The antioxidant N-isopropyl-N'-phenyl-p-phenylenediamine(4010NA)was dissolved in ethanol and impregnated into silica aerogel(SAG)via vacuum-pressure cycles,yielding composite particles(A-N)with enhanced sustained-...The antioxidant N-isopropyl-N'-phenyl-p-phenylenediamine(4010NA)was dissolved in ethanol and impregnated into silica aerogel(SAG)via vacuum-pressure cycles,yielding composite particles(A-N)with enhanced sustained-release and reinforcing capabilities.The effect of A-N on the mechanical properties and thermal-oxidative aging resistance of styrene-butadiene rubber(SBR)vulcanizates was investigated.TGA and BET assessments indicated that the loading efficiency of 4010NA in SAG reached 14.26%within ethanol's solu bility limit.Incorporating A-N into SBR vulcanizates significantly elevated tensile strength by 17.5%and elongation at break by 41.9%over those with fumed silica and free4010NA.Furthermore,A-N notably enhanced the thermal-oxidative aging resistance of SBR.After aging for 96 h at 100℃,the tensile strength and elongation at break of SBR with A-N sustained 70.09%and 58.61%of their initial values,respectively,with the retention rate of elongation at break being 62.8%higher than that of SBR with fumed silica and free antioxidant.The study revealed that A-N composite particles significantly inhibited the crosslinking in SBR's molecular chains,reducing hardening and embrittlement during later thermal-oxidative aging stages.展开更多
基金financially supported by Natural Science Foundation of Shanxi Province(No.202303021211075)Shanxi Province Science and Technology Key Research and Development Project(No.201903D321065)Shanxi-Zheda Institute of Advanced Materials and Chemical Engineering(No.2021SX-TD011)。
文摘The antioxidant N-isopropyl-N'-phenyl-p-phenylenediamine(4010NA)was dissolved in ethanol and impregnated into silica aerogel(SAG)via vacuum-pressure cycles,yielding composite particles(A-N)with enhanced sustained-release and reinforcing capabilities.The effect of A-N on the mechanical properties and thermal-oxidative aging resistance of styrene-butadiene rubber(SBR)vulcanizates was investigated.TGA and BET assessments indicated that the loading efficiency of 4010NA in SAG reached 14.26%within ethanol's solu bility limit.Incorporating A-N into SBR vulcanizates significantly elevated tensile strength by 17.5%and elongation at break by 41.9%over those with fumed silica and free4010NA.Furthermore,A-N notably enhanced the thermal-oxidative aging resistance of SBR.After aging for 96 h at 100℃,the tensile strength and elongation at break of SBR with A-N sustained 70.09%and 58.61%of their initial values,respectively,with the retention rate of elongation at break being 62.8%higher than that of SBR with fumed silica and free antioxidant.The study revealed that A-N composite particles significantly inhibited the crosslinking in SBR's molecular chains,reducing hardening and embrittlement during later thermal-oxidative aging stages.