In the present work,TiAlN coatings were deposited on Ti(C,N)-based cermet substrates by physical vapor deposition method.Emphasis was focused on the influence of grain size of cermet substrates on the microstructure,g...In the present work,TiAlN coatings were deposited on Ti(C,N)-based cermet substrates by physical vapor deposition method.Emphasis was focused on the influence of grain size of cermet substrates on the microstructure,growth behavior,mechanical properties,adhesion strength and wear behavior of the coatings.The results show that finer Ti(C,N)grain size leads to higher nucleation density and lower growth rate of coatings,indicating the crystallite size of the TiAlN coatings decreases with decreasing Ti(C,N)grain size.Nanoindentation tests show that the coatings deposited on cermets of the finest grain size exhibit the highest hardness(H),elastic modulus(E),H/E and H3/E2 of 34.5 GPa,433.2 GPa,0.080 and 0.22,respectively.The adhesion strength between coating and substrate is also enhanced with decreasing Ti(C,N)grain size by scratch test,which corresponds to the grain size and H/E and H3/E2 of the coating.Besides,the lower surface roughness and better mechanical properties of the coating deposited on finer grained cermet contribute to the better wear resistance of the coating.展开更多
The fast densification method of combustion reaction plus quick pressing was adopted to prepare nanocrystalline ceramics.The densification process of magnesia compact with a particle size of 100 nm was investigated,un...The fast densification method of combustion reaction plus quick pressing was adopted to prepare nanocrystalline ceramics.The densification process of magnesia compact with a particle size of 100 nm was investigated,under the applied pressure of up to 170 MPa,and the temperature range of 1740–2080 K with ultra-high heating rate(above 1700 K/min).High-purity magnesia ceramics with a relative density of 98.8%and an average grain size of 120 nm was obtained at 1740 K,and the grain growth during the densification process was effectively restrained.The characteristic morphology of evaporation-condensation was observed in the compact prepared at 2080 K,which revealed the actual process of mass transfer by gas diffusion.Moreover,the investigation on the microstructure evolution and mechanism of grain growth was carried out,on the basis of as-preserved nanocrystalline ceramics.The result indicated that the grain growth of the nanocrystalline MgO was controlled by the mechanism of evaporation-condensation rather than surface diffusion.Furthermore,the pressure had an influence of restraining the grain growth based on solid diffusion and strengthening the effect of gas diffusion with the increasing temperature.Under the particular conditions,there existed an appropriate temperature for the densification of nanocrystalline magnesia,while the excessive temperature would exaggerate grain growth and impede densification.展开更多
Microcontact measurement is employed to locally investigate the electric and dielectric properties of individual grains and grain boundaries in CaCu3Ti4O12 ceramic. The measurements give more detail of the impedance s...Microcontact measurement is employed to locally investigate the electric and dielectric properties of individual grains and grain boundaries in CaCu3Ti4O12 ceramic. The measurements give more detail of the impedance spectroscopy, capacitance, and I-V characteristics of the microstructure, and will help with further understanding of the mechanism of the electric and dielectric properties of CaCu3Ti4O12 ceramics.展开更多
基金Projects(51634006,51575368)supported by the National Natural Science Foundation of ChinaProject(2017GZ0041)supported by Science and Technology Support Program of Sichuan Province,China。
文摘In the present work,TiAlN coatings were deposited on Ti(C,N)-based cermet substrates by physical vapor deposition method.Emphasis was focused on the influence of grain size of cermet substrates on the microstructure,growth behavior,mechanical properties,adhesion strength and wear behavior of the coatings.The results show that finer Ti(C,N)grain size leads to higher nucleation density and lower growth rate of coatings,indicating the crystallite size of the TiAlN coatings decreases with decreasing Ti(C,N)grain size.Nanoindentation tests show that the coatings deposited on cermets of the finest grain size exhibit the highest hardness(H),elastic modulus(E),H/E and H3/E2 of 34.5 GPa,433.2 GPa,0.080 and 0.22,respectively.The adhesion strength between coating and substrate is also enhanced with decreasing Ti(C,N)grain size by scratch test,which corresponds to the grain size and H/E and H3/E2 of the coating.Besides,the lower surface roughness and better mechanical properties of the coating deposited on finer grained cermet contribute to the better wear resistance of the coating.
基金supported by the Ministry of Science and Technology of China(Grant No.S2010GR0771)the National Natural Science Foundation of China(Grant No.51161140399)
文摘The fast densification method of combustion reaction plus quick pressing was adopted to prepare nanocrystalline ceramics.The densification process of magnesia compact with a particle size of 100 nm was investigated,under the applied pressure of up to 170 MPa,and the temperature range of 1740–2080 K with ultra-high heating rate(above 1700 K/min).High-purity magnesia ceramics with a relative density of 98.8%and an average grain size of 120 nm was obtained at 1740 K,and the grain growth during the densification process was effectively restrained.The characteristic morphology of evaporation-condensation was observed in the compact prepared at 2080 K,which revealed the actual process of mass transfer by gas diffusion.Moreover,the investigation on the microstructure evolution and mechanism of grain growth was carried out,on the basis of as-preserved nanocrystalline ceramics.The result indicated that the grain growth of the nanocrystalline MgO was controlled by the mechanism of evaporation-condensation rather than surface diffusion.Furthermore,the pressure had an influence of restraining the grain growth based on solid diffusion and strengthening the effect of gas diffusion with the increasing temperature.Under the particular conditions,there existed an appropriate temperature for the densification of nanocrystalline magnesia,while the excessive temperature would exaggerate grain growth and impede densification.
基金supported by the National Nature Science Foundation of China (Grant Nos.50425721,50677029 and 50737001)
文摘Microcontact measurement is employed to locally investigate the electric and dielectric properties of individual grains and grain boundaries in CaCu3Ti4O12 ceramic. The measurements give more detail of the impedance spectroscopy, capacitance, and I-V characteristics of the microstructure, and will help with further understanding of the mechanism of the electric and dielectric properties of CaCu3Ti4O12 ceramics.