The bonding of steel and mushy Al 28Pb alloy was studied. The relationship model about preheat temperature of steel plate, solid fraction of mushy Al 28Pb alloy, rolling speed and interfacial shear strength of the bon...The bonding of steel and mushy Al 28Pb alloy was studied. The relationship model about preheat temperature of steel plate, solid fraction of mushy Al 28Pb alloy, rolling speed and interfacial shear strength of the bonding plate was established by artificial neural network perfectly. This model can be optimized by a genetic algorithm, and the optimum bonding parameters for the largest interfacial shear strength are: 546 ℃ for preheat temperature of steel plate, 43.5% for solid fraction of mushy Al 28Pb alloy and 8.6 mm/s for rolling speed, and the corresponding largest interfacial shear strength of bonding plate is 70.3 MPa. [展开更多
The interfacial properties of steel-mushy Al-28Pb bonding plate with different interfacial structures, and the influence of ratio of Fe-Al compound at the interface on interfacial shear strength were investigated. The...The interfacial properties of steel-mushy Al-28Pb bonding plate with different interfacial structures, and the influence of ratio of Fe-Al compound at the interface on interfacial shear strength were investigated. The results show that there is a nonlinear relationship between the ratio of Fe-Al compound at the interface and the interfacial shear strength. When the ratio of Fe-Al compound at the interface is smaller than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength increases gradually; when the ratio of Fe-Al compound at the interface is larger than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength decreases continuously; when the ratio of Fe-Al compound at the interface is 71.4%, the largest interfacial shear strength 70.2MPa is obtained.展开更多
The influence of solid fraction of Al 28Pb alloy mushy on distribution of Pb in Al Pb ingot was studied. The special electromagnetic stirring apparatus was used to prepare Al 28Pb alloy mushy and the relationship betw...The influence of solid fraction of Al 28Pb alloy mushy on distribution of Pb in Al Pb ingot was studied. The special electromagnetic stirring apparatus was used to prepare Al 28Pb alloy mushy and the relationship between solid fraction and stirring temperature was gotten. The results show that when solid fraction of Al 28Pb alloy mushy is less than 45%, Pb precipitation usually happens in the ingot. However, Pb precipitation in casting reduces gradually with increasing solid fraction of mushy, and when solid fraction is larger than 45%, Pb precipitation in casting can be removed. [展开更多
文摘The bonding of steel and mushy Al 28Pb alloy was studied. The relationship model about preheat temperature of steel plate, solid fraction of mushy Al 28Pb alloy, rolling speed and interfacial shear strength of the bonding plate was established by artificial neural network perfectly. This model can be optimized by a genetic algorithm, and the optimum bonding parameters for the largest interfacial shear strength are: 546 ℃ for preheat temperature of steel plate, 43.5% for solid fraction of mushy Al 28Pb alloy and 8.6 mm/s for rolling speed, and the corresponding largest interfacial shear strength of bonding plate is 70.3 MPa. [
文摘The interfacial properties of steel-mushy Al-28Pb bonding plate with different interfacial structures, and the influence of ratio of Fe-Al compound at the interface on interfacial shear strength were investigated. The results show that there is a nonlinear relationship between the ratio of Fe-Al compound at the interface and the interfacial shear strength. When the ratio of Fe-Al compound at the interface is smaller than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength increases gradually; when the ratio of Fe-Al compound at the interface is larger than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength decreases continuously; when the ratio of Fe-Al compound at the interface is 71.4%, the largest interfacial shear strength 70.2MPa is obtained.
文摘The influence of solid fraction of Al 28Pb alloy mushy on distribution of Pb in Al Pb ingot was studied. The special electromagnetic stirring apparatus was used to prepare Al 28Pb alloy mushy and the relationship between solid fraction and stirring temperature was gotten. The results show that when solid fraction of Al 28Pb alloy mushy is less than 45%, Pb precipitation usually happens in the ingot. However, Pb precipitation in casting reduces gradually with increasing solid fraction of mushy, and when solid fraction is larger than 45%, Pb precipitation in casting can be removed. [