The β-SiC/SiO2 core-shell nanowires with the 'stem-and-node' structure were synthesized in the presence of cerium oxide by the carbothermal reduction of the starch-SiO2 hybrids gel.The samples were characteri...The β-SiC/SiO2 core-shell nanowires with the 'stem-and-node' structure were synthesized in the presence of cerium oxide by the carbothermal reduction of the starch-SiO2 hybrids gel.The samples were characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),high-resolution transmission electron microscopy(HRTEM) and energy-dispersed X-ray(EDX).The results showed that the nanowires consisted of a 20-35 nm diameter crystalline β-SiC core wrapped with a 2-5 n...展开更多
A multi-component diffusion coating has been developed to protect Mo-based alloys from high temperature environmental attack. Aluminum addition was made during the coating process to improve the oxidation resistance b...A multi-component diffusion coating has been developed to protect Mo-based alloys from high temperature environmental attack. Aluminum addition was made during the coating process to improve the oxidation resistance by developing hexagonal Mo(Si, Al)2 through the development of the halide activated pack cementation coating process on pure Mo substrate. The results show that Mo(Si, Al)2 formed as a main phase on the surface and a little amount of Mo5Si3 also formed. The total thickness of coating is tens ofμm at 1373K. During the cyclic oxidation test at high temperature(at about 1323K in air), mullite (3Al2O3.2SiO2) and some SiO2 formed. The addition of Al is beneficial for MoSi2 coating and the Al-doped coating exhibited only a small weight gain and protected the Mo substrate, while the MoSi2 coating without Al suffered a significant weight loss, indicating a loss of volatile MoO3 after cycles.展开更多
基金supported by the National Key Technology R&D Program (2007BEA08B01)the Natural Science Foundation of Fujian Province of China (E0710004)Joint Research Program of Fuzhou University (DH-548)
文摘The β-SiC/SiO2 core-shell nanowires with the 'stem-and-node' structure were synthesized in the presence of cerium oxide by the carbothermal reduction of the starch-SiO2 hybrids gel.The samples were characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),high-resolution transmission electron microscopy(HRTEM) and energy-dispersed X-ray(EDX).The results showed that the nanowires consisted of a 20-35 nm diameter crystalline β-SiC core wrapped with a 2-5 n...
文摘A multi-component diffusion coating has been developed to protect Mo-based alloys from high temperature environmental attack. Aluminum addition was made during the coating process to improve the oxidation resistance by developing hexagonal Mo(Si, Al)2 through the development of the halide activated pack cementation coating process on pure Mo substrate. The results show that Mo(Si, Al)2 formed as a main phase on the surface and a little amount of Mo5Si3 also formed. The total thickness of coating is tens ofμm at 1373K. During the cyclic oxidation test at high temperature(at about 1323K in air), mullite (3Al2O3.2SiO2) and some SiO2 formed. The addition of Al is beneficial for MoSi2 coating and the Al-doped coating exhibited only a small weight gain and protected the Mo substrate, while the MoSi2 coating without Al suffered a significant weight loss, indicating a loss of volatile MoO3 after cycles.