In this study, to meet the development and application requirements for high-strength and hightoughness energetic structural materials, a representative volume element of a TA15 matrix embedded with a TaZrNb sphere wa...In this study, to meet the development and application requirements for high-strength and hightoughness energetic structural materials, a representative volume element of a TA15 matrix embedded with a TaZrNb sphere was designed and fabricated via diffusion bonding. The mechanisms of the microstructural evolution of the TaZrNb/TA15 interface were investigated via SEM, EBSD, EDS, and XRD.Interface mechanical property tests and in-situ tensile tests were conducted on the sphere-containing structure, and an equivalent tensile-strength model was established for the structure. The results revealed that the TA15 titanium alloy and joint had high density and no pores or cracks. The thickness of the planar joint was approximately 50-60 μm. The average tensile and shear strengths were 767 MPa and 608 MPa, respectively. The thickness of the spherical joint was approximately 60 μm. The Zr and Nb elements in the joint diffused uniformly and formed strong bonds with Ti without forming intermetallic compounds. The interface exhibited submicron grain refinement and a concave-convex interlocking structure. The tensile fracture surface primarily exhibited intergranular fracture combined with some transgranular fracture, which constituted a quasi-brittle fracture mode. The shear fracture surface exhibited brittle fracture with regular arrangements of furrows. Internal fracture occurred along the spherical interface, as revealed by advanced in-situ X-ray microcomputed tomography. The experimental results agreed well with the theoretical predictions, indicating that the high-strength interface contributes to the overall strength and toughness of the sphere-containing structure.展开更多
For a complex flow about multi-element airfoils a mixed grid method is set up. C-type grids are produced on each element′s body and in their wakes at first, O-type grids are given in the outmost area, and H-type grid...For a complex flow about multi-element airfoils a mixed grid method is set up. C-type grids are produced on each element′s body and in their wakes at first, O-type grids are given in the outmost area, and H-type grids are used in middle additional areas. An algebra method is used to produce the initial grids in each area. And the girds are optimized by elliptical differential equation method. Then C-O-H zonal patched grids around multi-element airfoils are produced automatically and efficiently. A time accurate finite-volume integration method is used to solve the compressible laminar and turbulent Navier-Stokes (N-S) equations on the grids. Computational results prove the method to be effective.展开更多
Plasma nitrocarburizing of nanocrystallized （NC） 3J33 steel were carried out at 400 and 430 ℃ for 4 h in a mixed gas of N2：3H2 and different flow rates of rare earths （RE） La and Ce reagents in this paper. Effec...Plasma nitrocarburizing of nanocrystallized （NC） 3J33 steel were carried out at 400 and 430 ℃ for 4 h in a mixed gas of N2：3H2 and different flow rates of rare earths （RE） La and Ce reagents in this paper. Effects of temperature, rare earth addition and its addition amount on the microstructure and hardness of the nitrocarburized layer of NC 3J33 steel were also investigated. Surface phase composition of the nitrocarburized samples was analyzed by X-ray diffraction. Metallurgical structure, La and Ce concentration and microhardness profiles of cross-sectional nitrocarburized samples were studied using an optical microscope, a scanning electron microscope equipped with an energy dispersive X-ray analyzer and Vickers microhardness tester, respectively. The results showed that the surfaces of the nitrocarburized samples were mainly composed of γ＇-Fe4N and α＇-Fe （α-Fe dissolved with N and C） when the NC 3J33 steel was nitrocarburized at 400 ℃. As the temperature was enhanced up to 430 ℃, the surfaces consisted of γ＇-Fe4N, α＇-Fe and low nitrogen compound FeNx （x=0.0324–0.0989）, and simple substance La was presented when RE flow rate was 0.1 L/min. The addition of La and Ce into nitrocarburized gas increased the thickness and hardness of the nitrocarburized layers. The samples nitrocarburized at 400 ℃ with RE flow rate of 0.025 L/min and 430 ℃ of 0.05 L/min possessed the thickest nitrocarburized layer, highest proportion of nitrides and hardness profile. RE elements could diffuse into the nitrocarburized layer and their concentration increased with temperature. The excess RE impeded the permeation of N, C elements and led to thinner compound layer as well as the diffusion layer.展开更多
Composite layer with nitrocarbonide and sulfide was made on the surface of CrMoCu alloy cast iron by combined treatment of ion nitrocarburizing and sulphurizing. The composite layer is composed of sulfide layer, nitro...Composite layer with nitrocarbonide and sulfide was made on the surface of CrMoCu alloy cast iron by combined treatment of ion nitrocarburizing and sulphurizing. The composite layer is composed of sulfide layer, nitrocarbonide hypo-surface layer and its diffusing layer, the size of sulfide globular grains distributing equably on the surface is in nano-micron-scale, and the phase structure of the composite layer is composed of FeS, FeS1-x, Fe2C and Fe3N. Under oil lubrication, sulphurized surface shows good scuffing-resistance only under low velocity, and nitrocarburized and sulphurized surface greatly improves the scuffing-resistance and wear-resistance of CrMoCu alloy cast iron, its integrated friction and wear properties are better than those of the plain and sulphurized surfaces under all the velocities.展开更多
Almost half of all flight accidents caused by inflight icing occur at the approach and landing phases when high-lift devices are deployed.The present study focuses on the optimization of an ice-tolerant multi-element ...Almost half of all flight accidents caused by inflight icing occur at the approach and landing phases when high-lift devices are deployed.The present study focuses on the optimization of an ice-tolerant multi-element airfoil.Dual-objective optimization is carried out with critical hornshaped ice accumulated during the holding phase.The optimization results show that the present optimization method significantly enhances the iced-state and clean-state performance.The optimal multi-element airfoil has a larger deflection angle and wider gap at the slat and the flap compared with the baseline configuration.The sensitivity of each design parameter is analyzed,which verifies the robustness of the design.The design is further assessed when ice is accreted during the approach and landing phases,which also shows performance improvement.展开更多
To study the effects of the gamma reflection of multi-element materials,gamma ray transport models of single-element materials,such as iron and lead,and multielement materials,such as polyethylene and ordinary concret...To study the effects of the gamma reflection of multi-element materials,gamma ray transport models of single-element materials,such as iron and lead,and multielement materials,such as polyethylene and ordinary concrete,were established in this study.Relationships among the albedo factors of the gamma photons and energies and average energy of the reflected gamma rays by material type,material thickness,incident gamma energy,and incidence angle of gamma rays were obtained by Monte Carlo simulation.The results show that the albedo factors of single-element and multi-element materials increase rapidly with an increase in the material thickness.When the thickness of the material increases to a certain value,the albedo factors do not increase further but rather tend to the saturation value.The saturation values for the albedo factors of the gamma photons,and energies and the reflection thickness are related not only to the type of material but also to the incident gamma energy and incidence angle of the gamma rays.At a given incident gamma energy,which is between 0.2 and 2.5 MeV,the smaller the effective atomic number of the multi-element material is,the higher the saturation values of the albedo factors are.The larger the incidence angle of the gamma ray is,the greater the saturation value of the gamma albedo factor,saturation reflection thickness,and average saturation energy of the reflected gamma photons are.展开更多
The paper is to integrate aerodynamic and aero-acoustic optimizatiom design of high lift devices,especially for two-element airfoils with slat.Aerodynamic analysis on flow field utilizes a high-order,high-resolution s...The paper is to integrate aerodynamic and aero-acoustic optimizatiom design of high lift devices,especially for two-element airfoils with slat.Aerodynamic analysis on flow field utilizes a high-order,high-resolution spatial differential method for large eddy simulation(LES),which can guarantee accuracy and efficiency.The aeroacoustic analysis for noise level is calculated with Ffowcs Williams-Hawkings(FW-H)integration formula.Fidelity of calculation is verified by standard models.Method of streamline-based Euler simulation(MSES)is used to obtain the aerodynamic characters.Based on the confirmation of numerical methods,detailed research has been conducted for the leading edge slat on multi-element airfoils.Various slot parameter influences on noise are analyzed.The results of the slot optimization parameters can be used in multi-element airfoil design.展开更多
Traditional distributed denial of service(DDoS)detection methods need a lot of computing resource,and many of them which are based on single element have high missing rate and false alarm rate.In order to solve the pr...Traditional distributed denial of service(DDoS)detection methods need a lot of computing resource,and many of them which are based on single element have high missing rate and false alarm rate.In order to solve the problems,this paper proposes a DDoS attack information fusion method based on CNN for multi-element data.Firstly,according to the distribution,concentration and high traffic abruptness of DDoS attacks,this paper defines six features which are respectively obtained from the elements of source IP address,destination IP address,source port,destination port,packet size and the number of IP packets.Then,we propose feature weight calculation algorithm based on principal component analysis to measure the importance of different features in different network environment.The algorithm of weighted multi-element feature fusion proposed in this paper is used to fuse different features,and obtain multi-element fusion feature(MEFF)value.Finally,the DDoS attack information fusion classification model is established by using convolutional neural network and support vector machine respectively based on the MEFF time series.Experimental results show that the information fusion method proposed can effectively fuse multi-element data,reduce the missing rate and total error rate,memory resource consumption,running time,and improve the detection rate.展开更多
A multivariate statistical analysis was performed on multi-element soil geochemical data from the Koda Hill-Bulenga gold prospects in the Wa-Lawra gold belt, northwest Ghana. The objectives of the study were to define...A multivariate statistical analysis was performed on multi-element soil geochemical data from the Koda Hill-Bulenga gold prospects in the Wa-Lawra gold belt, northwest Ghana. The objectives of the study were to define gold relationships with other trace elements to determine possible pathfinder elements for gold from the soil geochemical data. The study focused on seven elements, namely, Au, Fe, Pb, Mn, Ag, As and Cu. Factor analysis and hierarchical cluster analysis were performed on the analyzed samples. Factor analysis explained 79.093% of the total variance of the data through three factors. This had the gold factor being factor 3, having associations of copper, iron, lead and manganese and accounting for 20.903% of the total variance. From hierarchical clustering, gold was also observed to be clustering with lead, copper, arsenic and silver. There was further indication that, gold concentrations were lower than that of its associations. It can be inferred from the results that, the occurrence of gold and its associated elements can be linked to both primary dispersion from underlying rocks and secondary processes such as lateritization. This data shows that Fe and Mn strongly associated with gold, and alongside Pb, Ag, As and Cu, these elements can be used as pathfinders for gold in the area, with ferruginous zones as targets.展开更多
Low-temperature sulfurizing after nitrocarburizing are compared with only low-temperature sulfurizing on the surface of CrMoCu alloyed cast iron, the surface morphologies and microstructures are investigated by SEM an...Low-temperature sulfurizing after nitrocarburizing are compared with only low-temperature sulfurizing on the surface of CrMoCu alloyed cast iron, the surface morphologies and microstructures are investigated by SEM and EDS. Results show that under proper treatment parameters, there are sulfide layer on both of the surfaces, and can more easily obtain sulfide layers on the surface of nitrocarburizing. Forming mechanism of sulfides were also studied elementarily.展开更多
The technics of combined treatment of ion nitrocarburizing-ion sulphurizing of CrMoCu alloy cast iron has been investigated and the compound layer with nitrocarbonide and sulphide has been made on the surface of CrMoC...The technics of combined treatment of ion nitrocarburizing-ion sulphurizing of CrMoCu alloy cast iron has been investigated and the compound layer with nitrocarbonide and sulphide has been made on the surface of CrMoCu alloy cast iron. The compound layer is composed of sulfide surface layer and the nitrocarbonide hypo-surface layer and its diffusing layer. The size of sulfide globular grains distributing equably on the surface is in nano-rnicron-scale, and the phase structure of the compound layer is composed of FeS^ FeSi^ Fe2C and Fe3N. Under dry sliding condition, the friction-reducing of sulphurized surface is good, but its function time can’t last very long. The nitrocarbonided+sulphurized surface can greatly improve the wear-resistance and the friction-reducing of CrMoCu alloy cast iron, and its integrated friction and wear properties are better than plain and sulphurized surfaces’.展开更多
The paper presents the results of wear and metallography tests of tool steel grades: ASTM A681, Chl2M and CH12FS per COST, AMS 6437E i BS X46Crl3, all surface hardened by the Carbo process (carburizing) and by the NiC...The paper presents the results of wear and metallography tests of tool steel grades: ASTM A681, Chl2M and CH12FS per COST, AMS 6437E i BS X46Crl3, all surface hardened by the Carbo process (carburizing) and by the NiCar process (nitrocarburizing). The thermo-chemical treatment was conducted in powder pack for a duration of 6 h (carburizing) and for 4 h in the case of nitrocarburizing. Factors investigated were: morphology, depth and microhardness of the cases obtained, their microstructure, as well as phase composition. Wear tests were conducted by the three cylinder-cone method. Wear velocity was 0.58 m/s, unit load was 50 MPa and 400Mpa, wear path was 3470 m. Oil SAE30 was applied at the rate of 30 drops per minute.展开更多
In this paper the effect of rare earth elements on the toughness and impact wear resistance of nitrocarburiz- ing layers is studied.The experimental results show that the toughness and impact wear resistance of RE-nit...In this paper the effect of rare earth elements on the toughness and impact wear resistance of nitrocarburiz- ing layers is studied.The experimental results show that the toughness and impact wear resistance of RE-nitrocarburizing layers are increased significantly compared with that of conventional nitrocarburizing lay- ers.The service life of hot die for manufacturing bicycle bolts increased more than 100%.The impact wear mechanism of RE-nitrocarburizing layers is investigated by SEM as well.展开更多
A factor analysis was applied to soil geochemical data to define anomalies related to buried Pb-Zn mineralization.A favorable main factor with a strong association of the elements Zn,Cu and Pb,related to mineralizatio...A factor analysis was applied to soil geochemical data to define anomalies related to buried Pb-Zn mineralization.A favorable main factor with a strong association of the elements Zn,Cu and Pb,related to mineralization,was selected for interpretation.The median+2 MAD(median absolute deviation)method of exploratory data analysis(EDA)and C-A(concentration-area)fractal modeling were then applied to the Mahalanobis distance,as defined by Zn,Cu and Pb from the factor analysis to set the thresholds for defining multi-element anomalies.As a result,the median+2 MAD method more successfully identified the Pb-Zn mineralization than the C-A fractal model.The soil anomaly identified by the median+2 MAD method on the Mahalanobis distances defined by three principal elements(Zn,Cu and Pb)rather than thirteen elements(Co,Zn,Cu,V,Mo,Ni,Cr,Mn,Pb,Ba,Sr,Zr and Ti)was the more favorable reflection of the ore body.The identified soil geochemical anomalies were compared with the in situ economic Pb-Zn ore bodies for validation.The results showed that the median+2 MAD approach is capable of mapping both strong and weak geochemical anomalies related to buried Pb-Zn mineralization,which is therefore useful at the reconnaissance drilling stage.展开更多
Multi-element analysis in historical sites is a major issue in archaeological studies;however,this approach is almost unknown among Iranian scholars.Geochemical multi-element analysis of soil is very important to eval...Multi-element analysis in historical sites is a major issue in archaeological studies;however,this approach is almost unknown among Iranian scholars.Geochemical multi-element analysis of soil is very important to evaluate anthropogenic activities.The aim of this study consists of assessing the potential usefulness of multi-elemental soil analysis,obtained by Analytical Jena atomic absorption spectrophotometer(AAS) and ICP-MS,to recognize ancient anthropogenic features on the territory of Tappe Rivi(North Khorasan,Iran).For that purpose,a total of 80 ancient soil samples were sampled from each soil horizon and cultural layer.The research involved Fe,Al,Cd,Cu,Ni,Co,Cr,Pb,and P which trace element samples were extracted according to the International Standard ISO 11466 and phosphorus samples by Olsen method.Besides,the contamination of the soils was assessed based on enrichment factors(EFs) by using Fe as a reference element.This geochemical/archaeological approach highlights that the content of most elements in the Parthian and Sassanid ages were significantly higher than the contents of the elements in other zones,which shows that by the development of the eras,the content of the elements has also increased.Also,the accumulation of metals in the Rivi site was significantly higher than in the control area.Among the sampled zones,enrichment factor(EF) indicated that the enrichment of Cu and phosphate at the Parthian and Sassanid had the highest content.This result is important because it shows that the amount of metals and human activities are directly related to each other during different ages.展开更多
The effects of Al and Sc on mechanical properties of FeCoNi multi-element alloys(MEAs) were investigated by compressive tests. The microstructures of FeCoNi MEAs with different contents of Al and Sc were characterized...The effects of Al and Sc on mechanical properties of FeCoNi multi-element alloys(MEAs) were investigated by compressive tests. The microstructures of FeCoNi MEAs with different contents of Al and Sc were characterized and the strengthening mechanisms were discussed. The results show that FeCoNi MEA with a low content of Al has a face-centered cubic(FCC) structure. The yield strength increases linearly with the increase of Al content, which is largely caused by solid solution hardening. Further addition of Sc can promote the formation of a new phase in(FeCoNi)1-xAlx MEAs. A minor addition of Sc can significantly increase the yield strengths of(FeCoNi)1-xAlx MEAs with a low Al content and improve the compressive plasticity of(FeCoNi)1-xAlx MEAs with a high Al content.展开更多
Winter jujube(Ziziphus jujuba'Dongzao')is greatly appreciated by consumers for its excellent quality,but brand infringement frequently occurs in the market.Here,we first determined a total of 38 elements in 16...Winter jujube(Ziziphus jujuba'Dongzao')is greatly appreciated by consumers for its excellent quality,but brand infringement frequently occurs in the market.Here,we first determined a total of 38 elements in 167 winter jujube samples from the main winter jujube producing areas of China by inductively coupled plasma mass spectrometer(ICP-MS).As a result,16 elements(Mg,K,Mn,Cu,Zn,Mo,Ba,Be,As,Se,Cd,Sb,Ce,Er,Tl,and Pb)exhibited significant differences in samples from different producing areas.Supervised linear discriminant analysis(LDA)and orthogonal projection to latent structures discriminant analysis(OPLS-DA)showed better performance in identifying the origin of samples than unsupervised principal component analysis(PCA).LDA and OPLS-DA had a mean identification accuracy of 87.84 and 94.64%in the testing set,respectively.By using the multilayer perceptron(MLP)and C5.0,the prediction accuracy of the models could reach 96.36 and 91.06%,respectively.Based on the above four chemometric methods,Cd,Tl,Mo and Se were selected as the main variables and principal markers for the origin identification of winter jujube.Overall,this study demonstrates that it is practical and precise to identify the origin of winter jujube through multi-element fingerprint analysis with chemometrics,and may also provide reference for establishing the origin traceability system of other fruits.展开更多
A comparison has been made between plasma and gas nitrocarburizing processes for C60W steel in terms of structural features of the layers and the tribological properties of the specimens. Gaseous treatments were perfo...A comparison has been made between plasma and gas nitrocarburizing processes for C60W steel in terms of structural features of the layers and the tribological properties of the specimens. Gaseous treatments were performed in a sealed quench industrial furnace in optimized process cycles. For plasma nitrocarburizing, a semi - industrial size unit was operated at a range of process parameters. Experimental results indicate that increasing the treatment time increases the thickness of the compound layer but lowers the wear resistance. Plasma treatment produced a more effective case depth compared with gaseous process, providing a better uniformity. Analysis of X-ray diffraction patterns indicated that the compound layer in gas nitrocarburizing consisted of both e and y’ phases, whereas in plasma nitrocarburizing the e phase was not detected.展开更多
A hybrid Cartesian grid/gridless method is developed for calculating viscous flows over multi-element airfoils.The method adopts an unstructured Cartesian grid to cover most areas of the computational domain and leave...A hybrid Cartesian grid/gridless method is developed for calculating viscous flows over multi-element airfoils.The method adopts an unstructured Cartesian grid to cover most areas of the computational domain and leaves only small region adjacent to the aerodynamic bodies to be filled with the cloud of points used in the gridless methods,which results in a better combination of the computational efficiency of the Cartesian grid and the flexibility of the gridless method in handling complex geometries.The clouds of points in the local gridless region are implemented in an anisotropic way according to the features of the thin boundary layer of the viscous flows over the airfoils,and the clouds of points at the vicinity of the interface between the grid and the gridless regions are also controlled by using an adaptive refinement technique during the generation of the unstructured Cartesian grid.An implementation of the resulting hybrid method is presented for solving two-dimensional compressible Navier-Stokes(NS)equations.The simulations of the viscous flows over a RAE2822airfoil or a two-element airfoil are successfully carried out,and the obtained results agree well with the available experimental data.展开更多
Compared with the single sulphurating treatment,the duplex treatment of nitrocarburizing-sulphurating can more effectively improve the properties of steel such as friction-reducing,wear resistance and anti-scuffing.Un...Compared with the single sulphurating treatment,the duplex treatment of nitrocarburizing-sulphurating can more effectively improve the properties of steel such as friction-reducing,wear resistance and anti-scuffing.Under the same processing parameters,the sulphide layers were fabricated on the surface of CrMoCu alloy cast iron by single ion-sulphurating treatment and nitrocarburizing-sulphurating duplex treatment,respectively.Through the analysis of the sulphide,the effect of the nitrocarburizing on the fabrication of the sulphide layer was investigated.And the result shows that the fabrication of sulphide layer is promoted by the nitrocarburizing treatment.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.12372351).
文摘In this study, to meet the development and application requirements for high-strength and hightoughness energetic structural materials, a representative volume element of a TA15 matrix embedded with a TaZrNb sphere was designed and fabricated via diffusion bonding. The mechanisms of the microstructural evolution of the TaZrNb/TA15 interface were investigated via SEM, EBSD, EDS, and XRD.Interface mechanical property tests and in-situ tensile tests were conducted on the sphere-containing structure, and an equivalent tensile-strength model was established for the structure. The results revealed that the TA15 titanium alloy and joint had high density and no pores or cracks. The thickness of the planar joint was approximately 50-60 μm. The average tensile and shear strengths were 767 MPa and 608 MPa, respectively. The thickness of the spherical joint was approximately 60 μm. The Zr and Nb elements in the joint diffused uniformly and formed strong bonds with Ti without forming intermetallic compounds. The interface exhibited submicron grain refinement and a concave-convex interlocking structure. The tensile fracture surface primarily exhibited intergranular fracture combined with some transgranular fracture, which constituted a quasi-brittle fracture mode. The shear fracture surface exhibited brittle fracture with regular arrangements of furrows. Internal fracture occurred along the spherical interface, as revealed by advanced in-situ X-ray microcomputed tomography. The experimental results agreed well with the theoretical predictions, indicating that the high-strength interface contributes to the overall strength and toughness of the sphere-containing structure.
文摘For a complex flow about multi-element airfoils a mixed grid method is set up. C-type grids are produced on each element′s body and in their wakes at first, O-type grids are given in the outmost area, and H-type grids are used in middle additional areas. An algebra method is used to produce the initial grids in each area. And the girds are optimized by elliptical differential equation method. Then C-O-H zonal patched grids around multi-element airfoils are produced automatically and efficiently. A time accurate finite-volume integration method is used to solve the compressible laminar and turbulent Navier-Stokes (N-S) equations on the grids. Computational results prove the method to be effective.
基金supported by the National Natural Science Foundation of China (50871035 and 51071061)Program of Excellent Team at Harbin In-stitute of Technology
文摘Plasma nitrocarburizing of nanocrystallized （NC） 3J33 steel were carried out at 400 and 430 ℃ for 4 h in a mixed gas of N2：3H2 and different flow rates of rare earths （RE） La and Ce reagents in this paper. Effects of temperature, rare earth addition and its addition amount on the microstructure and hardness of the nitrocarburized layer of NC 3J33 steel were also investigated. Surface phase composition of the nitrocarburized samples was analyzed by X-ray diffraction. Metallurgical structure, La and Ce concentration and microhardness profiles of cross-sectional nitrocarburized samples were studied using an optical microscope, a scanning electron microscope equipped with an energy dispersive X-ray analyzer and Vickers microhardness tester, respectively. The results showed that the surfaces of the nitrocarburized samples were mainly composed of γ＇-Fe4N and α＇-Fe （α-Fe dissolved with N and C） when the NC 3J33 steel was nitrocarburized at 400 ℃. As the temperature was enhanced up to 430 ℃, the surfaces consisted of γ＇-Fe4N, α＇-Fe and low nitrogen compound FeNx （x=0.0324–0.0989）, and simple substance La was presented when RE flow rate was 0.1 L/min. The addition of La and Ce into nitrocarburized gas increased the thickness and hardness of the nitrocarburized layers. The samples nitrocarburized at 400 ℃ with RE flow rate of 0.025 L/min and 430 ℃ of 0.05 L/min possessed the thickest nitrocarburized layer, highest proportion of nitrides and hardness profile. RE elements could diffuse into the nitrocarburized layer and their concentration increased with temperature. The excess RE impeded the permeation of N, C elements and led to thinner compound layer as well as the diffusion layer.
基金Project (50235030) supported by the National Natural Science Foundation of China project (G1999065009) supported by the National Basic Research Program of China
文摘Composite layer with nitrocarbonide and sulfide was made on the surface of CrMoCu alloy cast iron by combined treatment of ion nitrocarburizing and sulphurizing. The composite layer is composed of sulfide layer, nitrocarbonide hypo-surface layer and its diffusing layer, the size of sulfide globular grains distributing equably on the surface is in nano-micron-scale, and the phase structure of the composite layer is composed of FeS, FeS1-x, Fe2C and Fe3N. Under oil lubrication, sulphurized surface shows good scuffing-resistance only under low velocity, and nitrocarburized and sulphurized surface greatly improves the scuffing-resistance and wear-resistance of CrMoCu alloy cast iron, its integrated friction and wear properties are better than those of the plain and sulphurized surfaces under all the velocities.
基金supported by the National Key Project of China(No.GJXM92579)National Natural Science Foundation of China(Nos.92052203,11872230 and 91852108)。
文摘Almost half of all flight accidents caused by inflight icing occur at the approach and landing phases when high-lift devices are deployed.The present study focuses on the optimization of an ice-tolerant multi-element airfoil.Dual-objective optimization is carried out with critical hornshaped ice accumulated during the holding phase.The optimization results show that the present optimization method significantly enhances the iced-state and clean-state performance.The optimal multi-element airfoil has a larger deflection angle and wider gap at the slat and the flap compared with the baseline configuration.The sensitivity of each design parameter is analyzed,which verifies the robustness of the design.The design is further assessed when ice is accreted during the approach and landing phases,which also shows performance improvement.
基金This work was supported by the State Key Lab of Intense Pulsed Radiation Simulation and Effect Basic Research Foundation(No.SKLIPR1504).
文摘To study the effects of the gamma reflection of multi-element materials,gamma ray transport models of single-element materials,such as iron and lead,and multielement materials,such as polyethylene and ordinary concrete,were established in this study.Relationships among the albedo factors of the gamma photons and energies and average energy of the reflected gamma rays by material type,material thickness,incident gamma energy,and incidence angle of gamma rays were obtained by Monte Carlo simulation.The results show that the albedo factors of single-element and multi-element materials increase rapidly with an increase in the material thickness.When the thickness of the material increases to a certain value,the albedo factors do not increase further but rather tend to the saturation value.The saturation values for the albedo factors of the gamma photons,and energies and the reflection thickness are related not only to the type of material but also to the incident gamma energy and incidence angle of the gamma rays.At a given incident gamma energy,which is between 0.2 and 2.5 MeV,the smaller the effective atomic number of the multi-element material is,the higher the saturation values of the albedo factors are.The larger the incidence angle of the gamma ray is,the greater the saturation value of the gamma albedo factor,saturation reflection thickness,and average saturation energy of the reflected gamma photons are.
文摘The paper is to integrate aerodynamic and aero-acoustic optimizatiom design of high lift devices,especially for two-element airfoils with slat.Aerodynamic analysis on flow field utilizes a high-order,high-resolution spatial differential method for large eddy simulation(LES),which can guarantee accuracy and efficiency.The aeroacoustic analysis for noise level is calculated with Ffowcs Williams-Hawkings(FW-H)integration formula.Fidelity of calculation is verified by standard models.Method of streamline-based Euler simulation(MSES)is used to obtain the aerodynamic characters.Based on the confirmation of numerical methods,detailed research has been conducted for the leading edge slat on multi-element airfoils.Various slot parameter influences on noise are analyzed.The results of the slot optimization parameters can be used in multi-element airfoil design.
基金This work was supported by the Hainan Provincial Natural Science Foundation of China[2018CXTD333,617048]National Natural Science Foundation of China[61762033,61702539]+1 种基金Hainan University Doctor Start Fund Project[kyqd1328]Hainan University Youth Fund Project[qnjj1444].
文摘Traditional distributed denial of service(DDoS)detection methods need a lot of computing resource,and many of them which are based on single element have high missing rate and false alarm rate.In order to solve the problems,this paper proposes a DDoS attack information fusion method based on CNN for multi-element data.Firstly,according to the distribution,concentration and high traffic abruptness of DDoS attacks,this paper defines six features which are respectively obtained from the elements of source IP address,destination IP address,source port,destination port,packet size and the number of IP packets.Then,we propose feature weight calculation algorithm based on principal component analysis to measure the importance of different features in different network environment.The algorithm of weighted multi-element feature fusion proposed in this paper is used to fuse different features,and obtain multi-element fusion feature(MEFF)value.Finally,the DDoS attack information fusion classification model is established by using convolutional neural network and support vector machine respectively based on the MEFF time series.Experimental results show that the information fusion method proposed can effectively fuse multi-element data,reduce the missing rate and total error rate,memory resource consumption,running time,and improve the detection rate.
文摘A multivariate statistical analysis was performed on multi-element soil geochemical data from the Koda Hill-Bulenga gold prospects in the Wa-Lawra gold belt, northwest Ghana. The objectives of the study were to define gold relationships with other trace elements to determine possible pathfinder elements for gold from the soil geochemical data. The study focused on seven elements, namely, Au, Fe, Pb, Mn, Ag, As and Cu. Factor analysis and hierarchical cluster analysis were performed on the analyzed samples. Factor analysis explained 79.093% of the total variance of the data through three factors. This had the gold factor being factor 3, having associations of copper, iron, lead and manganese and accounting for 20.903% of the total variance. From hierarchical clustering, gold was also observed to be clustering with lead, copper, arsenic and silver. There was further indication that, gold concentrations were lower than that of its associations. It can be inferred from the results that, the occurrence of gold and its associated elements can be linked to both primary dispersion from underlying rocks and secondary processes such as lateritization. This data shows that Fe and Mn strongly associated with gold, and alongside Pb, Ag, As and Cu, these elements can be used as pathfinders for gold in the area, with ferruginous zones as targets.
文摘Low-temperature sulfurizing after nitrocarburizing are compared with only low-temperature sulfurizing on the surface of CrMoCu alloyed cast iron, the surface morphologies and microstructures are investigated by SEM and EDS. Results show that under proper treatment parameters, there are sulfide layer on both of the surfaces, and can more easily obtain sulfide layers on the surface of nitrocarburizing. Forming mechanism of sulfides were also studied elementarily.
基金This rescarch is granted by National Natural Science Foundation of China(50235030)“973”Project(G1999065009).
文摘The technics of combined treatment of ion nitrocarburizing-ion sulphurizing of CrMoCu alloy cast iron has been investigated and the compound layer with nitrocarbonide and sulphide has been made on the surface of CrMoCu alloy cast iron. The compound layer is composed of sulfide surface layer and the nitrocarbonide hypo-surface layer and its diffusing layer. The size of sulfide globular grains distributing equably on the surface is in nano-rnicron-scale, and the phase structure of the compound layer is composed of FeS^ FeSi^ Fe2C and Fe3N. Under dry sliding condition, the friction-reducing of sulphurized surface is good, but its function time can’t last very long. The nitrocarbonided+sulphurized surface can greatly improve the wear-resistance and the friction-reducing of CrMoCu alloy cast iron, and its integrated friction and wear properties are better than plain and sulphurized surfaces’.
文摘The paper presents the results of wear and metallography tests of tool steel grades: ASTM A681, Chl2M and CH12FS per COST, AMS 6437E i BS X46Crl3, all surface hardened by the Carbo process (carburizing) and by the NiCar process (nitrocarburizing). The thermo-chemical treatment was conducted in powder pack for a duration of 6 h (carburizing) and for 4 h in the case of nitrocarburizing. Factors investigated were: morphology, depth and microhardness of the cases obtained, their microstructure, as well as phase composition. Wear tests were conducted by the three cylinder-cone method. Wear velocity was 0.58 m/s, unit load was 50 MPa and 400Mpa, wear path was 3470 m. Oil SAE30 was applied at the rate of 30 drops per minute.
基金the National Natural Science Foundation of China
文摘In this paper the effect of rare earth elements on the toughness and impact wear resistance of nitrocarburiz- ing layers is studied.The experimental results show that the toughness and impact wear resistance of RE-nitrocarburizing layers are increased significantly compared with that of conventional nitrocarburizing lay- ers.The service life of hot die for manufacturing bicycle bolts increased more than 100%.The impact wear mechanism of RE-nitrocarburizing layers is investigated by SEM as well.
文摘A factor analysis was applied to soil geochemical data to define anomalies related to buried Pb-Zn mineralization.A favorable main factor with a strong association of the elements Zn,Cu and Pb,related to mineralization,was selected for interpretation.The median+2 MAD(median absolute deviation)method of exploratory data analysis(EDA)and C-A(concentration-area)fractal modeling were then applied to the Mahalanobis distance,as defined by Zn,Cu and Pb from the factor analysis to set the thresholds for defining multi-element anomalies.As a result,the median+2 MAD method more successfully identified the Pb-Zn mineralization than the C-A fractal model.The soil anomaly identified by the median+2 MAD method on the Mahalanobis distances defined by three principal elements(Zn,Cu and Pb)rather than thirteen elements(Co,Zn,Cu,V,Mo,Ni,Cr,Mn,Pb,Ba,Sr,Zr and Ti)was the more favorable reflection of the ore body.The identified soil geochemical anomalies were compared with the in situ economic Pb-Zn ore bodies for validation.The results showed that the median+2 MAD approach is capable of mapping both strong and weak geochemical anomalies related to buried Pb-Zn mineralization,which is therefore useful at the reconnaissance drilling stage.
文摘Multi-element analysis in historical sites is a major issue in archaeological studies;however,this approach is almost unknown among Iranian scholars.Geochemical multi-element analysis of soil is very important to evaluate anthropogenic activities.The aim of this study consists of assessing the potential usefulness of multi-elemental soil analysis,obtained by Analytical Jena atomic absorption spectrophotometer(AAS) and ICP-MS,to recognize ancient anthropogenic features on the territory of Tappe Rivi(North Khorasan,Iran).For that purpose,a total of 80 ancient soil samples were sampled from each soil horizon and cultural layer.The research involved Fe,Al,Cd,Cu,Ni,Co,Cr,Pb,and P which trace element samples were extracted according to the International Standard ISO 11466 and phosphorus samples by Olsen method.Besides,the contamination of the soils was assessed based on enrichment factors(EFs) by using Fe as a reference element.This geochemical/archaeological approach highlights that the content of most elements in the Parthian and Sassanid ages were significantly higher than the contents of the elements in other zones,which shows that by the development of the eras,the content of the elements has also increased.Also,the accumulation of metals in the Rivi site was significantly higher than in the control area.Among the sampled zones,enrichment factor(EF) indicated that the enrichment of Cu and phosphate at the Parthian and Sassanid had the highest content.This result is important because it shows that the amount of metals and human activities are directly related to each other during different ages.
基金Projects(51671217,51604112) supported by the National Natural Science Foundation of ChinaProject(2017JJ3089) supported by the Natural Science Foundation of Hunan Province,China
文摘The effects of Al and Sc on mechanical properties of FeCoNi multi-element alloys(MEAs) were investigated by compressive tests. The microstructures of FeCoNi MEAs with different contents of Al and Sc were characterized and the strengthening mechanisms were discussed. The results show that FeCoNi MEA with a low content of Al has a face-centered cubic(FCC) structure. The yield strength increases linearly with the increase of Al content, which is largely caused by solid solution hardening. Further addition of Sc can promote the formation of a new phase in(FeCoNi)1-xAlx MEAs. A minor addition of Sc can significantly increase the yield strengths of(FeCoNi)1-xAlx MEAs with a low Al content and improve the compressive plasticity of(FeCoNi)1-xAlx MEAs with a high Al content.
基金This work was supported by the Scientific Research Foundation for High Level Talents of Qingdao Agricultural University,China(665-1120015)the National Program for Quality and Safety Risk Assessment of Agricultural Products of China(GJFP2019011)the National Natural Science Foundation of China(42207017).
文摘Winter jujube(Ziziphus jujuba'Dongzao')is greatly appreciated by consumers for its excellent quality,but brand infringement frequently occurs in the market.Here,we first determined a total of 38 elements in 167 winter jujube samples from the main winter jujube producing areas of China by inductively coupled plasma mass spectrometer(ICP-MS).As a result,16 elements(Mg,K,Mn,Cu,Zn,Mo,Ba,Be,As,Se,Cd,Sb,Ce,Er,Tl,and Pb)exhibited significant differences in samples from different producing areas.Supervised linear discriminant analysis(LDA)and orthogonal projection to latent structures discriminant analysis(OPLS-DA)showed better performance in identifying the origin of samples than unsupervised principal component analysis(PCA).LDA and OPLS-DA had a mean identification accuracy of 87.84 and 94.64%in the testing set,respectively.By using the multilayer perceptron(MLP)and C5.0,the prediction accuracy of the models could reach 96.36 and 91.06%,respectively.Based on the above four chemometric methods,Cd,Tl,Mo and Se were selected as the main variables and principal markers for the origin identification of winter jujube.Overall,this study demonstrates that it is practical and precise to identify the origin of winter jujube through multi-element fingerprint analysis with chemometrics,and may also provide reference for establishing the origin traceability system of other fruits.
基金Isfahan University of Technology for financial supportthe Iranian Surface Research and Engineering Centre for plasma processing equipment.
文摘A comparison has been made between plasma and gas nitrocarburizing processes for C60W steel in terms of structural features of the layers and the tribological properties of the specimens. Gaseous treatments were performed in a sealed quench industrial furnace in optimized process cycles. For plasma nitrocarburizing, a semi - industrial size unit was operated at a range of process parameters. Experimental results indicate that increasing the treatment time increases the thickness of the compound layer but lowers the wear resistance. Plasma treatment produced a more effective case depth compared with gaseous process, providing a better uniformity. Analysis of X-ray diffraction patterns indicated that the compound layer in gas nitrocarburizing consisted of both e and y’ phases, whereas in plasma nitrocarburizing the e phase was not detected.
基金Supported by the National Natural Science Foundation of China(11172134)the Funding of Jiangsu Innovation Program for Graduate Education(CXZZ110192)the Priority Academic Program Development of Jiangsu Higher Education Institutions
文摘A hybrid Cartesian grid/gridless method is developed for calculating viscous flows over multi-element airfoils.The method adopts an unstructured Cartesian grid to cover most areas of the computational domain and leaves only small region adjacent to the aerodynamic bodies to be filled with the cloud of points used in the gridless methods,which results in a better combination of the computational efficiency of the Cartesian grid and the flexibility of the gridless method in handling complex geometries.The clouds of points in the local gridless region are implemented in an anisotropic way according to the features of the thin boundary layer of the viscous flows over the airfoils,and the clouds of points at the vicinity of the interface between the grid and the gridless regions are also controlled by using an adaptive refinement technique during the generation of the unstructured Cartesian grid.An implementation of the resulting hybrid method is presented for solving two-dimensional compressible Navier-Stokes(NS)equations.The simulations of the viscous flows over a RAE2822airfoil or a two-element airfoil are successfully carried out,and the obtained results agree well with the available experimental data.
文摘Compared with the single sulphurating treatment,the duplex treatment of nitrocarburizing-sulphurating can more effectively improve the properties of steel such as friction-reducing,wear resistance and anti-scuffing.Under the same processing parameters,the sulphide layers were fabricated on the surface of CrMoCu alloy cast iron by single ion-sulphurating treatment and nitrocarburizing-sulphurating duplex treatment,respectively.Through the analysis of the sulphide,the effect of the nitrocarburizing on the fabrication of the sulphide layer was investigated.And the result shows that the fabrication of sulphide layer is promoted by the nitrocarburizing treatment.