partitioning temperature and partitioning time)which affect the properties dramatically.As a result,it remains a challenge to get the best parameters in a low-cost way for Q&P process.Here,the orthogonal experimental design combined with a local optimization was adopted to optimize the quenching and partitioning parameters of 65Si2MnWA steel.By using this method,the combination between strength and ductility was optimized;meanwhile,the number of experiments was reduced significantly.When treated by quenching at 180℃followed by partitioning at 330℃for 20 min,the steel reached the best combination between strength and ductility.In detail,the product of ultimate tensile strength and reduction in area was 1.36 times(from 64.9 to 88.8 GPa%)that treated by quenching and tempering.In addition,owing to the grain refinement,the strength and ductility increase simultaneously.Specifically,the reduction in area increased by 27.4%(from 35.8%to 45.6%)coupled with a little improvement in ultimate tensile strength(7.4%).展开更多
基金This work was supported by the National Natural Science Foundation of China(Grant No.51401099).The authors would like to acknowledge Yi Zhou,Rui-yang Li,Zhi-xuan Chen and Lian-bo Luo for useful advice and discussion.
文摘Quenching and partitioning(Q&P)which provides a balance between toughness and strength is a promising heat treatment in iron and steel industry.However,there are three parameters(quenching temperature,partitioning temperature and partitioning time)which affect the properties dramatically.As a result,it remains a challenge to get the best parameters in a low-cost way for Q&P process.Here,the orthogonal experimental design combined with a local optimization was adopted to optimize the quenching and partitioning parameters of 65Si2MnWA steel.By using this method,the combination between strength and ductility was optimized;meanwhile,the number of experiments was reduced significantly.When treated by quenching at 180℃followed by partitioning at 330℃for 20 min,the steel reached the best combination between strength and ductility.In detail,the product of ultimate tensile strength and reduction in area was 1.36 times(from 64.9 to 88.8 GPa%)that treated by quenching and tempering.In addition,owing to the grain refinement,the strength and ductility increase simultaneously.Specifically,the reduction in area increased by 27.4%(from 35.8%to 45.6%)coupled with a little improvement in ultimate tensile strength(7.4%).