Study on oxidizing cellulose to 2.3-dialdehyde cellulose by sodium periodate （NalO4） was carried out. The effects of reaction conditions such as pH of solution, temperature, oxidant concentration, oxidation time. th...Study on oxidizing cellulose to 2.3-dialdehyde cellulose by sodium periodate （NalO4） was carried out. The effects of reaction conditions such as pH of solution, temperature, oxidant concentration, oxidation time. the particle size of 2,3-dialdehyde cellulose and alkali treatment temperature on the dialdehyde concentration ot cellulose were investigated in detail, The results show that the aldehyde group content was created while reaction temperature and alkali treatment temperature increased. The most principal factors affecting the aldehyde group content of 2,3-dialdehyde cellulose were found out and the best oxidation conditions were as follows： the pH was 2. the reaction temperature was 45℃. the mass ratio of cellulose to NalO4 was 1/2, the reaction time was 4 h, the alkali treatment temperature was 70℃ and smaller particle size was 0.80 mm.展开更多
In this study,the efects of diferent heat treatment process parameters on the microstructure and mechanical properties of Al-12Si-5Cu-1.1Mg-2.3Ni-0.3La alloy were explored.Research showed that eutectic Si underwent th...In this study,the efects of diferent heat treatment process parameters on the microstructure and mechanical properties of Al-12Si-5Cu-1.1Mg-2.3Ni-0.3La alloy were explored.Research showed that eutectic Si underwent three stages during solution treatment:difusing,spheroidization and coarsening.As the solution temperature and time increased,the size of eutectic Si showed a trend of frst decreasing and then increasing.Compared with the heat treatment time,the heat treatment temperature had a more signifcant efect on the mechanical properties.The coarsening of microstructure was the main reason for the deterioration of mechanical properties.The Al_(3)Ti and Al_(3)CuNiLa in the microstructure after aging can signifcantly improve the mechanical properties of the alloy.The Al_(11)La_(3) with secondary precipitation occurred in the La-rich phase.The addition of La inhibited the growth of coherent/semi-coherentθandβphases,which was very benefcial for the improvement of high-temperature strength.Under the optimal heat treatment process parameters of 500℃×4 h+190℃×4 h,the ultimate tensile strength(UTS)of the alloy reached 366.65 MPa.The high-temperature strength and elongation of the alloy reached 101.98 MPa and 13.77%at 350℃,respectively.展开更多
基金Supported by Natural Science Foundation of Tianjin (No. 03380211, 043610611).
文摘Study on oxidizing cellulose to 2.3-dialdehyde cellulose by sodium periodate （NalO4） was carried out. The effects of reaction conditions such as pH of solution, temperature, oxidant concentration, oxidation time. the particle size of 2,3-dialdehyde cellulose and alkali treatment temperature on the dialdehyde concentration ot cellulose were investigated in detail, The results show that the aldehyde group content was created while reaction temperature and alkali treatment temperature increased. The most principal factors affecting the aldehyde group content of 2,3-dialdehyde cellulose were found out and the best oxidation conditions were as follows： the pH was 2. the reaction temperature was 45℃. the mass ratio of cellulose to NalO4 was 1/2, the reaction time was 4 h, the alkali treatment temperature was 70℃ and smaller particle size was 0.80 mm.
基金supported by the National Natural Science Foundation of China(NSFC)(Grant Nos.U2241232,U2341253 and 52375317)the National Key R&D Program of China(No.2022YFB3404204).
文摘In this study,the efects of diferent heat treatment process parameters on the microstructure and mechanical properties of Al-12Si-5Cu-1.1Mg-2.3Ni-0.3La alloy were explored.Research showed that eutectic Si underwent three stages during solution treatment:difusing,spheroidization and coarsening.As the solution temperature and time increased,the size of eutectic Si showed a trend of frst decreasing and then increasing.Compared with the heat treatment time,the heat treatment temperature had a more signifcant efect on the mechanical properties.The coarsening of microstructure was the main reason for the deterioration of mechanical properties.The Al_(3)Ti and Al_(3)CuNiLa in the microstructure after aging can signifcantly improve the mechanical properties of the alloy.The Al_(11)La_(3) with secondary precipitation occurred in the La-rich phase.The addition of La inhibited the growth of coherent/semi-coherentθandβphases,which was very benefcial for the improvement of high-temperature strength.Under the optimal heat treatment process parameters of 500℃×4 h+190℃×4 h,the ultimate tensile strength(UTS)of the alloy reached 366.65 MPa.The high-temperature strength and elongation of the alloy reached 101.98 MPa and 13.77%at 350℃,respectively.