Sealing quality strongly affects heat pipe performance, but few studies focus on the process of heat pipe sealing. Cold welding sealing technology based on a stamping process is applied for heat pipe sealing. The bond...Sealing quality strongly affects heat pipe performance, but few studies focus on the process of heat pipe sealing. Cold welding sealing technology based on a stamping process is applied for heat pipe sealing. The bonding mechanism of the cold welding sealing process （CWSP） is investigated and compared with the experimental results obtained from the bonding interface analysis. An orthogonal experiment is conducted to observe the effects of various parameters, including the sealing gap, sealing length, sealing diameter, and sealing velocity on bonding strength. A method with the utilization of saturated vapor pressure inside a copper tube is proposed to evaluate bonding strength. A corresponding finite element model is developed to investigate the effects of sealing gap and sealing velocity on plastic deformation during the cold welding process. Effects of various parameters on the bonding strength are determined and it is found that the sealing gap is the most critical factor and that the sealing velocity contributes the least effect. The best parameter combination （AIB3CID3, with a 0.5 mm sealing gap, 6 mm sealing length, 3.8 mm sealing diameter, and 50 mm/s sealing velocity） is derived within the experimental parameters. Plastic deformation results derived from the finite element model are consistent with those from the experiment. The instruction for the CWSP of heat pipes and the design of sealing dies of heat pipes are provided.展开更多
The Authors of this Article have done research on the cracking resistance of cold welding surfacing electrodes for blast furnace valves by adjusting the basicity of slag component, decreasing the hydrogen content and ...The Authors of this Article have done research on the cracking resistance of cold welding surfacing electrodes for blast furnace valves by adjusting the basicity of slag component, decreasing the hydrogen content and improving microstructure. The DF 2 Cold Welding Surfacing Electrodes prove to possess the following characters: 1) Excellent cracking resistance for surfacing alloys at normal temperature. 2) Excellent cracking resistance for repair welding and rewelding. 3) Excellent machinability for surfacing alloying.展开更多
The common Au nanostructures(nanospheres,nanorods and nanosheets)were prepared by the seed growth method to explore the cold welding phenomenon of these non-single crystal nanostructures at room temperature.Systematic...The common Au nanostructures(nanospheres,nanorods and nanosheets)were prepared by the seed growth method to explore the cold welding phenomenon of these non-single crystal nanostructures at room temperature.Systematic studies show that the concentration of surfactant cetyltrimethylammonium bromide(CTAB)and drying conditions are important factors to determine the evolution and final configuration of nanostructures during welding.The key factor of cold welding is the concentration of surfactant as low as 0.3 mm/L,and the welding should be carried out under the condition of slow evaporation and sufficient relaxation time,rather than rapid drying process.At the same time,the structural evolution during the welding process of gold rod head and tail is simulated by combining the electronic microscope characterization and density functional theory,which reveals that the stability of the welding nanostructure is better than that of the dispersed nanostructure.In the slow evaporation process of Au nanostructures with the same crystal structure,the low surfactant attached to the surface of the nanoparticles increases the attraction between the nanoparticles,which makes the nanoparticles close to each other adhere due to the interaction,and improves the physical properties of the intersection due to the diffusion,epitaxy and surface relaxation of the metal surface atoms.The results provide a research basis for the physical property analysis of nanostructures and the construction of defect devices.展开更多
The quality of micro heat pipe(MHP) is strongly affected by sealing technology. Based on the analysis of requirements of sealing technology, a cold welding technology was presented to seal MHP. In the cold welding pro...The quality of micro heat pipe(MHP) is strongly affected by sealing technology. Based on the analysis of requirements of sealing technology, a cold welding technology was presented to seal MHP. In the cold welding process, compression force was used to flatten micro groove copper(MGC) tube. Then the bonding of MGC tube was reached because of intensively plastic deformation of MGC tube under pressure. It is found that the plastic deformation area of the cold welding of MGC tube can be divided into three sections. The deformation of micro grooves in each section was investigated; the influence of the dimensions of cylindrical heads on the weld joint shape and strength was studied; and a comparison between smooth copper tube and MGC tube was done. The results show that a groove compression stage exists in the cold welding of MGC tube besides a flattened stage and a melting stage.展开更多
Aluminum and silver strips were cold welded by rolling and a bimetallic strip was produced. To create cold weld between A1 and Ag, mating surfaces were specially prepared and various rolling thickness reductions were ...Aluminum and silver strips were cold welded by rolling and a bimetallic strip was produced. To create cold weld between A1 and Ag, mating surfaces were specially prepared and various rolling thickness reductions were applied. The minimum critical thickness reduction to begin cold weld was specified as 70% which equals 0.1630 critical rolling shape factors. The bimetallic strips were treated by diffusion annealing at 400 ~C and various annealing time. The A1/Ag interface of strips was observed by scanning electron microscope to investigate the formation of hard and brittle probable phases. The effect of anneal time on diffusion distance and phase transformation was also analysed by EDS analysis and line scan. A diffusion region along the interface in the Ag side was observed and its width increased with prolonging annealing time. Some 8 phases were detected close to the interface after anneal treating for 3 h and 8 phase was thicker and more continuous by increasing annealing time. The microhardness measurement showed that in spite of formation of 8 phase due to diffusion annealing, the interface hardness was reduced.展开更多
In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc wel...In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc welding （FCAW） process were used making welds using austenitic stainless steel （ASS） and low hydrogen ferritic steel （LHF） consumables. The diffusible hydrogen levels in the weld metal of the ASS and LHF consumables were determined by mercury method. Residual stresses were evaluated using X-ray stress analyzer and implant test was carried out to study the cold cracking of the welds. Results indicate that ASS welds offer a greater resistance to cold cracking of armour grade Q＆T steel welds.展开更多
The technology of cold pressure welding was adopted to achieve the bonding of Al/Cu(limited soluble and forming compounds), Ag/Ni (hardly mutual soluble), and the relative state of interface was tested by HREM. The re...The technology of cold pressure welding was adopted to achieve the bonding of Al/Cu(limited soluble and forming compounds), Ag/Ni (hardly mutual soluble), and the relative state of interface was tested by HREM. The results indicate that stable interface is always corresponding to the low interfacial energy value; the stable interface is not coherent but partly-coherent because of the twisting of grain boundary caused by pressure, meanwhile existing dislocation. Namely, the interfacial match and other states under the condition of cold pressure welding are different from the situation that under the condition of thermal action. Moreover, theoretical analyses and calculation on the base of thermodynamics, crystallogeny, solid physics etc, were discussed.展开更多
The interfacial bonding of Ag-Cu (they are limited soluble) formed by the technology of cold pressure welding was discussed from the point of metallurgic view in this paper. Meanwhile, tensile test and microscopic tes...The interfacial bonding of Ag-Cu (they are limited soluble) formed by the technology of cold pressure welding was discussed from the point of metallurgic view in this paper. Meanwhile, tensile test and microscopic test were adopted for studying the state of interfacial bonding, suggesting that the joint of Ag-Cu has not only strong welding joint but also atomic diffusion on the interface. For Ag-Cu, the interaction of dislocation caused by plastic deformation will cause the strain and the vibration of microconstructer defects, accompanied by emitting energy. The energy increases the atomic action and the amplitude of atomic vibration, and the result is that the atom can diffuse to several lattice parameters deep from interface to inner metals. Therefore, under the condition of chemical potential gradient, the special technique, cold pressure welding rather than basic requirements of diffusion should be taken into account. During the cold pressure welding, plastic deformation plays an important role for it causes the metals′ displacement, crystal defects, further activates the surface atoms. Finally, the fracture of atomic bonding leads to the atomic exchange and diffusion between the new metals′ surfaces.In other words the metals Ag,Cu can achieve solidate bonding by cold pressure welding accompanied by the atomic diffusion. Moreover, theoretical analysis and calculation on the basis of thermodynamics, crystallogy, so- lid physics,etc, have been applied to calculate the amount of atomic diffusion, which has further proved the testing results that joint Ag-Cu has strong bonding strength through the mechanism of atomic diffusion.展开更多
Carbides in a series of cold-welding weld metals were studied by means of SEM, TEM and EPMA, and the forming mechanism of carbide was proposed according to their distribution and morphology. Due to their different car...Carbides in a series of cold-welding weld metals were studied by means of SEM, TEM and EPMA, and the forming mechanism of carbide was proposed according to their distribution and morphology. Due to their different carbide-forming tendency, Nb and Ti could combine with C to form particulate carbide in liquid weld metai and depleted the carbon content in matrix, while V induced the carbide precipitated along grain boundary. But too much Nb or Ti alone resulted in coarse carbide and poor strengthened matrix. When suitabie amount of Nb, Ti and V coexisted in weld metai, both uniformly distributed particulate carbide and well strengthened matrix could be achieved. It was proposed that the carbide nucleated on the oxlde which dispersed in liquid weld metai, and then grew into multi-layer complex carbide particies by epitaxial grovvth. At different sites, carbide particies may present as different morphologies.展开更多
With the means of electron backscattered diffraction(EBSD),mechanical properties test and digital eddy current metal conductivity,the single crystal copper cold-welded joint was tested and analyzed,the structure chang...With the means of electron backscattered diffraction(EBSD),mechanical properties test and digital eddy current metal conductivity,the single crystal copper cold-welded joint was tested and analyzed,the structure change of cold-welded joint and the effect of heat treating on the structure and property of cold-welded joint were discussed.The results show that:The deformation area of the single crystal copper cold welded joint is broken,the crystalline grain at the interface of the joint is refined,and the single crystal structure is still maintained in the base metal area.The hardness of the deformation area increases greatly,the conductivity of the joint does not change much,and the tensile strength of the joint reaches about 70%of that of the base metal.At the interface of the heat treating joint,the single crystal structure of the deformation area and the base metal area are destroyed,and the grains grow up at the interface and the orientation is different.The hardness of the joint interface is much lower than that of the non-heat treating joint,the electrical conductivity of the joint is good,and the tensile strength of the joint is higher than that of the base metal.展开更多
Aluminum killed cold rolled steel used for automobiles was welded in this paper by using CO 2 laser with wavelength 10.6μm.The experiment shows that high quality of welding can be realized at welding speed of 4 500m...Aluminum killed cold rolled steel used for automobiles was welded in this paper by using CO 2 laser with wavelength 10.6μm.The experiment shows that high quality of welding can be realized at welding speed of 4 500mm/min by optimizing the parameters.The strength and hardness of laser welded joints for aluminum killed cold rolled steel increased compared to those of the base metal while the formability decreased.Forming limit diagram of joint material indicated that the laser weld seam should avoid the maximum deformation area of automobile parts during the designing period for the position of weld seam.展开更多
To improve the corrosion resistance of friction stir welded(FSW)joints,in situ shot-peening-assisted cold spray coating was applied to the surface of FSW joints.The microstructure and corrosion behavior of the coating...To improve the corrosion resistance of friction stir welded(FSW)joints,in situ shot-peening-assisted cold spray coating was applied to the surface of FSW joints.The microstructure and corrosion behavior of the coatings were investigated.The results showed that a dense coating was obtained by cold spraying technology.Moreover,the use of in situ shot-peeningassisted technology significantly reduced the porosity of the coating,which has a positive impact on the microstructure and the mechanical performance.Exfoliation corrosion tests showed that the coating aff ected positively on the corrosion resistance.On the coated surface,the craters caused by shot-peening particles were corroded in the form of exfoliation corrosion,while the exposed particles were corroded in the form of intercrystalline corrosion.This work provides a new approach to the corrosion protection of FSW joints.展开更多
The area of combination actually is a kind of interfacial phenomena that exist on the surface or thin film. The properties of interface have important effect on the whole welded joint, even decide directly the interfa...The area of combination actually is a kind of interfacial phenomena that exist on the surface or thin film. The properties of interface have important effect on the whole welded joint, even decide directly the interfacial bonding strength. The bonding strength of metals in cold pressure welding such as Ag Ni (they are hardly mutual soluble) and Ag Cu(they are limited soluble) are discussed in this paper. The results of the tensile test suggest that two kinds of welded joints have enough strength to satisfy with the demand for being used. Moreover, thermodynamics, crystal logy, physics and metal electronic microscopic analysis etc are adopted to further calculate the bonding strength. The results of test and theoretical analyses prove that Ag Ni, Ag Cu, especially, for Ag Ni can form strong welded joint which is higher than that of the relative soft base metals in cold pressure welding.展开更多
The interfacial bonding state for the different metals Ag, Ni without metallurgic are actions was studied. The tensile test of the joint concludes that the bonding strength of Ag,Ni in cold pressure welding is strong ...The interfacial bonding state for the different metals Ag, Ni without metallurgic are actions was studied. The tensile test of the joint concludes that the bonding strength of Ag,Ni in cold pressure welding is strong enough to satisfy the demand of application, while the value of bonding strength is larger than that of Ag base. The conclusions further signify that the metals(hardly being mutual soluble) can be welded, and supply extremely important references to the further study either on test or theory for the weldability of different metals. The theoretical analysis and calculations of the bonding strength were made on the base of thermodynamics, crystallography, solid physics etc. Moreover, by means of microscopic test and analysis, especially drawing support from the research of Al Pb, this strong bonding mainly depends on the mechanical bonding power and metal atomic linkage, but not on the atomic diffusion.展开更多
采用冷金属过渡焊接(Cold metal transfer welding, CMT)对4 mm厚的410不锈钢进行焊接,焊后对CMT接头进行搅拌摩擦加工(Friction stir processing, FSP)。采用光学显微镜、扫描电镜、万能试验机和显微硬度仪等研究了CMT接头和FSP后接头...采用冷金属过渡焊接(Cold metal transfer welding, CMT)对4 mm厚的410不锈钢进行焊接,焊后对CMT接头进行搅拌摩擦加工(Friction stir processing, FSP)。采用光学显微镜、扫描电镜、万能试验机和显微硬度仪等研究了CMT接头和FSP后接头的表面形貌、微观结构和力学性能。结果表明:410不锈钢CMT接头经过FSP处理后,接头焊缝表面成型良好,内部无孔洞等缺陷,焊缝由大尺寸的柱状晶转变为细小的等轴晶,平均晶粒尺寸由155.07μm减小到17.78μm,大角度晶界比例从41.3%显著增加到67.19%;FSP接头焊核区的平均硬度达到300 HV0.2,抗拉强度为575.48 MPa,相比CMT焊接接头(514.27 MPa)提升了12%,伸长率从10%降至6%。展开更多
基金Supported by National Natural Science Foundation of China(Grant Nos.51175186,51675185)Guangdong Provincial Natural Science Foundation of China(Grant No.S2013020012757)EU project PIIF-GA-2012-332304(Grant No.ESR332304)
文摘Sealing quality strongly affects heat pipe performance, but few studies focus on the process of heat pipe sealing. Cold welding sealing technology based on a stamping process is applied for heat pipe sealing. The bonding mechanism of the cold welding sealing process （CWSP） is investigated and compared with the experimental results obtained from the bonding interface analysis. An orthogonal experiment is conducted to observe the effects of various parameters, including the sealing gap, sealing length, sealing diameter, and sealing velocity on bonding strength. A method with the utilization of saturated vapor pressure inside a copper tube is proposed to evaluate bonding strength. A corresponding finite element model is developed to investigate the effects of sealing gap and sealing velocity on plastic deformation during the cold welding process. Effects of various parameters on the bonding strength are determined and it is found that the sealing gap is the most critical factor and that the sealing velocity contributes the least effect. The best parameter combination （AIB3CID3, with a 0.5 mm sealing gap, 6 mm sealing length, 3.8 mm sealing diameter, and 50 mm/s sealing velocity） is derived within the experimental parameters. Plastic deformation results derived from the finite element model are consistent with those from the experiment. The instruction for the CWSP of heat pipes and the design of sealing dies of heat pipes are provided.
文摘The Authors of this Article have done research on the cracking resistance of cold welding surfacing electrodes for blast furnace valves by adjusting the basicity of slag component, decreasing the hydrogen content and improving microstructure. The DF 2 Cold Welding Surfacing Electrodes prove to possess the following characters: 1) Excellent cracking resistance for surfacing alloys at normal temperature. 2) Excellent cracking resistance for repair welding and rewelding. 3) Excellent machinability for surfacing alloying.
基金supported by the National Natural Science Foundations of China (Nos. 11774171,11874220,21805137)the Open Funds of Key Laboratory for Intelligent Nano Materials and Devices of the Ministry of Education (Nos. INMD-2019M02, INMD2020M03)+1 种基金the Scientific Foundation of Nanjing Institute of Technology(No. CKJB201708)the Fundamental Research Funds for the Central Universities(No.NS2017047) provided by Nanjing University of Aeronautics and Astronautics
文摘The common Au nanostructures(nanospheres,nanorods and nanosheets)were prepared by the seed growth method to explore the cold welding phenomenon of these non-single crystal nanostructures at room temperature.Systematic studies show that the concentration of surfactant cetyltrimethylammonium bromide(CTAB)and drying conditions are important factors to determine the evolution and final configuration of nanostructures during welding.The key factor of cold welding is the concentration of surfactant as low as 0.3 mm/L,and the welding should be carried out under the condition of slow evaporation and sufficient relaxation time,rather than rapid drying process.At the same time,the structural evolution during the welding process of gold rod head and tail is simulated by combining the electronic microscope characterization and density functional theory,which reveals that the stability of the welding nanostructure is better than that of the dispersed nanostructure.In the slow evaporation process of Au nanostructures with the same crystal structure,the low surfactant attached to the surface of the nanoparticles increases the attraction between the nanoparticles,which makes the nanoparticles close to each other adhere due to the interaction,and improves the physical properties of the intersection due to the diffusion,epitaxy and surface relaxation of the metal surface atoms.The results provide a research basis for the physical property analysis of nanostructures and the construction of defect devices.
基金Projects(50436010, 50705031) supported by the National Natural Science Foundation of ChinaProjects(07118064, 8151064101000058) supported by the Natural Science Foundation of Guangdong Province, China
文摘The quality of micro heat pipe(MHP) is strongly affected by sealing technology. Based on the analysis of requirements of sealing technology, a cold welding technology was presented to seal MHP. In the cold welding process, compression force was used to flatten micro groove copper(MGC) tube. Then the bonding of MGC tube was reached because of intensively plastic deformation of MGC tube under pressure. It is found that the plastic deformation area of the cold welding of MGC tube can be divided into three sections. The deformation of micro grooves in each section was investigated; the influence of the dimensions of cylindrical heads on the weld joint shape and strength was studied; and a comparison between smooth copper tube and MGC tube was done. The results show that a groove compression stage exists in the cold welding of MGC tube besides a flattened stage and a melting stage.
文摘Aluminum and silver strips were cold welded by rolling and a bimetallic strip was produced. To create cold weld between A1 and Ag, mating surfaces were specially prepared and various rolling thickness reductions were applied. The minimum critical thickness reduction to begin cold weld was specified as 70% which equals 0.1630 critical rolling shape factors. The bimetallic strips were treated by diffusion annealing at 400 ~C and various annealing time. The A1/Ag interface of strips was observed by scanning electron microscope to investigate the formation of hard and brittle probable phases. The effect of anneal time on diffusion distance and phase transformation was also analysed by EDS analysis and line scan. A diffusion region along the interface in the Ag side was observed and its width increased with prolonging annealing time. Some 8 phases were detected close to the interface after anneal treating for 3 h and 8 phase was thicker and more continuous by increasing annealing time. The microhardness measurement showed that in spite of formation of 8 phase due to diffusion annealing, the interface hardness was reduced.
基金Armament Research Board (ARMREB),New Delhi for funding this projectwork (Project No MAA/03/41)
文摘In this investigation, an attempt has been made to study the influence of welding consumables on the factors that influence cold cracking of armour grade quenched and tempered （Q＆.T） steel welds. Flux cored arc welding （FCAW） process were used making welds using austenitic stainless steel （ASS） and low hydrogen ferritic steel （LHF） consumables. The diffusible hydrogen levels in the weld metal of the ASS and LHF consumables were determined by mercury method. Residual stresses were evaluated using X-ray stress analyzer and implant test was carried out to study the cold cracking of the welds. Results indicate that ASS welds offer a greater resistance to cold cracking of armour grade Q＆T steel welds.
文摘The technology of cold pressure welding was adopted to achieve the bonding of Al/Cu(limited soluble and forming compounds), Ag/Ni (hardly mutual soluble), and the relative state of interface was tested by HREM. The results indicate that stable interface is always corresponding to the low interfacial energy value; the stable interface is not coherent but partly-coherent because of the twisting of grain boundary caused by pressure, meanwhile existing dislocation. Namely, the interfacial match and other states under the condition of cold pressure welding are different from the situation that under the condition of thermal action. Moreover, theoretical analyses and calculation on the base of thermodynamics, crystallogeny, solid physics etc, were discussed.
文摘The interfacial bonding of Ag-Cu (they are limited soluble) formed by the technology of cold pressure welding was discussed from the point of metallurgic view in this paper. Meanwhile, tensile test and microscopic test were adopted for studying the state of interfacial bonding, suggesting that the joint of Ag-Cu has not only strong welding joint but also atomic diffusion on the interface. For Ag-Cu, the interaction of dislocation caused by plastic deformation will cause the strain and the vibration of microconstructer defects, accompanied by emitting energy. The energy increases the atomic action and the amplitude of atomic vibration, and the result is that the atom can diffuse to several lattice parameters deep from interface to inner metals. Therefore, under the condition of chemical potential gradient, the special technique, cold pressure welding rather than basic requirements of diffusion should be taken into account. During the cold pressure welding, plastic deformation plays an important role for it causes the metals′ displacement, crystal defects, further activates the surface atoms. Finally, the fracture of atomic bonding leads to the atomic exchange and diffusion between the new metals′ surfaces.In other words the metals Ag,Cu can achieve solidate bonding by cold pressure welding accompanied by the atomic diffusion. Moreover, theoretical analysis and calculation on the basis of thermodynamics, crystallogy, so- lid physics,etc, have been applied to calculate the amount of atomic diffusion, which has further proved the testing results that joint Ag-Cu has strong bonding strength through the mechanism of atomic diffusion.
基金This work was supported by the Natural Science Foundation of Shandong Province under grant No.Y99F01.
文摘Carbides in a series of cold-welding weld metals were studied by means of SEM, TEM and EPMA, and the forming mechanism of carbide was proposed according to their distribution and morphology. Due to their different carbide-forming tendency, Nb and Ti could combine with C to form particulate carbide in liquid weld metai and depleted the carbon content in matrix, while V induced the carbide precipitated along grain boundary. But too much Nb or Ti alone resulted in coarse carbide and poor strengthened matrix. When suitabie amount of Nb, Ti and V coexisted in weld metai, both uniformly distributed particulate carbide and well strengthened matrix could be achieved. It was proposed that the carbide nucleated on the oxlde which dispersed in liquid weld metai, and then grew into multi-layer complex carbide particies by epitaxial grovvth. At different sites, carbide particies may present as different morphologies.
文摘With the means of electron backscattered diffraction(EBSD),mechanical properties test and digital eddy current metal conductivity,the single crystal copper cold-welded joint was tested and analyzed,the structure change of cold-welded joint and the effect of heat treating on the structure and property of cold-welded joint were discussed.The results show that:The deformation area of the single crystal copper cold welded joint is broken,the crystalline grain at the interface of the joint is refined,and the single crystal structure is still maintained in the base metal area.The hardness of the deformation area increases greatly,the conductivity of the joint does not change much,and the tensile strength of the joint reaches about 70%of that of the base metal.At the interface of the heat treating joint,the single crystal structure of the deformation area and the base metal area are destroyed,and the grains grow up at the interface and the orientation is different.The hardness of the joint interface is much lower than that of the non-heat treating joint,the electrical conductivity of the joint is good,and the tensile strength of the joint is higher than that of the base metal.
文摘Aluminum killed cold rolled steel used for automobiles was welded in this paper by using CO 2 laser with wavelength 10.6μm.The experiment shows that high quality of welding can be realized at welding speed of 4 500mm/min by optimizing the parameters.The strength and hardness of laser welded joints for aluminum killed cold rolled steel increased compared to those of the base metal while the formability decreased.Forming limit diagram of joint material indicated that the laser weld seam should avoid the maximum deformation area of automobile parts during the designing period for the position of weld seam.
基金financially supported by the National Natural Science Foundation of China(No.51774047)the Great Wall Scholars Program of Beijing(No.CIT&TCD20170309).
文摘To improve the corrosion resistance of friction stir welded(FSW)joints,in situ shot-peening-assisted cold spray coating was applied to the surface of FSW joints.The microstructure and corrosion behavior of the coatings were investigated.The results showed that a dense coating was obtained by cold spraying technology.Moreover,the use of in situ shot-peeningassisted technology significantly reduced the porosity of the coating,which has a positive impact on the microstructure and the mechanical performance.Exfoliation corrosion tests showed that the coating aff ected positively on the corrosion resistance.On the coated surface,the craters caused by shot-peening particles were corroded in the form of exfoliation corrosion,while the exposed particles were corroded in the form of intercrystalline corrosion.This work provides a new approach to the corrosion protection of FSW joints.
文摘The area of combination actually is a kind of interfacial phenomena that exist on the surface or thin film. The properties of interface have important effect on the whole welded joint, even decide directly the interfacial bonding strength. The bonding strength of metals in cold pressure welding such as Ag Ni (they are hardly mutual soluble) and Ag Cu(they are limited soluble) are discussed in this paper. The results of the tensile test suggest that two kinds of welded joints have enough strength to satisfy with the demand for being used. Moreover, thermodynamics, crystal logy, physics and metal electronic microscopic analysis etc are adopted to further calculate the bonding strength. The results of test and theoretical analyses prove that Ag Ni, Ag Cu, especially, for Ag Ni can form strong welded joint which is higher than that of the relative soft base metals in cold pressure welding.
文摘The interfacial bonding state for the different metals Ag, Ni without metallurgic are actions was studied. The tensile test of the joint concludes that the bonding strength of Ag,Ni in cold pressure welding is strong enough to satisfy the demand of application, while the value of bonding strength is larger than that of Ag base. The conclusions further signify that the metals(hardly being mutual soluble) can be welded, and supply extremely important references to the further study either on test or theory for the weldability of different metals. The theoretical analysis and calculations of the bonding strength were made on the base of thermodynamics, crystallography, solid physics etc. Moreover, by means of microscopic test and analysis, especially drawing support from the research of Al Pb, this strong bonding mainly depends on the mechanical bonding power and metal atomic linkage, but not on the atomic diffusion.