To improve the oxidation resistance of carbon/carbon （C/C） composites in air at high temperatures, a SiC- MoSi2/ZrO2-MoSi2 coating was prepared on the surface of C/C composites by pack cementation and slurry method....To improve the oxidation resistance of carbon/carbon （C/C） composites in air at high temperatures, a SiC- MoSi2/ZrO2-MoSi2 coating was prepared on the surface of C/C composites by pack cementation and slurry method. The microstructures and phase compositions of the coated C/C composites were analyzed by scanning electron microscopy and X-ray diffraction, respectively. The result shows that the SiC-MoSi2/ZrO2-MoSi2 coating is dense and crack-free with a thickness of 250-300 μm. The preparation and the high temperature oxidation property of the coated composites were investigated. The as-received coating has excellent oxidation protection ability and can protect C/C composites from oxidation for 260 h at 1773 K in air. The excellent anti-oxidation performance of the coating is considered to come from the formation of ZrSiO4, which improves the stability of the coating at high temperatures.展开更多
ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （...ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.展开更多
CeO2-TiO2 catalysts prepared by different methods were investigated for deep oxidation of 1,2-dichloroethane(DCE),as a typical representative of the chlorinated volatile organic compounds(CVOCs).Characterization analy...CeO2-TiO2 catalysts prepared by different methods were investigated for deep oxidation of 1,2-dichloroethane(DCE),as a typical representative of the chlorinated volatile organic compounds(CVOCs).Characterization analysis reveals that CeO2-TiO2 catalysts prepared by sol-gel and coprecipitation methods exhibit higher specific area,CeO2 and TiO2 particles are highly dispersed into each other and the reducibility and mobility of active oxygen species are obviously promoted due to the strong interaction between the two catalysts CeO2 and TiO2,resulting in higher catalytic activity for DCE oxidation to and less chlorinated byproduct.The high calcination temperature would lead to the formation of a new monoclinic phase Ce0.3Ti0.7O2 and sintering,which is the main reason for the catalytic activity for DCE oxidation markedly decreases.展开更多
The oxidation kinetics of O'-SiAlON-ZrO2 composite ceramics in the temperature range of 1373-1773K has been studied. The oxidation experiments with powder and plates of O'-SiAlON-ZrO2 composite ceramics in air...The oxidation kinetics of O'-SiAlON-ZrO2 composite ceramics in the temperature range of 1373-1773K has been studied. The oxidation experiments with powder and plates of O'-SiAlON-ZrO2 composite ceramics in air have been carried out. The overall activation energy of oxidation reaction is 263.69 kJ/mol. The products and structures of O'-SiAlON-ZrO2 oxidation layer have been analysed by XRD (X-ray diffraction), SEM (scanning electron microscope) and AFM (atomic force microscope).展开更多
The research of poly(ethylene oxide)(PEO)-based solid composite electrolyte with high ionic conductivity and excellent interfacial stability is the key to the development of all-solid-state lithium-ion batteries(ASSLI...The research of poly(ethylene oxide)(PEO)-based solid composite electrolyte with high ionic conductivity and excellent interfacial stability is the key to the development of all-solid-state lithium-ion batteries(ASSLIBs). Herein, uniform nanorod structured CeO_(2) fillers were controllably synthesized by electrospinning, which were subsequently filled into PEO polymer to prepare CeO_(2)/PEO solid composite electrolyte. The addition of CeO_(2) nanorods can reduce both the glass transition temperature and the melting point of PEO polymer, and also interact with PEO and lithium bis(trifluoromethanesulphonyl)imide(LITFSI) by Lewis acid—base reaction. Therefore, the solid composite electrolyte exhibits a high ionic conductivity of 4.52 × 10^(-4)S/cm, a wide electrochemical stability window of about 4.8 V, and a good interfacial stability with Li at 55℃. Moreover, the LiFePO_4/Li ASSLIB divulges the discharging specific capacity of 165, 162, 156 and 146 mA,h/g at 0.2, 0.5, 1 and 2 C, respectively, and achieves the capacity retention of 90.3% after 150 cycles at 0.5 C. Consequently, one dimensional CeO_(2) nanorods can be considered as an alternative filler for polymeric solid electrolyte.展开更多
To improve the oxidation resistance of carbon/carbon composites,ZrB2-MoSi2/SiC coating on the carbon/carbon substrate was prepared.The inner coating of SiC was prepared by pack cementation and the outer coating of ZrB...To improve the oxidation resistance of carbon/carbon composites,ZrB2-MoSi2/SiC coating on the carbon/carbon substrate was prepared.The inner coating of SiC was prepared by pack cementation and the outer coating of ZrB2-MoSi2 was prepared by slurry painting.The phase compositions and microstructures of the coating were characterized by XRD and SEM,respectively.The preparation and the high temperature oxidation property of the coated composites were investigated.The results show that the outer coating of carbon/carbon composites is composed of ZrB2,MoSi2 and SiC phases.The mass losses of the ZrB2-MoSi2/SiC coated samples with SiC nano-whiskers after 30 h and 10 h of oxidation at 1 273 K and 1 773 K were,respectively,5.3% and 3.0%.The ZrB2-MoSi2/SiC coated samples exhibit self-sealing performance and good oxidation resistance at high temperature.展开更多
CO2-TPD was demonstrated an effective way to investigate the phase formation during pyrolysis for the preparation of composite oxides using metal-organic molecules as precursors.Based on the CO2-TPD results, it was f...CO2-TPD was demonstrated an effective way to investigate the phase formation during pyrolysis for the preparation of composite oxides using metal-organic molecules as precursors.Based on the CO2-TPD results, it was found that calcination condition had deep effect on the carbonate formation and the minimum firing temperature to acquire pure phase composite oxide.An optimized calcination schedule was then developed.展开更多
The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. Acco...The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. According to the results, a CeO2-TiO2solid solution is formed when the mole ratio of cerium to titanium n（Ce）：n（Ti） is 5：5 or greater, and the most suitable n（Ce）：n（Ti） isdetermined as 7：3, over which the conversion rate of SO2 and the yield of sulfur at 500℃ reach 93% and 99%, respectively.According to the activity testing curve, Ce0.7Ti0.3O2 （n（Ce）：n（Ti）=7：3） without any pretreatment can be gradually activated by reagentgas after about 10 min, and reaches a steady activation status 60 min later. The XPS results of Ce0.7Ti0.3O2 after different time ofSO2＋CO reaction show that CeO2 is the active component that offers the redox couple Ce4＋/Ce3＋ and the labile oxygen vacancies, andTiO2 only functions as a catalyst structure stabilizer during the catalytic reaction process. After 48 h of catalytic reaction at 500℃,Ce0.7Ti0.3O2 still maintains a stable structure without being vulcanized, demonstrating its good anti-sulfur poisoning performance.展开更多
Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and coppe...Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.展开更多
C/SiC/MoSi2-SiC-Si oxidation protective multilayer coating for carbon/carbon （C/C） composites was prepared by pack cementation and slurry method. The microstructure, element distribution and phase composition of the...C/SiC/MoSi2-SiC-Si oxidation protective multilayer coating for carbon/carbon （C/C） composites was prepared by pack cementation and slurry method. The microstructure, element distribution and phase composition of the as-received coating were analyzed by scanning electron microscopy （SEM）, energy dispersive X-ray spectroscopy （EDS） and X-ray diffraction （XRD）. The results show that the multilayer coating was composed of MoSi2, SiC and Si. It could effectively protect C/C composites against oxidation for 200 h with the mass loss of 3.25% at 1873 K in static air. The mass loss of the coated C/C composites results from the volatilization of SiO2 and the formation of cracks and bubble holes in the coating.展开更多
Ni-La2O3/CeO2 composite films were prepared by electrodeposition from a nickel sulfate bath containing certain content of micrometer and nanometer La2O3/CeO2 particles. The effect of La2O3 or CeO2 particle size on the...Ni-La2O3/CeO2 composite films were prepared by electrodeposition from a nickel sulfate bath containing certain content of micrometer and nanometer La2O3/CeO2 particles. The effect of La2O3 or CeO2 particle size on the oxidation resistance of the electrodeposited Ni-La2O3/CeO2 composites in air at 1000 °C was studied. The results indicate that, compared with the electrodeposited Ni-film, Ni-La2O3/CeO2 composites exhibit a superior oxidation resistance due to the codeposited La2O3 or CeO2 particles blocking the outward diffusion of nickel. Moreover, compared with nanoparticles, La2O3 or CeO2 microparticles have stronger effect because La2O3 or CeO2 microparticles also act as a diffusion barrier layer at the onset of oxidation.展开更多
Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employ...Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employed to investigate the oxidation resistance of the composite coatings. The results revealed that the applied Al2O3/Au nano-laminated composite coatings improved the oxidation and spallation resistance of the stainless steel substrate significantly. The mechanism accounting for oxidation resistance was related with the suppression of inward oxygen diffusion and selective oxidation of Cr in the substrate. The mechanism accounting for spallation resistance was attributed to the relaxation of thermal stress by the nano-laminated structure.展开更多
Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO...Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.展开更多
The Ru（bpy）3^2＋ doped graphene oxide-silica composite film（Ru/GO-SiCF） was synthesized by one pot hydrolysis and condensation of tetraethylorthosilicate（TEOS） in the water-alcohol solution of graphene oxide and...The Ru（bpy）3^2＋ doped graphene oxide-silica composite film（Ru/GO-SiCF） was synthesized by one pot hydrolysis and condensation of tetraethylorthosilicate（TEOS） in the water-alcohol solution of graphene oxide and Ru（bpy）3^2＋ at room temperature.The prepared Ru/GO-SiCF modified glassy carbon electrode（GCE） showed excellent electrochemiluminescence（ECL） behavior for the determination of tripropylamine（TPA） with high sensitivity and good stability.We expected this simple and novel material will find further application in construction of other targets sensors.展开更多
The La2O3/Fe2O3-CeO2 composite oxide catalysts were prepared by coprecipitation method, sol-gel method and hydrothermal method. The effect of preparation methods on structure morphology and photocatalytic properties o...The La2O3/Fe2O3-CeO2 composite oxide catalysts were prepared by coprecipitation method, sol-gel method and hydrothermal method. The effect of preparation methods on structure morphology and photocatalytic properties of La2O3/Fe2O3-CeO2 samples was investigated. The results show that the cubic CeO2 structure can be obtained at 600℃. The rod-shaped sample prepared by coprecipitation method, displays the highest crystalline and the strongest diffraction peak intensity. The spherical sample is acquired from sol-gel method, while the small granular sample prepared by hydrothermal method tends to aggregate. The maximum specific surface area of the sample prepared by coprecipitation method is 76.21 m2/g, the minimum specific area of the sample from sol-gel method is 32.66 m2/g and the maximum pore size is 13.84 nm, while the minimum pore volume and pore size of the sample by hydrothermal method are 0.038 cm3/g and 3.95 nm respectively. The band gap energy of catalyst samples is in the following order: sample-CP < sample-SG < sample-HT. The sample obtained by coprecipitation method has the best catalytic degradation performance for methylene blue. Under the excitation of visible light, the degradation rate was 99.58% at 50 minutes, which was higher than those of sol-gel method and hydrothermal method by 5.58% and 9.54% respectively. The catalytic degradation reaction is a first-order kinetic model: ln (c0/ct) = kt + qe. The maximum k-value of the sample degradation process obtained by coprecipitation method is 0.074 min-1.展开更多
A composites of (Mo<sub>0.9</sub>Cr<sub>0.1</sub>)Si<sub>2</sub> + 15vol% ZrO<sub>2</sub> was prepared with powder metallurgy and Pressure- Less Sintering (PLS) method, ...A composites of (Mo<sub>0.9</sub>Cr<sub>0.1</sub>)Si<sub>2</sub> + 15vol% ZrO<sub>2</sub> was prepared with powder metallurgy and Pressure- Less Sintering (PLS) method, aiming at applications of high temperature structural materials. Mechanical properties of the composites were assessed with hardness, indentation fracture toughness K<sub>c</sub> and K<sub>IC</sub> tested using SEVNB, flexure strength at room temperature and 1200?C, and isothermal oxidation at 1400?C. The results showed that the native silica oxide and molybdenum-oxides on the silicide feedstock surface were significantly reduced in terms of Cr-alloying. (Mo<sub>0.9</sub>Cr<sub>0.1</sub>)Si<sub>2</sub> and its composite also exhibited improved sinterability and grain growth, owing to the presence of (Cr, Mo)<sub>5</sub>Si<sub>3</sub> at grain boundaries. Fracture toughness of the composite was increased by a factor of 1.6 to that in the monolithic silicide. Mechanical property of the composite at high temperature was not affected by Cr addition. However, the high temperature oxidation resistance was greatly improved in the (Mo<sub>0.9</sub>Cr<sub>0.1</sub>)Si<sub>2</sub> + 15vol% ZrO<sub>2</sub> compared with the non Cr-alloyed counterpart. The Cr-alloying effects on the microstructure, fracture behaviour, and high temperature oxidation resistance were discussed.展开更多
The interfacial interaction existing in the Ni ZrO 2 composite plating has been investigated. The experimental results show that no new phases were formed in the interfacial regions between matrix Ni and ZrO 2 part...The interfacial interaction existing in the Ni ZrO 2 composite plating has been investigated. The experimental results show that no new phases were formed in the interfacial regions between matrix Ni and ZrO 2 particles, but an orbital interaction through the mutual overlap of the d orbits does exist in the interfacial regions between Ni atoms and Zr 3+ ions.展开更多
Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process...Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process of β-Sialon. The rate of oxidation process is controlled by chemicalreaction at the initial stage and then by diffusion. The apparent activation energies and appar-ent rate constants at different temperatures are determined by treating TG data of the overallprocess.展开更多
To improve the uniformity and the content of HfBin Hf B-Si-based ceramic coating and alleviate the damage of substrate,and then enhance the high-temperature(1700°C)oxidation and cyclic ablation resistances of car...To improve the uniformity and the content of HfBin Hf B-Si-based ceramic coating and alleviate the damage of substrate,and then enhance the high-temperature(1700°C)oxidation and cyclic ablation resistances of carbon/carbon composites,a close-knit double layer HfB_(2)-SiC/SiC coatings with a mosaic structure and high content of HfBwere prepared by a novel dipping-carbonization assisted pack cementation methods(DPC–HS/S).In contrast,a HfB_(2)-SiC/SiC coatings were also fabricated by pack cementation(PC–HS/S).Results revealed that the oxidation and ablation protective performances of the DPC–HS/S coatings were superior to those of PC–HS/S coatings.After 30 thermal cycles between 1500°C and room temperature,the mass gain of the coated sample was 0.78%,and the mass loss was 1.65%after oxidation at 1700°C for 156 h.Moreover,under an oxyacetylene torch ablation for 180 s(3 cycles),the linear ablation rate of the DPC–HS/S coated specimen was 1.62μm/s,which was much lower than that of PC–HS/S coated specimen(3.08μm/s).展开更多
Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxida...Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxidation test was performed at 1050℃ for 5, 50, 100,150, 200, and 400 h. The microstructure and phase composition of powders and coatings were characterized by scanning electron microscopy and X-ray diffraction, respectively. The bonding strength of the coatings was also evaluated. The results proved that with the increase in the percentage of nanoparticles(from 2wt% to 6wt%), the amount of porosity(from 1vol% to 4.7vol%), unmelted particles, and roughness of the coatings(from 4.8 to 8.8 μm) increased, and the bonding strength decreased from 71 to 48 MPa. The thicknesses of the thermally grown oxide layer of pure and composite coatings(2wt%, 4wt%, and 6wt%) after 400 h oxidation were measured as 6.5, 5.5, 7.6, and 8.1 μm, respectively.The CoNiCrAlY–2wt% Al_(2)O_(3)coating showed the highest oxidation resistance due to the diffusion barrier effect of well-dispersed nanoparticles. The CoNiCrAlY–6wt% Al_(2)O_(3)coating had the lowest oxidation resistance due to its rough surface morphology and porous microstructure.展开更多
基金Projects(51221001,51222207)supported by the National Natural Science Foundation of ChinaProject(090677)supported by the Program for New Century Excellent Talents in University of ChinaProject(B08040)supported by Program of Introducing Talents of Discipline to Universities,China
文摘To improve the oxidation resistance of carbon/carbon （C/C） composites in air at high temperatures, a SiC- MoSi2/ZrO2-MoSi2 coating was prepared on the surface of C/C composites by pack cementation and slurry method. The microstructures and phase compositions of the coated C/C composites were analyzed by scanning electron microscopy and X-ray diffraction, respectively. The result shows that the SiC-MoSi2/ZrO2-MoSi2 coating is dense and crack-free with a thickness of 250-300 μm. The preparation and the high temperature oxidation property of the coated composites were investigated. The as-received coating has excellent oxidation protection ability and can protect C/C composites from oxidation for 260 h at 1773 K in air. The excellent anti-oxidation performance of the coating is considered to come from the formation of ZrSiO4, which improves the stability of the coating at high temperatures.
基金Project(gf200901002)supported by the Open Research Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang Hangkong University,China
文摘ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.
基金Project supported by the National Natural Science Foundation of China(21477109)National Key Research and Development Program of China(2016YFC0204300)。
文摘CeO2-TiO2 catalysts prepared by different methods were investigated for deep oxidation of 1,2-dichloroethane(DCE),as a typical representative of the chlorinated volatile organic compounds(CVOCs).Characterization analysis reveals that CeO2-TiO2 catalysts prepared by sol-gel and coprecipitation methods exhibit higher specific area,CeO2 and TiO2 particles are highly dispersed into each other and the reducibility and mobility of active oxygen species are obviously promoted due to the strong interaction between the two catalysts CeO2 and TiO2,resulting in higher catalytic activity for DCE oxidation to and less chlorinated byproduct.The high calcination temperature would lead to the formation of a new monoclinic phase Ce0.3Ti0.7O2 and sintering,which is the main reason for the catalytic activity for DCE oxidation markedly decreases.
文摘The oxidation kinetics of O'-SiAlON-ZrO2 composite ceramics in the temperature range of 1373-1773K has been studied. The oxidation experiments with powder and plates of O'-SiAlON-ZrO2 composite ceramics in air have been carried out. The overall activation energy of oxidation reaction is 263.69 kJ/mol. The products and structures of O'-SiAlON-ZrO2 oxidation layer have been analysed by XRD (X-ray diffraction), SEM (scanning electron microscope) and AFM (atomic force microscope).
基金Project supported by the Education Department of Henan Province(22A170017)the Science and Technology Department of Henan Province(232102240011)+1 种基金Henan Institute of Science and Technology(2016034)National College Students'Innovation and Entrepreneurship Training Program(202211071012)。
文摘The research of poly(ethylene oxide)(PEO)-based solid composite electrolyte with high ionic conductivity and excellent interfacial stability is the key to the development of all-solid-state lithium-ion batteries(ASSLIBs). Herein, uniform nanorod structured CeO_(2) fillers were controllably synthesized by electrospinning, which were subsequently filled into PEO polymer to prepare CeO_(2)/PEO solid composite electrolyte. The addition of CeO_(2) nanorods can reduce both the glass transition temperature and the melting point of PEO polymer, and also interact with PEO and lithium bis(trifluoromethanesulphonyl)imide(LITFSI) by Lewis acid—base reaction. Therefore, the solid composite electrolyte exhibits a high ionic conductivity of 4.52 × 10^(-4)S/cm, a wide electrochemical stability window of about 4.8 V, and a good interfacial stability with Li at 55℃. Moreover, the LiFePO_4/Li ASSLIB divulges the discharging specific capacity of 165, 162, 156 and 146 mA,h/g at 0.2, 0.5, 1 and 2 C, respectively, and achieves the capacity retention of 90.3% after 150 cycles at 0.5 C. Consequently, one dimensional CeO_(2) nanorods can be considered as an alternative filler for polymeric solid electrolyte.
基金Project(50721003) supported by the Innovation Community Foundation of National Natural Science of ChinaProject(2011CB605805) supported by the National Basic Research Program of China
文摘To improve the oxidation resistance of carbon/carbon composites,ZrB2-MoSi2/SiC coating on the carbon/carbon substrate was prepared.The inner coating of SiC was prepared by pack cementation and the outer coating of ZrB2-MoSi2 was prepared by slurry painting.The phase compositions and microstructures of the coating were characterized by XRD and SEM,respectively.The preparation and the high temperature oxidation property of the coated composites were investigated.The results show that the outer coating of carbon/carbon composites is composed of ZrB2,MoSi2 and SiC phases.The mass losses of the ZrB2-MoSi2/SiC coated samples with SiC nano-whiskers after 30 h and 10 h of oxidation at 1 273 K and 1 773 K were,respectively,5.3% and 3.0%.The ZrB2-MoSi2/SiC coated samples exhibit self-sealing performance and good oxidation resistance at high temperature.
文摘CO2-TPD was demonstrated an effective way to investigate the phase formation during pyrolysis for the preparation of composite oxides using metal-organic molecules as precursors.Based on the CO2-TPD results, it was found that calcination condition had deep effect on the carbonate formation and the minimum firing temperature to acquire pure phase composite oxide.An optimized calcination schedule was then developed.
文摘The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. According to the results, a CeO2-TiO2solid solution is formed when the mole ratio of cerium to titanium n（Ce）：n（Ti） is 5：5 or greater, and the most suitable n（Ce）：n（Ti） isdetermined as 7：3, over which the conversion rate of SO2 and the yield of sulfur at 500℃ reach 93% and 99%, respectively.According to the activity testing curve, Ce0.7Ti0.3O2 （n（Ce）：n（Ti）=7：3） without any pretreatment can be gradually activated by reagentgas after about 10 min, and reaches a steady activation status 60 min later. The XPS results of Ce0.7Ti0.3O2 after different time ofSO2＋CO reaction show that CeO2 is the active component that offers the redox couple Ce4＋/Ce3＋ and the labile oxygen vacancies, andTiO2 only functions as a catalyst structure stabilizer during the catalytic reaction process. After 48 h of catalytic reaction at 500℃,Ce0.7Ti0.3O2 still maintains a stable structure without being vulcanized, demonstrating its good anti-sulfur poisoning performance.
基金National Natural Science Foundation of China (50432020)Henan Innovation Project for University Prominent Re- search Talents (2007KYCX008)+3 种基金Henan Education Department Science and Technology Project (2007430004)Henan Plan Project for College Youth Backbone TeacherHenan University of Science and Technology Major Pre-research Foundation (2005ZD003)Henan University of Science and Technology Personnel Scientific Research Foundation (of023)
文摘Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.
基金Projects(51272213,51221001)supported by the National Natural Science Foundation of ChinaProject(73-QP-2010)supported by the Research Fund of the State Key Laboratory of Solidification Processing(NWPU)Project(B08040)supported by Program of Introducing Talents of Discipline to Universities,China
文摘C/SiC/MoSi2-SiC-Si oxidation protective multilayer coating for carbon/carbon （C/C） composites was prepared by pack cementation and slurry method. The microstructure, element distribution and phase composition of the as-received coating were analyzed by scanning electron microscopy （SEM）, energy dispersive X-ray spectroscopy （EDS） and X-ray diffraction （XRD）. The results show that the multilayer coating was composed of MoSi2, SiC and Si. It could effectively protect C/C composites against oxidation for 200 h with the mass loss of 3.25% at 1873 K in static air. The mass loss of the coated C/C composites results from the volatilization of SiO2 and the formation of cracks and bubble holes in the coating.
基金Project(GC13A113)supported by the Technology Research and Development Program of Heilongjiang Provincial Science and Technology DepartmentProject(12511469)supported by Heilongjiang Provincial Science and Technology Department
文摘Ni-La2O3/CeO2 composite films were prepared by electrodeposition from a nickel sulfate bath containing certain content of micrometer and nanometer La2O3/CeO2 particles. The effect of La2O3 or CeO2 particle size on the oxidation resistance of the electrodeposited Ni-La2O3/CeO2 composites in air at 1000 °C was studied. The results indicate that, compared with the electrodeposited Ni-film, Ni-La2O3/CeO2 composites exhibit a superior oxidation resistance due to the codeposited La2O3 or CeO2 particles blocking the outward diffusion of nickel. Moreover, compared with nanoparticles, La2O3 or CeO2 microparticles have stronger effect because La2O3 or CeO2 microparticles also act as a diffusion barrier layer at the onset of oxidation.
基金Project (50771021) supported by the National Natural Science Foundation of China
文摘Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employed to investigate the oxidation resistance of the composite coatings. The results revealed that the applied Al2O3/Au nano-laminated composite coatings improved the oxidation and spallation resistance of the stainless steel substrate significantly. The mechanism accounting for oxidation resistance was related with the suppression of inward oxygen diffusion and selective oxidation of Cr in the substrate. The mechanism accounting for spallation resistance was attributed to the relaxation of thermal stress by the nano-laminated structure.
文摘Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.
基金supported in part by the Key Project of Natural Science Foundation of China(Nos.21175039,21322509, 21305035,21190044,and 21221003)Research Fund for the Doctoral Program of Higher Education of China(No. 20110161110016)+1 种基金the project supported by Hunan Provincial Natural Science FoundationHunan Provincial Science and Technology Plan of China(No.2012TT1003)
文摘The Ru（bpy）3^2＋ doped graphene oxide-silica composite film（Ru/GO-SiCF） was synthesized by one pot hydrolysis and condensation of tetraethylorthosilicate（TEOS） in the water-alcohol solution of graphene oxide and Ru（bpy）3^2＋ at room temperature.The prepared Ru/GO-SiCF modified glassy carbon electrode（GCE） showed excellent electrochemiluminescence（ECL） behavior for the determination of tripropylamine（TPA） with high sensitivity and good stability.We expected this simple and novel material will find further application in construction of other targets sensors.
文摘The La2O3/Fe2O3-CeO2 composite oxide catalysts were prepared by coprecipitation method, sol-gel method and hydrothermal method. The effect of preparation methods on structure morphology and photocatalytic properties of La2O3/Fe2O3-CeO2 samples was investigated. The results show that the cubic CeO2 structure can be obtained at 600℃. The rod-shaped sample prepared by coprecipitation method, displays the highest crystalline and the strongest diffraction peak intensity. The spherical sample is acquired from sol-gel method, while the small granular sample prepared by hydrothermal method tends to aggregate. The maximum specific surface area of the sample prepared by coprecipitation method is 76.21 m2/g, the minimum specific area of the sample from sol-gel method is 32.66 m2/g and the maximum pore size is 13.84 nm, while the minimum pore volume and pore size of the sample by hydrothermal method are 0.038 cm3/g and 3.95 nm respectively. The band gap energy of catalyst samples is in the following order: sample-CP < sample-SG < sample-HT. The sample obtained by coprecipitation method has the best catalytic degradation performance for methylene blue. Under the excitation of visible light, the degradation rate was 99.58% at 50 minutes, which was higher than those of sol-gel method and hydrothermal method by 5.58% and 9.54% respectively. The catalytic degradation reaction is a first-order kinetic model: ln (c0/ct) = kt + qe. The maximum k-value of the sample degradation process obtained by coprecipitation method is 0.074 min-1.
文摘A composites of (Mo<sub>0.9</sub>Cr<sub>0.1</sub>)Si<sub>2</sub> + 15vol% ZrO<sub>2</sub> was prepared with powder metallurgy and Pressure- Less Sintering (PLS) method, aiming at applications of high temperature structural materials. Mechanical properties of the composites were assessed with hardness, indentation fracture toughness K<sub>c</sub> and K<sub>IC</sub> tested using SEVNB, flexure strength at room temperature and 1200?C, and isothermal oxidation at 1400?C. The results showed that the native silica oxide and molybdenum-oxides on the silicide feedstock surface were significantly reduced in terms of Cr-alloying. (Mo<sub>0.9</sub>Cr<sub>0.1</sub>)Si<sub>2</sub> and its composite also exhibited improved sinterability and grain growth, owing to the presence of (Cr, Mo)<sub>5</sub>Si<sub>3</sub> at grain boundaries. Fracture toughness of the composite was increased by a factor of 1.6 to that in the monolithic silicide. Mechanical property of the composite at high temperature was not affected by Cr addition. However, the high temperature oxidation resistance was greatly improved in the (Mo<sub>0.9</sub>Cr<sub>0.1</sub>)Si<sub>2</sub> + 15vol% ZrO<sub>2</sub> compared with the non Cr-alloyed counterpart. The Cr-alloying effects on the microstructure, fracture behaviour, and high temperature oxidation resistance were discussed.
文摘The interfacial interaction existing in the Ni ZrO 2 composite plating has been investigated. The experimental results show that no new phases were formed in the interfacial regions between matrix Ni and ZrO 2 particles, but an orbital interaction through the mutual overlap of the d orbits does exist in the interfacial regions between Ni atoms and Zr 3+ ions.
文摘Non-isothermal kinetic research has been carried out on oxidation behavior of β-Sialon in diphaseβ-Sialon/Al_2O_3 composite at high temperatures. A kinetic formula is established for non-isothermal oxidation process of β-Sialon. The rate of oxidation process is controlled by chemicalreaction at the initial stage and then by diffusion. The apparent activation energies and appar-ent rate constants at different temperatures are determined by treating TG data of the overallprocess.
基金financially supported by the National Natural Science Foundation of China(Nos.51872239,52061135102,52002321)the Creative Research Foundation of Science and Technology on Thermostructural Composite Materials Laboratory(No.5050200015)+1 种基金the Fundamental Research Funds for the Central Universities(No.G2020KY05125)the Xi’an Association for Science and Technology"Young Talent Support Project"(No.095920211338)。
文摘To improve the uniformity and the content of HfBin Hf B-Si-based ceramic coating and alleviate the damage of substrate,and then enhance the high-temperature(1700°C)oxidation and cyclic ablation resistances of carbon/carbon composites,a close-knit double layer HfB_(2)-SiC/SiC coatings with a mosaic structure and high content of HfBwere prepared by a novel dipping-carbonization assisted pack cementation methods(DPC–HS/S).In contrast,a HfB_(2)-SiC/SiC coatings were also fabricated by pack cementation(PC–HS/S).Results revealed that the oxidation and ablation protective performances of the DPC–HS/S coatings were superior to those of PC–HS/S coatings.After 30 thermal cycles between 1500°C and room temperature,the mass gain of the coated sample was 0.78%,and the mass loss was 1.65%after oxidation at 1700°C for 156 h.Moreover,under an oxyacetylene torch ablation for 180 s(3 cycles),the linear ablation rate of the DPC–HS/S coated specimen was 1.62μm/s,which was much lower than that of PC–HS/S coated specimen(3.08μm/s).
文摘Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxidation test was performed at 1050℃ for 5, 50, 100,150, 200, and 400 h. The microstructure and phase composition of powders and coatings were characterized by scanning electron microscopy and X-ray diffraction, respectively. The bonding strength of the coatings was also evaluated. The results proved that with the increase in the percentage of nanoparticles(from 2wt% to 6wt%), the amount of porosity(from 1vol% to 4.7vol%), unmelted particles, and roughness of the coatings(from 4.8 to 8.8 μm) increased, and the bonding strength decreased from 71 to 48 MPa. The thicknesses of the thermally grown oxide layer of pure and composite coatings(2wt%, 4wt%, and 6wt%) after 400 h oxidation were measured as 6.5, 5.5, 7.6, and 8.1 μm, respectively.The CoNiCrAlY–2wt% Al_(2)O_(3)coating showed the highest oxidation resistance due to the diffusion barrier effect of well-dispersed nanoparticles. The CoNiCrAlY–6wt% Al_(2)O_(3)coating had the lowest oxidation resistance due to its rough surface morphology and porous microstructure.