A recrystallization and partial melting(RAP) process was introduced to prepare the semi-solid 7075 aluminum alloy used for thixoforming. In order to obtain an ideal semi-solid microstructure, a series of extrusion exp...A recrystallization and partial melting(RAP) process was introduced to prepare the semi-solid 7075 aluminum alloy used for thixoforming. In order to obtain an ideal semi-solid microstructure, a series of extrusion experiments were conducted to comparatively investigate the optimum extrusion process parameters. Commercial 7075 Al alloy samples were firstly extruded with varying extrusion ratios below the recrystallization temperature followed by homogenization, then these samples were reheated to the semi-solid state and held in the range of 5 to 50 minutes. The experimental results show that varying process cause the difference in the deformation degree and microstructure for as-extruded samples, resulting in various semi-solid microstructure. It is verified that the formation of equiaxed grains in semi-solid microstructure depends on recrystallization behavior of extruded samples during partial melting. Both relative high extrusion temperature and low extrusion ratio lead to high volume fraction of recrystallized area, thus entirely equiaxed solid grains in semi-solid 7075 Al alloy samples can be obtained finally. In addition, Ostwald ripening was determined as the dominate coarsening mechanism of solid grains in semi-solid state for this 7075 Al alloy during the RAP route. The influence of predeformation on recrystallization behavior of this 7075 Al alloy was discussed in detail.展开更多
This paper have made a systematic study of the superconducting Bi-2212 phase transition temperature, which has a transition temperature (Tc) around 80-93 K, and depends on precise control of synthesis conditions, main...This paper have made a systematic study of the superconducting Bi-2212 phase transition temperature, which has a transition temperature (Tc) around 80-93 K, and depends on precise control of synthesis conditions, mainly including heat treatment parameters, oxygen partial pressure, and annealing temperature. Partial melting of the sample during preparation helps to raise its Tc. To elucidate the origin of this strong effect, the samples were heated with different melting process. The rapid changes in Tc value are associated with small changes in oxygen content, which depends on the annealing temperature and the oxygen partial pressure. We have optimized the above mentioned parameters for Bi-2212 film, and Tconset was improved to 93 K.展开更多
基金Funded by the National Natural Science Foundation of China(Nos.51774054 and 51974050)
文摘A recrystallization and partial melting(RAP) process was introduced to prepare the semi-solid 7075 aluminum alloy used for thixoforming. In order to obtain an ideal semi-solid microstructure, a series of extrusion experiments were conducted to comparatively investigate the optimum extrusion process parameters. Commercial 7075 Al alloy samples were firstly extruded with varying extrusion ratios below the recrystallization temperature followed by homogenization, then these samples were reheated to the semi-solid state and held in the range of 5 to 50 minutes. The experimental results show that varying process cause the difference in the deformation degree and microstructure for as-extruded samples, resulting in various semi-solid microstructure. It is verified that the formation of equiaxed grains in semi-solid microstructure depends on recrystallization behavior of extruded samples during partial melting. Both relative high extrusion temperature and low extrusion ratio lead to high volume fraction of recrystallized area, thus entirely equiaxed solid grains in semi-solid 7075 Al alloy samples can be obtained finally. In addition, Ostwald ripening was determined as the dominate coarsening mechanism of solid grains in semi-solid state for this 7075 Al alloy during the RAP route. The influence of predeformation on recrystallization behavior of this 7075 Al alloy was discussed in detail.
基金National Key Basic Research Program of China("973"Program)(2011CBA00104)the International Scientific and Technological Cooperation Projects of China(S2010GR0518)the National Natural Science Foundation of China(51102198)
文摘This paper have made a systematic study of the superconducting Bi-2212 phase transition temperature, which has a transition temperature (Tc) around 80-93 K, and depends on precise control of synthesis conditions, mainly including heat treatment parameters, oxygen partial pressure, and annealing temperature. Partial melting of the sample during preparation helps to raise its Tc. To elucidate the origin of this strong effect, the samples were heated with different melting process. The rapid changes in Tc value are associated with small changes in oxygen content, which depends on the annealing temperature and the oxygen partial pressure. We have optimized the above mentioned parameters for Bi-2212 film, and Tconset was improved to 93 K.