The corrosion behaviors of Sn-0.75Cu solder and Sn-0.75Cu/Cu joint in 3.5% NaCl（mass fraction） solution were studied by potentiodynamic polarization test and leaching measurement.The polarization curves indicated th...The corrosion behaviors of Sn-0.75Cu solder and Sn-0.75Cu/Cu joint in 3.5% NaCl（mass fraction） solution were studied by potentiodynamic polarization test and leaching measurement.The polarization curves indicated that the corrosion rate of Sn-0.75Cu solder was lower than that of Sn-0.75Cu/Cu joint.The morphology observation and phase composition analysis on the corroded product at each interesting potential suggested that Sn3O（OH）2Cl2 formed on the surface of Sn-0.75Cu solder at active dissolution stage.As the potential increased from active/passive transition stage,all the surface of Sn-0.75Cu solder was covered by the Sn3O（OH）2Cl2 and some pits appeared after the polarization test.Compared to the Sn-0.75Cu solder alloy,much more Sn3O（OH）2Cl2 formed at active dissolution stage and the pits with bigger size were observed after polarization test for the Sn-0.75Cu/Cu solder joints.The leaching test confirmed that the faster electrochemical corrosion rate resulted in the larger amount of Sn released from the Sn-0.75Cu/Cu solder joints.展开更多
基金Project (2005DKA10400-Z23) supported by Chinese National Science and Technology InfrastructureProject (DUT10R:(3)65) supported by Fundamental Research Funds for the Central Universities,China
文摘The corrosion behaviors of Sn-0.75Cu solder and Sn-0.75Cu/Cu joint in 3.5% NaCl（mass fraction） solution were studied by potentiodynamic polarization test and leaching measurement.The polarization curves indicated that the corrosion rate of Sn-0.75Cu solder was lower than that of Sn-0.75Cu/Cu joint.The morphology observation and phase composition analysis on the corroded product at each interesting potential suggested that Sn3O（OH）2Cl2 formed on the surface of Sn-0.75Cu solder at active dissolution stage.As the potential increased from active/passive transition stage,all the surface of Sn-0.75Cu solder was covered by the Sn3O（OH）2Cl2 and some pits appeared after the polarization test.Compared to the Sn-0.75Cu solder alloy,much more Sn3O（OH）2Cl2 formed at active dissolution stage and the pits with bigger size were observed after polarization test for the Sn-0.75Cu/Cu solder joints.The leaching test confirmed that the faster electrochemical corrosion rate resulted in the larger amount of Sn released from the Sn-0.75Cu/Cu solder joints.