Ru O2·n H2O film was deposited on tantalum foils by electrodeposition and heat treatment using Ru Cl3·3H2O as precursor.Surface morphology, composition change and cyclic voltammetry from precursor to amorpho...Ru O2·n H2O film was deposited on tantalum foils by electrodeposition and heat treatment using Ru Cl3·3H2O as precursor.Surface morphology, composition change and cyclic voltammetry from precursor to amorphous and crystalline RuO2·n H2O films were studied by X-ray diffractometer, Fourier transformation infrared spectrometer, differential thermal analyzer, scanning electron microscope and electrochemical analyzer, respectively. The results show that the precursor was transformed gradually from amorphous to crystalline phase with temperature. When heat treated at 300 °C for 2h, RuO2·n H2O electrode surface gains mass of2.5 mg/cm2 with specific capacitance of 782 F/g. Besides, it is found that the specific capacitance of the film decreased by roughly20% with voltage scan rate increasing from 5 to 250 m V/s.展开更多
Although poly(lactic acid)(PLA)is a good environmentally-friendly bio-degradable polymer which is used to substitute traditional petrochemical-based polymer packaging films,the barrier properties of PLA films are stil...Although poly(lactic acid)(PLA)is a good environmentally-friendly bio-degradable polymer which is used to substitute traditional petrochemical-based polymer packaging films,the barrier properties of PLA films are still insufficient for high-barrier packaging applications.In this study,oxygen scavenger hydroxyl-terminated polybutadiene(HTPB)and cobalt salt catalyst were incorporated into the PLA/poly(butylene adipate-co-terephthalate)(PLA/PBAT),followed by melting extrusion and three-layer co-extrusion blown film process to prepare the composite films.The oxygen permeability coefficient of the composite film combined with 6 wt%oxygen scavenger and 0.4 wt%catalyst was decreased significantly from 377.00 cc·mil·m^(-2)·day^(-1)·0.1 MPa^(-1) to 0.98 cc·mil·m^(-2)·day^(-1)·0.1 MPa^(-1),showing a remarkable enhancement of 384.69 times compared with the PLA/PBAT composite film.Meanwhile,the degradation behavior of the composite film was also accelerated,exhibiting a mass loss of nearly 60%of the original mass after seven days of degradation in an alkaline environment,whereas PLA/PBAT composite film only showed a mass loss of 32%.This work has successfully prepared PLA/PBAT composite films with simultaneously improved oxygen barrier property and degradation behavior,which has great potential for high-demanding green chemistry packaging industries,including food,agricultural,and military packaging.展开更多
Metal Fe/Pd compositionally modulated films(CMFs) were prepared by vapour depo- sition from two sources onto glass substrate under vacuum.The modulation and crystal structures of the films were examined by X-ray diffr...Metal Fe/Pd compositionally modulated films(CMFs) were prepared by vapour depo- sition from two sources onto glass substrate under vacuum.The modulation and crystal structures of the films were examined by X-ray diffraction.The magnetic properties were determined by vibrating sample magnetometer.The Pd layers in the Fe/Pd CMFs are of fcc structure,and the Fe layer structure transits from bcc into amorphous,state with decreasing thickness of Fe layer.The dependence of specific saturation magnetization on thickness of Fe layers has also been discussed.展开更多
To alleviate the quality deterioration and extend the shelf life of crucian carp fillets,a bio-based active composite film integrating eugenol(EG)-loaded mesoporous silica nanoparticles(MSNs)modified with caffeic acid...To alleviate the quality deterioration and extend the shelf life of crucian carp fillets,a bio-based active composite film integrating eugenol(EG)-loaded mesoporous silica nanoparticles(MSNs)modified with caffeic acid(CA)within the zein matrix(EG/CA-MSN/Zein)was developed.This study compared the effects of EG/CA-MSN/Zein,polyethylene(PE),and zein films on the quality of fish fillets during refrigerated storage.The results showed that the EG/CA-MSN/Zein film significantly retarded the increase in pH and microbial growth.Moreover,the film had higher water-holding capacity(WHC),better texture,and color stability,as indicated by low-field nuclear magnetic resonance(LF-NMR),magnetic resonance imaging(MRI),and sensory evaluation.The EG/CA-MSN/Zein composite film extended the shelf life of crucian carp fillets by 3-4 days,highlighting its potential as an environmentally friendly and efficient packaging material for aquatic products.展开更多
The full arrival of 5 G and advances in electronic integration make efficient heat dissipation crucial for stable operation and longer product lifespan. In this study, a vacuum-assisted filtration process was employed...The full arrival of 5 G and advances in electronic integration make efficient heat dissipation crucial for stable operation and longer product lifespan. In this study, a vacuum-assisted filtration process was employed to fabricate ammoniated alumina/MXene/bacterial cellulose (Al_(2)O_(3)-NH_(2)/MXene/BC) composite films that display a unique integration of properties, encompassing ultra-high thermal conductivity (λ), mechanical flexibility, and high photothermal conversion performance. By leveraging the bridging effect among spherical Al_(2)O_(3)-NH_(2) and MXene nanosheets, a densely packed “point-surface” structure was constructed in BC by using a one-step preparation process. When the mass fraction of Al_(2)O_(3)-NH_(2)/MXene (1:3, w/w) is 40 wt%, the O-BAl1M3 exhibited an in-plane λ of 20.02 W m^(-1) K^(-1), which was 436 % and 94 % higher than that of pure BC and T-BAl1M3 (prepared by a two-step method), respectively. Furthermore, constructing an intact thermal conductive network within BC notably promoted photothermal and photoelectric conversion performance. The maximum surface temperature and voltage of the O-BAl1M3 film reached 106.9 ℃ and 48.34 mV when a sample with an area of 1.56 cm^(2) was exposed under a light intensity of 200 mW cm^(-2). By applying O-BAl1M3 film, the temperature inside a self-built greenhouse model reached up to 64.8 ℃ within 1200 s under a light intensity of 100 mW cm^(-2), which validated the practical application of the composite films and offered a novel approach for creating flexible films with superior photothermal conversion capability. This work provided insights into preparing functional composite films for efficient thermal management and photothermal conversion applications.展开更多
White light illumination is essential in daily life,however,the substantial amount of blue light it contains can damage human eyes.Therefore,it is important to block this high-energy blue light to protect visual healt...White light illumination is essential in daily life,however,the substantial amount of blue light it contains can damage human eyes.Therefore,it is important to block this high-energy blue light to protect visual health.In this study,yellow-emitting carbon dots(CDs)with a quantum yield exceeding 94%were synthesized using citric acid and urea.These CDs effectively absorb blue light.By incorporating them into polystyrene,multiple films termed CDs-based blue light blocking films(CBFs)were developed,each offering different levels of blue light absorption.These CBFs exhibited excellent transparency and efficient blue light filtering capabilities.This study highlights the potential of high quantum yield CDs,which specifically absorb blue light,as foundational materials for developing light-blocking solutions against highenergy short-wavelength light.展开更多
This work reports a soft chemistry approach for the synthesis of magnesium oxide nanoparticles(MgO)incorporated in a polyaniline(PANI)matrix to give PANI/MgO nanocomposite.Using spin coating method,three different per...This work reports a soft chemistry approach for the synthesis of magnesium oxide nanoparticles(MgO)incorporated in a polyaniline(PANI)matrix to give PANI/MgO nanocomposite.Using spin coating method,three different percentages of MgO/PVC(1,2,and 3%in wt.%)were deposited on glass substrates.These films of PANI/MgO nanocomposite were characterized by X-ray diffraction(XRD),atomic force microscopy(AFM),and UV-visible spectroscopy.The results of the XRD pattern revealed the embedding of MgO nanoparticles in the PANI matrix with cubic phase,with the average size of nanoparticles varying from 35.12 to 59.55 nm.The AFM images displayed a significant change in the morphology of the PANI/MgO NPs composite films as MgO concentration was increased.The optical transmittance analysis revealed that at very low concentrations of MgO in PANI/MgO nanocomposite films,there is a high transparency,reaching close to 90%.However,this transmittance decreases significantly as the concentration of MgO increases.The photocatalytic activity of the nanocomposite film was then evaluated for the degradation of methylene blue(MB)dye under UV light irradiation.The results indicated a strong potential for PANI/MgO nanocomposite films in effectively degrading MB,supported by a proposed mechanism for the photocatalytic reaction.Compared with other composites such as PVC/MgO,PANI/MgO nanocomposite presented better MB degradation efficiency.展开更多
To mitigate secondary electromagnetic pollution,there is an urgent need to develop absorption-dominant electromagnetic interference(EMI)shielding materials with low density,reduced thickness,lightweight construction,f...To mitigate secondary electromagnetic pollution,there is an urgent need to develop absorption-dominant electromagnetic interference(EMI)shielding materials with low density,reduced thickness,lightweight construction,flexibility,exceptional mechanical strength,and superior electrothermal and photothermal properties,particularly for flexible and wearable electronics.In this regard,we designed an absorption-based composite film comprising carbon nanotubes(CNT)and α-Fe_(2)O_(3),featuring a CNT layer sandwiched between twoα-Fe_(2)O_(3)layers on the upper and lower surfaces.This composite film was fabricated through an electrodeposition process followed by a thermal annealing procedure to achieve enhanced EMI shielding performance along with improved electrothermal and photothermal properties.The strategically designed sandwich structure allows the rough surface of the upper α-Fe_(2)O_(3)layer to not only improve the impedance mismatch between free space and the composite film,facilitating the penetration of incident electromagnetic(EM)waves into the film and promoting increased EM absorption rather than reflection,but also to enhance electrical conductivity,thereby improving electron mobility and density.Consequently,the average total shielding effectiveness(SE)of the CNT/Fe_(16)-300 composite demonstrates remarkable EMI shielding effectiveness(EMI SE:56.8 dB).Furthermore,the alteration in the absorption-to-reflection ratio(A/R)signifies a transition in the EMI shielding mechanism from reflection(0.69 for the pristine CNT film)to absorption(1.86 for the CNT/Fe_(16)-300)with the incremental deposition of α-Fe_(2)O_(3)nanoparticles.This work presents a feasible manufacturing approach for developing composite films with a sandwich structure that exhibits absorption-dominant EMI shielding capabilities,contributing to advancements in thermal management and multifunctional electromagnetic shielding applications.展开更多
ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （...ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.展开更多
A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of...A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of the composite films was studied in the conditions of the ambient air and N2 gas atmosphere by ball-on-disk tester.The results indicate that the composite films show dense and amorphous microstructure.The WCx and WSx compounds are found in amorphous diamond like carbon matrix in the top layers of W-S-C.A proper WSx content is beneficial for improving the adhesion of the composite films.In air atmosphere,the composite films with high C content have better wear resistance and the friction coefficients range from 0.15 to 0.25.In N2 condition,high WSx content is benefit for the wear resistance and the friction coefficients of the composite films range from 0.03 to 0.1.展开更多
A specific revised HFCVD apparatus and a novel process combining HFCVD and polishing technique were presented to deposit the micro-and nano-crystalline multilayered ultra-smooth diamond（USCD） film on the interior-ho...A specific revised HFCVD apparatus and a novel process combining HFCVD and polishing technique were presented to deposit the micro-and nano-crystalline multilayered ultra-smooth diamond（USCD） film on the interior-hole surface of WC-Co drawing dies with aperture ranging from d1.0 mm to 60 mm.Characterization results indicate that the surface roughness values（Ra） in the entry zone,drawing zone and bearing zone of as-fabricated USCD coated drawing die were measured as low as 25.7,23.3 and 25.5 nm,respectively.Furthermore,the friction properties of USCD films were examined in both dry sliding and water-lubricating conditions,and the results show that the USCD film presents much superior friction properties.Its friction coefficients against ball-bearing steel,copper and silicon nitride balls（d4 mm）,is always lower than that of microcrystalline diamond（MCD） or WC-Co sample,regardless of the lubricating condition.Meanwhile,it still presents competitive wear resistance with the MCD films.Finally,the working lifetime and performance of as-fabricated USCD coated drawing dies were examined under producing low-carbon steel pipes in dry-sliding and water-lubricating conditions.Under the water-lubricating drawing condition,its production significantly increases by about 20 times compared with the conventional WC-Co drawing dies.展开更多
CoFe204/Pb（Zr0.53Ti0.47）O3 （CFO/PZT） magnetoelectric composite thin films of 2-2 type structure had been prepared onto Pt/Ti/SiO2/Si substrate by a sol-gel process and spin coat- ing technique. The structure of th...CoFe204/Pb（Zr0.53Ti0.47）O3 （CFO/PZT） magnetoelectric composite thin films of 2-2 type structure had been prepared onto Pt/Ti/SiO2/Si substrate by a sol-gel process and spin coat- ing technique. The structure of the prepared thin film is substrate/PZT/CFO/PZT/CFO. Two CFO ferromagnetic layers are separated from each other by a thin PZT layer. The upper CFO layer is magnetostatically coupled with the lower CFO layer. Subsequent scan- ning electron microscopy （SEM） investigations show that the prepared thin films exhibit good morphologies and compact structure, and cross-sectional micrographs clearly display a multilayered nanostructure of multilayered thin films. The composite thin films exhibit both good magnetic and ferroelectric properties. The spacing between ferromagnetic layers can be varied by adjusting the thickness of intermediate PZT layer. It is found that the strength of magnetostatic coupling has a great impact on magnetoelectric properties of composite thin films, i.e., the magnetoelectric voltage coefficient of composite thin film tends to increase with the decreasing of pacing between two neighboring CFO ferromagnetic layers as a result of magnetostatic coupling effect.展开更多
The nonlinear optical properties of Al-doped nc-Si-SiO2 composite films have been investigated using the time-resolved four-wave mixing technique with a femtosecond laser. The off-resonant third-order nonlinear suscep...The nonlinear optical properties of Al-doped nc-Si-SiO2 composite films have been investigated using the time-resolved four-wave mixing technique with a femtosecond laser. The off-resonant third-order nonlinear susceptibility is observed to be 1.0 × 10-10 esu at 800nm. The relaxation time of the optical nonlinearity in the films is as short as 60fs. The optical nonlinearity is enhanced due to the quantum confinement of electrons in Si nanocrystals embedded in the SiO2 films. The enhanced optical nonlinearity does not originate from Al dopant because there are no Al clusters in the films.展开更多
The composite films, XW11O39n-/SiO2, (X refers to Si, Ge or P, respectively) were prepared by tetraethoxysilane (TEOS) hydrolysis sol-gel method via spin-coating technique. Formation of the composite films is due to s...The composite films, XW11O39n-/SiO2, (X refers to Si, Ge or P, respectively) were prepared by tetraethoxysilane (TEOS) hydrolysis sol-gel method via spin-coating technique. Formation of the composite films is due to strong chemical reaction of organic silanol group with the surface oxygen atoms of XW11O39n-, resulted in the saturation of the surface of the lacunary polyoxometalates (POMs). Therefore, the coordination structural model of the films was proposed. As for the films, retention of the primary Keggin structure was confirmed by UV-vis, FT-IR spectra and MAS NMR. The surface morphology of the films was characterized by SEM, indicating that the film surface is relatively uniform, and the layer thickness is in the range of 250~350 nm. Aqueous formic acid (FA) (0-20 mmol/L) was degraded into CO2 and H2O by irradiating the films in the near-UV area. The results show that all the films have photocatalytic activities and the degradation reaction follows Langmuir-Hinshelwood first order kinetics.展开更多
Pipelines are extensively used in environments such as nuclear power plants,chemical factories,and medical devices to transport gases and liquids.These tubular environments often feature complex geometries,confined sp...Pipelines are extensively used in environments such as nuclear power plants,chemical factories,and medical devices to transport gases and liquids.These tubular environments often feature complex geometries,confined spaces,and millimeter-scale height restrictions,presenting significant challenges to conventional inspection methods.Here,we present an ultrasonic microrobot(weight,80 mg;dimensions,24 mm×7 mm;thickness,210μm)to realize agile and bidirectional navigation in narrow pipelines.The ultrathin structural design of the robot is achieved through a high-performance piezoelectric composite film microstructure based on MEMS technology.The robot exhibits various vibration modes when driven by ultrasonic frequency signals,its motion speed reaches81 cm s-1 at 54.8 k Hz,exceeding that of the fastest piezoelectric microrobots,and its forward and backward motion direction is controllable through frequency modulation,while the minimum driving voltage for initial movement can be as low as 3 VP-P.Additionally,the robot can effortlessly climb slopes up to 24.25°and carry loads more than 36 times its weight.The robot is capable of agile navigation through curved L-shaped pipes,pipes made of various materials(acrylic,stainless steel,and polyvinyl chloride),and even over water.To further demonstrate its inspection capabilities,a micro-endoscope camera is integrated into the robot,enabling real-time image capture inside glass pipes.展开更多
Cross-band camouflage technology is a critical necessity,enabling personnel and equipment to evade detection across evolving surveillance systems,thereby enhancing survivability and mission success.Herein,this work de...Cross-band camouflage technology is a critical necessity,enabling personnel and equipment to evade detection across evolving surveillance systems,thereby enhancing survivability and mission success.Herein,this work develops a layer-structured composite system based on carbon nanotube(CNT)film comprising ionic liquid(IL)interlayer for infrared(IR)modulation and surface-engineered Cu_(2)O nanoparticles for visible camouflage.The CNT/IL/CNT architecture enables reversible IR emissivity switching(Δε≈0.55)through electrically driven ion intercalation/deintercalation within 2 s,while spray-coated Cu_(2)O nanoparticles(100~400 nm diameter)on the top CNT film layer generate rich structure colors with 90%IR transmittance.This spectral-decoupling design overcomes the traditional trade-off between color visibility and IR transmittance observed in pigment-based systems.Remarkably,due to physical interface coupling,the Cu_(2)O-coated layer-structured system maintains exceptional electrical conductivity,enabling simultaneous electromagnetic interference shielding and electrothermal energy conversion.The integrated system demonstrates long-term operational stability.By unifying visible-IR camouflage,electromagnetic protection,and energy management in a lightweight platform,this work provides an important paradigm for cross-band camouflage technologies.展开更多
The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The c...The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.展开更多
In recent years,graphene-based composite films have been greatly developed in the field of electromagnetic shielding interference(EMI).However,it is still a huge challenge to prepare graphene-based composite films wit...In recent years,graphene-based composite films have been greatly developed in the field of electromagnetic shielding interference(EMI).However,it is still a huge challenge to prepare graphene-based composite films with excellent mechanical properties,conductivity and electromagnetic shielding properties.In this work,we adopted a facile and effective method by annealing the alkali-treated polyacrylonitrile(aPAN)nanofibers reinforced graphene oxide(GO)composite films at 2000°C to obtain graphene-carbon nanofibers composite films(GCFs).Microscopically,carbon nanofibers(CNFs)were intercalated into the graphene sheets,and microgasbags structure was formed during the heat treatment process.The special structure makes GCFs have superior tensile strength(10.4 MPa)at 5%strain.After repeated folding over1000 times,the films still demonstrate excellent structural integrity and flexibility performance.Interestingly,the graphene-based composite films with 10 wt%a PAN nanofibers exhibit an extremely low density of about 0.678 g/cm^(3)and excellent electrical conductivity of 1.72×10^(5)S/m.Further,an outstanding electromagnetic shielding effectiveness(SE)of 55–57 d B was achieved,and the corresponding value of the specific SE/thickness can reach 67,601–70,059 d B·cm^(2)/g,which is the highest among reported graphenebased shielding materials.The significant electromagnetic shielding performance is due to the synergistic enhancement effect brought by the excellent conductivity of carbon nanofibers and graphene,the formed effective conductive network and the microgasbags structure.Electromagnetism simulation further clarified that the underlying mechanism should be mainly attributed to the conduction loss and multiple reflections caused by the special structure of GCFs.This work will provide new solutions for low density,high flexibility and excellent electromagnetic shielding properties materials in the next generation of foldable and wearable electronics.展开更多
A tin film of 320 nm in thickness on Cu foil and its composite film with graphite of-50 nm in thickness on it were fabricated by magnetron sputtering. The surface morphology, composition, surface distributions of allo...A tin film of 320 nm in thickness on Cu foil and its composite film with graphite of-50 nm in thickness on it were fabricated by magnetron sputtering. The surface morphology, composition, surface distributions of alloy elements, and lithium intercalation/de-intercalation behaviors of the fabricated films were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, electron probe microanalyzer （EPMA）, X-ray photoelectron spectroscopy （XPS）, inductively coupled plasma atomic emission spectrometry （ICP）, cyclic voltammetry （CV）, and galvanostatic charge/discharge （GC） measurements. It is found that the lithium intercalation/de-intercalation behavior of the Sn film can be significantly improved by its composite with graphite. With cycling, the discharge capacity of the Sn film without composite changes from 570 mAh/g of the 2nd cycle to 270 mAh/g of the 20th cycle, and its efficiency for the discharge and charge is between 90% and 95%. Nevertheless, the discharge capacity of the composite Sn/C film changes from 575 mAh/g of the 2nd cycle to 515 mAh/g of the 20th cycle, and its efficiency for the discharge and charge is between 95% and 100%. The performance improvement of tin by its composite with graphite is ascribed to the retardation of the bulk tin cracking from volume change during lithium intercalation and de-intercalation, which leads to the pulverization of tin.展开更多
With rapid progressive application of TiO2 thin films, magnetron sputtering becomes a very interesting method to prepare such multi-functional thin films. This paper focuses on influences of various deposition process...With rapid progressive application of TiO2 thin films, magnetron sputtering becomes a very interesting method to prepare such multi-functional thin films. This paper focuses on influences of various deposition processes and deposition rate on the structures and properties of TiO2 thin films. Anatase, rutile or amorphous TiO2 films with various crystalline structures and different photocatalytic, optical and electrical properties can be produced by varying sputtering gases, substrate temperature, annealing process, deposition rate and the characteristics of magnetron sputtering. This may in turn affect the functions of TiO2 films in many applications. Furthermore, TiO2-based composites films can overcome many limitations and improve the properties of TiO2 films.展开更多
基金Project(S2013040015492)supported by the Natural Science Foundation of Guangdong Province,ChinaProject(2007AA03Z240)supported by Hi-tech Research and Development Program of China
文摘Ru O2·n H2O film was deposited on tantalum foils by electrodeposition and heat treatment using Ru Cl3·3H2O as precursor.Surface morphology, composition change and cyclic voltammetry from precursor to amorphous and crystalline RuO2·n H2O films were studied by X-ray diffractometer, Fourier transformation infrared spectrometer, differential thermal analyzer, scanning electron microscope and electrochemical analyzer, respectively. The results show that the precursor was transformed gradually from amorphous to crystalline phase with temperature. When heat treated at 300 °C for 2h, RuO2·n H2O electrode surface gains mass of2.5 mg/cm2 with specific capacitance of 782 F/g. Besides, it is found that the specific capacitance of the film decreased by roughly20% with voltage scan rate increasing from 5 to 250 m V/s.
基金financial support of this work by the National Natural Science Foundation of China(Nos.22378332,52003219)the Open Fund of Zhejiang Key Laboratory of Flexible Electronics(No.2022FE008)+1 种基金the Natural Science Foundation of Ningbo(NO.2022J058)Ministry of Industry and Information Technology high quality development project(TC220A04A-206).
文摘Although poly(lactic acid)(PLA)is a good environmentally-friendly bio-degradable polymer which is used to substitute traditional petrochemical-based polymer packaging films,the barrier properties of PLA films are still insufficient for high-barrier packaging applications.In this study,oxygen scavenger hydroxyl-terminated polybutadiene(HTPB)and cobalt salt catalyst were incorporated into the PLA/poly(butylene adipate-co-terephthalate)(PLA/PBAT),followed by melting extrusion and three-layer co-extrusion blown film process to prepare the composite films.The oxygen permeability coefficient of the composite film combined with 6 wt%oxygen scavenger and 0.4 wt%catalyst was decreased significantly from 377.00 cc·mil·m^(-2)·day^(-1)·0.1 MPa^(-1) to 0.98 cc·mil·m^(-2)·day^(-1)·0.1 MPa^(-1),showing a remarkable enhancement of 384.69 times compared with the PLA/PBAT composite film.Meanwhile,the degradation behavior of the composite film was also accelerated,exhibiting a mass loss of nearly 60%of the original mass after seven days of degradation in an alkaline environment,whereas PLA/PBAT composite film only showed a mass loss of 32%.This work has successfully prepared PLA/PBAT composite films with simultaneously improved oxygen barrier property and degradation behavior,which has great potential for high-demanding green chemistry packaging industries,including food,agricultural,and military packaging.
文摘Metal Fe/Pd compositionally modulated films(CMFs) were prepared by vapour depo- sition from two sources onto glass substrate under vacuum.The modulation and crystal structures of the films were examined by X-ray diffraction.The magnetic properties were determined by vibrating sample magnetometer.The Pd layers in the Fe/Pd CMFs are of fcc structure,and the Fe layer structure transits from bcc into amorphous,state with decreasing thickness of Fe layer.The dependence of specific saturation magnetization on thickness of Fe layers has also been discussed.
文摘To alleviate the quality deterioration and extend the shelf life of crucian carp fillets,a bio-based active composite film integrating eugenol(EG)-loaded mesoporous silica nanoparticles(MSNs)modified with caffeic acid(CA)within the zein matrix(EG/CA-MSN/Zein)was developed.This study compared the effects of EG/CA-MSN/Zein,polyethylene(PE),and zein films on the quality of fish fillets during refrigerated storage.The results showed that the EG/CA-MSN/Zein film significantly retarded the increase in pH and microbial growth.Moreover,the film had higher water-holding capacity(WHC),better texture,and color stability,as indicated by low-field nuclear magnetic resonance(LF-NMR),magnetic resonance imaging(MRI),and sensory evaluation.The EG/CA-MSN/Zein composite film extended the shelf life of crucian carp fillets by 3-4 days,highlighting its potential as an environmentally friendly and efficient packaging material for aquatic products.
基金support of this work by the Project of Education Department of Shaanxi Province(No.23JK0373)the Shaanxi University of Technology Graduate Innovation Fund(No.SLGYCX2402)the Talent Start-up Fund of Shaanxi University of Technology(No.SLGRCQD2329).
文摘The full arrival of 5 G and advances in electronic integration make efficient heat dissipation crucial for stable operation and longer product lifespan. In this study, a vacuum-assisted filtration process was employed to fabricate ammoniated alumina/MXene/bacterial cellulose (Al_(2)O_(3)-NH_(2)/MXene/BC) composite films that display a unique integration of properties, encompassing ultra-high thermal conductivity (λ), mechanical flexibility, and high photothermal conversion performance. By leveraging the bridging effect among spherical Al_(2)O_(3)-NH_(2) and MXene nanosheets, a densely packed “point-surface” structure was constructed in BC by using a one-step preparation process. When the mass fraction of Al_(2)O_(3)-NH_(2)/MXene (1:3, w/w) is 40 wt%, the O-BAl1M3 exhibited an in-plane λ of 20.02 W m^(-1) K^(-1), which was 436 % and 94 % higher than that of pure BC and T-BAl1M3 (prepared by a two-step method), respectively. Furthermore, constructing an intact thermal conductive network within BC notably promoted photothermal and photoelectric conversion performance. The maximum surface temperature and voltage of the O-BAl1M3 film reached 106.9 ℃ and 48.34 mV when a sample with an area of 1.56 cm^(2) was exposed under a light intensity of 200 mW cm^(-2). By applying O-BAl1M3 film, the temperature inside a self-built greenhouse model reached up to 64.8 ℃ within 1200 s under a light intensity of 100 mW cm^(-2), which validated the practical application of the composite films and offered a novel approach for creating flexible films with superior photothermal conversion capability. This work provided insights into preparing functional composite films for efficient thermal management and photothermal conversion applications.
基金supported by Medical Science and Technology Research Project of Henan Province(Joint Construction Project)(No.LHGJ20200433)National Natural Science Foundation of China(No.52122308)。
文摘White light illumination is essential in daily life,however,the substantial amount of blue light it contains can damage human eyes.Therefore,it is important to block this high-energy blue light to protect visual health.In this study,yellow-emitting carbon dots(CDs)with a quantum yield exceeding 94%were synthesized using citric acid and urea.These CDs effectively absorb blue light.By incorporating them into polystyrene,multiple films termed CDs-based blue light blocking films(CBFs)were developed,each offering different levels of blue light absorption.These CBFs exhibited excellent transparency and efficient blue light filtering capabilities.This study highlights the potential of high quantum yield CDs,which specifically absorb blue light,as foundational materials for developing light-blocking solutions against highenergy short-wavelength light.
文摘This work reports a soft chemistry approach for the synthesis of magnesium oxide nanoparticles(MgO)incorporated in a polyaniline(PANI)matrix to give PANI/MgO nanocomposite.Using spin coating method,three different percentages of MgO/PVC(1,2,and 3%in wt.%)were deposited on glass substrates.These films of PANI/MgO nanocomposite were characterized by X-ray diffraction(XRD),atomic force microscopy(AFM),and UV-visible spectroscopy.The results of the XRD pattern revealed the embedding of MgO nanoparticles in the PANI matrix with cubic phase,with the average size of nanoparticles varying from 35.12 to 59.55 nm.The AFM images displayed a significant change in the morphology of the PANI/MgO NPs composite films as MgO concentration was increased.The optical transmittance analysis revealed that at very low concentrations of MgO in PANI/MgO nanocomposite films,there is a high transparency,reaching close to 90%.However,this transmittance decreases significantly as the concentration of MgO increases.The photocatalytic activity of the nanocomposite film was then evaluated for the degradation of methylene blue(MB)dye under UV light irradiation.The results indicated a strong potential for PANI/MgO nanocomposite films in effectively degrading MB,supported by a proposed mechanism for the photocatalytic reaction.Compared with other composites such as PVC/MgO,PANI/MgO nanocomposite presented better MB degradation efficiency.
基金financially supported by the National Natural Science Foundation of China(Nos.52222202 and 51772310)Chinese Academy of Sciences Key Research Program of Frontier Sciences(No.QYZDY-SSWJSC031)Shanghai Pilot Program for Basic Research-Chinese Academy of Science,Shanghai Branch(No.JCYJ-SHFY-2021-001).
文摘To mitigate secondary electromagnetic pollution,there is an urgent need to develop absorption-dominant electromagnetic interference(EMI)shielding materials with low density,reduced thickness,lightweight construction,flexibility,exceptional mechanical strength,and superior electrothermal and photothermal properties,particularly for flexible and wearable electronics.In this regard,we designed an absorption-based composite film comprising carbon nanotubes(CNT)and α-Fe_(2)O_(3),featuring a CNT layer sandwiched between twoα-Fe_(2)O_(3)layers on the upper and lower surfaces.This composite film was fabricated through an electrodeposition process followed by a thermal annealing procedure to achieve enhanced EMI shielding performance along with improved electrothermal and photothermal properties.The strategically designed sandwich structure allows the rough surface of the upper α-Fe_(2)O_(3)layer to not only improve the impedance mismatch between free space and the composite film,facilitating the penetration of incident electromagnetic(EM)waves into the film and promoting increased EM absorption rather than reflection,but also to enhance electrical conductivity,thereby improving electron mobility and density.Consequently,the average total shielding effectiveness(SE)of the CNT/Fe_(16)-300 composite demonstrates remarkable EMI shielding effectiveness(EMI SE:56.8 dB).Furthermore,the alteration in the absorption-to-reflection ratio(A/R)signifies a transition in the EMI shielding mechanism from reflection(0.69 for the pristine CNT film)to absorption(1.86 for the CNT/Fe_(16)-300)with the incremental deposition of α-Fe_(2)O_(3)nanoparticles.This work presents a feasible manufacturing approach for developing composite films with a sandwich structure that exhibits absorption-dominant EMI shielding capabilities,contributing to advancements in thermal management and multifunctional electromagnetic shielding applications.
基金Project(gf200901002)supported by the Open Research Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang Hangkong University,China
文摘ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.
文摘A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of the composite films was studied in the conditions of the ambient air and N2 gas atmosphere by ball-on-disk tester.The results indicate that the composite films show dense and amorphous microstructure.The WCx and WSx compounds are found in amorphous diamond like carbon matrix in the top layers of W-S-C.A proper WSx content is beneficial for improving the adhesion of the composite films.In air atmosphere,the composite films with high C content have better wear resistance and the friction coefficients range from 0.15 to 0.25.In N2 condition,high WSx content is benefit for the wear resistance and the friction coefficients of the composite films range from 0.03 to 0.1.
基金Project(51005154) supported by the National Natural Science Foundation of ChinaProject(12CG11) supported by the Chenguang Program of Shanghai Municipal Education Commission,ChinaProject(201104271) supported by the China Postdoctoral Science Foundation Special Funded Project
文摘A specific revised HFCVD apparatus and a novel process combining HFCVD and polishing technique were presented to deposit the micro-and nano-crystalline multilayered ultra-smooth diamond（USCD） film on the interior-hole surface of WC-Co drawing dies with aperture ranging from d1.0 mm to 60 mm.Characterization results indicate that the surface roughness values（Ra） in the entry zone,drawing zone and bearing zone of as-fabricated USCD coated drawing die were measured as low as 25.7,23.3 and 25.5 nm,respectively.Furthermore,the friction properties of USCD films were examined in both dry sliding and water-lubricating conditions,and the results show that the USCD film presents much superior friction properties.Its friction coefficients against ball-bearing steel,copper and silicon nitride balls（d4 mm）,is always lower than that of microcrystalline diamond（MCD） or WC-Co sample,regardless of the lubricating condition.Meanwhile,it still presents competitive wear resistance with the MCD films.Finally,the working lifetime and performance of as-fabricated USCD coated drawing dies were examined under producing low-carbon steel pipes in dry-sliding and water-lubricating conditions.Under the water-lubricating drawing condition,its production significantly increases by about 20 times compared with the conventional WC-Co drawing dies.
文摘CoFe204/Pb（Zr0.53Ti0.47）O3 （CFO/PZT） magnetoelectric composite thin films of 2-2 type structure had been prepared onto Pt/Ti/SiO2/Si substrate by a sol-gel process and spin coat- ing technique. The structure of the prepared thin film is substrate/PZT/CFO/PZT/CFO. Two CFO ferromagnetic layers are separated from each other by a thin PZT layer. The upper CFO layer is magnetostatically coupled with the lower CFO layer. Subsequent scan- ning electron microscopy （SEM） investigations show that the prepared thin films exhibit good morphologies and compact structure, and cross-sectional micrographs clearly display a multilayered nanostructure of multilayered thin films. The composite thin films exhibit both good magnetic and ferroelectric properties. The spacing between ferromagnetic layers can be varied by adjusting the thickness of intermediate PZT layer. It is found that the strength of magnetostatic coupling has a great impact on magnetoelectric properties of composite thin films, i.e., the magnetoelectric voltage coefficient of composite thin film tends to increase with the decreasing of pacing between two neighboring CFO ferromagnetic layers as a result of magnetostatic coupling effect.
文摘The nonlinear optical properties of Al-doped nc-Si-SiO2 composite films have been investigated using the time-resolved four-wave mixing technique with a femtosecond laser. The off-resonant third-order nonlinear susceptibility is observed to be 1.0 × 10-10 esu at 800nm. The relaxation time of the optical nonlinearity in the films is as short as 60fs. The optical nonlinearity is enhanced due to the quantum confinement of electrons in Si nanocrystals embedded in the SiO2 films. The enhanced optical nonlinearity does not originate from Al dopant because there are no Al clusters in the films.
文摘The composite films, XW11O39n-/SiO2, (X refers to Si, Ge or P, respectively) were prepared by tetraethoxysilane (TEOS) hydrolysis sol-gel method via spin-coating technique. Formation of the composite films is due to strong chemical reaction of organic silanol group with the surface oxygen atoms of XW11O39n-, resulted in the saturation of the surface of the lacunary polyoxometalates (POMs). Therefore, the coordination structural model of the films was proposed. As for the films, retention of the primary Keggin structure was confirmed by UV-vis, FT-IR spectra and MAS NMR. The surface morphology of the films was characterized by SEM, indicating that the film surface is relatively uniform, and the layer thickness is in the range of 250~350 nm. Aqueous formic acid (FA) (0-20 mmol/L) was degraded into CO2 and H2O by irradiating the films in the near-UV area. The results show that all the films have photocatalytic activities and the degradation reaction follows Langmuir-Hinshelwood first order kinetics.
基金supported by the National Key Research and Development Program of China(No.2024YFB3212901)National Natural Science Foundation of China(12072189)the Medicine and Engineering Interdisciplinary Research Fund of Shanghai Jiao Tong University(No.YG2025ZD05)。
文摘Pipelines are extensively used in environments such as nuclear power plants,chemical factories,and medical devices to transport gases and liquids.These tubular environments often feature complex geometries,confined spaces,and millimeter-scale height restrictions,presenting significant challenges to conventional inspection methods.Here,we present an ultrasonic microrobot(weight,80 mg;dimensions,24 mm×7 mm;thickness,210μm)to realize agile and bidirectional navigation in narrow pipelines.The ultrathin structural design of the robot is achieved through a high-performance piezoelectric composite film microstructure based on MEMS technology.The robot exhibits various vibration modes when driven by ultrasonic frequency signals,its motion speed reaches81 cm s-1 at 54.8 k Hz,exceeding that of the fastest piezoelectric microrobots,and its forward and backward motion direction is controllable through frequency modulation,while the minimum driving voltage for initial movement can be as low as 3 VP-P.Additionally,the robot can effortlessly climb slopes up to 24.25°and carry loads more than 36 times its weight.The robot is capable of agile navigation through curved L-shaped pipes,pipes made of various materials(acrylic,stainless steel,and polyvinyl chloride),and even over water.To further demonstrate its inspection capabilities,a micro-endoscope camera is integrated into the robot,enabling real-time image capture inside glass pipes.
基金Financial support from the National Nature Science Foundation of China(No.:52373244)the Foundation of National Science and Technology Key Laboratory(No.:KZ571801)。
文摘Cross-band camouflage technology is a critical necessity,enabling personnel and equipment to evade detection across evolving surveillance systems,thereby enhancing survivability and mission success.Herein,this work develops a layer-structured composite system based on carbon nanotube(CNT)film comprising ionic liquid(IL)interlayer for infrared(IR)modulation and surface-engineered Cu_(2)O nanoparticles for visible camouflage.The CNT/IL/CNT architecture enables reversible IR emissivity switching(Δε≈0.55)through electrically driven ion intercalation/deintercalation within 2 s,while spray-coated Cu_(2)O nanoparticles(100~400 nm diameter)on the top CNT film layer generate rich structure colors with 90%IR transmittance.This spectral-decoupling design overcomes the traditional trade-off between color visibility and IR transmittance observed in pigment-based systems.Remarkably,due to physical interface coupling,the Cu_(2)O-coated layer-structured system maintains exceptional electrical conductivity,enabling simultaneous electromagnetic interference shielding and electrothermal energy conversion.The integrated system demonstrates long-term operational stability.By unifying visible-IR camouflage,electromagnetic protection,and energy management in a lightweight platform,this work provides an important paradigm for cross-band camouflage technologies.
基金Sponsored by Hi-Tech Research and Development Program of China (2003AA305120)
文摘The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.
基金financially supported by the National Natural Science Foundation of China(NSFC,No.51903213 and No.5217130190)the Science and Technology Planning Project of Sichuan Province(No.2020YFH0053)Central Government Guides the Local Science and Technology Development Special Funds to freely explore basic research projects(No.2021Szvup124)。
文摘In recent years,graphene-based composite films have been greatly developed in the field of electromagnetic shielding interference(EMI).However,it is still a huge challenge to prepare graphene-based composite films with excellent mechanical properties,conductivity and electromagnetic shielding properties.In this work,we adopted a facile and effective method by annealing the alkali-treated polyacrylonitrile(aPAN)nanofibers reinforced graphene oxide(GO)composite films at 2000°C to obtain graphene-carbon nanofibers composite films(GCFs).Microscopically,carbon nanofibers(CNFs)were intercalated into the graphene sheets,and microgasbags structure was formed during the heat treatment process.The special structure makes GCFs have superior tensile strength(10.4 MPa)at 5%strain.After repeated folding over1000 times,the films still demonstrate excellent structural integrity and flexibility performance.Interestingly,the graphene-based composite films with 10 wt%a PAN nanofibers exhibit an extremely low density of about 0.678 g/cm^(3)and excellent electrical conductivity of 1.72×10^(5)S/m.Further,an outstanding electromagnetic shielding effectiveness(SE)of 55–57 d B was achieved,and the corresponding value of the specific SE/thickness can reach 67,601–70,059 d B·cm^(2)/g,which is the highest among reported graphenebased shielding materials.The significant electromagnetic shielding performance is due to the synergistic enhancement effect brought by the excellent conductivity of carbon nanofibers and graphene,the formed effective conductive network and the microgasbags structure.Electromagnetism simulation further clarified that the underlying mechanism should be mainly attributed to the conduction loss and multiple reflections caused by the special structure of GCFs.This work will provide new solutions for low density,high flexibility and excellent electromagnetic shielding properties materials in the next generation of foldable and wearable electronics.
基金the National Nature Science Foundation of China (Nos. 50771046 and 20373016) the Natural Science Foundation of Guangdong Province (No. 05200534)the Key Projects of Guangdong Province and Guangzhou City, China (Nos. 2006A10704003 and 2006Z3-D2031)
文摘A tin film of 320 nm in thickness on Cu foil and its composite film with graphite of-50 nm in thickness on it were fabricated by magnetron sputtering. The surface morphology, composition, surface distributions of alloy elements, and lithium intercalation/de-intercalation behaviors of the fabricated films were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, electron probe microanalyzer （EPMA）, X-ray photoelectron spectroscopy （XPS）, inductively coupled plasma atomic emission spectrometry （ICP）, cyclic voltammetry （CV）, and galvanostatic charge/discharge （GC） measurements. It is found that the lithium intercalation/de-intercalation behavior of the Sn film can be significantly improved by its composite with graphite. With cycling, the discharge capacity of the Sn film without composite changes from 570 mAh/g of the 2nd cycle to 270 mAh/g of the 20th cycle, and its efficiency for the discharge and charge is between 90% and 95%. Nevertheless, the discharge capacity of the composite Sn/C film changes from 575 mAh/g of the 2nd cycle to 515 mAh/g of the 20th cycle, and its efficiency for the discharge and charge is between 95% and 100%. The performance improvement of tin by its composite with graphite is ascribed to the retardation of the bulk tin cracking from volume change during lithium intercalation and de-intercalation, which leads to the pulverization of tin.
文摘With rapid progressive application of TiO2 thin films, magnetron sputtering becomes a very interesting method to prepare such multi-functional thin films. This paper focuses on influences of various deposition processes and deposition rate on the structures and properties of TiO2 thin films. Anatase, rutile or amorphous TiO2 films with various crystalline structures and different photocatalytic, optical and electrical properties can be produced by varying sputtering gases, substrate temperature, annealing process, deposition rate and the characteristics of magnetron sputtering. This may in turn affect the functions of TiO2 films in many applications. Furthermore, TiO2-based composites films can overcome many limitations and improve the properties of TiO2 films.