The microstructure and mechanical properties of Mg94Zn2Y4 extruded alloy containing long-period stacking ordered structures were systematically investigated by SEM and TEM analyses. The results show that the 18R-LPSO ...The microstructure and mechanical properties of Mg94Zn2Y4 extruded alloy containing long-period stacking ordered structures were systematically investigated by SEM and TEM analyses. The results show that the 18R-LPSO structure and α-Mg phase are observed in cast Mg94Zn2Y4 alloy. After extrusion, the LPSO structures are delaminated and Mg-slices with width of 50-200 nm are generated. By ageing at 498 K for 36 h, the ageing peak is attained andβ′phase is precipitated. Due to this novel precipitation, the microhardness ofα-Mg matrix increases apparently from HV108.9 to HV129.7. While the microhardness for LPSO structure is stabilized at about HV145. TEM observations and SAED patterns indicate that the β′ phase has unique orientation relationships betweenα-Mg and LPSO structures, the direction in the close-packed planes ofβ′precipitates perpendicular to that ofα-Mg and LPSO structures. The ultimate tensile strength for the peak-aged alloy achieves 410.7 MPa and the significant strength originates from the coexistence ofβ′precipitates and 18R-LPSO structures.展开更多
14H, 18R and 24R long-period stacking ordered （LPSO） structures were observed in the as-cast Mg-3Cu-1Mn-2Zn-1Y damping alloy using transmission electron microscopy （TEM）. These LPSO structures contained Mg, Y, Cu ...14H, 18R and 24R long-period stacking ordered （LPSO） structures were observed in the as-cast Mg-3Cu-1Mn-2Zn-1Y damping alloy using transmission electron microscopy （TEM）. These LPSO structures contained Mg, Y, Cu and Zn and thus they were quaternary phases. Sharp diffraction pattern of the 24R structure was obtained and the angle between and g10024R was measured to be 5.03°. During high resolution TEM observations, lattice fringes with two characteristic spacings were observed within the 24R structure. Based on the experimental results, 6H, 7H and three 8H are suggested as the building blocks of 18R, 14H and 24R structures, respectively. The 24R unit cell can be interpreted as the stacking of 8H building blocks in the same shear direction with a shear angle of about 5.03°. The imperfect 24R structures are in order or disorder arrangements of principal 8H and minor 6H blocks. This double-block structure model is also applicable to other reported defects in LPSO structures.展开更多
Mg-Y-Zn alloys with long period stacking ordered(LPSO)structure have received much attention recently and exhibit great potential in applications such as automotive,aerospace and in bio-medical fields.This paper aimed...Mg-Y-Zn alloys with long period stacking ordered(LPSO)structure have received much attention recently and exhibit great potential in applications such as automotive,aerospace and in bio-medical fields.This paper aimed to investigate the effect of different phase constitution of LPSO structures on corrosion rate of bio-medical Mg-Y-Zn alloys.The results showed that as-cast Mg98.5Y1Zn0.5 alloys containing only 18R structure exhibited the highest corrosion resistance with the corrosion rate of 2.78 mm/year.The precipitation of 14H lamellas within a-Mg grains during solid solution treatment introduced the crystallographic orientation corrosion by accelerating micro-galvanic corrosion.The increase of 18R/14H interfaces deteriorated the corrosion resistance,and the grain boundaries also suffered from severe electrochemical dissolution.This work suggested that Mg-Y-Zn alloys with single LPSO structure(either 18R or 14H)exhibited better corrosion resistance than alloys with co-existence 18R and I4H LPSO structures.展开更多
Corrosion is one of the most drawbacks which restricts the wide applications of Mg alloys.In the last decade,the corrosion behaviors of Mg alloys with stacking fault(SF)and/or long period stacking ordered(LPSO)structu...Corrosion is one of the most drawbacks which restricts the wide applications of Mg alloys.In the last decade,the corrosion behaviors of Mg alloys with stacking fault(SF)and/or long period stacking ordered(LPSO)structures have obtained increasing attention.However,the corrosion mechanism of the SF–or LPSO–containing Mg alloys has not been well illustrated and even reverse results have been reported.In this paper,we have reviewed recent reports on corrosion behaviors of SF–or LPSO–containing Mg alloys to better clarify and understand the significance and mechanism.Moreover,some deficiencies are presented and advises are proposed for the development of corrosion resistant Mg alloys with SF or LPSO structures.展开更多
The microstructure of the precipitated phases of Mg95.sGd3Zn1Zro.2 alloys with long-period stacking ordered structure before and after heat treatment is discussed. The corrosion properties of the as-cast （F）, solid-...The microstructure of the precipitated phases of Mg95.sGd3Zn1Zro.2 alloys with long-period stacking ordered structure before and after heat treatment is discussed. The corrosion properties of the as-cast （F）, solid-solution （T4） and aging-treated （T6） alloys in 1% NaC1 solution are studied. The hydrogen evolution and electrochemical measurements display that the as-cast Mg95.sGd3Zn1Zro.2 alloy with the continuous network eutectic phase exhibits the greatest corrosion resistance, while T6 sample with some needle-like phases and the particle phases is the worst among the three alloys. It is proposed to be mainly related to the amount, composition, microstructure and distribution of the precipitated phases.展开更多
Both the solid solution and precipitation are mainly strengthening mechanism for the magnesium-based alloys. A great number of alloying elements can be dissolved into the Mg matrix to form the solutes and precipitates...Both the solid solution and precipitation are mainly strengthening mechanism for the magnesium-based alloys. A great number of alloying elements can be dissolved into the Mg matrix to form the solutes and precipitates.Moreover, the type of precipitates varies with different alloying elements and heat treatments, which makes it quite difficult to understand the formation mechanism of the precipitates in Mg-based alloys in depth. Thus, it is very hard to give a systematical regularity in precipitation process for the Mg-based alloys. This review is mainly focused on the formation and microstructural evolution of the precipitates, as a hot topic for the past few years, including Guinier-Preston Zones, quasicrystals and long-period stacking ordered phases formed in a number of Mg-TM-RE alloy systems, where TM = Al, Zn, Zr and RE = Y,Gd, Hd, Ce and La.展开更多
Alloys with composition of Mg_(96-x)Gd_3Zn_1Li_x(at.%)(x=0, 2, 4, and 6) were prepared by conventional casting. The microstructures of these alloys under as-cast and solid-solution conditions have been observed, and t...Alloys with composition of Mg_(96-x)Gd_3Zn_1Li_x(at.%)(x=0, 2, 4, and 6) were prepared by conventional casting. The microstructures of these alloys under as-cast and solid-solution conditions have been observed, and the mechanical properties were investigated. The results showed that Li is an effective element to refine the grains and break the eutectic networks in as-cast MgGd_3Zn_1 alloy. During solid solution treatment, these broken eutectic networks are spheroidized and highly dispersed. In addition, plentiful lamellar long period stacking ordered(LPSO) phases are precipitated in an α-Mg matrix when the Li addition is not more than 4%. Solid-solution treated Mg_(92)Gd_3Zn_1Li_4 alloy exhibits an optimal ultimate tensile strength(UTS) of 226 MPa and elongation of 5.8%. The strength of MgGd_3Zn_1 alloy is improved significantly, meanwhile, the toughness is apparently increased.展开更多
Mg-Zn-Y alloys with long-period stacking ordered structures were prepared by an ingot casting method. The corrosion performance of Mg-Zn-Y alloys was studied by combining gas-collecting test, immersion test and electr...Mg-Zn-Y alloys with long-period stacking ordered structures were prepared by an ingot casting method. The corrosion performance of Mg-Zn-Y alloys was studied by combining gas-collecting test, immersion test and electrochemical measurements in order to determine the corrosion rate and mechanism of the alloys. The results showed that the volume fraction of Mg（12）YZn phase increased and the shape of the Mg（12）YZn phase changed from discontinuous to continuous net-like with increasing Zn and Y content. The corrosion rate of the alloys greatly depended on the distribution and volume fraction of the Mg（12）YZn phase. Corrosion products appeared at the junction of Mg phase and Mg（12）YZn phase, indicating that the Mg（12）YZn phase accelerated galvanic corrosion of Mg matrix. Mg（97）Zn1Y2 alloy shows the lowest corrosion rate due to the continuous distribution of Mg（12）YZn phase.展开更多
The microstructure and damping capacities of MgZnxYi.33x(x=l-4at.%)alloys were discussed and researched.The main phase composition of the alloys consists of a_Mg and long-period stacking ordered(LPSO)phase.Due to incr...The microstructure and damping capacities of MgZnxYi.33x(x=l-4at.%)alloys were discussed and researched.The main phase composition of the alloys consists of a_Mg and long-period stacking ordered(LPSO)phase.Due to increasedLPSO phase,grain size was refined.LPSO phase was advantageous to the damping properties of the Mg-Zn-Y alloys.Mg-7%Zn-12.8%Y has the highest damping capacity up to0.04.Due to stacking fault probability,the LPSO phase in the Mg-Zn-Yalloys could be new damping source to dissipate energy so as to contribute to the improvement of damping capacities.展开更多
Phase compositions and microstructure evolutions of three Mg-Y-Zn cast alloys during isothermal annealing at 773 K have been systematically investigated to clarify the formation behavior of 14 H long period stacking o...Phase compositions and microstructure evolutions of three Mg-Y-Zn cast alloys during isothermal annealing at 773 K have been systematically investigated to clarify the formation behavior of 14 H long period stacking ordered（LPSO） structure from α-Mg grains.The annealed microstructure characteristics indicate that the 18 R phase is thermal stable in Mg86Y8Zn6 alloy where 18 R serves as matrix,and 14 H lamellar phase only forms within tiny α-Mg slices（less than 1% for volume fraction）.The α-Mg grains in Mg88Y8Zn4 and Mg89Y8Zn3 alloys exhibit cellular shape,and 14 H phase forms and develops into lamellar shape in these cellular grains after annealing.The results suggest that the presence of α-Mg grains is a requirement for the generation of 14 H phase.The nucleation and growth rates of 14 H lamellas are accelerated in α-Mg grains with higher concentrations of stacking faults and solute atoms.Moreover,the 14 H lamellas are parallel to adjacent 18 R plates in Mg86Y8Zn6 alloy,but the 14 H phase precipitated in cellularα-Mg grains of Mg88Y8Zn4 and Mg89Y8Zn3 alloys exhibits random orientation relationship with surrounding 18 R phase,indicating that the orientation relationship between 14 H and 18 R phases depends on the relationship between α-Mg grains and 18 R phase.展开更多
Based on experiments and first-principles calculations,the microstructures and mechanical properties of as-cast and solution treated Mg-10Gd-4Y-xZn-0.6Zr(x=0,1,2,wt.%)alloys are investigated.The transformation process...Based on experiments and first-principles calculations,the microstructures and mechanical properties of as-cast and solution treated Mg-10Gd-4Y-xZn-0.6Zr(x=0,1,2,wt.%)alloys are investigated.The transformation process of long-period stacking ordered(LPSO)structure during solidification and heat treatment and its effect on the mechanical properties of experimental alloys are discussed.Results reveal that the stacking faults and 18R LPSO phases appear in the as-cast Mg-10Gd-4Y-1Zn-0.6Zr and Mg-10Gd-4Y-2Zn-0.6Zr alloys,respectively.After solution treatment,the stacking faults and 18R LPSO phase transform into 14H LPSO phase.The Enthalpies of formation and reaction energy of 14H and 18R LPSO are calculated based on first-principles.Results show that the alloying ability of 18R is stronger than that of 14H.The reaction energies show that the 14H LPSO phase is more stable than the 18R LPSO.The elastic properties of the 14H and 18R LPSO phases are also evaluated by first-principles calculations,and the results are in good agreement with the experimental results.The precipitation of LPSO phase improves the tensile strength,yield strength and elongation of the alloy.After solution treatment,the Mg-10Gd-4Y-2Zn-0.6Zr alloy has the best mechanical properties,and its ultimate tensile strength and yield strength are 278.7 MPa and 196.4 MPa,respectively.The elongation of Mg-10Gd-4Y-2Zn-0.6Zr reaches 15.1,which is higher than that of Mg-10Gd-4Y0.6Zr alloy.The improving mechanism of elastic modulus by the LPSO phases and the influence on the alloy mechanical properties are also analyzed.展开更多
Magnesium alloys with a long-period stacking ordered(LPSO)structure usually possess excellent static strength,but their fatigue behaviors are poorly understood.This work presents the effect of the LPSO structure on th...Magnesium alloys with a long-period stacking ordered(LPSO)structure usually possess excellent static strength,but their fatigue behaviors are poorly understood.This work presents the effect of the LPSO structure on the crack behaviors of Mg alloys in a very high cycle fatigue(VHCF)regime.The LPSO lamellas lead to a facet-like cracking process along the basal planes at the crack initiation site and strongly prohibit the early crack propagation by deflecting the growth direction.The stress intensity factor at the periphery of the faceted area is much higher than the conventional LPSO-free Mg alloys,contributing higher fatigue crack propagation threshold of LPSO-containing Mg alloys.Microstructure observation at the facets reveals a layer of ultrafine grains at the fracture surface due to the cyclic contact of the crack surface,which supports the numerous cyclic pressing model describing the VHCF crack initiation behavior.展开更多
The microstructure evolution of Mg100-2xYxZnx （x=2, 2.5, 3, 3.5） alloys was investigated. Results show that the Mg100-2xYxZnx alloys are composed of a-Mg, long period stacking ordered （LPSO） phase and eutectic str...The microstructure evolution of Mg100-2xYxZnx （x=2, 2.5, 3, 3.5） alloys was investigated. Results show that the Mg100-2xYxZnx alloys are composed of a-Mg, long period stacking ordered （LPSO） phase and eutectic structure phase （W phase）, and the Mg95Y2.5Zn2.5 alloy has the best comprehensive mechanical properties. Subsequently, the microstructure evolution of the optimized alloy Mg95Y2.5Zn2.5 during solidification and heat treatment processes was analyzed and discussed by means of OM, SEM, TEM, XRD and DTA. After heat treatment, the lamellar phase 14H-LPSO precipitated in a-Mg and W phase transforms into particle phase （MgyZn2）. Due to the compound reinforcement effect of the particle phase and LPSO phase （18R＋14H）, the mechanical properties of the alloy are enhanced. The tensile strength and elongation of the Mg95Y2.5Zn2.5 alloy is improved by 9.1% and 31.3% to 215 MPa and 10.5%, respectively, after solid-solution treatment.展开更多
Understanding the interface between strengthening precipitates and matrix in alloys, especially at the atomic level, is a critical issue for tailoring the precipitate strengthening to achieve desired mechanical proper...Understanding the interface between strengthening precipitates and matrix in alloys, especially at the atomic level, is a critical issue for tailoring the precipitate strengthening to achieve desired mechanical properties. Using high-resolution scanning transmission electron microscopy, we here clarify the semicoherent interfaces between the matrix and long-period stacking ordered(LPSO) phases, including 18 R and 14 H, in Mg–Zn–Y alloys. The LPSO/Mg interface features the unique configuration of the Shockley partial dislocations, which produces a near zero macroscopic strain because the net Burgers vectors equal zero. The 18 R/Mg interface characterizes a dissociated structure that can be described as a narrow slab of 54 R. There are two dislocation arrays accompanied to the 18 R/54 R and 54 R/Mg interface, resulting a slight deviation(about 2.3°). The 14 R/Mg interface exhibits the dislocation pairs associated with solute atoms. We further evaluate the stability and morphology of the corresponding interfaces based on elastic interaction, via calculating the mutual strong interactions between dislocation arrays, as well as that between the dislocations and solute atoms. The synchronized migration of interfacial dislocations and solute atoms, like move-drag behavior, dominates the lateral growth of LPSO phases in Mg alloys.展开更多
Herein,the evolution of long-period stacking ordered(LPSO)phases in the as-cast Mg-6Gd-1Zn-0.6Zr(wt.%)alloy are investigated via transmission electron microscopy(TEM)and atom probe tomography(APT).The TEM results reve...Herein,the evolution of long-period stacking ordered(LPSO)phases in the as-cast Mg-6Gd-1Zn-0.6Zr(wt.%)alloy are investigated via transmission electron microscopy(TEM)and atom probe tomography(APT).The TEM results reveal that two types of LPSO phase(a bulky interdendritic phase and a plate-like matrix LPSO phase)are formed in the as-cast sample.Most of the LPSO phases are confirmed to be of the 14H type,with a smaller proportion being of the 18R LPSO.Further,the APT results reveal that the composition of the interdendritic LPSO phase is closer to that of the ideal 14H phase compared to the matrix LPSO phase,and both the interdendritic and matrix LPSO phases exhibit a Gd/Zn ratio of 2.5,thereby indicating a deficient Zn content compared to the ideal 14H phase(i.e.,1.3).In addition,the influence of the LPSO phases on the deformation behavior is investigated at different compressive plastic strains using electron backscatter diffraction(EBSD)analysis to reveal twinning and slip behavior during deformation.The results indicate that the LPSO phase induces additional work hardening in the late stage of deformation via the suppression of{1011}compressive twinning and the activation of non-basal slip systems.展开更多
In order to solve the problem that the testing cost of the three-dimensional integrated circuit(3D IC)is too high,an optimal stacking order scheme is proposed to reduce the mid-bond test cost.A new testing model is bu...In order to solve the problem that the testing cost of the three-dimensional integrated circuit(3D IC)is too high,an optimal stacking order scheme is proposed to reduce the mid-bond test cost.A new testing model is built with the general consideration of both the test time for automatic test equipment(ATE)and manufacturing failure factors.An algorithm for testing cost and testing order optimization is proposed,and the minimum testing cost and optimized stacking order can be carried out by taking testing bandwidth and testing power as constraints.To prove the influence of the optimal stacking order on testing costs,two baselines stacked in sequential either in pyramid type or in inverted pyramid type are compared.Based on the benchmarks from ITC 02,experimental results show that for a 5-layer 3D IC,under different constraints,the optimal stacking order can reduce the test costs on average by 13%and 62%,respectively,compared to the pyramid type and inverted pyramid type.Furthermore,with the increase of the stack size,the test costs of the optimized stack order can be decreased.展开更多
The study of the stacking stability of bilayer MoS2 is essential since a bilayer has exhibited advantages over single layer MoS2 in many aspects for nanoelectronic applications. We explored the relative stability, opt...The study of the stacking stability of bilayer MoS2 is essential since a bilayer has exhibited advantages over single layer MoS2 in many aspects for nanoelectronic applications. We explored the relative stability, optimal sliding path between different stacking orders of bilayer MoS2, and （especially） the effect of inter-layer stress, by combining first-principles density functional total energy calculations and the climbing-image nudge-elastic-band （CI-NEB） method. Among five typical stacking orders, which can be categorized into two kinds （I： AA＇, AB and II： AA＇, AB＇, A＇B）, we found that stacking orders with Mo and S superposing from both layers, such as AA＇ and AB, is more stable than the others. With smaller computational efforts than potential energy profile searching, we can study the effect of inter-layer stress on the stacking stability. Under isobaric condition, the sliding barrier increases by a few eV/（uc.GPa） from AA＇ to ABt, compared to 0.1 eV/（uc.GPa） from AB to [AB]. Moreover, we found that interlayer compressive stress can help enhance the transport properties of AA＇. This study can help understand why inter-layer stress by dielectric gating materials can be an effective means to improving MoS2 on nanoelectronic applications.展开更多
We have systematically investigated the microstructures of as-cast Mg_(97.49)Ho_(1.99)Cu_(0.43)Zr_(0.09)alloy by atomic resolution high-angle annular dark field scanning transmission electron microscopy(HAADF-STEM), r...We have systematically investigated the microstructures of as-cast Mg_(97.49)Ho_(1.99)Cu_(0.43)Zr_(0.09)alloy by atomic resolution high-angle annular dark field scanning transmission electron microscopy(HAADF-STEM), revealing the coexistence of 18R, 14H and 24R long period stacking/order(LPSO) phases with fully coherent interfaces along step-like composition gradient in a blocky intermetallic compound distributed at grain boundary. The short-range order(SRO) L1_(2)-type Cu_(6)Ho_(8)clusters embedded across AB’C’A-stacking fault layers are directly revealed at atomic scale. Importantly, the order degree of SRO clusters in the present dilute alloy is significant lower than previous 6M and 7M in-plane order reported in ternary Mg-TM(transition metal)-RE(rare earth) alloys, which can be well matched by 9M in-plane order. This directly demonstrates that SRO in-plane L1_(2)-type clusters can be expanded into more dilute composition regions bounded along the definite TM/RE ratio of 3/4. In addition, the estimated chemical compositions of solute enriched stacking fault(SESF) in all LPSO variants are almost identical with the ideal SESF composition of 9M in-plane order, regardless of the type of LPSO phases. The results further support the viewpoint that robust L1_(2)-type TM_(6)RE_(8)clusters play an important role in governing LPSO phase formation.展开更多
The Mg-Gd-Y-Zn-Zr(GWZ)alloy containing a long-period ordered stacking(LPSO)phase fabricated by Wire arc additive manufacturing(WAAM)shows substantial potential in the aerospace and automotive industries.In this work,M...The Mg-Gd-Y-Zn-Zr(GWZ)alloy containing a long-period ordered stacking(LPSO)phase fabricated by Wire arc additive manufacturing(WAAM)shows substantial potential in the aerospace and automotive industries.In this work,Mg-9Gd-4Y-1Zn-0.4Zr(wt%)single-layer and multilayer components with high-forming-quality were fabricated using WAAM based on cold metal transfer(WAAM-CMT).The deposition parameters were optimized,achieving better deposition morphology and surface quality.The layer-by-layer cyclic microstructure includes remelting zone(RMZ)and non-remelting zone(NRZ),which consisted of α-Mg matrix,blocky LPSO phase,and eutectic phase.The average grain size were 26.8μm in RMZ and 39.3μm in NRZ,and the volume fraction of secondary phases was around 8%,remaining consistent across different layers.The coarse-fine-grain alternating structure generated hetero deformation induced(HDI)strengthening,while at the same time caused the fracture occurring between the NRZ and RMZ due to the weak interlayer bonding.The thermally stabilized blocky LPSO phase played an effective role on inhibiting grain growth during the solid-solution treatment.The specimen achieved highest isotropic mechanical properties after optimized heat treatment with yield strength,ultimate tensile strength,and elongation higher than 220 MPa,370 MPa,and 8.0%,respectively.The GWZ alloys fabricated by WAAM with great isotropic strength-ductility-synergy are promising candidates to replace the conventionally cast counterparts.展开更多
The effect of rotational-die equal channel angular pressing(RD-ECAP)temperature and deformation route on the microstructure and mechanical properties of pre-extruded Mg-5Gd-3Y-1Zn-0.5Zr(wt%)alloys were investigated.Th...The effect of rotational-die equal channel angular pressing(RD-ECAP)temperature and deformation route on the microstructure and mechanical properties of pre-extruded Mg-5Gd-3Y-1Zn-0.5Zr(wt%)alloys were investigated.The results indicate that the RD-ECAP updates both theα-Mg texture and long-period stack-ing ordered(LPSO)arrangement in the pre-extruded alloy,while theα-Mg texture is more sensitive to the change of deformation route.The LPSO streamlines modify the anisotropy of mechanical properties of the ECAP alloys via exerting different reinforcing effects and modifying the crack propagation.The lower ECAP temperature of 350℃ rather than 400℃ promotes dynamic precipitation which deteriorates the following ageing-hardening response but conduces to refining theα-Mg grains and preventing a sharp drop in elongation after peak ageing.The 350A peak-aged alloy exhibits the optimal mechanical proper-ties with the average tensile yield strength(TYS)of 311 MPa(S_(TYS)=3.7,S indicates standard deviation)and elongation of 7.6%(S_(EL)=0.7).Its higher strength should mainly be attributed to the finer grain size,and its quasi-isotropic performance should be inherited from the ECAP state induced by the rational arrangement of LPSO phases.展开更多
基金Project (BK2010392) supported by the Natural Science Foundation of Jiangsu Province of ChinaProject (3212000502) supported by the Innovation Foundation of Southeast University,China
文摘The microstructure and mechanical properties of Mg94Zn2Y4 extruded alloy containing long-period stacking ordered structures were systematically investigated by SEM and TEM analyses. The results show that the 18R-LPSO structure and α-Mg phase are observed in cast Mg94Zn2Y4 alloy. After extrusion, the LPSO structures are delaminated and Mg-slices with width of 50-200 nm are generated. By ageing at 498 K for 36 h, the ageing peak is attained andβ′phase is precipitated. Due to this novel precipitation, the microhardness ofα-Mg matrix increases apparently from HV108.9 to HV129.7. While the microhardness for LPSO structure is stabilized at about HV145. TEM observations and SAED patterns indicate that the β′ phase has unique orientation relationships betweenα-Mg and LPSO structures, the direction in the close-packed planes ofβ′precipitates perpendicular to that ofα-Mg and LPSO structures. The ultimate tensile strength for the peak-aged alloy achieves 410.7 MPa and the significant strength originates from the coexistence ofβ′precipitates and 18R-LPSO structures.
基金Project (2009CB623704) supported by the National Basic Research Program of ChinaProject (50971076) supported by the National Natural Science Foundation of China
文摘14H, 18R and 24R long-period stacking ordered （LPSO） structures were observed in the as-cast Mg-3Cu-1Mn-2Zn-1Y damping alloy using transmission electron microscopy （TEM）. These LPSO structures contained Mg, Y, Cu and Zn and thus they were quaternary phases. Sharp diffraction pattern of the 24R structure was obtained and the angle between and g10024R was measured to be 5.03°. During high resolution TEM observations, lattice fringes with two characteristic spacings were observed within the 24R structure. Based on the experimental results, 6H, 7H and three 8H are suggested as the building blocks of 18R, 14H and 24R structures, respectively. The 24R unit cell can be interpreted as the stacking of 8H building blocks in the same shear direction with a shear angle of about 5.03°. The imperfect 24R structures are in order or disorder arrangements of principal 8H and minor 6H blocks. This double-block structure model is also applicable to other reported defects in LPSO structures.
基金the National Natural Science Foundation of China(Grant Nos.51774109 and 51979099)the Fundamental Research Funds for the Central Universities(Grant No.2018B48414 and 2018B690X14)+3 种基金Postgraduate Research&Practice Innovation Program of Jiangsu Province(Grant No.KYCX18_0570)The Key Research and Development Project of Jiangsu Province of China(Grant No.BE2017148)Postgraduate Education Reform Project of Jiangsu Province(JGLX19_027)Natural Science Foundation of China(Grant No.51979099).
文摘Mg-Y-Zn alloys with long period stacking ordered(LPSO)structure have received much attention recently and exhibit great potential in applications such as automotive,aerospace and in bio-medical fields.This paper aimed to investigate the effect of different phase constitution of LPSO structures on corrosion rate of bio-medical Mg-Y-Zn alloys.The results showed that as-cast Mg98.5Y1Zn0.5 alloys containing only 18R structure exhibited the highest corrosion resistance with the corrosion rate of 2.78 mm/year.The precipitation of 14H lamellas within a-Mg grains during solid solution treatment introduced the crystallographic orientation corrosion by accelerating micro-galvanic corrosion.The increase of 18R/14H interfaces deteriorated the corrosion resistance,and the grain boundaries also suffered from severe electrochemical dissolution.This work suggested that Mg-Y-Zn alloys with single LPSO structure(either 18R or 14H)exhibited better corrosion resistance than alloys with co-existence 18R and I4H LPSO structures.
基金supported by the Natural Science Foundation of Jiangsu Province for Outstanding Youth(BK20160081)the Natural Science Foundation of Jiangsu Province(BK20181020)+2 种基金the Natural Science Foundation of Higher Education Institutions of Jiangsu Province–Key Project(18KJA430008)the“333 Project”of Jiangsu Province(BRA2018338)the Practical Innovative Project for Postgraduates of Jiangsu Province(SJCX19_0493).
文摘Corrosion is one of the most drawbacks which restricts the wide applications of Mg alloys.In the last decade,the corrosion behaviors of Mg alloys with stacking fault(SF)and/or long period stacking ordered(LPSO)structures have obtained increasing attention.However,the corrosion mechanism of the SF–or LPSO–containing Mg alloys has not been well illustrated and even reverse results have been reported.In this paper,we have reviewed recent reports on corrosion behaviors of SF–or LPSO–containing Mg alloys to better clarify and understand the significance and mechanism.Moreover,some deficiencies are presented and advises are proposed for the development of corrosion resistant Mg alloys with SF or LPSO structures.
基金supported by the National Natural Science Foundation of China(Nos.51574175 and 51474153)the Ph.D.Programs Foundation of Ministry of Education of China(No. 20111402110004)the Natural Science Foundation of Shanxi Province(Nos.2009011028-3 and 2012011022-1)
文摘The microstructure of the precipitated phases of Mg95.sGd3Zn1Zro.2 alloys with long-period stacking ordered structure before and after heat treatment is discussed. The corrosion properties of the as-cast （F）, solid-solution （T4） and aging-treated （T6） alloys in 1% NaC1 solution are studied. The hydrogen evolution and electrochemical measurements display that the as-cast Mg95.sGd3Zn1Zro.2 alloy with the continuous network eutectic phase exhibits the greatest corrosion resistance, while T6 sample with some needle-like phases and the particle phases is the worst among the three alloys. It is proposed to be mainly related to the amount, composition, microstructure and distribution of the precipitated phases.
基金supported by National Natural Science Fundation of China (Nos. 51171192 and51271183)National Basic Research Program of China(No. 2013CB632205)Innovation Fund of Institute of Metal Research (IMR), Chinese Academy of Sciences(CAS)
文摘Both the solid solution and precipitation are mainly strengthening mechanism for the magnesium-based alloys. A great number of alloying elements can be dissolved into the Mg matrix to form the solutes and precipitates.Moreover, the type of precipitates varies with different alloying elements and heat treatments, which makes it quite difficult to understand the formation mechanism of the precipitates in Mg-based alloys in depth. Thus, it is very hard to give a systematical regularity in precipitation process for the Mg-based alloys. This review is mainly focused on the formation and microstructural evolution of the precipitates, as a hot topic for the past few years, including Guinier-Preston Zones, quasicrystals and long-period stacking ordered phases formed in a number of Mg-TM-RE alloy systems, where TM = Al, Zn, Zr and RE = Y,Gd, Hd, Ce and La.
基金supported by the National Natural Science Foundation of China(Nos.50571073,51574175 and 51474153)the Ph. D. Programs Foundation of Ministry of Education of China(20111402110004)the Natural Science Foundation of Shanxi Province(Nos.2009011028-3 and 2012011022-1)
文摘Alloys with composition of Mg_(96-x)Gd_3Zn_1Li_x(at.%)(x=0, 2, 4, and 6) were prepared by conventional casting. The microstructures of these alloys under as-cast and solid-solution conditions have been observed, and the mechanical properties were investigated. The results showed that Li is an effective element to refine the grains and break the eutectic networks in as-cast MgGd_3Zn_1 alloy. During solid solution treatment, these broken eutectic networks are spheroidized and highly dispersed. In addition, plentiful lamellar long period stacking ordered(LPSO) phases are precipitated in an α-Mg matrix when the Li addition is not more than 4%. Solid-solution treated Mg_(92)Gd_3Zn_1Li_4 alloy exhibits an optimal ultimate tensile strength(UTS) of 226 MPa and elongation of 5.8%. The strength of MgGd_3Zn_1 alloy is improved significantly, meanwhile, the toughness is apparently increased.
基金support of the National Natural Science Foundation of China (No.50571073)the Ph.D. Programs Foundation of Ministry of Education of China (No. 20111402110004)the Natural Science Foundation of Shanxi Province, China (No.2009011028-3)
文摘Mg-Zn-Y alloys with long-period stacking ordered structures were prepared by an ingot casting method. The corrosion performance of Mg-Zn-Y alloys was studied by combining gas-collecting test, immersion test and electrochemical measurements in order to determine the corrosion rate and mechanism of the alloys. The results showed that the volume fraction of Mg（12）YZn phase increased and the shape of the Mg（12）YZn phase changed from discontinuous to continuous net-like with increasing Zn and Y content. The corrosion rate of the alloys greatly depended on the distribution and volume fraction of the Mg（12）YZn phase. Corrosion products appeared at the junction of Mg phase and Mg（12）YZn phase, indicating that the Mg（12）YZn phase accelerated galvanic corrosion of Mg matrix. Mg（97）Zn1Y2 alloy shows the lowest corrosion rate due to the continuous distribution of Mg（12）YZn phase.
基金National Natural Science Foundation of China(Nos.U1610123,51674226,51574207,51574206,51274175)International Cooperation project of the Ministry of Science and Technology of China(No.2014DFA50320)+4 种基金The Science and Technology Major Project of Shanxi Province(No.MC2016-06)International Science and Technology Cooperation Project of Shanxi Province(No.2015081041)Research Project Supported by Shanxi Scholarship Council of China(No.2016-Key 2)Transformation of Scientific and Technological Achievements Special Guide Project of Shanxi Province(No.201604D131029)Shanxi Province Science Foundation for Youths(No.201601D021062)
文摘The microstructure and damping capacities of MgZnxYi.33x(x=l-4at.%)alloys were discussed and researched.The main phase composition of the alloys consists of a_Mg and long-period stacking ordered(LPSO)phase.Due to increasedLPSO phase,grain size was refined.LPSO phase was advantageous to the damping properties of the Mg-Zn-Y alloys.Mg-7%Zn-12.8%Y has the highest damping capacity up to0.04.Due to stacking fault probability,the LPSO phase in the Mg-Zn-Yalloys could be new damping source to dissipate energy so as to contribute to the improvement of damping capacities.
基金supported by the Natural Science Foundation of Jiangsu Province of China(No.BK2010392)the Fundamental Research Funds for the Central Universities(No.2015B01314)
文摘Phase compositions and microstructure evolutions of three Mg-Y-Zn cast alloys during isothermal annealing at 773 K have been systematically investigated to clarify the formation behavior of 14 H long period stacking ordered（LPSO） structure from α-Mg grains.The annealed microstructure characteristics indicate that the 18 R phase is thermal stable in Mg86Y8Zn6 alloy where 18 R serves as matrix,and 14 H lamellar phase only forms within tiny α-Mg slices（less than 1% for volume fraction）.The α-Mg grains in Mg88Y8Zn4 and Mg89Y8Zn3 alloys exhibit cellular shape,and 14 H phase forms and develops into lamellar shape in these cellular grains after annealing.The results suggest that the presence of α-Mg grains is a requirement for the generation of 14 H phase.The nucleation and growth rates of 14 H lamellas are accelerated in α-Mg grains with higher concentrations of stacking faults and solute atoms.Moreover,the 14 H lamellas are parallel to adjacent 18 R plates in Mg86Y8Zn6 alloy,but the 14 H phase precipitated in cellularα-Mg grains of Mg88Y8Zn4 and Mg89Y8Zn3 alloys exhibits random orientation relationship with surrounding 18 R phase,indicating that the orientation relationship between 14 H and 18 R phases depends on the relationship between α-Mg grains and 18 R phase.
基金supported by the National Key Research and Development Program of China[grant No.2018YFB2001800]National Natural Science Foundation of China[grant No.51871184]Dalian High-level Talents Innovation Support Program[grant No.2021RD06]。
文摘Based on experiments and first-principles calculations,the microstructures and mechanical properties of as-cast and solution treated Mg-10Gd-4Y-xZn-0.6Zr(x=0,1,2,wt.%)alloys are investigated.The transformation process of long-period stacking ordered(LPSO)structure during solidification and heat treatment and its effect on the mechanical properties of experimental alloys are discussed.Results reveal that the stacking faults and 18R LPSO phases appear in the as-cast Mg-10Gd-4Y-1Zn-0.6Zr and Mg-10Gd-4Y-2Zn-0.6Zr alloys,respectively.After solution treatment,the stacking faults and 18R LPSO phase transform into 14H LPSO phase.The Enthalpies of formation and reaction energy of 14H and 18R LPSO are calculated based on first-principles.Results show that the alloying ability of 18R is stronger than that of 14H.The reaction energies show that the 14H LPSO phase is more stable than the 18R LPSO.The elastic properties of the 14H and 18R LPSO phases are also evaluated by first-principles calculations,and the results are in good agreement with the experimental results.The precipitation of LPSO phase improves the tensile strength,yield strength and elongation of the alloy.After solution treatment,the Mg-10Gd-4Y-2Zn-0.6Zr alloy has the best mechanical properties,and its ultimate tensile strength and yield strength are 278.7 MPa and 196.4 MPa,respectively.The elongation of Mg-10Gd-4Y-2Zn-0.6Zr reaches 15.1,which is higher than that of Mg-10Gd-4Y0.6Zr alloy.The improving mechanism of elastic modulus by the LPSO phases and the influence on the alloy mechanical properties are also analyzed.
基金The authors gratefully acknowledge the financial support from the National Natural Science Foundation of China(Nos.12072212 and 11832007)the National Key Research and Development Program of China(No.2018YFE0307104)the Applied Basic Research Programs of Sichuan Province(No.2021YJ0071).We also highly appreciate the help of Dr.Yan Li from the Department of Mechanics,Sichuan University.
文摘Magnesium alloys with a long-period stacking ordered(LPSO)structure usually possess excellent static strength,but their fatigue behaviors are poorly understood.This work presents the effect of the LPSO structure on the crack behaviors of Mg alloys in a very high cycle fatigue(VHCF)regime.The LPSO lamellas lead to a facet-like cracking process along the basal planes at the crack initiation site and strongly prohibit the early crack propagation by deflecting the growth direction.The stress intensity factor at the periphery of the faceted area is much higher than the conventional LPSO-free Mg alloys,contributing higher fatigue crack propagation threshold of LPSO-containing Mg alloys.Microstructure observation at the facets reveals a layer of ultrafine grains at the fracture surface due to the cyclic contact of the crack surface,which supports the numerous cyclic pressing model describing the VHCF crack initiation behavior.
基金financially supported by the National Natural Science Foundation of China(Nos.50571073,51574175 and 51474153)Ph.D.Programs Foundation of Ministry of Education of China(20111402110004)Natural Science Foundation of Shanxi Province(Nos.2009011028-3 and 2012011022-1)
文摘The microstructure evolution of Mg100-2xYxZnx （x=2, 2.5, 3, 3.5） alloys was investigated. Results show that the Mg100-2xYxZnx alloys are composed of a-Mg, long period stacking ordered （LPSO） phase and eutectic structure phase （W phase）, and the Mg95Y2.5Zn2.5 alloy has the best comprehensive mechanical properties. Subsequently, the microstructure evolution of the optimized alloy Mg95Y2.5Zn2.5 during solidification and heat treatment processes was analyzed and discussed by means of OM, SEM, TEM, XRD and DTA. After heat treatment, the lamellar phase 14H-LPSO precipitated in a-Mg and W phase transforms into particle phase （MgyZn2）. Due to the compound reinforcement effect of the particle phase and LPSO phase （18R＋14H）, the mechanical properties of the alloy are enhanced. The tensile strength and elongation of the Mg95Y2.5Zn2.5 alloy is improved by 9.1% and 31.3% to 215 MPa and 10.5%, respectively, after solid-solution treatment.
基金supported financially by the National Natural Science Foundation of China(Nos.51801214 and 51871222)the Liaoning Provincial Natural Science Foundation(No.2019-MS-335)。
文摘Understanding the interface between strengthening precipitates and matrix in alloys, especially at the atomic level, is a critical issue for tailoring the precipitate strengthening to achieve desired mechanical properties. Using high-resolution scanning transmission electron microscopy, we here clarify the semicoherent interfaces between the matrix and long-period stacking ordered(LPSO) phases, including 18 R and 14 H, in Mg–Zn–Y alloys. The LPSO/Mg interface features the unique configuration of the Shockley partial dislocations, which produces a near zero macroscopic strain because the net Burgers vectors equal zero. The 18 R/Mg interface characterizes a dissociated structure that can be described as a narrow slab of 54 R. There are two dislocation arrays accompanied to the 18 R/54 R and 54 R/Mg interface, resulting a slight deviation(about 2.3°). The 14 R/Mg interface exhibits the dislocation pairs associated with solute atoms. We further evaluate the stability and morphology of the corresponding interfaces based on elastic interaction, via calculating the mutual strong interactions between dislocation arrays, as well as that between the dislocations and solute atoms. The synchronized migration of interfacial dislocations and solute atoms, like move-drag behavior, dominates the lateral growth of LPSO phases in Mg alloys.
基金This work was supported by the National Research Foundation of Korea(Grant number:NRF-2019K1A3A1A18116059 and NRF-2023R1A2C200529811)Austrian Science Fund(FWF)(P 32378-N37)Federal Ministry of Austria Education,Science and Research(BMBWF)(KR 06/2020).
文摘Herein,the evolution of long-period stacking ordered(LPSO)phases in the as-cast Mg-6Gd-1Zn-0.6Zr(wt.%)alloy are investigated via transmission electron microscopy(TEM)and atom probe tomography(APT).The TEM results reveal that two types of LPSO phase(a bulky interdendritic phase and a plate-like matrix LPSO phase)are formed in the as-cast sample.Most of the LPSO phases are confirmed to be of the 14H type,with a smaller proportion being of the 18R LPSO.Further,the APT results reveal that the composition of the interdendritic LPSO phase is closer to that of the ideal 14H phase compared to the matrix LPSO phase,and both the interdendritic and matrix LPSO phases exhibit a Gd/Zn ratio of 2.5,thereby indicating a deficient Zn content compared to the ideal 14H phase(i.e.,1.3).In addition,the influence of the LPSO phases on the deformation behavior is investigated at different compressive plastic strains using electron backscatter diffraction(EBSD)analysis to reveal twinning and slip behavior during deformation.The results indicate that the LPSO phase induces additional work hardening in the late stage of deformation via the suppression of{1011}compressive twinning and the activation of non-basal slip systems.
基金The National Natural Science Foundation of China(No.61674048,61574052,61474036,61371025)the Project of Anhui Institute of Economics and Management(No.YJKT1417T01)
文摘In order to solve the problem that the testing cost of the three-dimensional integrated circuit(3D IC)is too high,an optimal stacking order scheme is proposed to reduce the mid-bond test cost.A new testing model is built with the general consideration of both the test time for automatic test equipment(ATE)and manufacturing failure factors.An algorithm for testing cost and testing order optimization is proposed,and the minimum testing cost and optimized stacking order can be carried out by taking testing bandwidth and testing power as constraints.To prove the influence of the optimal stacking order on testing costs,two baselines stacked in sequential either in pyramid type or in inverted pyramid type are compared.Based on the benchmarks from ITC 02,experimental results show that for a 5-layer 3D IC,under different constraints,the optimal stacking order can reduce the test costs on average by 13%and 62%,respectively,compared to the pyramid type and inverted pyramid type.Furthermore,with the increase of the stack size,the test costs of the optimized stack order can be decreased.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.11004201 and 50831006)the National Basic Research Program of China(Grant No.2012CB933103)+1 种基金the IMR SYNL-Young Merit ScholarsT.S.Ke Research Grant for support
文摘The study of the stacking stability of bilayer MoS2 is essential since a bilayer has exhibited advantages over single layer MoS2 in many aspects for nanoelectronic applications. We explored the relative stability, optimal sliding path between different stacking orders of bilayer MoS2, and （especially） the effect of inter-layer stress, by combining first-principles density functional total energy calculations and the climbing-image nudge-elastic-band （CI-NEB） method. Among five typical stacking orders, which can be categorized into two kinds （I： AA＇, AB and II： AA＇, AB＇, A＇B）, we found that stacking orders with Mo and S superposing from both layers, such as AA＇ and AB, is more stable than the others. With smaller computational efforts than potential energy profile searching, we can study the effect of inter-layer stress on the stacking stability. Under isobaric condition, the sliding barrier increases by a few eV/（uc.GPa） from AA＇ to ABt, compared to 0.1 eV/（uc.GPa） from AB to [AB]. Moreover, we found that interlayer compressive stress can help enhance the transport properties of AA＇. This study can help understand why inter-layer stress by dielectric gating materials can be an effective means to improving MoS2 on nanoelectronic applications.
基金supported by JSPS KAKENHI for Scientific Research on Innovative Areas “Materials Science of a Millefeuille Structure (Grant Nos. JP18H05475, JP18H05479)”“Nanotechnology Platform” of the MEXT, Japan+1 种基金supported by Grant-in-Aid for JSPS Fellows (JP19F19775)the Open Funds of the State Key Laboratory of Rare Earth Resource Utilization (RERU2020012)。
文摘We have systematically investigated the microstructures of as-cast Mg_(97.49)Ho_(1.99)Cu_(0.43)Zr_(0.09)alloy by atomic resolution high-angle annular dark field scanning transmission electron microscopy(HAADF-STEM), revealing the coexistence of 18R, 14H and 24R long period stacking/order(LPSO) phases with fully coherent interfaces along step-like composition gradient in a blocky intermetallic compound distributed at grain boundary. The short-range order(SRO) L1_(2)-type Cu_(6)Ho_(8)clusters embedded across AB’C’A-stacking fault layers are directly revealed at atomic scale. Importantly, the order degree of SRO clusters in the present dilute alloy is significant lower than previous 6M and 7M in-plane order reported in ternary Mg-TM(transition metal)-RE(rare earth) alloys, which can be well matched by 9M in-plane order. This directly demonstrates that SRO in-plane L1_(2)-type clusters can be expanded into more dilute composition regions bounded along the definite TM/RE ratio of 3/4. In addition, the estimated chemical compositions of solute enriched stacking fault(SESF) in all LPSO variants are almost identical with the ideal SESF composition of 9M in-plane order, regardless of the type of LPSO phases. The results further support the viewpoint that robust L1_(2)-type TM_(6)RE_(8)clusters play an important role in governing LPSO phase formation.
基金supported by the National Key Research and Development Program of China(No.2021YFB3701004)National Natural Science Foundation of China(No.52071211)Joint Research Center of Advanced Aerospace Technology of Shanghai Academy of Spaceflight Technology-Shanghai Jiao Tong University(No.USCAST2020-1).
文摘The Mg-Gd-Y-Zn-Zr(GWZ)alloy containing a long-period ordered stacking(LPSO)phase fabricated by Wire arc additive manufacturing(WAAM)shows substantial potential in the aerospace and automotive industries.In this work,Mg-9Gd-4Y-1Zn-0.4Zr(wt%)single-layer and multilayer components with high-forming-quality were fabricated using WAAM based on cold metal transfer(WAAM-CMT).The deposition parameters were optimized,achieving better deposition morphology and surface quality.The layer-by-layer cyclic microstructure includes remelting zone(RMZ)and non-remelting zone(NRZ),which consisted of α-Mg matrix,blocky LPSO phase,and eutectic phase.The average grain size were 26.8μm in RMZ and 39.3μm in NRZ,and the volume fraction of secondary phases was around 8%,remaining consistent across different layers.The coarse-fine-grain alternating structure generated hetero deformation induced(HDI)strengthening,while at the same time caused the fracture occurring between the NRZ and RMZ due to the weak interlayer bonding.The thermally stabilized blocky LPSO phase played an effective role on inhibiting grain growth during the solid-solution treatment.The specimen achieved highest isotropic mechanical properties after optimized heat treatment with yield strength,ultimate tensile strength,and elongation higher than 220 MPa,370 MPa,and 8.0%,respectively.The GWZ alloys fabricated by WAAM with great isotropic strength-ductility-synergy are promising candidates to replace the conventionally cast counterparts.
基金supported by the National Natural Science Foundation of China(No.51904036)the Hunan Provincial Key Research and Development Program(No.2023GK2049).
文摘The effect of rotational-die equal channel angular pressing(RD-ECAP)temperature and deformation route on the microstructure and mechanical properties of pre-extruded Mg-5Gd-3Y-1Zn-0.5Zr(wt%)alloys were investigated.The results indicate that the RD-ECAP updates both theα-Mg texture and long-period stack-ing ordered(LPSO)arrangement in the pre-extruded alloy,while theα-Mg texture is more sensitive to the change of deformation route.The LPSO streamlines modify the anisotropy of mechanical properties of the ECAP alloys via exerting different reinforcing effects and modifying the crack propagation.The lower ECAP temperature of 350℃ rather than 400℃ promotes dynamic precipitation which deteriorates the following ageing-hardening response but conduces to refining theα-Mg grains and preventing a sharp drop in elongation after peak ageing.The 350A peak-aged alloy exhibits the optimal mechanical proper-ties with the average tensile yield strength(TYS)of 311 MPa(S_(TYS)=3.7,S indicates standard deviation)and elongation of 7.6%(S_(EL)=0.7).Its higher strength should mainly be attributed to the finer grain size,and its quasi-isotropic performance should be inherited from the ECAP state induced by the rational arrangement of LPSO phases.