In this study,the anti-penetration performance of polyurea/ASTM1405-steel composite plate subjected to high velocity projectile was analyzed.Two kinds of modified polyurea material(AMMT-053 and AMMT-055)were selected ...In this study,the anti-penetration performance of polyurea/ASTM1405-steel composite plate subjected to high velocity projectile was analyzed.Two kinds of modified polyurea material(AMMT-053 and AMMT-055)were selected and a ballistic impact testing system including speed measuring target system and high-speed camera was designed.This experiment was conducted with a rifle and 5.8 mm projectile to explore the effects by the polyurea coating thickness,the polyurea coating position and the glass-fiber cloth on the anti-penetration performance of polyurea/ASTM1405-steel composite plate.The result showed that the effects of polyurea coating position were different between two types of polyurea,and that the effects of glass-fiber position were disparate between two types of polyurea as well.For AMMT-053 polyurea material,it was better to be on front face than on rear face;whereas for AMMT-055 polyurea,it was better to be on rear surface although the difference was very subtle.Additionally,formulas had been given to describe the relationship between the effectiveness of polyurea and the thickness of polyurea coating.In general,AMMT-055 had better anti-penetration performance than AMMT-053.Furthermore,five typical damage modes including self-healing,crack,local bulge,spallation and local fragmentation were defined and the failure mechanism was analyzed with the results of SHPB test.Additionally,the bonding strength played an important role in the anti-penetration performance of polyurea/steel composite plate.展开更多
In this paper fretting fatigue crack behavior in 1045 steel is studied by in-situ observation and finite element analysis.in-situ fretting fatigue experiments are conducted to capture real-time fretting fatigue crack ...In this paper fretting fatigue crack behavior in 1045 steel is studied by in-situ observation and finite element analysis.in-situ fretting fatigue experiments are conducted to capture real-time fretting fatigue crack formation and propagation process.The fretting fatigue tests under different load conditions are carried out,then the lifetime and fracture surface are obtained.The crack propagation rates under different loading conditions are measured by in-situ observations.With in-situ observation,crack initiation location and direction are analyzed.Finite element model is used to calculate J-integral which then is applied to fitting with experimental crack growth rate,and establishing crack growth rate model.From fitted S-N curve,it turns out that smaller load ratio leads to higher lifetime.Crack initiates slightly below the point equivalent to line contact of the contact surface in different test conditions,and crack direction shows no obvious relationship with load parameters.The established crack growth rate model well agrees with the test results.展开更多
To investigate the effect of alternating magnetic field on austenite transformation process in the case of rapid heating,the austenite kinetics model of AISI 1045 steel was built for spot continual induction hardening...To investigate the effect of alternating magnetic field on austenite transformation process in the case of rapid heating,the austenite kinetics model of AISI 1045 steel was built for spot continual induction hardening(SCIH)process.The results shows that the effect of alternating magnetic field on austenite transformation fraction reaches the maximum(about 3%)when heating rate is the lowest.Relatively low magnetic flux density still has a certain effect on the austenite transformation process during the SCIH process.Concave surface structure can reduce the influence scope of alternating magnetic field on surface in all cases and the minimum influence scope appears when the feed path of inductor is longitudinal.Convex surface structure can minimize the influence scope of alternating magnetic field in depth when the feed path of inductor is longitudinal.The austenite distribution of transitional region on surface for horizontal movement is more uniform than that for longitudinal movement.The austenite distribution of transitional region in depth for longitudinal movement is more uniform than that for horizontal movement.The simulated results are consistent with the experimental results and the austenite transformation kinetics model developed for SCIH process is valid.展开更多
To improve the bonding strength between the nickel bond and the hub of the electroplated diamond grinding wheel,a hybrid technique was proposed to combine laser prequenching steel substrate and post-electroplating nic...To improve the bonding strength between the nickel bond and the hub of the electroplated diamond grinding wheel,a hybrid technique was proposed to combine laser prequenching steel substrate and post-electroplating nickel.To validate the effectiveness of the proposed technique,AISI 1045 substrate was nickel-coated.The bonding properties between the electroplated nickel coating and substrate with or without laser-discrete-quenching were discussed comparatively by scratch,indentation,and thermal shock tests.The results show that the prequenching treatment leads to phase transformation of AISI 1045 microstructure from the mixed pearlite and ferrite phases into the martensitic phase.Since the martensitic phase is characterized as a high corrosion resistance,the interface of substrate/coating is smooth and flat in the prequenched zone,and the coating is bonded well with the steel substrate.In contrast to the steel substrate without pre-quenching treatment,the proposed technique significantly enhanced the bonding strengths of the electroplated nickel-coating.On one hand,the average hardness of electroplated nickel-coating on the laser pre-quenched zone is increased by 18.7%,and the scratch depth with the same load become narrower and shallower.On the other hand,the coefficient of friction(CoF)and the vibration amplitude are reduced,and the coating is bonded effectively with the substrate to inhibit the crack initialization at the interface.This prevents effectively the coating from peeling off and improves significantly the thermal shock resistance property.展开更多
基金This research was supported by the National Natural Science Foundation of China(Nos.51978660).
文摘In this study,the anti-penetration performance of polyurea/ASTM1405-steel composite plate subjected to high velocity projectile was analyzed.Two kinds of modified polyurea material(AMMT-053 and AMMT-055)were selected and a ballistic impact testing system including speed measuring target system and high-speed camera was designed.This experiment was conducted with a rifle and 5.8 mm projectile to explore the effects by the polyurea coating thickness,the polyurea coating position and the glass-fiber cloth on the anti-penetration performance of polyurea/ASTM1405-steel composite plate.The result showed that the effects of polyurea coating position were different between two types of polyurea,and that the effects of glass-fiber position were disparate between two types of polyurea as well.For AMMT-053 polyurea material,it was better to be on front face than on rear face;whereas for AMMT-055 polyurea,it was better to be on rear surface although the difference was very subtle.Additionally,formulas had been given to describe the relationship between the effectiveness of polyurea and the thickness of polyurea coating.In general,AMMT-055 had better anti-penetration performance than AMMT-053.Furthermore,five typical damage modes including self-healing,crack,local bulge,spallation and local fragmentation were defined and the failure mechanism was analyzed with the results of SHPB test.Additionally,the bonding strength played an important role in the anti-penetration performance of polyurea/steel composite plate.
基金financially supported by the National Natural Science Foundation of China(Nos.91860101,11632010,11902370 and 11572171)National Major Science and Technology Projects of China(No.2017-VI-0003-0073)。
文摘In this paper fretting fatigue crack behavior in 1045 steel is studied by in-situ observation and finite element analysis.in-situ fretting fatigue experiments are conducted to capture real-time fretting fatigue crack formation and propagation process.The fretting fatigue tests under different load conditions are carried out,then the lifetime and fracture surface are obtained.The crack propagation rates under different loading conditions are measured by in-situ observations.With in-situ observation,crack initiation location and direction are analyzed.Finite element model is used to calculate J-integral which then is applied to fitting with experimental crack growth rate,and establishing crack growth rate model.From fitted S-N curve,it turns out that smaller load ratio leads to higher lifetime.Crack initiates slightly below the point equivalent to line contact of the contact surface in different test conditions,and crack direction shows no obvious relationship with load parameters.The established crack growth rate model well agrees with the test results.
基金Projects(51905390,51575415)supported by the National Natural Science Foundation of China。
文摘To investigate the effect of alternating magnetic field on austenite transformation process in the case of rapid heating,the austenite kinetics model of AISI 1045 steel was built for spot continual induction hardening(SCIH)process.The results shows that the effect of alternating magnetic field on austenite transformation fraction reaches the maximum(about 3%)when heating rate is the lowest.Relatively low magnetic flux density still has a certain effect on the austenite transformation process during the SCIH process.Concave surface structure can reduce the influence scope of alternating magnetic field on surface in all cases and the minimum influence scope appears when the feed path of inductor is longitudinal.Convex surface structure can minimize the influence scope of alternating magnetic field in depth when the feed path of inductor is longitudinal.The austenite distribution of transitional region on surface for horizontal movement is more uniform than that for longitudinal movement.The austenite distribution of transitional region in depth for longitudinal movement is more uniform than that for horizontal movement.The simulated results are consistent with the experimental results and the austenite transformation kinetics model developed for SCIH process is valid.
基金the National Natural Science Foundation of China(No.51875050)Hunan Provincial Natural Science Foundation of China(No.2019JJ40293)Changsha City Planned Science and Technology Project(No.kq1907088)。
文摘To improve the bonding strength between the nickel bond and the hub of the electroplated diamond grinding wheel,a hybrid technique was proposed to combine laser prequenching steel substrate and post-electroplating nickel.To validate the effectiveness of the proposed technique,AISI 1045 substrate was nickel-coated.The bonding properties between the electroplated nickel coating and substrate with or without laser-discrete-quenching were discussed comparatively by scratch,indentation,and thermal shock tests.The results show that the prequenching treatment leads to phase transformation of AISI 1045 microstructure from the mixed pearlite and ferrite phases into the martensitic phase.Since the martensitic phase is characterized as a high corrosion resistance,the interface of substrate/coating is smooth and flat in the prequenched zone,and the coating is bonded well with the steel substrate.In contrast to the steel substrate without pre-quenching treatment,the proposed technique significantly enhanced the bonding strengths of the electroplated nickel-coating.On one hand,the average hardness of electroplated nickel-coating on the laser pre-quenched zone is increased by 18.7%,and the scratch depth with the same load become narrower and shallower.On the other hand,the coefficient of friction(CoF)and the vibration amplitude are reduced,and the coating is bonded effectively with the substrate to inhibit the crack initialization at the interface.This prevents effectively the coating from peeling off and improves significantly the thermal shock resistance property.