The structure and magnetocaloric properties of La1–xCexFe11.44Si1.56 and their hydrides La1–xCexFe11.44Si1.56Hy（x=0, 0.1, 0.2, 0.3, 0.4） were investigated.The samples crystallized mainly in the cubic Na Zn13-type ...The structure and magnetocaloric properties of La1–xCexFe11.44Si1.56 and their hydrides La1–xCexFe11.44Si1.56Hy（x=0, 0.1, 0.2, 0.3, 0.4） were investigated.The samples crystallized mainly in the cubic Na Zn13-type structure with a small amount of α-Fe phase as impurity.The lattice constants and Curie temperature presented the same change tendency with increasing of Ce content.For the hydrides, the influence of Ce content on lattice constants was weakened and the values of H concentration y were approximate to be 1.56.The La1–xCexFe11.44Si1.56 compounds exhibited large values of isothermal entropy change –ΔSm around the Curie temperature TC under a low magnetic field change of 1.5 T.The value of –ΔSm increased and then decreased with increasing Ce content, reached the maximum, 26.07 J/kg·K for x=0.3.TC increased up to the vicinity of room temperature by hydrogen absorption for the Ce substituted compounds, but TC only slightly decreased with increasing Ce content.The first-order metamagnetic transition was still kept in the hydrides and the maximum values of –ΔSm were lower than those of the La1–xCexFe11.44Si1.56 compounds, but still remained large values, about 10.5 J/kg K under a magnetic field change of 1.5 T.The values of –ΔSm were nearly independent of the Ce content and did not increase with increasing x for the hydrides.The La1–xCexFe11.44Si1.56Hy（x=0–0.4） hydrides exhibited large magnetic entropy changes, small hysteresis loss and effective refrigerant capacity covered the room temperature range from 305 to 317 K.These hydrides are very useful for the magnetic refrigeration applications near room temperature under low magnetic field change.展开更多
We demonstrate an all-fiber, high-power, and high stability ultrafast laser source operating at 1563 nm. A highly stable, self-starting carbon nanotube（CNT） mode-locked femtosecond fiber laser is used as the seed so...We demonstrate an all-fiber, high-power, and high stability ultrafast laser source operating at 1563 nm. A highly stable, self-starting carbon nanotube（CNT） mode-locked femtosecond fiber laser is used as the seed source. The amplifier stage uses a fiber chirped pulse amplification configuration. The main power amplifier is based on a cladding-pumped Er–Yb co-doped fiber with 10 μm active single-mode core diameter. The laser source provides 3.4 W average output power at 75 MHz repetition rate. The pulses are compressed to 765 fs by a low-loss transmission grating pair. The robust, compact, and high-power 1560 nm fiber laser source can be used for eye surgery and solar cell micromachining.展开更多
The authors would like to apologize for some mistakes in the article and wish to make the corrections described below：1） Designate Youjian Song （宋有建） as the corresponding author of this article. His Email addre...The authors would like to apologize for some mistakes in the article and wish to make the corrections described below：1） Designate Youjian Song （宋有建） as the corresponding author of this article. His Email address is yjsong^tju.edu.cn.展开更多
基金Project supported by National Natural Science Foundation of China(51261001)
文摘The structure and magnetocaloric properties of La1–xCexFe11.44Si1.56 and their hydrides La1–xCexFe11.44Si1.56Hy（x=0, 0.1, 0.2, 0.3, 0.4） were investigated.The samples crystallized mainly in the cubic Na Zn13-type structure with a small amount of α-Fe phase as impurity.The lattice constants and Curie temperature presented the same change tendency with increasing of Ce content.For the hydrides, the influence of Ce content on lattice constants was weakened and the values of H concentration y were approximate to be 1.56.The La1–xCexFe11.44Si1.56 compounds exhibited large values of isothermal entropy change –ΔSm around the Curie temperature TC under a low magnetic field change of 1.5 T.The value of –ΔSm increased and then decreased with increasing Ce content, reached the maximum, 26.07 J/kg·K for x=0.3.TC increased up to the vicinity of room temperature by hydrogen absorption for the Ce substituted compounds, but TC only slightly decreased with increasing Ce content.The first-order metamagnetic transition was still kept in the hydrides and the maximum values of –ΔSm were lower than those of the La1–xCexFe11.44Si1.56 compounds, but still remained large values, about 10.5 J/kg K under a magnetic field change of 1.5 T.The values of –ΔSm were nearly independent of the Ce content and did not increase with increasing x for the hydrides.The La1–xCexFe11.44Si1.56Hy（x=0–0.4） hydrides exhibited large magnetic entropy changes, small hysteresis loss and effective refrigerant capacity covered the room temperature range from 305 to 317 K.These hydrides are very useful for the magnetic refrigeration applications near room temperature under low magnetic field change.
基金supported by the National Basic Research Program of China(Nos.2011CB808101 and 2010CB327604)the National High Technology Research and Development Program of China(No.2013AA122602)+2 种基金the National Natural Science Foundation of China(Nos.61322502,and 61227010,61205131,and 11274239)the Specialized Research Fund for the Doctoral Program of Higher Education of China(No.20120032120071)the Tianjin Research Program of Application Foundation and Advanced Technology(No.13JCQNJC01400)
文摘We demonstrate an all-fiber, high-power, and high stability ultrafast laser source operating at 1563 nm. A highly stable, self-starting carbon nanotube（CNT） mode-locked femtosecond fiber laser is used as the seed source. The amplifier stage uses a fiber chirped pulse amplification configuration. The main power amplifier is based on a cladding-pumped Er–Yb co-doped fiber with 10 μm active single-mode core diameter. The laser source provides 3.4 W average output power at 75 MHz repetition rate. The pulses are compressed to 765 fs by a low-loss transmission grating pair. The robust, compact, and high-power 1560 nm fiber laser source can be used for eye surgery and solar cell micromachining.
文摘The authors would like to apologize for some mistakes in the article and wish to make the corrections described below：1） Designate Youjian Song （宋有建） as the corresponding author of this article. His Email address is yjsong^tju.edu.cn.