Ultra-high nickel material is considered to be a promising cathode material.However,with the increase of nickel content,the interfacial side reactions between the cathode and electrolyte become increasingly serious.He...Ultra-high nickel material is considered to be a promising cathode material.However,with the increase of nickel content,the interfacial side reactions between the cathode and electrolyte become increasingly serious.Herein,an atomically controllable ionic conductor Li_(3)PO_(4)(LPO)coating is deposited on the LiNi_(0.90)Co_(0.06)Mn_(0.04)O_(2)(NCM9064)based electrode by the atomic layer deposition method.The results shows that the LPO coating is uniformly and densely covered on the surface of secondary particles of NCM9064,helping to prevent the direct contact between the electrolyte and cathode during the chargingdischarging process.In addition,the coating layer is electrochemically stable.As a result,the interfacial side reactions during the long cycle are effectively suppressed,and the solid electrolyte interphase layer at the interface is stabilized.The electrode with 20 layers of LPO deposition(ALD-LPO-20)exhibits an excellent capacity retention of 81%after 200 cycles in 2.8-4.3 V at 25℃,which is 18%higher than the unmodified material(ALD-LPO-0).Besides,the moderate LPO coating improves the rate capability and high temperature cycling performance of NCM9064.This study provides a method for the modification of ultra-high nickel cathode materials and corresponding electrodes.展开更多
Thick-film thermistor with negative temperature coefficient（NTC）, low room-temperature resistivity and modest thermistor constant was screen-printed on the alumina substrate by the combination of 30.94III0.04II0.02 ...Thick-film thermistor with negative temperature coefficient（NTC）, low room-temperature resistivity and modest thermistor constant was screen-printed on the alumina substrate by the combination of 30.94III0.04II0.02 B OBi Coa Co with Ba0.5Bi0.5Fe0.9Sn0.1O3. The electrical properties of the thick films were characterized by a digital multimeter, a Keithley 2400 and an impedance analyzer. The results show that with the Ba0.5Bi0.5Fe0.9Sn0.1O3 content increasing from 0.05 to 0.25, the values of room-temperature resistivity, thermistor constant and peak voltage of the thick films increases and are in the ranges of 1.47-26.5 ？·cm, 678-1345 K and 18.9-47.0 V, respectively. The corresponding current at the peak voltage of the thick films decreases and is in the range of 40-240 m A. The impedance spectroscopy measurement demonstrates that the as-prepared thick films show the abnormal electrical heterogeneous microstructure, consisting of high-resistive grains and less resistive grain boundary regions. It can be concluded that the addition of Ba0.5Bi0.5Fe0.9Sn0.1O3 into 30.94III0.04II0.02 Ba Co OBi Co improves the thermistor behavior and but also deteriorates the current characteristics.展开更多
基金supported by the National Natural Science Foundation of China(No.52174285)the Science and Technology Innovation Program of Hunan Province(No.2022RC3048)+1 种基金the Key Research and Development Program of Yunnan Province(No.202103AA080019)the Research Foundation of Education Bureau of Hunan Province(No.18B477).
文摘Ultra-high nickel material is considered to be a promising cathode material.However,with the increase of nickel content,the interfacial side reactions between the cathode and electrolyte become increasingly serious.Herein,an atomically controllable ionic conductor Li_(3)PO_(4)(LPO)coating is deposited on the LiNi_(0.90)Co_(0.06)Mn_(0.04)O_(2)(NCM9064)based electrode by the atomic layer deposition method.The results shows that the LPO coating is uniformly and densely covered on the surface of secondary particles of NCM9064,helping to prevent the direct contact between the electrolyte and cathode during the chargingdischarging process.In addition,the coating layer is electrochemically stable.As a result,the interfacial side reactions during the long cycle are effectively suppressed,and the solid electrolyte interphase layer at the interface is stabilized.The electrode with 20 layers of LPO deposition(ALD-LPO-20)exhibits an excellent capacity retention of 81%after 200 cycles in 2.8-4.3 V at 25℃,which is 18%higher than the unmodified material(ALD-LPO-0).Besides,the moderate LPO coating improves the rate capability and high temperature cycling performance of NCM9064.This study provides a method for the modification of ultra-high nickel cathode materials and corresponding electrodes.
基金Projects(5110205551462005)supported by the National Natural Science Foundation of China
文摘Thick-film thermistor with negative temperature coefficient（NTC）, low room-temperature resistivity and modest thermistor constant was screen-printed on the alumina substrate by the combination of 30.94III0.04II0.02 B OBi Coa Co with Ba0.5Bi0.5Fe0.9Sn0.1O3. The electrical properties of the thick films were characterized by a digital multimeter, a Keithley 2400 and an impedance analyzer. The results show that with the Ba0.5Bi0.5Fe0.9Sn0.1O3 content increasing from 0.05 to 0.25, the values of room-temperature resistivity, thermistor constant and peak voltage of the thick films increases and are in the ranges of 1.47-26.5 ？·cm, 678-1345 K and 18.9-47.0 V, respectively. The corresponding current at the peak voltage of the thick films decreases and is in the range of 40-240 m A. The impedance spectroscopy measurement demonstrates that the as-prepared thick films show the abnormal electrical heterogeneous microstructure, consisting of high-resistive grains and less resistive grain boundary regions. It can be concluded that the addition of Ba0.5Bi0.5Fe0.9Sn0.1O3 into 30.94III0.04II0.02 Ba Co OBi Co improves the thermistor behavior and but also deteriorates the current characteristics.