PS/SiO2 particles with core-shell structure were synthesized by coating silica on surface of polystyrene(PS) colloidal particles.The reaction parameters,such as initial tetraethyl orthosilicate(TEOS) concentration,wat...PS/SiO2 particles with core-shell structure were synthesized by coating silica on surface of polystyrene(PS) colloidal particles.The reaction parameters,such as initial tetraethyl orthosilicate(TEOS) concentration,water concentration and reaction temperature,have been investigated to control the thickness of silica shells.The shell thickness was prepositional to the square root of the initial concentration of TEOS and first increased with increasing water concentration,reached a maximum at about 2.0 mol/L and then started decreasing beyond that concentration.It was also found that the shell thickness decreased firstly with the reaction temperature added,then tended to a constant.The so-synthesized PS/SiO2 core-shell particles were directly crystallized into 3-D ordered thin film,then sintered at 570℃ into the ordered macroporous thin film.Compared with the conditional method,the present approach avoids repeatedly filling the precursor in the templetes and save time more.展开更多
In this study, novel core-shell SiO<sub>2</sub>-coated iron nanoparticles (SiO<sub>2</sub>-nZVI) were synthesized using a one-step Stoeber method. The Malachite green degradation abilities of t...In this study, novel core-shell SiO<sub>2</sub>-coated iron nanoparticles (SiO<sub>2</sub>-nZVI) were synthesized using a one-step Stoeber method. The Malachite green degradation abilities of the nanoparticles were investigated. The effects of ethanol/distilled water volume ratio, presence and absence of PEG, tetraethyl orthosilicate (TEOS) dosage, and hydrolysis time used in the nanoparticles preparation process were investigated. The results indicated that the SiO<sub>2</sub>-coated iron nanoparticles had the highest reduction activity when the particles synthesized with ethanol/H<sub>2</sub>O ratio of 2:1, PEG of 0.15 ml, TEOS of 0.5 ml and the reaction time was 4 h. The SiO<sub>2</sub>-nZVI nanoparticles were characterized using Transmission Electron Microscopy (TEM), Energy Dispersive Spectrometry (EDS) and powder X-Ray Diffraction (XRD). The results showed that the average particles diameter of the SiO<sub>2</sub>-nZVI was 20 - 30 nm. The thickness of the outside SiO<sub>2</sub> film is consistent and approximately 10 nm. The results indicated that the nanoparticles coated completely with a transparent SiO<sub>2</sub>-film. Such nanoparticles could have wide applications in dye decolorization.展开更多
基金Supported by the National Natural Science Foundation of China(No.:20221603)
文摘PS/SiO2 particles with core-shell structure were synthesized by coating silica on surface of polystyrene(PS) colloidal particles.The reaction parameters,such as initial tetraethyl orthosilicate(TEOS) concentration,water concentration and reaction temperature,have been investigated to control the thickness of silica shells.The shell thickness was prepositional to the square root of the initial concentration of TEOS and first increased with increasing water concentration,reached a maximum at about 2.0 mol/L and then started decreasing beyond that concentration.It was also found that the shell thickness decreased firstly with the reaction temperature added,then tended to a constant.The so-synthesized PS/SiO2 core-shell particles were directly crystallized into 3-D ordered thin film,then sintered at 570℃ into the ordered macroporous thin film.Compared with the conditional method,the present approach avoids repeatedly filling the precursor in the templetes and save time more.
文摘In this study, novel core-shell SiO<sub>2</sub>-coated iron nanoparticles (SiO<sub>2</sub>-nZVI) were synthesized using a one-step Stoeber method. The Malachite green degradation abilities of the nanoparticles were investigated. The effects of ethanol/distilled water volume ratio, presence and absence of PEG, tetraethyl orthosilicate (TEOS) dosage, and hydrolysis time used in the nanoparticles preparation process were investigated. The results indicated that the SiO<sub>2</sub>-coated iron nanoparticles had the highest reduction activity when the particles synthesized with ethanol/H<sub>2</sub>O ratio of 2:1, PEG of 0.15 ml, TEOS of 0.5 ml and the reaction time was 4 h. The SiO<sub>2</sub>-nZVI nanoparticles were characterized using Transmission Electron Microscopy (TEM), Energy Dispersive Spectrometry (EDS) and powder X-Ray Diffraction (XRD). The results showed that the average particles diameter of the SiO<sub>2</sub>-nZVI was 20 - 30 nm. The thickness of the outside SiO<sub>2</sub> film is consistent and approximately 10 nm. The results indicated that the nanoparticles coated completely with a transparent SiO<sub>2</sub>-film. Such nanoparticles could have wide applications in dye decolorization.