Polycrystalline YBa2Cu3O6＋δbulks were synthesized by sol-gel method. Sintering processing played a vital role in the evolution of phase structure and microstructure, and thus significantly influenced their supercond...Polycrystalline YBa2Cu3O6＋δbulks were synthesized by sol-gel method. Sintering processing played a vital role in the evolution of phase structure and microstructure, and thus significantly influenced their superconducting properties. The influence of calcination temperature, sintering temperature, on the bulks structure, morphology and superconducting behaviors were investigated. The results showed that the oxygen content drastically increased with calcination temperature and sintering temperature. The SEM images revealed that the grains grew up monotonously with increase of calcination temperature. With increased calcination and sintering temperature, the resistivity was reduced gradually and the superconducting properties increased. Moreover, it was found that the optimal superconducting properties（with the highest superconducting transition temperature Tc^onset and the narrowest transition width ΔT） were obtained at calcination temperature of 900℃ and sintering temperature of 950 ℃.展开更多
The morphology and the formation of Y2BaCuO5 phase in powder melting processed YBa2Cu3O7-x superconductors were investigated. The experimental results show the heat treatment can not change the shape of Y2BaCuO5 parti...The morphology and the formation of Y2BaCuO5 phase in powder melting processed YBa2Cu3O7-x superconductors were investigated. The experimental results show the heat treatment can not change the shape of Y2BaCuO5 particles in powder melting processed samples. The formation of round Y2BaCuO5 phase is due to relative content of each constitution of precursor powders in powder melting process. For powder melting process, the excessive liquid phase is eliminated, which restrains the preferred growth of Y2BaCuO5 particles.展开更多
The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymeri...The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymerization of YBa2Cu3O7-x in the Sol-Gel synthetic reaction has bee studied. The particle size ,pruity, sintering activity and superconducting properties of YBa2Cu3O7-x prepared by Sol-Gel method are better than by solid state reaction.展开更多
YBa2Cu3O7-δ-Agx composite superconductors were prepared by hybrid sintering process using YBa2Cu3O7-δ-Agx ultrafine powder and Ag2O finepower, which were prepared by sol-gel process and precipitation process respect...YBa2Cu3O7-δ-Agx composite superconductors were prepared by hybrid sintering process using YBa2Cu3O7-δ-Agx ultrafine powder and Ag2O finepower, which were prepared by sol-gel process and precipitation process respectively. The effect of the Ag content on superconducting crictical transition temperature of YBa2Cu3O7-δ-Agx was not evident as long as YBa2Cu3O7-δ-Agx can form continuous network. But Ag can increase superconduction crictical current and density of the composite superconductors. The normal state (i.e. non-superconducting state at room temperature) resistivity shows a percolation threshold at 20%-30% Ag, whereas the superconducting net-work shows a percolationthreshold at 70% -80% Ag.展开更多
基金Project supported by the National Natural Science Foundation of China(11564021)
文摘Polycrystalline YBa2Cu3O6＋δbulks were synthesized by sol-gel method. Sintering processing played a vital role in the evolution of phase structure and microstructure, and thus significantly influenced their superconducting properties. The influence of calcination temperature, sintering temperature, on the bulks structure, morphology and superconducting behaviors were investigated. The results showed that the oxygen content drastically increased with calcination temperature and sintering temperature. The SEM images revealed that the grains grew up monotonously with increase of calcination temperature. With increased calcination and sintering temperature, the resistivity was reduced gradually and the superconducting properties increased. Moreover, it was found that the optimal superconducting properties（with the highest superconducting transition temperature Tc^onset and the narrowest transition width ΔT） were obtained at calcination temperature of 900℃ and sintering temperature of 950 ℃.
基金Funded by the National Natural Science Foundation of China (50432050)the National High Technology Research and Development Program of China(2007AA03Z241)
文摘The morphology and the formation of Y2BaCuO5 phase in powder melting processed YBa2Cu3O7-x superconductors were investigated. The experimental results show the heat treatment can not change the shape of Y2BaCuO5 particles in powder melting processed samples. The formation of round Y2BaCuO5 phase is due to relative content of each constitution of precursor powders in powder melting process. For powder melting process, the excessive liquid phase is eliminated, which restrains the preferred growth of Y2BaCuO5 particles.
文摘The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymerization of YBa2Cu3O7-x in the Sol-Gel synthetic reaction has bee studied. The particle size ,pruity, sintering activity and superconducting properties of YBa2Cu3O7-x prepared by Sol-Gel method are better than by solid state reaction.
文摘YBa2Cu3O7-δ-Agx composite superconductors were prepared by hybrid sintering process using YBa2Cu3O7-δ-Agx ultrafine powder and Ag2O finepower, which were prepared by sol-gel process and precipitation process respectively. The effect of the Ag content on superconducting crictical transition temperature of YBa2Cu3O7-δ-Agx was not evident as long as YBa2Cu3O7-δ-Agx can form continuous network. But Ag can increase superconduction crictical current and density of the composite superconductors. The normal state (i.e. non-superconducting state at room temperature) resistivity shows a percolation threshold at 20%-30% Ag, whereas the superconducting net-work shows a percolationthreshold at 70% -80% Ag.