To explain the precipitation mechanism ofχphase in Co-based superalloys,the microstructural evolution of Co−Ti−Mo superalloys subjected to aging was investigated by X-ray diffraction(XRD),scanning electron microscope...To explain the precipitation mechanism ofχphase in Co-based superalloys,the microstructural evolution of Co−Ti−Mo superalloys subjected to aging was investigated by X-ray diffraction(XRD),scanning electron microscope(SEM)and transmission electron microscope(TEM).The results show that the needle-likeχphase is mainly composed ofD0_(19)-Co_(3)(Ti,Mo),which is transformed from L1_(2-γ′)phase,and a specific orientation relationship exists between them.χphase is nucleated through the shearing ofγ′phase due to the influence of stacking fault.The crystal orientation relationship between L1_(2) andD0_(19)can be confirmed as{111}L1_(2)//{0001}_(D0_(19)),and<112>_(L1_(2))//<1100>_(D0_(19)).The growth ofD0_(19-χ)phase depends on the diffusions of Ti and Mo,and consumes a large number of elements.This progress leads to the appearance ofγ′precipitation depletion zone(PDZ)aroundD0_(19-χ)phase.The addition of Ni improves the stability of L1_(2-γ′)phase and the mechanical properties of Co-based superalloys.展开更多
基金The financial supports from the National Natural Science Foundation of China(Nos.52171107,52201203)the National Natural Science Foundation of China-Joint Fund of Iron and Steel Research(No.U1960204)the“333”Talent Project of Hebei Province,China(No.B20221001)are gratefully acknowledged.
文摘To explain the precipitation mechanism ofχphase in Co-based superalloys,the microstructural evolution of Co−Ti−Mo superalloys subjected to aging was investigated by X-ray diffraction(XRD),scanning electron microscope(SEM)and transmission electron microscope(TEM).The results show that the needle-likeχphase is mainly composed ofD0_(19)-Co_(3)(Ti,Mo),which is transformed from L1_(2-γ′)phase,and a specific orientation relationship exists between them.χphase is nucleated through the shearing ofγ′phase due to the influence of stacking fault.The crystal orientation relationship between L1_(2) andD0_(19)can be confirmed as{111}L1_(2)//{0001}_(D0_(19)),and<112>_(L1_(2))//<1100>_(D0_(19)).The growth ofD0_(19-χ)phase depends on the diffusions of Ti and Mo,and consumes a large number of elements.This progress leads to the appearance ofγ′precipitation depletion zone(PDZ)aroundD0_(19-χ)phase.The addition of Ni improves the stability of L1_(2-γ′)phase and the mechanical properties of Co-based superalloys.