By using sub-overquenching and annealing method which has a wide processing window, (Nd, Pr), ( Fe-CoZr)(94-x)B-6(x = 12, 10.5, 10, 9) bonded magnets were prepared and the effect of rare earths content on magnetic pro...By using sub-overquenching and annealing method which has a wide processing window, (Nd, Pr), ( Fe-CoZr)(94-x)B-6(x = 12, 10.5, 10, 9) bonded magnets were prepared and the effect of rare earths content on magnetic properties was investigated. Being spun at sub-ove.quenching speed the as-spun ribbons consist of amorphous phases mixed with fine crystallites. After crystallization under optimum annealing conditions and bonded with 3.25% (mass fraction) epoxy, the magnets obtained the optimum magnetic properties. The rare earths content directly determines the magnetic properties. With the reduction of rare earths content, B-r increases but H-ci and (BH)(max) decrease. x = 10 is the critical value for the magnetic proper-ties change. Below this value, Br increases slowly meanwhile H-ci and (BH)(max) decrease strongly because alloy contains extra fractions of soft magnetic phase which are not coupled with the hard magnetic phase.. This experimental result is consistent with the calculated results using the model of volume fraction of soft magnetic phase coupled completely suggested.展开更多
文摘By using sub-overquenching and annealing method which has a wide processing window, (Nd, Pr), ( Fe-CoZr)(94-x)B-6(x = 12, 10.5, 10, 9) bonded magnets were prepared and the effect of rare earths content on magnetic properties was investigated. Being spun at sub-ove.quenching speed the as-spun ribbons consist of amorphous phases mixed with fine crystallites. After crystallization under optimum annealing conditions and bonded with 3.25% (mass fraction) epoxy, the magnets obtained the optimum magnetic properties. The rare earths content directly determines the magnetic properties. With the reduction of rare earths content, B-r increases but H-ci and (BH)(max) decrease. x = 10 is the critical value for the magnetic proper-ties change. Below this value, Br increases slowly meanwhile H-ci and (BH)(max) decrease strongly because alloy contains extra fractions of soft magnetic phase which are not coupled with the hard magnetic phase.. This experimental result is consistent with the calculated results using the model of volume fraction of soft magnetic phase coupled completely suggested.