A yield phenomenon was firstly reported in an extruded Mg-6.8Y-2.5Cu alloy and the corresponding microstructure was also investigated in this work,The cast alloy is mainly composed ofα-Mg,18R long period stacking ord...A yield phenomenon was firstly reported in an extruded Mg-6.8Y-2.5Cu alloy and the corresponding microstructure was also investigated in this work,The cast alloy is mainly composed ofα-Mg,18R long period stacking order(LPSO)phase,eutectic phase(Mg_(20)Cu_(4)Y_(1)),and Mg_(2)Cu phase.The 18R LPSO phase at the dendritic grain boundary transforms into the 14H LPSO phase in the grain interior during homogenization.After extrusion,the grain size of the homogenized alloy is remarkably refined to-3.69μm and the second phase is significantly broken and distributed in the extrusion direction.Tensile testing curves of the extrude alloy at room temperature indicate that the yield strength and ultimate tensile strength increase while the elongation of the alloy decreases with increasing strain rate.Interestingly,a yield plateau fo rms and gradually decreases with increasing strain rate.The yield phenomenon is related to the dislocation multiplication and the interaction between the movable dislocations and solute atoms.展开更多
Mechanical properties of Mg-3Gd(wt.%)samples with average grain sizes ranging from 3 to 45μm were characterized by room temperature tensile test.A reversal of the trade-off,i.e.,high yield strength and large tensile ...Mechanical properties of Mg-3Gd(wt.%)samples with average grain sizes ranging from 3 to 45μm were characterized by room temperature tensile test.A reversal of the trade-off,i.e.,high yield strength and large tensile elongation,was simultaneously observed in the fine-grained samples.The microstructures and hardening response were analyzed in terms of the viewpoint of strain evolution,including local strain evolution by tensile digital image correlation strain measurement,and lattice strain by using synchrotronbased in-situ high energy X-ray diffraction technique.The dislocation-based deformation mechanisms were investigated to underpin the microstructural origin of the yield point phenomenon and enhancement in work-hardening.The occurrence of the yield point phenomenon represented by a yield drop and propagation of the Lüders band is related to the absence of mobile dislocations at an early stage and to the slip transmission between the adjacent grain.The extraordinary work-hardening enhancement over an extended range can be ascribed mainly to the increases in dislocation multiplication and accumulation capabilities by the activation and interaction of multiple slip systems includingand<c+a>types.These results contribute to the design of strong and ductile Mg alloys.展开更多
Fine-grained Mg-6Zn-4Y alloy was prepared by an ingot metallurgy process with hot extrusion at 300 ℃.The microstructure was studied by XRD,OM,SEM and TEM,and the tensile properties were tested at room temperature.The...Fine-grained Mg-6Zn-4Y alloy was prepared by an ingot metallurgy process with hot extrusion at 300 ℃.The microstructure was studied by XRD,OM,SEM and TEM,and the tensile properties were tested at room temperature.The results show that the alloy is composed of α-Mg and W-phase.The microstructure of the as-extruded alloy has a bimodal grain size distribution.The fine grains with the mean size of 1.2 μm are formed by dynamic recrystallization.The coarse grains（about 23% in area fraction） are unrecrystallized regions which are elongated along extrusion direction.The engineering stress—strain curve shows a pronounced yield point.The ultimate tensile strength,yield strength,and elongation are（371±10） MPa,（350±5） MPa and（7±2）%,respectively.The high strengths are attributed to the fine-grained matrix structure enhanced by W-phase particles,nano-scaled precipitates,and strong basal plane texture.展开更多
为扩大品种范围、提升产品竞争力,成渝钒钛科技有限公司决定在高线产线上开发φ6 mm HRB400E带肋钢筋盘条。设计了带肋钢筋盘条化学成分,通过控轧控冷工艺参数对热轧盘条组织性能影响的相关分析,制定了轧制工艺参数,并研究了不同风冷工...为扩大品种范围、提升产品竞争力,成渝钒钛科技有限公司决定在高线产线上开发φ6 mm HRB400E带肋钢筋盘条。设计了带肋钢筋盘条化学成分,通过控轧控冷工艺参数对热轧盘条组织性能影响的相关分析,制定了轧制工艺参数,并研究了不同风冷工艺对其组织性能的影响。结果表明,通过控轧控冷工艺的优化,可以稳定生产出φ6 mm热轧带肋钢筋盘条,盘条微观组织均匀,各项指标均符合国家标准对抗震钢筋的要求;轧后风冷速度对盘条组织性能的影响较大,当冷速过快时钢筋组织中会出现贝氏体,使钢筋出现无屈服平台现象,应采用适当冷速。展开更多
基金Project supported by the National Natural Science Foundation of China(51961021,52001152 and 51901174)China Postdoctoral Science Foundation(2020M673383)。
文摘A yield phenomenon was firstly reported in an extruded Mg-6.8Y-2.5Cu alloy and the corresponding microstructure was also investigated in this work,The cast alloy is mainly composed ofα-Mg,18R long period stacking order(LPSO)phase,eutectic phase(Mg_(20)Cu_(4)Y_(1)),and Mg_(2)Cu phase.The 18R LPSO phase at the dendritic grain boundary transforms into the 14H LPSO phase in the grain interior during homogenization.After extrusion,the grain size of the homogenized alloy is remarkably refined to-3.69μm and the second phase is significantly broken and distributed in the extrusion direction.Tensile testing curves of the extrude alloy at room temperature indicate that the yield strength and ultimate tensile strength increase while the elongation of the alloy decreases with increasing strain rate.Interestingly,a yield plateau fo rms and gradually decreases with increasing strain rate.The yield phenomenon is related to the dislocation multiplication and the interaction between the movable dislocations and solute atoms.
基金financially supported by the National Key Research and Develop-ment Program(No.2023YFB3712702)the National Natural Science Foundation of China(Nos.52071038,52071039,and 52301156)the Natural Science Foundation of Jiangsu Province(Nos.BK20232025 and BK20243005)。
文摘Mechanical properties of Mg-3Gd(wt.%)samples with average grain sizes ranging from 3 to 45μm were characterized by room temperature tensile test.A reversal of the trade-off,i.e.,high yield strength and large tensile elongation,was simultaneously observed in the fine-grained samples.The microstructures and hardening response were analyzed in terms of the viewpoint of strain evolution,including local strain evolution by tensile digital image correlation strain measurement,and lattice strain by using synchrotronbased in-situ high energy X-ray diffraction technique.The dislocation-based deformation mechanisms were investigated to underpin the microstructural origin of the yield point phenomenon and enhancement in work-hardening.The occurrence of the yield point phenomenon represented by a yield drop and propagation of the Lüders band is related to the absence of mobile dislocations at an early stage and to the slip transmission between the adjacent grain.The extraordinary work-hardening enhancement over an extended range can be ascribed mainly to the increases in dislocation multiplication and accumulation capabilities by the activation and interaction of multiple slip systems includingand<c+a>types.These results contribute to the design of strong and ductile Mg alloys.
基金Project (50271054) supported by the National Natural Science Foundation of ChinaProject (20070700003) supported by the Doctorate Programs Foundation of Ministry of Education of China+1 种基金Project (102102210031) supported by the Science and Technologies Foundation of Henan Province, ChinaProject (2010A430008) supported by the Natural Science Foundation of Henan Educational Committee of China
文摘Fine-grained Mg-6Zn-4Y alloy was prepared by an ingot metallurgy process with hot extrusion at 300 ℃.The microstructure was studied by XRD,OM,SEM and TEM,and the tensile properties were tested at room temperature.The results show that the alloy is composed of α-Mg and W-phase.The microstructure of the as-extruded alloy has a bimodal grain size distribution.The fine grains with the mean size of 1.2 μm are formed by dynamic recrystallization.The coarse grains（about 23% in area fraction） are unrecrystallized regions which are elongated along extrusion direction.The engineering stress—strain curve shows a pronounced yield point.The ultimate tensile strength,yield strength,and elongation are（371±10） MPa,（350±5） MPa and（7±2）%,respectively.The high strengths are attributed to the fine-grained matrix structure enhanced by W-phase particles,nano-scaled precipitates,and strong basal plane texture.
文摘为扩大品种范围、提升产品竞争力,成渝钒钛科技有限公司决定在高线产线上开发φ6 mm HRB400E带肋钢筋盘条。设计了带肋钢筋盘条化学成分,通过控轧控冷工艺参数对热轧盘条组织性能影响的相关分析,制定了轧制工艺参数,并研究了不同风冷工艺对其组织性能的影响。结果表明,通过控轧控冷工艺的优化,可以稳定生产出φ6 mm热轧带肋钢筋盘条,盘条微观组织均匀,各项指标均符合国家标准对抗震钢筋的要求;轧后风冷速度对盘条组织性能的影响较大,当冷速过快时钢筋组织中会出现贝氏体,使钢筋出现无屈服平台现象,应采用适当冷速。