The influences of different nano-SiO2（NS） contents on the mechanical properties and rheological behavior of sulfoaluminate cement（SAC） based composite materials were studied.Results show that with increasing conte...The influences of different nano-SiO2（NS） contents on the mechanical properties and rheological behavior of sulfoaluminate cement（SAC） based composite materials were studied.Results show that with increasing content of NS,the apparent viscosity,and shearing strength of fresh paste gradually increase but the fluidity decreases.With a dosage of 3.0%NS,the tensile and flexural strengths of mortars at 56 days were increased by 87.0%and 84.6%,respectively,compared with that in the absence of NS,indicating that the toughness of hardened mortars is significantly improved.Besides,the exothermic peaks of hydration are obviously increased and will earlier occur,and the second and the third peaks appear 2.61 hours and 2.56 hours earlier,respectively than that in the absence of NS,and the hydration of SAC before 8 hours is accelerated.The forming mechanism of strengths was revealed by scanning electron microscopy（SEM）,hydration heat,X-ray diffraction（XRD） and derivative thermogravimetry（DTG）.The micro-aggregate filling effect and nucleation effect at early age and weak pozzolanic effect at late age of NS make the microstructure more compact,which obviously enhances the strength of SAC mortars.展开更多
Liquid SiO2 solutions produced by silicon-based nano- powder are covered on the fabric surface by using spray method. Fabric surfaces were coated at the room temperature in air with the different spray nozzles. Surfac...Liquid SiO2 solutions produced by silicon-based nano- powder are covered on the fabric surface by using spray method. Fabric surfaces were coated at the room temperature in air with the different spray nozzles. Surface analysis of the coated fabric was performed by using Contact Angle and SEM pictures. According to the Contact Angles measurements, the coated fabric surfaces showed hydrophobic character between 126 and 146 degrees, and the SiO2 particles sticked to the fabric fibers as seen from SEM picture.展开更多
In this study, novel core-shell SiO<sub>2</sub>-coated iron nanoparticles (SiO<sub>2</sub>-nZVI) were synthesized using a one-step Stoeber method. The Malachite green degradation abilities of t...In this study, novel core-shell SiO<sub>2</sub>-coated iron nanoparticles (SiO<sub>2</sub>-nZVI) were synthesized using a one-step Stoeber method. The Malachite green degradation abilities of the nanoparticles were investigated. The effects of ethanol/distilled water volume ratio, presence and absence of PEG, tetraethyl orthosilicate (TEOS) dosage, and hydrolysis time used in the nanoparticles preparation process were investigated. The results indicated that the SiO<sub>2</sub>-coated iron nanoparticles had the highest reduction activity when the particles synthesized with ethanol/H<sub>2</sub>O ratio of 2:1, PEG of 0.15 ml, TEOS of 0.5 ml and the reaction time was 4 h. The SiO<sub>2</sub>-nZVI nanoparticles were characterized using Transmission Electron Microscopy (TEM), Energy Dispersive Spectrometry (EDS) and powder X-Ray Diffraction (XRD). The results showed that the average particles diameter of the SiO<sub>2</sub>-nZVI was 20 - 30 nm. The thickness of the outside SiO<sub>2</sub> film is consistent and approximately 10 nm. The results indicated that the nanoparticles coated completely with a transparent SiO<sub>2</sub>-film. Such nanoparticles could have wide applications in dye decolorization.展开更多
基金Funded by the Fundamental Research Funds for the Central Universities(No.2013-YB-25)the National Natural Science Foundation of China(No.51378408)
文摘The influences of different nano-SiO2（NS） contents on the mechanical properties and rheological behavior of sulfoaluminate cement（SAC） based composite materials were studied.Results show that with increasing content of NS,the apparent viscosity,and shearing strength of fresh paste gradually increase but the fluidity decreases.With a dosage of 3.0%NS,the tensile and flexural strengths of mortars at 56 days were increased by 87.0%and 84.6%,respectively,compared with that in the absence of NS,indicating that the toughness of hardened mortars is significantly improved.Besides,the exothermic peaks of hydration are obviously increased and will earlier occur,and the second and the third peaks appear 2.61 hours and 2.56 hours earlier,respectively than that in the absence of NS,and the hydration of SAC before 8 hours is accelerated.The forming mechanism of strengths was revealed by scanning electron microscopy（SEM）,hydration heat,X-ray diffraction（XRD） and derivative thermogravimetry（DTG）.The micro-aggregate filling effect and nucleation effect at early age and weak pozzolanic effect at late age of NS make the microstructure more compact,which obviously enhances the strength of SAC mortars.
文摘Liquid SiO2 solutions produced by silicon-based nano- powder are covered on the fabric surface by using spray method. Fabric surfaces were coated at the room temperature in air with the different spray nozzles. Surface analysis of the coated fabric was performed by using Contact Angle and SEM pictures. According to the Contact Angles measurements, the coated fabric surfaces showed hydrophobic character between 126 and 146 degrees, and the SiO2 particles sticked to the fabric fibers as seen from SEM picture.
文摘In this study, novel core-shell SiO<sub>2</sub>-coated iron nanoparticles (SiO<sub>2</sub>-nZVI) were synthesized using a one-step Stoeber method. The Malachite green degradation abilities of the nanoparticles were investigated. The effects of ethanol/distilled water volume ratio, presence and absence of PEG, tetraethyl orthosilicate (TEOS) dosage, and hydrolysis time used in the nanoparticles preparation process were investigated. The results indicated that the SiO<sub>2</sub>-coated iron nanoparticles had the highest reduction activity when the particles synthesized with ethanol/H<sub>2</sub>O ratio of 2:1, PEG of 0.15 ml, TEOS of 0.5 ml and the reaction time was 4 h. The SiO<sub>2</sub>-nZVI nanoparticles were characterized using Transmission Electron Microscopy (TEM), Energy Dispersive Spectrometry (EDS) and powder X-Ray Diffraction (XRD). The results showed that the average particles diameter of the SiO<sub>2</sub>-nZVI was 20 - 30 nm. The thickness of the outside SiO<sub>2</sub> film is consistent and approximately 10 nm. The results indicated that the nanoparticles coated completely with a transparent SiO<sub>2</sub>-film. Such nanoparticles could have wide applications in dye decolorization.