SiO2 coated Ce2S3 red pigment was prepared in ethanol/H2O system via sol-gel method and TEOS were used as silica sources. X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive spectroscopy...SiO2 coated Ce2S3 red pigment was prepared in ethanol/H2O system via sol-gel method and TEOS were used as silica sources. X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDX）, UV-visible spectro-photometer and automatic colorimeter were used to investigate the properties of the samples. The results showed that the compact SiO2 film formed on the surface of Ce2S3 pigment at a cerium silicon molar ratio of 2. The thermal stability temperature of Ce2S3 pigment was improved to 450 oC after SiO2 coating. In addition, the color of Ce2S3 pigment was not affected significantly through coating colorless and transparent SiO2 and it could be used as safe red pigment in higher temperature fields.展开更多
基金Project supported by National Science and Technology Support Program(2011BAE30B03)Special Fund from Shaanxi Provincial Department of Education(12JK0467the Graduate Innovation Fund of Shaanxi Universityof Science and Technology for the financial support
文摘SiO2 coated Ce2S3 red pigment was prepared in ethanol/H2O system via sol-gel method and TEOS were used as silica sources. X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDX）, UV-visible spectro-photometer and automatic colorimeter were used to investigate the properties of the samples. The results showed that the compact SiO2 film formed on the surface of Ce2S3 pigment at a cerium silicon molar ratio of 2. The thermal stability temperature of Ce2S3 pigment was improved to 450 oC after SiO2 coating. In addition, the color of Ce2S3 pigment was not affected significantly through coating colorless and transparent SiO2 and it could be used as safe red pigment in higher temperature fields.