The pozzolanic activity of nano-SiO2 and silica fume was comparatirely stndied by X-ray diffraction （ XRD ） , differential scanning calorimetry （DSC）, scanning electron micrascopy （SEM） and the compressive , bon...The pozzolanic activity of nano-SiO2 and silica fume was comparatirely stndied by X-ray diffraction （ XRD ） , differential scanning calorimetry （DSC）, scanning electron micrascopy （SEM） and the compressive , bond and bending streugths of hardened paste and concrete were also measured. Results indicate that the compressive strength development of the paste made from Ca（OH）2 and nano-SiO2, the reaction rate of Ca（ OH）2 with nano- SiO2 and the velocity of C-S-H gel formation from Ca （ OH）2 with nano-SiO2 showed marked increases over those of Ca（ OH）2 with silica fume. Furthermore, the bond strength at the interface between aggregate and hardened cement paste, and the bending strength of concrete incorporated with 3% .NS increased more than those with SF, especially at early ages. To sum up, the pozzolanic activity of nano-SiO2 was much greater than that of silica fume. The results suggest that with a small amount of nano-SiO2, the Ca（ OH）2 crystal at the interface between hardened cement paste and aggregate at early ages may be effectively absorbed in high performance concrete.展开更多
In this work, four samples containing different contents of fumed SiO_2 were prepared to improve the pore size distribution and various properties of b nucleated isotatic polypropylene（b-i PP） biaxial membrane used ...In this work, four samples containing different contents of fumed SiO_2 were prepared to improve the pore size distribution and various properties of b nucleated isotatic polypropylene（b-i PP） biaxial membrane used for lithium-ion battery separator. The wide-angle X-ray diffraction（WAXD） and differential scanning calorimetry（DSC） results show that the fumed SiO_2 promotes the formation of b-crystal slightly and narrows down the thickness distribution of b-lamellae; meanwhile, evenly distributed SiO_2 within b-i PP can be inspected by scanning electron microscopy（SEM）. Moreover, further detailed characterization of morphological evolutions during biaxial stretching by tensile testing and SEM manifests that SiO_2 can strengthen b-i PP and make the samples deform more homogeneously, resulting in a gradually elaborate and finer oriented microfibril structure after longitudinal stretching, in which more uniform defects distribute between fibrils and restrain the formation of coarse fibrils effectively. Therefore, more superior microporous structure emerges with the addition of SiO_2, accompanied by narrower pore size distribution and better connectivity between microvoids, which is confirmed by mercury porosimeter and diminished Gurley value. Moreover, the lower thermal shrinkage, decreased shrinkage rate and suppressed porosity reduction indicate that fumed SiO_2 improves thermal and dimensional stability of membrane dramatically. Furthermore, due to the excellent wettability of SiO_2 with electrolyte, the microporous membranes doped with SiO_2 have higher electrolyte uptake, even after heat treatment at elevated temperature.展开更多
The nano-concentrates and flame retardant nano-coating were prepared in thhis study.The effect of nano-SiO2 on the corrosion resistance and fire resistance of ammonium polyphosphate-pentaerythritol-melamine(APP-PER-ME...The nano-concentrates and flame retardant nano-coating were prepared in thhis study.The effect of nano-SiO2 on the corrosion resistance and fire resistance of ammonium polyphosphate-pentaerythritol-melamine(APP-PER-MEL)coating was investigated by differential thermal analysis(DTA),scanning electron microscopy(SEM),effective thermal conductivity(λ/d),X-ray photoelectron spectroscopy(XPS)and fire protection test.The chemical action and endothermic effect of ammonium polyphosphate,pentaerythritol and melamine in traditional flame retardant coating were damaged by salt spray condition,whereas the flame-retardant additives in the nano-coating demonstrated the good chemical interaction in salt spray condition.The uniformly dispersed nano-SiO2 particles could improve corrosion resistance of the coating,and hence nano-coating could remain the good fire-resistant properties even after 500 h salt spray test.展开更多
The test of fast-freezing method is employed to research the freezing resistance of C60 and C80 high-performance concrete with nanometer-SiO2, and XRD and SEM are employed to analyze the mechanism of its influence. Th...The test of fast-freezing method is employed to research the freezing resistance of C60 and C80 high-performance concrete with nanometer-SiO2, and XRD and SEM are employed to analyze the mechanism of its influence. The experimental results show that the freezing resistance of high-performance concrete has been effectively improved. The compressive strength of C60, C70 and C80 high-performance concrete added with nano-SiO2 can be improved by 8%, 6% and 5% respectively, the weight loss can be reduced by 1%, 0.6% and 0.3% respectively and the relative dynamic elastic modulus can be improved by 7%, 4% and 6% respectively after the 300 times freeze-thaw cycle.展开更多
We put forward a large-area and cost-effective method to fabricate superhydrophobic coating by introducing in-situ functionalized nano-SiO2 into side-amino modified hydroxy-terminated polydimethylsiloxane （SA-HTPDMS...We put forward a large-area and cost-effective method to fabricate superhydrophobic coating by introducing in-situ functionalized nano-SiO2 into side-amino modified hydroxy-terminated polydimethylsiloxane （SA-HTPDMS） curing system. With the characterization using water contact angle （WCA） tester, Fourier transform infrared spectroscopy （FTIR）, scanning electron microscope （SEM）, atomic force microscopy （AFM） and simultaneous thermal analysis, the as-prepared coating displayed a tremendous WCA of 154.8±1°, sliding angle （SA） about 3.5° and stable self-cleaning property range from -10 to 80 ℃. It was also found that the synergistic effect of surface micro-nano hierarchical structure and chemical hydrophobicity, stability from matrix had made contributions to the superhydrophobicity and excellent heat resistance up to 300 ℃.展开更多
The influences of different nano-SiO2（NS） contents on the mechanical properties and rheological behavior of sulfoaluminate cement（SAC） based composite materials were studied.Results show that with increasing conte...The influences of different nano-SiO2（NS） contents on the mechanical properties and rheological behavior of sulfoaluminate cement（SAC） based composite materials were studied.Results show that with increasing content of NS,the apparent viscosity,and shearing strength of fresh paste gradually increase but the fluidity decreases.With a dosage of 3.0%NS,the tensile and flexural strengths of mortars at 56 days were increased by 87.0%and 84.6%,respectively,compared with that in the absence of NS,indicating that the toughness of hardened mortars is significantly improved.Besides,the exothermic peaks of hydration are obviously increased and will earlier occur,and the second and the third peaks appear 2.61 hours and 2.56 hours earlier,respectively than that in the absence of NS,and the hydration of SAC before 8 hours is accelerated.The forming mechanism of strengths was revealed by scanning electron microscopy（SEM）,hydration heat,X-ray diffraction（XRD） and derivative thermogravimetry（DTG）.The micro-aggregate filling effect and nucleation effect at early age and weak pozzolanic effect at late age of NS make the microstructure more compact,which obviously enhances the strength of SAC mortars.展开更多
基金Funded bythe Center of Science Research, Zhejiang Universityof Technology of China
文摘The pozzolanic activity of nano-SiO2 and silica fume was comparatirely stndied by X-ray diffraction （ XRD ） , differential scanning calorimetry （DSC）, scanning electron micrascopy （SEM） and the compressive , bond and bending streugths of hardened paste and concrete were also measured. Results indicate that the compressive strength development of the paste made from Ca（OH）2 and nano-SiO2, the reaction rate of Ca（ OH）2 with nano- SiO2 and the velocity of C-S-H gel formation from Ca （ OH）2 with nano-SiO2 showed marked increases over those of Ca（ OH）2 with silica fume. Furthermore, the bond strength at the interface between aggregate and hardened cement paste, and the bending strength of concrete incorporated with 3% .NS increased more than those with SF, especially at early ages. To sum up, the pozzolanic activity of nano-SiO2 was much greater than that of silica fume. The results suggest that with a small amount of nano-SiO2, the Ca（ OH）2 crystal at the interface between hardened cement paste and aggregate at early ages may be effectively absorbed in high performance concrete.
基金financially supported by the National Natural Science Foundation of China (No. 51421061)
文摘In this work, four samples containing different contents of fumed SiO_2 were prepared to improve the pore size distribution and various properties of b nucleated isotatic polypropylene（b-i PP） biaxial membrane used for lithium-ion battery separator. The wide-angle X-ray diffraction（WAXD） and differential scanning calorimetry（DSC） results show that the fumed SiO_2 promotes the formation of b-crystal slightly and narrows down the thickness distribution of b-lamellae; meanwhile, evenly distributed SiO_2 within b-i PP can be inspected by scanning electron microscopy（SEM）. Moreover, further detailed characterization of morphological evolutions during biaxial stretching by tensile testing and SEM manifests that SiO_2 can strengthen b-i PP and make the samples deform more homogeneously, resulting in a gradually elaborate and finer oriented microfibril structure after longitudinal stretching, in which more uniform defects distribute between fibrils and restrain the formation of coarse fibrils effectively. Therefore, more superior microporous structure emerges with the addition of SiO_2, accompanied by narrower pore size distribution and better connectivity between microvoids, which is confirmed by mercury porosimeter and diminished Gurley value. Moreover, the lower thermal shrinkage, decreased shrinkage rate and suppressed porosity reduction indicate that fumed SiO_2 improves thermal and dimensional stability of membrane dramatically. Furthermore, due to the excellent wettability of SiO_2 with electrolyte, the microporous membranes doped with SiO_2 have higher electrolyte uptake, even after heat treatment at elevated temperature.
文摘The nano-concentrates and flame retardant nano-coating were prepared in thhis study.The effect of nano-SiO2 on the corrosion resistance and fire resistance of ammonium polyphosphate-pentaerythritol-melamine(APP-PER-MEL)coating was investigated by differential thermal analysis(DTA),scanning electron microscopy(SEM),effective thermal conductivity(λ/d),X-ray photoelectron spectroscopy(XPS)and fire protection test.The chemical action and endothermic effect of ammonium polyphosphate,pentaerythritol and melamine in traditional flame retardant coating were damaged by salt spray condition,whereas the flame-retardant additives in the nano-coating demonstrated the good chemical interaction in salt spray condition.The uniformly dispersed nano-SiO2 particles could improve corrosion resistance of the coating,and hence nano-coating could remain the good fire-resistant properties even after 500 h salt spray test.
文摘The test of fast-freezing method is employed to research the freezing resistance of C60 and C80 high-performance concrete with nanometer-SiO2, and XRD and SEM are employed to analyze the mechanism of its influence. The experimental results show that the freezing resistance of high-performance concrete has been effectively improved. The compressive strength of C60, C70 and C80 high-performance concrete added with nano-SiO2 can be improved by 8%, 6% and 5% respectively, the weight loss can be reduced by 1%, 0.6% and 0.3% respectively and the relative dynamic elastic modulus can be improved by 7%, 4% and 6% respectively after the 300 times freeze-thaw cycle.
基金Supported by National High Technology Research and Development ProgramofChina(863Program)(No.2003AA305920)
文摘We put forward a large-area and cost-effective method to fabricate superhydrophobic coating by introducing in-situ functionalized nano-SiO2 into side-amino modified hydroxy-terminated polydimethylsiloxane （SA-HTPDMS） curing system. With the characterization using water contact angle （WCA） tester, Fourier transform infrared spectroscopy （FTIR）, scanning electron microscope （SEM）, atomic force microscopy （AFM） and simultaneous thermal analysis, the as-prepared coating displayed a tremendous WCA of 154.8±1°, sliding angle （SA） about 3.5° and stable self-cleaning property range from -10 to 80 ℃. It was also found that the synergistic effect of surface micro-nano hierarchical structure and chemical hydrophobicity, stability from matrix had made contributions to the superhydrophobicity and excellent heat resistance up to 300 ℃.
基金Funded by the Fundamental Research Funds for the Central Universities(No.2013-YB-25)the National Natural Science Foundation of China(No.51378408)
文摘The influences of different nano-SiO2（NS） contents on the mechanical properties and rheological behavior of sulfoaluminate cement（SAC） based composite materials were studied.Results show that with increasing content of NS,the apparent viscosity,and shearing strength of fresh paste gradually increase but the fluidity decreases.With a dosage of 3.0%NS,the tensile and flexural strengths of mortars at 56 days were increased by 87.0%and 84.6%,respectively,compared with that in the absence of NS,indicating that the toughness of hardened mortars is significantly improved.Besides,the exothermic peaks of hydration are obviously increased and will earlier occur,and the second and the third peaks appear 2.61 hours and 2.56 hours earlier,respectively than that in the absence of NS,and the hydration of SAC before 8 hours is accelerated.The forming mechanism of strengths was revealed by scanning electron microscopy（SEM）,hydration heat,X-ray diffraction（XRD） and derivative thermogravimetry（DTG）.The micro-aggregate filling effect and nucleation effect at early age and weak pozzolanic effect at late age of NS make the microstructure more compact,which obviously enhances the strength of SAC mortars.