2Y-PSZ/TRIP steel composites have been sintered by hot-pressing method. Their microstructure and mechanical properties were investigated by means of SEM, TEM, XRD and static tension, split Hopkinson pressure bar metho...2Y-PSZ/TRIP steel composites have been sintered by hot-pressing method. Their microstructure and mechanical properties were investigated by means of SEM, TEM, XRD and static tension, split Hopkinson pressure bar method. The results showed that the strength and elastic modulus of 2Y-PSZ/TRIP steel composites at room temperature decreased with the increase of 2Y-PSZ content. The main reason was that the combining strength was quite weak between the grains of ZrO2. Distortion induced martensite transformation and plasticity during the dynamic loading increased the strength and distortion capability of the composites. The transformation was carried out mainly through twins formation. The shape of martensite induced by distortion was lamellate with substructures of twins. The habit plane was near {259}T with no mid-ridge and no explosion phenomena. The interface was straight between the austenite and martensite induced by distortion. The increase of 2Y-PSZ content, on the one hand, made the composite dynamic flow stress improved. Thereby, the fracture strength was improved. On the other hand, it depressed both the distortion capability and the martensite transformation induced by distortion. This resulted in the decrease of dynamic fracture strength.展开更多
Due to the high content of the Al-TRIP steel, Al reacts with SiO2 in the mold slag during the casting process, which results in the increase of ωAl2O3 /ωSiO2 ratio and the Al2O3 content, respectively; the characteri...Due to the high content of the Al-TRIP steel, Al reacts with SiO2 in the mold slag during the casting process, which results in the increase of ωAl2O3 /ωSiO2 ratio and the Al2O3 content, respectively; the characteristic of heat transfer through the slag film is then changed, which influences the smooth operation of the continuous casting process. The heat flux simulator of mold slag film was used to study the change tendency of the heat flux density through slag film and the results were discussed; at the same time, the characteristics of the crystals in the No. 15 mold slag were determined by BSE and XRD. The results obtained show that heat flux density decreases with the increase of ωAl2O3 /ωSiO2 ratio. Heat flux density increases with the increase of Li2O and/or B2O3 content in the mold slag which contains 30 % of Al2 O3. Compared with the heat flux density of common slag of peritectic steel, a suitable mold slag containing 4% of B2O3 and 4% of Li2O is designed. The heat flux density is 0. 645 MW/m^2 when ωAl2O3 /ωSiO2 = 1. 46. Under this experimental condition, the CaF2 crystals precipitate in the mold slag used for Al-TRIP steel.展开更多
文摘2Y-PSZ/TRIP steel composites have been sintered by hot-pressing method. Their microstructure and mechanical properties were investigated by means of SEM, TEM, XRD and static tension, split Hopkinson pressure bar method. The results showed that the strength and elastic modulus of 2Y-PSZ/TRIP steel composites at room temperature decreased with the increase of 2Y-PSZ content. The main reason was that the combining strength was quite weak between the grains of ZrO2. Distortion induced martensite transformation and plasticity during the dynamic loading increased the strength and distortion capability of the composites. The transformation was carried out mainly through twins formation. The shape of martensite induced by distortion was lamellate with substructures of twins. The habit plane was near {259}T with no mid-ridge and no explosion phenomena. The interface was straight between the austenite and martensite induced by distortion. The increase of 2Y-PSZ content, on the one hand, made the composite dynamic flow stress improved. Thereby, the fracture strength was improved. On the other hand, it depressed both the distortion capability and the martensite transformation induced by distortion. This resulted in the decrease of dynamic fracture strength.
基金Item Sponsored by National Natural Science Foundation of China (50874125)
文摘Due to the high content of the Al-TRIP steel, Al reacts with SiO2 in the mold slag during the casting process, which results in the increase of ωAl2O3 /ωSiO2 ratio and the Al2O3 content, respectively; the characteristic of heat transfer through the slag film is then changed, which influences the smooth operation of the continuous casting process. The heat flux simulator of mold slag film was used to study the change tendency of the heat flux density through slag film and the results were discussed; at the same time, the characteristics of the crystals in the No. 15 mold slag were determined by BSE and XRD. The results obtained show that heat flux density decreases with the increase of ωAl2O3 /ωSiO2 ratio. Heat flux density increases with the increase of Li2O and/or B2O3 content in the mold slag which contains 30 % of Al2 O3. Compared with the heat flux density of common slag of peritectic steel, a suitable mold slag containing 4% of B2O3 and 4% of Li2O is designed. The heat flux density is 0. 645 MW/m^2 when ωAl2O3 /ωSiO2 = 1. 46. Under this experimental condition, the CaF2 crystals precipitate in the mold slag used for Al-TRIP steel.