Dynamic oxygen storage and release capability （OSC） measurement apparatus was designed to evaluate the OSC performance of ceria-based oxygen storage material. The optimum measurement condition was at a frequency of ...Dynamic oxygen storage and release capability （OSC） measurement apparatus was designed to evaluate the OSC performance of ceria-based oxygen storage material. The optimum measurement condition was at a frequency of 0.1 Hz with the inlet gas-flow sequence CO （5S）→O2（5S）→CO→O2 and a flow rate of 300 ml·min^-1. Under this condition, similar regular square wave in the inlet and outlet of the reactor was obtained to guarantee the reliability of the dynamic OSC results. The dynamic OSC performance of the CeO2 and Ce0.67Zr0.33O2 mixed oxide prepared using the citric sol-gel method was studied at the optimum measurement condition with focus on both quantitative and qualitative analyses, The results reveal distinctly that Ce0.67Zr0.33O2 had better dynamic OSC performance because of its higher oxygen migration rate than CeO2. Under dynamic conditions, two CO2 production peaks occurred corresponding to the CO pulse and the O2 pulse, respectively, during the entire cycle. The intensity and ratio between the two CO2 productions were highly influenced by temperature and frequency indicating complex surface phenomena during the oxygen storage/release process, As a result, this set-up can be applied to the evaluation of ceria-based material on the OSC performance.展开更多
CeO2-ZrO2-MnOx mixed oxide series were prepared by sol-gel method. CO pulse and CO-O2 cycle measurements were carried out to examine the oxygen storage complete capacity （OSCC） and dynamic oxygen storage capacity （...CeO2-ZrO2-MnOx mixed oxide series were prepared by sol-gel method. CO pulse and CO-O2 cycle measurements were carried out to examine the oxygen storage complete capacity （OSCC） and dynamic oxygen storage capacity （OSC） of the samples. The doping method brought about strong interactions between manganese oxide and ceria, both in the bulk and on the surface. Only a small part of Mn cations are incorporated into the ceria lattice to form solid solutions and the remaining are left on the surface as finely dispersed Mn3O4. The OSC behaviors of the materials are influenced by the doping amount of Mn and the solubility of Mn in the CeO2 lattice. The OSC is more easily affected by available contents of oxygen storage components when the measurement frequency is low. Comparatively, the concentration of lattice defects, which affects the mobility of bulk oxygen, is the determining factor under high frequency.展开更多
基金Project supported by the National"973"Project (2004CB719503) and the Programfor New Century Excellent Talents in University
文摘Dynamic oxygen storage and release capability （OSC） measurement apparatus was designed to evaluate the OSC performance of ceria-based oxygen storage material. The optimum measurement condition was at a frequency of 0.1 Hz with the inlet gas-flow sequence CO （5S）→O2（5S）→CO→O2 and a flow rate of 300 ml·min^-1. Under this condition, similar regular square wave in the inlet and outlet of the reactor was obtained to guarantee the reliability of the dynamic OSC results. The dynamic OSC performance of the CeO2 and Ce0.67Zr0.33O2 mixed oxide prepared using the citric sol-gel method was studied at the optimum measurement condition with focus on both quantitative and qualitative analyses, The results reveal distinctly that Ce0.67Zr0.33O2 had better dynamic OSC performance because of its higher oxygen migration rate than CeO2. Under dynamic conditions, two CO2 production peaks occurred corresponding to the CO pulse and the O2 pulse, respectively, during the entire cycle. The intensity and ratio between the two CO2 productions were highly influenced by temperature and frequency indicating complex surface phenomena during the oxygen storage/release process, As a result, this set-up can be applied to the evaluation of ceria-based material on the OSC performance.
基金Project supported by the National "973"Project (2004CB719503)Project supported by the National Natural ScienceFoundation of China (50502023)
文摘CeO2-ZrO2-MnOx mixed oxide series were prepared by sol-gel method. CO pulse and CO-O2 cycle measurements were carried out to examine the oxygen storage complete capacity （OSCC） and dynamic oxygen storage capacity （OSC） of the samples. The doping method brought about strong interactions between manganese oxide and ceria, both in the bulk and on the surface. Only a small part of Mn cations are incorporated into the ceria lattice to form solid solutions and the remaining are left on the surface as finely dispersed Mn3O4. The OSC behaviors of the materials are influenced by the doping amount of Mn and the solubility of Mn in the CeO2 lattice. The OSC is more easily affected by available contents of oxygen storage components when the measurement frequency is low. Comparatively, the concentration of lattice defects, which affects the mobility of bulk oxygen, is the determining factor under high frequency.