CO2 laser quick assembly technology is adopted on the surface of cast aluminum ZL104 to form a dense ceramic coating containing a great deal of nanometer Al2O3/TiO2 particles which eliminate cracks and porosities.The ...CO2 laser quick assembly technology is adopted on the surface of cast aluminum ZL104 to form a dense ceramic coating containing a great deal of nanometer Al2O3/TiO2 particles which eliminate cracks and porosities.The major phases of the coating are α-Al2O3 andβ-TiO2. The micro-hardness distribution of the coating is 1 813,1 504, 1 485 and 1 232 (HV0.05). The bonding strength of the coating LC1 is 11.4 N, which is 7.26 times higher than that of the conventional hot-spraying Al2O3/TiO2 coating. It has been proved by analysis that the bonding strength is achieved because of the effects of both super-quick laser consolidation and the nanometer effect of nanometer ceramic material.展开更多
The ceramic coating technology of microarc oxidation (MAO) was utilized to modify surface properties of the movable endplate of a high pressure gear pump used in water-hydraulic system, which is made of aluminium allo...The ceramic coating technology of microarc oxidation (MAO) was utilized to modify surface properties of the movable endplate of a high pressure gear pump used in water-hydraulic system, which is made of aluminium alloy. A coMPact ceramic layer of more than 130 μm was developed on the movable endplate with the hardness up to HV1000 by means of microarc oxidation. A trial of tests conducted in a water power transmission system show that the maximum outlet pressure of the gear pump with the movable endplate treated by microarc oxidation, can reach 16 MPa. It is pointed out that the ceramic coating developed by microarc oxidation technology on the surface of aluminium alloy, is economical and feasible.展开更多
文摘CO2 laser quick assembly technology is adopted on the surface of cast aluminum ZL104 to form a dense ceramic coating containing a great deal of nanometer Al2O3/TiO2 particles which eliminate cracks and porosities.The major phases of the coating are α-Al2O3 andβ-TiO2. The micro-hardness distribution of the coating is 1 813,1 504, 1 485 and 1 232 (HV0.05). The bonding strength of the coating LC1 is 11.4 N, which is 7.26 times higher than that of the conventional hot-spraying Al2O3/TiO2 coating. It has been proved by analysis that the bonding strength is achieved because of the effects of both super-quick laser consolidation and the nanometer effect of nanometer ceramic material.
基金Sponsored by the National Natural Science Foundation of China(Grant No.60772077)
文摘The ceramic coating technology of microarc oxidation (MAO) was utilized to modify surface properties of the movable endplate of a high pressure gear pump used in water-hydraulic system, which is made of aluminium alloy. A coMPact ceramic layer of more than 130 μm was developed on the movable endplate with the hardness up to HV1000 by means of microarc oxidation. A trial of tests conducted in a water power transmission system show that the maximum outlet pressure of the gear pump with the movable endplate treated by microarc oxidation, can reach 16 MPa. It is pointed out that the ceramic coating developed by microarc oxidation technology on the surface of aluminium alloy, is economical and feasible.