Electron beam welding （EBW） of 304 stainless steel to QCr0.8 copper alloy with copper filler wire was carried out. Orthogonal experiment was performed to investigate the effects of process parameters on the tensile ...Electron beam welding （EBW） of 304 stainless steel to QCr0.8 copper alloy with copper filler wire was carried out. Orthogonal experiment was performed to investigate the effects of process parameters on the tensile strength of the joints, and the process parameters were optimized. The optimum process parameters are as follows：beam current of 30 mA, welding speed of 100 mm/min, wire feed rate of 1 m/min and beam offset of-0.3 mm. The microstructures of the optimum joint were studied. The results indicate that the weld is mainly composed of dendriticαphase with little globularεphase, and copper inhomogeneity only occurs at the top of the fusion zone. In addition, a melted region without mixing exists near the weld junction of copper side. This region with a coarser grain size is the weakest section of the joints. It is found that the microhardness of the weld decreases with the increase of the copper content in solid solution. The highest tensile strength of the joint is 276 MPa.展开更多
The influence of hot working on the microstructures of TC11/Ti2 Al Nb dual-alloy joints welded by electron beam welding(EBW) process was investigated. The tensile tests were performed at room temperature for specimens...The influence of hot working on the microstructures of TC11/Ti2 Al Nb dual-alloy joints welded by electron beam welding(EBW) process was investigated. The tensile tests were performed at room temperature for specimens before and after thermal exposure. The results show that the fusion zone of TC11/Ti2 Al Nb dual-alloy joint welded by EBW is mainly composed of β phase. After deformation and heat treatment, the grain boundaries of the as-cast alloy are broken and the fusion zone mainly consists of β, α2and α phases. The fusion zone performs poor property in the tensile test. Specimens before and after thermal exposure all fail in this area under different deformation conditions. The ultimate tensile strength of specimens after heat treatment is up to 1190 MPa at room temperature. The joints by water quenching after deformation have better plasticity with an elongation up to 4.4%. After thermal exposure at 500 °C for 100 h, the tensile strength of the specimen slightly rises while the ductility changes a little. SEM observation shows that the fracture mechanism is predominantly transgranular under different deformation conditions.展开更多
Electron beam welding experiments of titanium alloy to stainless steel were carried out with different filler metals, such as Ni, V, and Cu. Microstructures of the joints were examined by optical microscopy, scanning ...Electron beam welding experiments of titanium alloy to stainless steel were carried out with different filler metals, such as Ni, V, and Cu. Microstructures of the joints were examined by optical microscopy, scanning electron microscopy and X-ray diffraction analysis. Mechanical properties of the joints were evaluated according to tensile strength and microhardness. As a result, influences of filler metals on microstructures and mechanical properties of electron beam welded titanium-stainless steel joints were discussed. The results showed that all the filler metals were helpful to restrain the Ti-Fe intermetallics. The welds with different filler metals were all characterized by solid solution and interfacial intermetallics. For each type of the filler metal, the type of solid solution and interfacial intermetallics depended on the metallurgical reactions between the filler metals and base metals. The interfacial intermetallics were Fe2Ti＋Ni3Ti＋NiTi2, TiFe, and Cu2Ti＋CuTi＋CuTi2 in the joints welded with Ni, V, and Cu filler metals, respectively. The tensile strengths of the joints were dependent on the hardness of the interfacial intermetallics. The joint welded with Ag filler metal had the highest tensile strength, which is about 310 MPa.展开更多
NiTi/Stainless Steel(SS) sheets have been welded via a vacuum electron beam welding process, with three methods(offsetting electron beam to SS side without interlayer, adding Ni interlayer and adding Fe Ni interlayer)...NiTi/Stainless Steel(SS) sheets have been welded via a vacuum electron beam welding process, with three methods(offsetting electron beam to SS side without interlayer, adding Ni interlayer and adding Fe Ni interlayer), to promote mechanical properties of the Ni Ti/SS joints. The joints with different interlayers are all fractured in the weld zone near the Ni Ti side, which is attributed to the enrichment of intermetallic compounds including Fe2 Ti and Ni3 Ti. The fracture mechanisms of different joints are strongly dependent on the types of interlayers, and the joints without interlayer, adding Ni interlayer and adding Fe Ni interlayer exhibit cleavage fracture, intergranular fracture and mixed fracture composed of cleavage and tearing ridge, respectively. Compared with the brittle laves phase Fe2 Ti, Ni3 Ti phase can exhibit certain plasticity, block the crack propagation and change the direction of crack propagation. The composite structure of Ni3 Ti and Fe2 Ti will be formed when the Fe Ni alloy is taken as the interlayer, which provides the joint excellent mechanical properties, with rupture strength of 343 MPa.展开更多
Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy...Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy(SEM) and X-ray diffractometry(XRD).In addition,the mechanical properties of the joint were evaluated by tensile test and the microhardness was measured.These two alloys were successfully welded by adding copper transition layer into the weld.Solid solution with a certain thickness was located at the interfaces between weld and base metal in both sides.Regions inside the weld and near the stainless steel were characterized by solid solution of copper with TiFe2 intermetallics dispersedly distributed in it.While weld near titanium alloy contained Ti-Cu and Ti-Fe-Cu intermetallics layer,in which the hardness of weld came to the highest value.Brittle fracture occurred in the intermetallics layer when the joint was stretched.展开更多
A two-dimensional mathematical model based on volume-of-fluid method is proposed to investigate the heat transfer,fluidflow and keyhole dynamics during electron beam welding(EBW)on20mm-thick2219aluminum alloy plate.In...A two-dimensional mathematical model based on volume-of-fluid method is proposed to investigate the heat transfer,fluidflow and keyhole dynamics during electron beam welding(EBW)on20mm-thick2219aluminum alloy plate.In the model,anadaptive heat source model tracking keyhole depth is employed to simulate the heating process of electron beam.Heat and masstransport of different vortexes induced by surface tension,thermo-capillary force,recoil pressure,hydrostatic pressure and thermalbuoyancy is coupled with keyhole evolution.A series of physical phenomena involving keyhole drilling,collapse,reopening,quasi-stability,backfilling and the coupled thermal field are analyzed systematically.The results indicate that the decreased heat fluxof beam in depth can decelerate the keyholing velocity of recoil pressure and promote the quasi-steady state.Before and close to thisstate,the keyhole collapses and complicates the fluid transport of vortexes.Finally,all simulation results are validated againstexperiments.展开更多
This work was to reveal the residual stress profile in electron beam welded Ti-6Al-4V alloy plates（50 mm thick） by using finite element and contour measurement methods.A three-dimensional finite element model of 50-...This work was to reveal the residual stress profile in electron beam welded Ti-6Al-4V alloy plates（50 mm thick） by using finite element and contour measurement methods.A three-dimensional finite element model of 50-mmthick titanium component was proposed,in which a column–cone combined heat source model was used to simulate the temperature field and a thermo-elastic–plastic model to analyze residual stress in a weld joint based on ABAQUS software.Considering the uncertainty of welding simulation,the computation was calibrated by experimental data of contour measurement method.Both test and simulated results show that residual stresses on the surface and inside the weld zone are significantly different and present a narrow and large gradient feature in the weld joint.The peak tensile stress exceeds the yield strength of base materials inside weld,which are distinctly different from residual stress of the thin Ti-6Al-4V alloy plates presented in references before.展开更多
The Ti-24Al-15Nb-1.5Mo alloy, in the as-forged and heat-treated states, was joined to the as-forged TC 11 titanium alloy by electron beam welding with the heat inputs of 135 and 150 kJ/m. Then the microstructure and p...The Ti-24Al-15Nb-1.5Mo alloy, in the as-forged and heat-treated states, was joined to the as-forged TC 11 titanium alloy by electron beam welding with the heat inputs of 135 and 150 kJ/m. Then the microstructure and property of the Ti-24Al-15Nb- 1.5Mo/TC 11 welding interface were investigated. The results show that the phase constitution of the weld is not related to the heat input, and is mainly composed of α＇ phase. Moreover, the intermetallic phases of TiEAlNb, MoNb, NbaAl, and TiAl3 are formed in the weld zone. Therefore, the microhardness value of the weld zone is higher than that of the other portions in the same sample. The profile of the weld is asymmetrically fimnel-like. The grain sizes of the weld and its heat-affected zones are increased with increasing heat input. There is an obvious difference in the element content of the welding interface; only the alloying elements in the fusion zone reach a new balance during solidification.展开更多
Electron beam welding experiments of TZM alloy and 30CrMnSiA steel butt joints were carried out with different beam currents.Microstructures and chemical compositions of typical zones were analyzed by optical microsco...Electron beam welding experiments of TZM alloy and 30CrMnSiA steel butt joints were carried out with different beam currents.Microstructures and chemical compositions of typical zones were analyzed by optical microscopy,scanning electron microscopy and X-ray diffraction.The mechanical properties of the joints were evaluated by tensile strength tests.Besides,nanoindentation tests were carried out to compare the brittleness of the reaction layer and other typical microstructures.The results illustrated that the reaction layer at the interface between fusion zone(FZ)and TZM alloy was the weak position of the joint,which was divided into Fe2Mo layer and a mixture layer of Fe2Mo and a-Fe phases.As the beam current increased,the thickness of the Fe2Mo layer decreased,which resulted in the increasing of the tensile strength of the joints.When the beam current exceeded 24 m A,the formation of the joint was poor with a low tensile strength.When the beam current was 24 mA,the joint presented the highest strength of 191.3 MPa and the joint fractured along the Fe2Mo layer near the TZM alloy side with a brittle fracture mode.展开更多
Post-weld single aging treatment（solution treatment at 510 ℃ for 1 h, water quenching,and aging at 155 ℃ for 16 h） and post-weld double aging treatment（solution treatment at 510 ℃ for 1 h, water quenching, aging...Post-weld single aging treatment（solution treatment at 510 ℃ for 1 h, water quenching,and aging at 155 ℃ for 16 h） and post-weld double aging treatment（solution treatment at 510 ℃ for 1 h, water quenching, aging at 155 ℃ for 16 h, and aging at 130 ℃ for 12 h） are carried out on Al-Cu-Li alloy joints by electron beam welding（EBW） respectively. The effects of aging treatments on microstructures and mechanical properties of welded joints are investigated. Results show that the mechanical properties of welded joints are obviously improved after both aging treatments. The strength coefficient of joints is increased from 0.64 in an as-welded condition（AW） to 0.90 after post-weld double aging treatment. Microstructure analysis shows that the precipitates of the fusion zone within grains and grain boundaries are less in the AW condition. After post-weld heat treatment（PWHT）, a lot of fine needle-like phases T_1（Al_2 Cu Li） precipitate in grain boundaries of the fusion zone, and more horseshoe-shaped β＇ （Al_3 Zr） particles precipitate within grains. In addition,grains of the fusion zone are refined after post-weld double aging treatment, which leads to an effect of grain refinement strengthening. Consequently, the mechanical properties of welded joints are greatly improved.展开更多
In this paper, the common heat source model of point and linear heat source in the numerical simulation of electron beam welding （EBW） were summarized and introduced. The combined point-linear heat source model was ...In this paper, the common heat source model of point and linear heat source in the numerical simulation of electron beam welding （EBW） were summarized and introduced. The combined point-linear heat source model was brought forward and to simulate the welding temperature fields of EBW and predicting the weld shape. The model parameters were put forward and regulated in the combined model, which included the ratio of point heat source to linear heat source Qpr and the distribution of linear heat source Lr. Based on the combined model, the welding temperature fields of EBW were investigated. The results show that the predicted weld shapes are conformable to those of the actual, the temperature fields are reasonable and correct by simulating with combined point-linear heat source model and the typical weld shapes are gained.展开更多
In order to maintain the structural consistency during the welding of precipitation hardened copperchromium-zirconium(PH-CuCrZr)alloy components,electron beam welding(EBW)process was employed.Experimental study and nu...In order to maintain the structural consistency during the welding of precipitation hardened copperchromium-zirconium(PH-CuCrZr)alloy components,electron beam welding(EBW)process was employed.Experimental study and numerical modeling of EBW process during welding of PH-CuCrZr alloy components were carried out.A 3D finite element model was developed to predict the output responses(bead penetration and bead width)as a function of EBW input parameters(beam current,acceleration voltage and weld speed).A combined circular and conical source with Gaussian heat distribution was used to model the deep penetration characteristic of the EBW process.Numerical modeling was carried out by developing user defined function in Ansys software.Numerical predictions were compared with the experimental results which had a good agreement with each other.The developed model can be used for parametric study in wide range of problems involving complex geometries which are to be welded using EBW process.The present work illustrates that the input current with a contribution of 44.56%and 81.13%is the most significant input parameter for the bead penetration and bead width,respectively.展开更多
SiCp/2024 matrix composites reinforced with SiC particles and 2219 aluminum alloy were joined via centered electron beam welding and deflection beam welding,respectively,and the microstructures and mechanical properti...SiCp/2024 matrix composites reinforced with SiC particles and 2219 aluminum alloy were joined via centered electron beam welding and deflection beam welding,respectively,and the microstructures and mechanical properties of these joints were investigated.The results revealed that SiC particle segregation was more likely during centered electron beam welding(than during deflection beam welding),and strong interface reactions led to the formation of many Al4C3 brittle intermetallic compounds.Moreover,the tensile strength of the joints was 104 MPa.The interface reaction was restrained via deflection electron beam welding,and only a few Al4C3 intermetallic compounds formed at the top of the joint and heat affected zone of SiCp/Al.Quasi-cleavage fracture occurred at the interface reaction layer of the base metal.Both methods yielded a hardness transition zone near the SiCp/2024 fusion zone,and the brittle intermetallic Al4C3compounds formed in this zone resulted in high hardness.展开更多
The basic principle and features of ultrasonic phased array imaging are discussed in this paper. Through the ultrasonic phased array technology, the electron beam welding defects and frozen keyholes characterization a...The basic principle and features of ultrasonic phased array imaging are discussed in this paper. Through the ultrasonic phased array technology, the electron beam welding defects and frozen keyholes characterization and imaging were realized. The ultrasonic phased array technology can detect kinds of defects in electron beam welding (EBW) quickly and easily.展开更多
A three-dimensional mathematical model using volume-of-fluid method is developed to investigate the heat transfer, fluid flow and keyhole dynamics during electron beam welding of 2219 aluminum alloy plate. In the mode...A three-dimensional mathematical model using volume-of-fluid method is developed to investigate the heat transfer, fluid flow and keyhole dynamics during electron beam welding of 2219 aluminum alloy plate. In the model, an adaptive heat source is employed to simulate the heating process of electron beam. Fluid flow is mainly driven by surface tension, thermo-capillary force, recoil pressure, hydrostatic pressure and thermal buoyancy. The thermal-fluid transport behaviors of welding pool during the drilling and backfilling stages of keyhole and the formation reason of the nail-shaped weld with an arc crater are systematically analyzed. Finally, all calculation results are validated by experiments and show good agreements.展开更多
Electron beam welding of titanium alloy to aluminum alloy was carried out by melting and melt-brazing to investigate the effects of welding parameters on microstructure of the joint. The results indicated that the joi...Electron beam welding of titanium alloy to aluminum alloy was carried out by melting and melt-brazing to investigate the effects of welding parameters on microstructure of the joint. The results indicated that the joint of the specimen welded by melting was well-formed but contained a large amount of intermetallic compounds. These intermetallic compounds were mainly composed of brittle phases such as TiAl and TiAl3 that decreased the ductility of the joints and resulted in a tensile strength 50 % lower than that of the base metal. In the melt-brazing experiment, direct heat was applied to the aluminum alloy to melt the aluminum rather than the titanium alloy, creating a well-formed joint. The weld was mainly composed of Al element and only a 3 ~m thickness of intermetallic compounds formed near the fusion line at the Ti side. The ductility and the performauce of the joint were significantly improved compared with those of the melting-only joint. In addition, the tensile strength of the joint reached 80 % of that of the aluminum base metal.展开更多
The residual stresses distribution of 7075 aluminum alloy in vacuum electron beam welding joint was numerically simulated using nonlinear finite element method. The result shows that the longitudinal residual stress i...The residual stresses distribution of 7075 aluminum alloy in vacuum electron beam welding joint was numerically simulated using nonlinear finite element method. The result shows that the longitudinal residual stress is tension stress along weld center and the stress peak value appears in the middle of the welded seam; the transversal residual stress is compression stress ; the residual stress in thickness direction is very small.展开更多
The effects of two post-weld heat treatment processes on the microstructure and fatigue properties of the electron beam welded joints of 30CrMnSiNi2A steel were studied. Electron beam local post-weld heat treatment (E...The effects of two post-weld heat treatment processes on the microstructure and fatigue properties of the electron beam welded joints of 30CrMnSiNi2A steel were studied. Electron beam local post-weld heat treatment (EBLPWHT), in a vacuum chamber, immediately after welding and a traditional furnace whole post-weld heat treatment (FWPWHT) were accepted. The experimental results show that, after EBLPWHT, the main microstructure of weld is changed from coarse acicular martensite into lath martensite, and base metal is changed from ferrite and perlite into upper bainite and residual austenite, however the microstructures of different zones of joints in FWPWHT conditions are tempered sorbite. The fatigue crack growth rate da/dN of welds and base metal are not obviously changed among EBLPWHT, FWPWHT test and as-welded (AW) test, as the mechanical properties of materials have a certain but not large effect on the da/dN of welded joints. The resistance to near threshold fatigue crack growth data of welded joints can be largely improved by EBLPWHT and it is related to microstructure and crack closure effect.展开更多
The microstructural and mechanical characterization of electron beam welded joints of forged Ti-6Al- 4V were investigated. Microhardness tests indicate that the hardness of the fusion zone （FZ） is higher than that o...The microstructural and mechanical characterization of electron beam welded joints of forged Ti-6Al- 4V were investigated. Microhardness tests indicate that the hardness of the fusion zone （FZ） is higher than that of the heat-affected zone （HAZ） and base metal. The tensile results show that the mechanical properties of the welded joints are comparable with those of the base metal in terms of static strength and are in accordance with the relationship between microstructure and mechanical properties of welded joints. The ultimate tensile strength of the weld is equal to that of the hourglass joint, which indicates that the mechanical properties of the longitudinal FZ and those of the transverse FZ are the same. Macromechanical behavior and macrofracture and microfracture of the base material, joint, and weld specimens are observed. A comparison among the three types of specimen fracture phenomena reveals the following distinctive differences： （1） the fracture mode, （2） the micrograph of the dimple pattern at the central region, and （3） the size of the dimple at the central region and the transition region.展开更多
Electron beam welding of in situ TiB2p reinforced aluminum composites was studied. The results show that no obvious pores or cracks is presented in the weld seam. The grains in the weld seam are remarkably refined and...Electron beam welding of in situ TiB2p reinforced aluminum composites was studied. The results show that no obvious pores or cracks is presented in the weld seam. The grains in the weld seam are remarkably refined and TiB2 particles distribute much more homogeneously than that in base metal. The hardness values of fusion zone and heat affected zone （HAZ） are both increased in comparison with that of base metal. There are no interface reactions between TiB2 particle and A1 matrix. This results supply the evidence that the novel TiB2p reinforced aluminum composites can be well joined with the electron beam welding.展开更多
基金Project(2010CB731704)supported by the National Basic Research Program of ChinaProject(2011DFR50760)supported by International Science&Technology Cooperation Program of China
文摘Electron beam welding （EBW） of 304 stainless steel to QCr0.8 copper alloy with copper filler wire was carried out. Orthogonal experiment was performed to investigate the effects of process parameters on the tensile strength of the joints, and the process parameters were optimized. The optimum process parameters are as follows：beam current of 30 mA, welding speed of 100 mm/min, wire feed rate of 1 m/min and beam offset of-0.3 mm. The microstructures of the optimum joint were studied. The results indicate that the weld is mainly composed of dendriticαphase with little globularεphase, and copper inhomogeneity only occurs at the top of the fusion zone. In addition, a melted region without mixing exists near the weld junction of copper side. This region with a coarser grain size is the weakest section of the joints. It is found that the microhardness of the weld decreases with the increase of the copper content in solid solution. The highest tensile strength of the joint is 276 MPa.
基金Project(51175431)supported by the National Natural Science Foundation of China
文摘The influence of hot working on the microstructures of TC11/Ti2 Al Nb dual-alloy joints welded by electron beam welding(EBW) process was investigated. The tensile tests were performed at room temperature for specimens before and after thermal exposure. The results show that the fusion zone of TC11/Ti2 Al Nb dual-alloy joint welded by EBW is mainly composed of β phase. After deformation and heat treatment, the grain boundaries of the as-cast alloy are broken and the fusion zone mainly consists of β, α2and α phases. The fusion zone performs poor property in the tensile test. Specimens before and after thermal exposure all fail in this area under different deformation conditions. The ultimate tensile strength of specimens after heat treatment is up to 1190 MPa at room temperature. The joints by water quenching after deformation have better plasticity with an elongation up to 4.4%. After thermal exposure at 500 °C for 100 h, the tensile strength of the specimen slightly rises while the ductility changes a little. SEM observation shows that the fracture mechanism is predominantly transgranular under different deformation conditions.
基金Project(2011DFR50760)supported by International Science&Technology Cooperation Program of China
文摘Electron beam welding experiments of titanium alloy to stainless steel were carried out with different filler metals, such as Ni, V, and Cu. Microstructures of the joints were examined by optical microscopy, scanning electron microscopy and X-ray diffraction analysis. Mechanical properties of the joints were evaluated according to tensile strength and microhardness. As a result, influences of filler metals on microstructures and mechanical properties of electron beam welded titanium-stainless steel joints were discussed. The results showed that all the filler metals were helpful to restrain the Ti-Fe intermetallics. The welds with different filler metals were all characterized by solid solution and interfacial intermetallics. For each type of the filler metal, the type of solid solution and interfacial intermetallics depended on the metallurgical reactions between the filler metals and base metals. The interfacial intermetallics were Fe2Ti＋Ni3Ti＋NiTi2, TiFe, and Cu2Ti＋CuTi＋CuTi2 in the joints welded with Ni, V, and Cu filler metals, respectively. The tensile strengths of the joints were dependent on the hardness of the interfacial intermetallics. The joint welded with Ag filler metal had the highest tensile strength, which is about 310 MPa.
文摘NiTi/Stainless Steel(SS) sheets have been welded via a vacuum electron beam welding process, with three methods(offsetting electron beam to SS side without interlayer, adding Ni interlayer and adding Fe Ni interlayer), to promote mechanical properties of the Ni Ti/SS joints. The joints with different interlayers are all fractured in the weld zone near the Ni Ti side, which is attributed to the enrichment of intermetallic compounds including Fe2 Ti and Ni3 Ti. The fracture mechanisms of different joints are strongly dependent on the types of interlayers, and the joints without interlayer, adding Ni interlayer and adding Fe Ni interlayer exhibit cleavage fracture, intergranular fracture and mixed fracture composed of cleavage and tearing ridge, respectively. Compared with the brittle laves phase Fe2 Ti, Ni3 Ti phase can exhibit certain plasticity, block the crack propagation and change the direction of crack propagation. The composite structure of Ni3 Ti and Fe2 Ti will be formed when the Fe Ni alloy is taken as the interlayer, which provides the joint excellent mechanical properties, with rupture strength of 343 MPa.
文摘Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy(SEM) and X-ray diffractometry(XRD).In addition,the mechanical properties of the joint were evaluated by tensile test and the microhardness was measured.These two alloys were successfully welded by adding copper transition layer into the weld.Solid solution with a certain thickness was located at the interfaces between weld and base metal in both sides.Regions inside the weld and near the stainless steel were characterized by solid solution of copper with TiFe2 intermetallics dispersedly distributed in it.While weld near titanium alloy contained Ti-Cu and Ti-Fe-Cu intermetallics layer,in which the hardness of weld came to the highest value.Brittle fracture occurred in the intermetallics layer when the joint was stretched.
文摘A two-dimensional mathematical model based on volume-of-fluid method is proposed to investigate the heat transfer,fluidflow and keyhole dynamics during electron beam welding(EBW)on20mm-thick2219aluminum alloy plate.In the model,anadaptive heat source model tracking keyhole depth is employed to simulate the heating process of electron beam.Heat and masstransport of different vortexes induced by surface tension,thermo-capillary force,recoil pressure,hydrostatic pressure and thermalbuoyancy is coupled with keyhole evolution.A series of physical phenomena involving keyhole drilling,collapse,reopening,quasi-stability,backfilling and the coupled thermal field are analyzed systematically.The results indicate that the decreased heat fluxof beam in depth can decelerate the keyholing velocity of recoil pressure and promote the quasi-steady state.Before and close to thisstate,the keyhole collapses and complicates the fluid transport of vortexes.Finally,all simulation results are validated againstexperiments.
基金supported by the National Natural Science Foundation of China (No.50935008)
文摘This work was to reveal the residual stress profile in electron beam welded Ti-6Al-4V alloy plates（50 mm thick） by using finite element and contour measurement methods.A three-dimensional finite element model of 50-mmthick titanium component was proposed,in which a column–cone combined heat source model was used to simulate the temperature field and a thermo-elastic–plastic model to analyze residual stress in a weld joint based on ABAQUS software.Considering the uncertainty of welding simulation,the computation was calibrated by experimental data of contour measurement method.Both test and simulated results show that residual stresses on the surface and inside the weld zone are significantly different and present a narrow and large gradient feature in the weld joint.The peak tensile stress exceeds the yield strength of base materials inside weld,which are distinctly different from residual stress of the thin Ti-6Al-4V alloy plates presented in references before.
基金supported by the National Natural Science Foundation of China (No.50775187)
文摘The Ti-24Al-15Nb-1.5Mo alloy, in the as-forged and heat-treated states, was joined to the as-forged TC 11 titanium alloy by electron beam welding with the heat inputs of 135 and 150 kJ/m. Then the microstructure and property of the Ti-24Al-15Nb- 1.5Mo/TC 11 welding interface were investigated. The results show that the phase constitution of the weld is not related to the heat input, and is mainly composed of α＇ phase. Moreover, the intermetallic phases of TiEAlNb, MoNb, NbaAl, and TiAl3 are formed in the weld zone. Therefore, the microhardness value of the weld zone is higher than that of the other portions in the same sample. The profile of the weld is asymmetrically fimnel-like. The grain sizes of the weld and its heat-affected zones are increased with increasing heat input. There is an obvious difference in the element content of the welding interface; only the alloying elements in the fusion zone reach a new balance during solidification.
基金supported by Shandong Provincial Key Research and Development Program of China(No.2019JZZY010439)International Science&Technology Cooperation Program of China(No.2011DFR50760)。
文摘Electron beam welding experiments of TZM alloy and 30CrMnSiA steel butt joints were carried out with different beam currents.Microstructures and chemical compositions of typical zones were analyzed by optical microscopy,scanning electron microscopy and X-ray diffraction.The mechanical properties of the joints were evaluated by tensile strength tests.Besides,nanoindentation tests were carried out to compare the brittleness of the reaction layer and other typical microstructures.The results illustrated that the reaction layer at the interface between fusion zone(FZ)and TZM alloy was the weak position of the joint,which was divided into Fe2Mo layer and a mixture layer of Fe2Mo and a-Fe phases.As the beam current increased,the thickness of the Fe2Mo layer decreased,which resulted in the increasing of the tensile strength of the joints.When the beam current exceeded 24 m A,the formation of the joint was poor with a low tensile strength.When the beam current was 24 mA,the joint presented the highest strength of 191.3 MPa and the joint fractured along the Fe2Mo layer near the TZM alloy side with a brittle fracture mode.
基金project was supported by the Aeronautical Science Foundation of China (No. 2015ZE52048)A Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions
文摘Post-weld single aging treatment（solution treatment at 510 ℃ for 1 h, water quenching,and aging at 155 ℃ for 16 h） and post-weld double aging treatment（solution treatment at 510 ℃ for 1 h, water quenching, aging at 155 ℃ for 16 h, and aging at 130 ℃ for 12 h） are carried out on Al-Cu-Li alloy joints by electron beam welding（EBW） respectively. The effects of aging treatments on microstructures and mechanical properties of welded joints are investigated. Results show that the mechanical properties of welded joints are obviously improved after both aging treatments. The strength coefficient of joints is increased from 0.64 in an as-welded condition（AW） to 0.90 after post-weld double aging treatment. Microstructure analysis shows that the precipitates of the fusion zone within grains and grain boundaries are less in the AW condition. After post-weld heat treatment（PWHT）, a lot of fine needle-like phases T_1（Al_2 Cu Li） precipitate in grain boundaries of the fusion zone, and more horseshoe-shaped β＇ （Al_3 Zr） particles precipitate within grains. In addition,grains of the fusion zone are refined after post-weld double aging treatment, which leads to an effect of grain refinement strengthening. Consequently, the mechanical properties of welded joints are greatly improved.
基金co-supported by the National Basic Research Program (No.61362)the National Natural Science Foundation of China(No. 50935008 and 10902113)Science Foundation of Aeronautics (No. 2010ZE25006)
文摘In this paper, the common heat source model of point and linear heat source in the numerical simulation of electron beam welding （EBW） were summarized and introduced. The combined point-linear heat source model was brought forward and to simulate the welding temperature fields of EBW and predicting the weld shape. The model parameters were put forward and regulated in the combined model, which included the ratio of point heat source to linear heat source Qpr and the distribution of linear heat source Lr. Based on the combined model, the welding temperature fields of EBW were investigated. The results show that the predicted weld shapes are conformable to those of the actual, the temperature fields are reasonable and correct by simulating with combined point-linear heat source model and the typical weld shapes are gained.
文摘In order to maintain the structural consistency during the welding of precipitation hardened copperchromium-zirconium(PH-CuCrZr)alloy components,electron beam welding(EBW)process was employed.Experimental study and numerical modeling of EBW process during welding of PH-CuCrZr alloy components were carried out.A 3D finite element model was developed to predict the output responses(bead penetration and bead width)as a function of EBW input parameters(beam current,acceleration voltage and weld speed).A combined circular and conical source with Gaussian heat distribution was used to model the deep penetration characteristic of the EBW process.Numerical modeling was carried out by developing user defined function in Ansys software.Numerical predictions were compared with the experimental results which had a good agreement with each other.The developed model can be used for parametric study in wide range of problems involving complex geometries which are to be welded using EBW process.The present work illustrates that the input current with a contribution of 44.56%and 81.13%is the most significant input parameter for the bead penetration and bead width,respectively.
基金Project was supported by the National Nature Science Foundation of China(51375115).
文摘SiCp/2024 matrix composites reinforced with SiC particles and 2219 aluminum alloy were joined via centered electron beam welding and deflection beam welding,respectively,and the microstructures and mechanical properties of these joints were investigated.The results revealed that SiC particle segregation was more likely during centered electron beam welding(than during deflection beam welding),and strong interface reactions led to the formation of many Al4C3 brittle intermetallic compounds.Moreover,the tensile strength of the joints was 104 MPa.The interface reaction was restrained via deflection electron beam welding,and only a few Al4C3 intermetallic compounds formed at the top of the joint and heat affected zone of SiCp/Al.Quasi-cleavage fracture occurred at the interface reaction layer of the base metal.Both methods yielded a hardness transition zone near the SiCp/2024 fusion zone,and the brittle intermetallic Al4C3compounds formed in this zone resulted in high hardness.
文摘The basic principle and features of ultrasonic phased array imaging are discussed in this paper. Through the ultrasonic phased array technology, the electron beam welding defects and frozen keyholes characterization and imaging were realized. The ultrasonic phased array technology can detect kinds of defects in electron beam welding (EBW) quickly and easily.
文摘A three-dimensional mathematical model using volume-of-fluid method is developed to investigate the heat transfer, fluid flow and keyhole dynamics during electron beam welding of 2219 aluminum alloy plate. In the model, an adaptive heat source is employed to simulate the heating process of electron beam. Fluid flow is mainly driven by surface tension, thermo-capillary force, recoil pressure, hydrostatic pressure and thermal buoyancy. The thermal-fluid transport behaviors of welding pool during the drilling and backfilling stages of keyhole and the formation reason of the nail-shaped weld with an arc crater are systematically analyzed. Finally, all calculation results are validated by experiments and show good agreements.
文摘Electron beam welding of titanium alloy to aluminum alloy was carried out by melting and melt-brazing to investigate the effects of welding parameters on microstructure of the joint. The results indicated that the joint of the specimen welded by melting was well-formed but contained a large amount of intermetallic compounds. These intermetallic compounds were mainly composed of brittle phases such as TiAl and TiAl3 that decreased the ductility of the joints and resulted in a tensile strength 50 % lower than that of the base metal. In the melt-brazing experiment, direct heat was applied to the aluminum alloy to melt the aluminum rather than the titanium alloy, creating a well-formed joint. The weld was mainly composed of Al element and only a 3 ~m thickness of intermetallic compounds formed near the fusion line at the Ti side. The ductility and the performauce of the joint were significantly improved compared with those of the melting-only joint. In addition, the tensile strength of the joint reached 80 % of that of the aluminum base metal.
基金The project is supported by the Found of Key Fields Project of Inner Mongolia Education Department (No ZL02021)
文摘The residual stresses distribution of 7075 aluminum alloy in vacuum electron beam welding joint was numerically simulated using nonlinear finite element method. The result shows that the longitudinal residual stress is tension stress along weld center and the stress peak value appears in the middle of the welded seam; the transversal residual stress is compression stress ; the residual stress in thickness direction is very small.
基金thefoundationoftheNationalDefenseTechnologyKeyLaboratory (No .99JS5 0 .3 .2JW14 0 2 )
文摘The effects of two post-weld heat treatment processes on the microstructure and fatigue properties of the electron beam welded joints of 30CrMnSiNi2A steel were studied. Electron beam local post-weld heat treatment (EBLPWHT), in a vacuum chamber, immediately after welding and a traditional furnace whole post-weld heat treatment (FWPWHT) were accepted. The experimental results show that, after EBLPWHT, the main microstructure of weld is changed from coarse acicular martensite into lath martensite, and base metal is changed from ferrite and perlite into upper bainite and residual austenite, however the microstructures of different zones of joints in FWPWHT conditions are tempered sorbite. The fatigue crack growth rate da/dN of welds and base metal are not obviously changed among EBLPWHT, FWPWHT test and as-welded (AW) test, as the mechanical properties of materials have a certain but not large effect on the da/dN of welded joints. The resistance to near threshold fatigue crack growth data of welded joints can be largely improved by EBLPWHT and it is related to microstructure and crack closure effect.
基金financially supported by the Beijing Municipal Science&Technology Commission(No.D131100003113003)the Hi-Tech Research and Development Program of China(No.2012AA052102)and the Program of International S&T Cooperation of China(No.2013DFA61590)
文摘The microstructural and mechanical characterization of electron beam welded joints of forged Ti-6Al- 4V were investigated. Microhardness tests indicate that the hardness of the fusion zone （FZ） is higher than that of the heat-affected zone （HAZ） and base metal. The tensile results show that the mechanical properties of the welded joints are comparable with those of the base metal in terms of static strength and are in accordance with the relationship between microstructure and mechanical properties of welded joints. The ultimate tensile strength of the weld is equal to that of the hourglass joint, which indicates that the mechanical properties of the longitudinal FZ and those of the transverse FZ are the same. Macromechanical behavior and macrofracture and microfracture of the base material, joint, and weld specimens are observed. A comparison among the three types of specimen fracture phenomena reveals the following distinctive differences： （1） the fracture mode, （2） the micrograph of the dimple pattern at the central region, and （3） the size of the dimple at the central region and the transition region.
文摘Electron beam welding of in situ TiB2p reinforced aluminum composites was studied. The results show that no obvious pores or cracks is presented in the weld seam. The grains in the weld seam are remarkably refined and TiB2 particles distribute much more homogeneously than that in base metal. The hardness values of fusion zone and heat affected zone （HAZ） are both increased in comparison with that of base metal. There are no interface reactions between TiB2 particle and A1 matrix. This results supply the evidence that the novel TiB2p reinforced aluminum composites can be well joined with the electron beam welding.