In the present work,the sheets of Zr-1Sn-0.3Nb-0.3Fe-0.1Cr alloy were hot rolled with different reductions(10%,30%,50%,and 60%) at 1023 K and 1073 K.The micro structure evolutions including grain micro structure,textu...In the present work,the sheets of Zr-1Sn-0.3Nb-0.3Fe-0.1Cr alloy were hot rolled with different reductions(10%,30%,50%,and 60%) at 1023 K and 1073 K.The micro structure evolutions including grain micro structure,texture,and dislocation were investigated,using electron backscattering diffraction and transmission electron microscope.The results showed that dislocation slip,twinning,and dynamic recrystallization(DRX) were the main deformation mechanisms.DRX was found to be promoted by larger reduction and higher rolling temperature.The predominant texture formed during hot rolling was basal <0001>//ND,whose intensity reached peak value after 30% reduction hot rolling.While the intensity of DRX texture <10-10>//ND and<1-210>//ND increased with increasing reduction and temperature.This study provided an effective way to tailor the texture and microstructure of the alloy,for optimizing process parameters.展开更多
The influence of Al alloying on the microstructures and the mechanical properties of Mg–x Al–1 Sn–0.3 Mn alloy sheets was investigated. The microstructure of Mg– x Al–1 Sn–0.3 Mn consisted of α-Mg and Mg 17 Al ...The influence of Al alloying on the microstructures and the mechanical properties of Mg–x Al–1 Sn–0.3 Mn alloy sheets was investigated. The microstructure of Mg– x Al–1 Sn–0.3 Mn consisted of α-Mg and Mg 17 Al 12 precipitates. Alloying with Al increased the amount of Mg17Al12 and the average grain size. Uniaxial tensile tests were carried out along the extrusion direction(ED), the transverse direction(TD) and 45° toward the ED. Mg–5 Al–1 Sn–0.3 Mn alloy sheet exhibited the best combination of mechanical properties along the ED: a yield strength of 142 MPa, an ultimate tensile strength of 282 MPa and an elongation of 23%. The good performance of Mg–5 Al–1 Sn–0.3 Mn sheet was mainly attributed to the large quantity of Mg17Al12 precipitates and a weak basal texture. Annealing caused static dynamic recrystallization, refined the grain size and enhanced the mechanical properties: yield strength of 186 MPa, ultimate tensile strength of 304 MPa, elongation of 21% along ED. Both strength and ductility were enhanced by Al alloying.展开更多
Utilization and transfer of nitrogen （N）in a strip intercropping system of garlic （Allium safivum L.） and broad bean （Vicia faba L.） have been investigated rarely. The objectives of this study were to quantify N...Utilization and transfer of nitrogen （N）in a strip intercropping system of garlic （Allium safivum L.） and broad bean （Vicia faba L.） have been investigated rarely. The objectives of this study were to quantify N uptake and utilization by intercropped broad bean and garlic and determine the magnitude of N transfer from broad bean to garlic. Field and pot trials were carried out in the Erhai Lake Basin in China using ^15N tracer applied to the soil or injected into broad bean plants. Strip intercropping of garlic and broad bean increased N absorption （47.2%） compared with sole crop broad bean （31.9%） or sole crop garlic （40.7%） and reduced soil residual N. Nearly 15% of 15N injected into petioles of broad bean intercropped with garlic was recovered in garlic at harvest, suggesting that N could be transferred from broad bean to strip intercropped garlic. The findings provide a basis for evaluating legumes＇ role in optimizing N fertilization when intercropped with non-legumes.展开更多
基金National Key Research and Development Program of China(2016YFB0700403)National Natural Science Foundation of China(51571040)+3 种基金Chongqing Research Program of Basic Research and Frontier Technology(cstc2019jcyj-msxmX0306,cstc2019jcyj-msxmX0539)Fundamental Research Funds for Central Universities(2021CDJJMRH-001)111 Project of Ministry of Education and State Administration of Foreign Experts Affairs of China(B16007)Sharing Fund of Chongqing University Large-Scale Equipment(201612150024,201612150092)。
基金financially supported by the National Natural Science Foundation of China (No. U1867201).
文摘In the present work,the sheets of Zr-1Sn-0.3Nb-0.3Fe-0.1Cr alloy were hot rolled with different reductions(10%,30%,50%,and 60%) at 1023 K and 1073 K.The micro structure evolutions including grain micro structure,texture,and dislocation were investigated,using electron backscattering diffraction and transmission electron microscope.The results showed that dislocation slip,twinning,and dynamic recrystallization(DRX) were the main deformation mechanisms.DRX was found to be promoted by larger reduction and higher rolling temperature.The predominant texture formed during hot rolling was basal <0001>//ND,whose intensity reached peak value after 30% reduction hot rolling.While the intensity of DRX texture <10-10>//ND and<1-210>//ND increased with increasing reduction and temperature.This study provided an effective way to tailor the texture and microstructure of the alloy,for optimizing process parameters.
基金the National Key R&D Program of China(No.2016YFB0301100)the National Natural Science Foundation of China(No.51571043)the Graduate Scientific Research and Innovation Foundation of Chongqing,China(Grant No.CYB18004)。
文摘The influence of Al alloying on the microstructures and the mechanical properties of Mg–x Al–1 Sn–0.3 Mn alloy sheets was investigated. The microstructure of Mg– x Al–1 Sn–0.3 Mn consisted of α-Mg and Mg 17 Al 12 precipitates. Alloying with Al increased the amount of Mg17Al12 and the average grain size. Uniaxial tensile tests were carried out along the extrusion direction(ED), the transverse direction(TD) and 45° toward the ED. Mg–5 Al–1 Sn–0.3 Mn alloy sheet exhibited the best combination of mechanical properties along the ED: a yield strength of 142 MPa, an ultimate tensile strength of 282 MPa and an elongation of 23%. The good performance of Mg–5 Al–1 Sn–0.3 Mn sheet was mainly attributed to the large quantity of Mg17Al12 precipitates and a weak basal texture. Annealing caused static dynamic recrystallization, refined the grain size and enhanced the mechanical properties: yield strength of 186 MPa, ultimate tensile strength of 304 MPa, elongation of 21% along ED. Both strength and ductility were enhanced by Al alloying.
基金supported by the Special Fund for Agroscientific Research in the Public Interest,China (201003014)the National Natural Science Foundation of China (31460143)
文摘Utilization and transfer of nitrogen （N）in a strip intercropping system of garlic （Allium safivum L.） and broad bean （Vicia faba L.） have been investigated rarely. The objectives of this study were to quantify N uptake and utilization by intercropped broad bean and garlic and determine the magnitude of N transfer from broad bean to garlic. Field and pot trials were carried out in the Erhai Lake Basin in China using ^15N tracer applied to the soil or injected into broad bean plants. Strip intercropping of garlic and broad bean increased N absorption （47.2%） compared with sole crop broad bean （31.9%） or sole crop garlic （40.7%） and reduced soil residual N. Nearly 15% of 15N injected into petioles of broad bean intercropped with garlic was recovered in garlic at harvest, suggesting that N could be transferred from broad bean to strip intercropped garlic. The findings provide a basis for evaluating legumes＇ role in optimizing N fertilization when intercropped with non-legumes.