Through molecular dynamics（MD） simulation, the dependencies of temperature, grain size and strain rate on the mechanical properties were studied. The simulation results demonstrated that the strain rate from 0.05 to...Through molecular dynamics（MD） simulation, the dependencies of temperature, grain size and strain rate on the mechanical properties were studied. The simulation results demonstrated that the strain rate from 0.05 to 2 ns–1 affected the Young＇s modulus of nickel nanowires slightly, whereas the yield stress increased. The Young＇s modulus decreased approximately linearly; however, the yield stress firstly increased and subsequently dropped as the temperature increased. The Young＇s modulus and yield stress increased as the mean grain size increased from 2.66 to 6.72 nm. Moreover, certain efforts have been made in the microstructure evolution with mechanical properties association under uniaxial tension. Certain phenomena such as the formation of twin structures, which were found in nanowires with larger grain size at higher strain rate and lower temperature, as well as the movement of grain boundaries and dislocation, were detected and discussed in detail. The results demonstrated that the plastic deformation was mainly accommodated by the motion of grain boundaries for smaller grain size. However, for larger grain size, the formations of stacking faults and twins were the main mechanisms of plastic deformation in the polycrystalline nickel nanowire.展开更多
The（submicron＋micron） bimodal size Si Cp-reinforced Mg matrix composite was compressed at the temperature of 270–420 °C and strain rate of 0.001–1 s^-1. Then, dynamic recrystallization（DRX） behavior of the...The（submicron＋micron） bimodal size Si Cp-reinforced Mg matrix composite was compressed at the temperature of 270–420 °C and strain rate of 0.001–1 s^-1. Then, dynamic recrystallization（DRX） behavior of the composite was investigated by thermodynamic method and verified by microstructure analysis. Results illustrated that the composite possess the lower critical strain and higher DRX ratio as compared to monolithic Mg alloys during hot deformation process. The predicted DRX ratio increased with the proceeding of compression, which was well consistent with the experimental value. Results from thermodynamic calculation suggested that the occurrence of DRX could be promoted by Si Cp, which would be further proved by microstructure analysis. Formation of particle deformation zone around micron Si Cp played a significant role in promoting DRX nucleation. Nevertheless, the distribution of submicron Si Cp was increasingly uniform with the proceeding of compression, which could fully restrain grain growth. Therefore, the corporate effects of micron and submicron Si Cp on DRX contributed to the improvement of DRXed ratio and the refinement of grain size for the composite during compression process.展开更多
Single-and two-step hot compression experiments were carried out on 16Cr25Ni6Mo superaustenitic stainless steel in the temperature range from 950 to 1150°C and at a strain rate of 0.1 s^（-1）. In the two-step te...Single-and two-step hot compression experiments were carried out on 16Cr25Ni6Mo superaustenitic stainless steel in the temperature range from 950 to 1150°C and at a strain rate of 0.1 s^（-1）. In the two-step tests, the first pass was interrupted at a strain of 0.2; after an interpass time of 5, 20, 40, 60, or 80 s, the test was resumed. The progress of dynamic recrystallization at the interruption strain was less than 10%. The static softening in the interpass period increased with increasing deformation temperature and increasing interpass time. The static recrystallization was found to be responsible for fast static softening in the temperature range from 950 to 1050°C. However, the gentle static softening at 1100 and 1150°C was attributed to the combination of static and metadynamic recrystallizations. The correlation between calculated fractional softening and microstructural observations showed that approximately 30% of interpass softening could be attributed to the static recovery. The microstructural observations illustrated the formation of fine recrystallized grains at the grain boundaries at longer interpass time. The Avrami kinetics equation was used to establish a relationship between the fractional softening and the interpass period. The activation energy for static softening was determined as 276 kJ/mol.展开更多
The microstructure evolution and formability of Ti-10V-2Fe-3Al alloy related to the initial microstructures and processing variables were investigated during hot forming process. The experimental results show that the...The microstructure evolution and formability of Ti-10V-2Fe-3Al alloy related to the initial microstructures and processing variables were investigated during hot forming process. The experimental results show that the α-phase growth is controlled by solute diffusion during the heat treatment processes. Four different microstructures were established by combinations of several heat treatments, and Ti-10V-2Fe-3Al alloy shows excellent formability both above and below the β transus temperature. The alloy possesses low deformation resistance and active restoration mechanism during the deformation. A constitutive equation describing the hot deformation behavior of Ti-10V-2Fe-3Al alloy was obtained. Higher fl ow stress was observed for the acicular morphology of α phase in microstructures with large aspect ratios as compared with that of small aspect ratios. Due to the dynamic recovery in soft β phase, and the dynamic recrystallization and breakage of acicular α-phase, fl ow softening occurred signifi cantly during deformation. Dynamic recrystallization also occurred especially in the severely deformed regions of forged parts.展开更多
Results of a large set of tensile and compressive creep tests on pure Al were reanalyzed for the influence of low-and high-angle grain boundaries on the deformation resistance at the temperature T = 473 K = 0.51 Tmwhe...Results of a large set of tensile and compressive creep tests on pure Al were reanalyzed for the influence of low-and high-angle grain boundaries on the deformation resistance at the temperature T = 473 K = 0.51 Tmwhere Tm is the melting point.Thermomechanical treatment by equal channel angular pressing followed by heating to T led to strong increase of areal fraction of high-angle boundaries in a structure of subgrains of ≈10^-6m in size,accompanied by significant reduction of subgrain strengthening and of the stress sensitivity of the deformation rate.（Sub）grain strengthening by low-angle boundaries is most effective;the strengthening effect virtually disappears during creep as the boundary spacings coarsen toward their stress-dependent,quasi-stationary size wqs.The same type of coarsening is found for（sub）grain structures with large fraction of high-angle boundaries;in the quasi-stationary state they lead to softening at low and strengthening at high stresses,and a significant increase in tensile fracture strain to values up to 0.8.The results are analogous to former results for Cu and are explained in the same way by the influence of boundaries on storage and recovery of crystal defects and the homogenization of glide.展开更多
Bio-scaffolds which are most commonly open celled porous structures are increasingly used for tissue engineering and regenerative medicine. A number of studies have shown that the bulk properties of such irregular str...Bio-scaffolds which are most commonly open celled porous structures are increasingly used for tissue engineering and regenerative medicine. A number of studies have shown that the bulk properties of such irregular structures are poorly modeled using idealized unit cell approaches. The paper therefore uses novel image based meshing techniques to explore both fluid flow and bulk structural properties of a bone scaffold, as accurate modeling of bio-scaffolds with non-uniform cellular structures is very important for the development of optimal scaffolds for tissue engineering application. In this study, a porous hydroxyapatite/tricalcium phosphate (HA/TCP) bone scaffold has been scanned in a Micro-CT scanner, and converted into a volumetric mesh using image processing software developed by the authors. The resulting mesh was then exported to commercial FEA and CFD solvers for analysis. Initial FEA and CFD studies have shown promising results and have highlighted the importance of accurate modeling to understand how microstructures influence the mechanical property of the scaffold, and to analyze flow regimes through the sample. The work highlights the potential use of image based meshing for the ad hoc characterization of scaffolds as well as for assisting in the design of scaffolds with tailored strength, stiffness, and transport properties.展开更多
A visco-plastic rate-dependent homogenization theory for particle-reinforced composites was derived and the equivalent elastic constants and the equivalent visco-plastic parameters of these composites were obtained. A...A visco-plastic rate-dependent homogenization theory for particle-reinforced composites was derived and the equivalent elastic constants and the equivalent visco-plastic parameters of these composites were obtained. A framework of homogenization the- ory for particle-reinforced W-Ni-Fe composites, a kind of tungsten alloy, was established. Based on the homogenization theory and a fixed-point iteration method, a unit cell model with typical microstructnres of the composite was established by using dynamic analysis program. The effects of tungsten content, tungsten particle shape and particle size and interface strength on the mechanical properties and the crack propagation of the W-Ni-Fe composite are analyzed under quasi-static and dynamic loadings. The stress-strain curves of the composite are given and the relation between the macro-mechanical characteristics and the microstructure parameters is explored, which provides an important theoretical basis for the optimization of the W-Ni-Fe composites.展开更多
基金Supported by the National Natural Science Foundation of China(11102139,11472195)the Natural Science Foundation of Hubei Province of China(2014CFB713)
文摘Through molecular dynamics（MD） simulation, the dependencies of temperature, grain size and strain rate on the mechanical properties were studied. The simulation results demonstrated that the strain rate from 0.05 to 2 ns–1 affected the Young＇s modulus of nickel nanowires slightly, whereas the yield stress increased. The Young＇s modulus decreased approximately linearly; however, the yield stress firstly increased and subsequently dropped as the temperature increased. The Young＇s modulus and yield stress increased as the mean grain size increased from 2.66 to 6.72 nm. Moreover, certain efforts have been made in the microstructure evolution with mechanical properties association under uniaxial tension. Certain phenomena such as the formation of twin structures, which were found in nanowires with larger grain size at higher strain rate and lower temperature, as well as the movement of grain boundaries and dislocation, were detected and discussed in detail. The results demonstrated that the plastic deformation was mainly accommodated by the motion of grain boundaries for smaller grain size. However, for larger grain size, the formations of stacking faults and twins were the main mechanisms of plastic deformation in the polycrystalline nickel nanowire.
基金supported by the National Natural Science Foundation of China (Nos. 51201112, 51274149 and 51474152)the Natural Science Foundation of Shanxi (No. 2013021013-3)the Specialized Research Fund for the Doctoral Program of Higher Education (No. 20121402120004)
文摘The（submicron＋micron） bimodal size Si Cp-reinforced Mg matrix composite was compressed at the temperature of 270–420 °C and strain rate of 0.001–1 s^-1. Then, dynamic recrystallization（DRX） behavior of the composite was investigated by thermodynamic method and verified by microstructure analysis. Results illustrated that the composite possess the lower critical strain and higher DRX ratio as compared to monolithic Mg alloys during hot deformation process. The predicted DRX ratio increased with the proceeding of compression, which was well consistent with the experimental value. Results from thermodynamic calculation suggested that the occurrence of DRX could be promoted by Si Cp, which would be further proved by microstructure analysis. Formation of particle deformation zone around micron Si Cp played a significant role in promoting DRX nucleation. Nevertheless, the distribution of submicron Si Cp was increasingly uniform with the proceeding of compression, which could fully restrain grain growth. Therefore, the corporate effects of micron and submicron Si Cp on DRX contributed to the improvement of DRXed ratio and the refinement of grain size for the composite during compression process.
文摘Single-and two-step hot compression experiments were carried out on 16Cr25Ni6Mo superaustenitic stainless steel in the temperature range from 950 to 1150°C and at a strain rate of 0.1 s^（-1）. In the two-step tests, the first pass was interrupted at a strain of 0.2; after an interpass time of 5, 20, 40, 60, or 80 s, the test was resumed. The progress of dynamic recrystallization at the interruption strain was less than 10%. The static softening in the interpass period increased with increasing deformation temperature and increasing interpass time. The static recrystallization was found to be responsible for fast static softening in the temperature range from 950 to 1050°C. However, the gentle static softening at 1100 and 1150°C was attributed to the combination of static and metadynamic recrystallizations. The correlation between calculated fractional softening and microstructural observations showed that approximately 30% of interpass softening could be attributed to the static recovery. The microstructural observations illustrated the formation of fine recrystallized grains at the grain boundaries at longer interpass time. The Avrami kinetics equation was used to establish a relationship between the fractional softening and the interpass period. The activation energy for static softening was determined as 276 kJ/mol.
基金Funded by the National Natural Science Foundation of China(Nos.51222405 and 51474063)
文摘The microstructure evolution and formability of Ti-10V-2Fe-3Al alloy related to the initial microstructures and processing variables were investigated during hot forming process. The experimental results show that the α-phase growth is controlled by solute diffusion during the heat treatment processes. Four different microstructures were established by combinations of several heat treatments, and Ti-10V-2Fe-3Al alloy shows excellent formability both above and below the β transus temperature. The alloy possesses low deformation resistance and active restoration mechanism during the deformation. A constitutive equation describing the hot deformation behavior of Ti-10V-2Fe-3Al alloy was obtained. Higher fl ow stress was observed for the acicular morphology of α phase in microstructures with large aspect ratios as compared with that of small aspect ratios. Due to the dynamic recovery in soft β phase, and the dynamic recrystallization and breakage of acicular α-phase, fl ow softening occurred signifi cantly during deformation. Dynamic recrystallization also occurred especially in the severely deformed regions of forged parts.
基金support by the Central European Institute of Technology CEITEC(Project CZ.1.05/1.1.00/02.0068 and the European Regional Development Fund)
文摘Results of a large set of tensile and compressive creep tests on pure Al were reanalyzed for the influence of low-and high-angle grain boundaries on the deformation resistance at the temperature T = 473 K = 0.51 Tmwhere Tm is the melting point.Thermomechanical treatment by equal channel angular pressing followed by heating to T led to strong increase of areal fraction of high-angle boundaries in a structure of subgrains of ≈10^-6m in size,accompanied by significant reduction of subgrain strengthening and of the stress sensitivity of the deformation rate.（Sub）grain strengthening by low-angle boundaries is most effective;the strengthening effect virtually disappears during creep as the boundary spacings coarsen toward their stress-dependent,quasi-stationary size wqs.The same type of coarsening is found for（sub）grain structures with large fraction of high-angle boundaries;in the quasi-stationary state they lead to softening at low and strengthening at high stresses,and a significant increase in tensile fracture strain to values up to 0.8.The results are analogous to former results for Cu and are explained in the same way by the influence of boundaries on storage and recovery of crystal defects and the homogenization of glide.
文摘Bio-scaffolds which are most commonly open celled porous structures are increasingly used for tissue engineering and regenerative medicine. A number of studies have shown that the bulk properties of such irregular structures are poorly modeled using idealized unit cell approaches. The paper therefore uses novel image based meshing techniques to explore both fluid flow and bulk structural properties of a bone scaffold, as accurate modeling of bio-scaffolds with non-uniform cellular structures is very important for the development of optimal scaffolds for tissue engineering application. In this study, a porous hydroxyapatite/tricalcium phosphate (HA/TCP) bone scaffold has been scanned in a Micro-CT scanner, and converted into a volumetric mesh using image processing software developed by the authors. The resulting mesh was then exported to commercial FEA and CFD solvers for analysis. Initial FEA and CFD studies have shown promising results and have highlighted the importance of accurate modeling to understand how microstructures influence the mechanical property of the scaffold, and to analyze flow regimes through the sample. The work highlights the potential use of image based meshing for the ad hoc characterization of scaffolds as well as for assisting in the design of scaffolds with tailored strength, stiffness, and transport properties.
基金supported by the National Natural Science Foundation of China (Grant No. 11032002 and 91016013)the program for New Century Excellent Talents in University+1 种基金National Basic Research Program of China (Grant No. 2010CB832706)the project of State Key Laboratory of Explosion Science and Technology (Beijing Institute of Technology)(Grant No. ZDKT10-03a)
文摘A visco-plastic rate-dependent homogenization theory for particle-reinforced composites was derived and the equivalent elastic constants and the equivalent visco-plastic parameters of these composites were obtained. A framework of homogenization the- ory for particle-reinforced W-Ni-Fe composites, a kind of tungsten alloy, was established. Based on the homogenization theory and a fixed-point iteration method, a unit cell model with typical microstructnres of the composite was established by using dynamic analysis program. The effects of tungsten content, tungsten particle shape and particle size and interface strength on the mechanical properties and the crack propagation of the W-Ni-Fe composite are analyzed under quasi-static and dynamic loadings. The stress-strain curves of the composite are given and the relation between the macro-mechanical characteristics and the microstructure parameters is explored, which provides an important theoretical basis for the optimization of the W-Ni-Fe composites.