Synergistic interplays involving multiple active centers originating from TiO2 nanotube layers(TNT)and ruthenium(Ru)species comprising of both single atoms(SAs)and nanoparticles(NPs)augment the alkaline hydrogen evolu...Synergistic interplays involving multiple active centers originating from TiO2 nanotube layers(TNT)and ruthenium(Ru)species comprising of both single atoms(SAs)and nanoparticles(NPs)augment the alkaline hydrogen evolution reaction(HER)by enhancing Volmer kinetics from rapid water dissociation and improving Tafel kinetics from efficient H*desorption.Atomic layer deposition of Ru with 50 process cycles results in a mixture of Ru SAs and 2.8-0.4 nm NPs present on TNT layers,and it emerges with the highest HER activity among all the electrodes synthesized.A detailed study of the Ti and Ru species using different high-resolution techniques confirmed the presence of Ti^(3+)states and the coexistence of Ru SAs and NPs.With insights from literature,the role of Ti^(3+),appropriate work functions of TNT layers and Ru,and the synergistic effect of Ru SAs and Ru NPs in improving the performance of alkaline HER were elaborated and justified.The aforementioned characteristics led to a remarkable performance by having 9mV onset potentials and 33 mV dec^(-1) of Tafel slopes and a higher turnover frequency of 1.72 H2 s^(-1) at 30 mV.Besides,a notable stability from 28 h staircase chronopotentiometric measurements for TNT@Ru surpasses TNT@Pt in comparison.展开更多
纳米 Ti O2 改性不饱和聚酯树脂 ,其目的是对不饱和聚酯进行同时增韧增强改性。用“反应法”制备的纳米 Ti O2 /UPR,在纳米 Ti O2 与 UPR之间产生的新化学键将纳米 Ti O2 粒子接入 UPR长链上 ,这种新的结构决定了纳米 Ti O2 /UPR的性能...纳米 Ti O2 改性不饱和聚酯树脂 ,其目的是对不饱和聚酯进行同时增韧增强改性。用“反应法”制备的纳米 Ti O2 /UPR,在纳米 Ti O2 与 UPR之间产生的新化学键将纳米 Ti O2 粒子接入 UPR长链上 ,这种新的结构决定了纳米 Ti O2 /UPR的性能。研究结果表明 ,纳米 Ti O2 /UPR的反应活性高于 UPR,纳米 Ti O2 /UPR的冲击韧性和弯曲强度较 UPR分别提高 46%和 5 5 % ,纳米 Ti O2 /UPR的耐热性及介电性与展开更多
A new combination method consisting of ball milling, carbothermic reduction and hydrochloric acid leaching was proposed for the preparation of nanosized synthetic rutile from natural ilmenite. The ball milling was emp...A new combination method consisting of ball milling, carbothermic reduction and hydrochloric acid leaching was proposed for the preparation of nanosized synthetic rutile from natural ilmenite. The ball milling was employed to grind ilmenite into small particles. The carbothermic reduction was carried out to yield a high titanium slag, which would be easily purified by subsequent leaching procedure. Factors affecting the hydrochloric acid process, namely the leaching time, temperature, and acid concentration, were studied. After leaching and calcining the milled and annealed mixture of FeTiO3/C under the optimal conditions, the TiO2 nanoparticles with size of 10-200 nm and purity〉98.0% were obtained.展开更多
The surface of Titanium Hydride (TiH 2) is coated by Nano Titanium Dioxide (TiO 2) particles prepared in both of methods of hydrolysis reaction of Ti(OC 4H 9) 4 and base precipitation reaction of Ti(SO 4) 2. ...The surface of Titanium Hydride (TiH 2) is coated by Nano Titanium Dioxide (TiO 2) particles prepared in both of methods of hydrolysis reaction of Ti(OC 4H 9) 4 and base precipitation reaction of Ti(SO 4) 2. TiH 2 coated with nano TiO 2 particles, in which there is an oxidation film on its surface, shown in the experiments, will obviously achieve good effects on releasing hydrogen slowly in high temperature. There are different structures and properties of TiH 2 coated by nano TiO 2 particles prepared in different ways in high temperature, which can influence on releasing hydrogen.展开更多
TiO2 nanotube arrays （TNTs） electrode loaded with Zn nanoparticles was prepared by anodization and the size of Zn nanoparticle loaded on TNTs electrode was controlled by chronoamperometry deposition time. Results of...TiO2 nanotube arrays （TNTs） electrode loaded with Zn nanoparticles was prepared by anodization and the size of Zn nanoparticle loaded on TNTs electrode was controlled by chronoamperometry deposition time. Results of SEM and XRD analysis show that Zn nanoparticles had a diameter of about 15-25 nm when the deposition time was 3-5 s. The UV-Vis diffuse reflectance spectra show the Zn loaded harvest light with 480-780 nm more effectively than the unloaded sample. The photocurrent response of Zn loaded TNTs electrodes were studied, the results showed that TNTs electrodes loaded with Zn nanoparti-cles has 50% increased photocurrent response under high-pressure mercury lamp irradiation compared with unloaded TNTs electrode.展开更多
基金support from the European Union Horizon 2020 program(project HERMES,nr.952184)the Ministry of Education,Youth and Sports of the Czech Republic for supporting CEMNAT(LM2023037)+1 种基金Czech-NanoLab(LM2023051)infrastructures for providing ALD,SEM,EDX,XPS,TEM,and XRDCzech Science Foundation(project 23-08019X,EXPRO).
文摘Synergistic interplays involving multiple active centers originating from TiO2 nanotube layers(TNT)and ruthenium(Ru)species comprising of both single atoms(SAs)and nanoparticles(NPs)augment the alkaline hydrogen evolution reaction(HER)by enhancing Volmer kinetics from rapid water dissociation and improving Tafel kinetics from efficient H*desorption.Atomic layer deposition of Ru with 50 process cycles results in a mixture of Ru SAs and 2.8-0.4 nm NPs present on TNT layers,and it emerges with the highest HER activity among all the electrodes synthesized.A detailed study of the Ti and Ru species using different high-resolution techniques confirmed the presence of Ti^(3+)states and the coexistence of Ru SAs and NPs.With insights from literature,the role of Ti^(3+),appropriate work functions of TNT layers and Ru,and the synergistic effect of Ru SAs and Ru NPs in improving the performance of alkaline HER were elaborated and justified.The aforementioned characteristics led to a remarkable performance by having 9mV onset potentials and 33 mV dec^(-1) of Tafel slopes and a higher turnover frequency of 1.72 H2 s^(-1) at 30 mV.Besides,a notable stability from 28 h staircase chronopotentiometric measurements for TNT@Ru surpasses TNT@Pt in comparison.
文摘采用溶胶-凝胶法制备高活性Ti基纳米TiO2-ZrO2膜电极.通过X射线衍射分析表明,纳米TiO2-ZrO2粉体呈微-纳二级结构.扫描电子显微镜测试表明,颗粒平均尺寸约为30 nm.通过循环伏安和恒电流电解技术研究发现,Ti/nanoTiO2-ZrO2电极对马来酸电催化还原制备丁二酸的活性要高于Ti/nanoTiO2电极,反应过程受扩散控制.以钛基氧化钌电极为阳极,Ti/nano TiO2-ZrO2膜电极为阴极进行恒电流电解实验.结果表明,控制电流密度20 mA cm-2,温度60℃,丁二酸的产率达到96%.
文摘纳米 Ti O2 改性不饱和聚酯树脂 ,其目的是对不饱和聚酯进行同时增韧增强改性。用“反应法”制备的纳米 Ti O2 /UPR,在纳米 Ti O2 与 UPR之间产生的新化学键将纳米 Ti O2 粒子接入 UPR长链上 ,这种新的结构决定了纳米 Ti O2 /UPR的性能。研究结果表明 ,纳米 Ti O2 /UPR的反应活性高于 UPR,纳米 Ti O2 /UPR的冲击韧性和弯曲强度较 UPR分别提高 46%和 5 5 % ,纳米 Ti O2 /UPR的耐热性及介电性与
基金Project (2007CB613601) supported by the National Basic Research Program of ChinaProject supported by the Postdoctoral Science Foundation of Central South University, China
文摘A new combination method consisting of ball milling, carbothermic reduction and hydrochloric acid leaching was proposed for the preparation of nanosized synthetic rutile from natural ilmenite. The ball milling was employed to grind ilmenite into small particles. The carbothermic reduction was carried out to yield a high titanium slag, which would be easily purified by subsequent leaching procedure. Factors affecting the hydrochloric acid process, namely the leaching time, temperature, and acid concentration, were studied. After leaching and calcining the milled and annealed mixture of FeTiO3/C under the optimal conditions, the TiO2 nanoparticles with size of 10-200 nm and purity〉98.0% were obtained.
文摘The surface of Titanium Hydride (TiH 2) is coated by Nano Titanium Dioxide (TiO 2) particles prepared in both of methods of hydrolysis reaction of Ti(OC 4H 9) 4 and base precipitation reaction of Ti(SO 4) 2. TiH 2 coated with nano TiO 2 particles, in which there is an oxidation film on its surface, shown in the experiments, will obviously achieve good effects on releasing hydrogen slowly in high temperature. There are different structures and properties of TiH 2 coated by nano TiO 2 particles prepared in different ways in high temperature, which can influence on releasing hydrogen.
基金ACKNOWLEDGMENTS This work was supported by the Science Foundation of Chongqing Science and Technology Committee （No.CSTS2009BB4047）, and Innovative Talent Training Project, the Third Stage of ＂211 Project＂ of Chongqing University （No.S-09109）.
文摘TiO2 nanotube arrays （TNTs） electrode loaded with Zn nanoparticles was prepared by anodization and the size of Zn nanoparticle loaded on TNTs electrode was controlled by chronoamperometry deposition time. Results of SEM and XRD analysis show that Zn nanoparticles had a diameter of about 15-25 nm when the deposition time was 3-5 s. The UV-Vis diffuse reflectance spectra show the Zn loaded harvest light with 480-780 nm more effectively than the unloaded sample. The photocurrent response of Zn loaded TNTs electrodes were studied, the results showed that TNTs electrodes loaded with Zn nanoparti-cles has 50% increased photocurrent response under high-pressure mercury lamp irradiation compared with unloaded TNTs electrode.