Metallosupramolecular coordination polyelectrolyte, Fe（II）-metalloviologen（FEN）, was prepared by the reaction of Fe（II） with a novel bisterpyridine ligand. As active components, FENs could be assembled into elec...Metallosupramolecular coordination polyelectrolyte, Fe（II）-metalloviologen（FEN）, was prepared by the reaction of Fe（II） with a novel bisterpyridine ligand. As active components, FENs could be assembled into electrochromic multilayer films with negative charged polystyrene sulfate（PSS） by the sequential deposition layer-by-layer technique. Numerous analytical instruments, such as UV-Vis spectroscopy, atomic force microscopy（AFM）, tunneling electron microscopy（TEM）, zeta-potential measurement and electrochemical measurement have been utilized to characterize their morphology, optical and electrochromic properties. It has been observed that as-prepared films exhibited multi-colour changes by triggering with different potentials. However, the low optical contrast of multilayer films would limit their further applications. In order to overcome this problem, semiconductor TiO2 nanoparticles（TiO2） were incorporated into FEN multilayers by layer-by-layer approach. By carefully optimizing the film structure, as-resulted hybrid films containing FEN, TiO2 and PSS exhibited high optical contrast, suitable response time and long-term stability. Such hybrid films should be promising candidates to meet the requirements for developing flexible displays and electrochromic devices.展开更多
In order to improve the corrosion resistance and biocompatibility of NiTi surgical alloy, TiO2 and TiO2-SiO2 thin films were prepared by sol-gel method. The surface characteristics of the film, which include surface c...In order to improve the corrosion resistance and biocompatibility of NiTi surgical alloy, TiO2 and TiO2-SiO2 thin films were prepared by sol-gel method. The surface characteristics of the film, which include surface composition, microstructure and surface morphology, were studied by X-ray diffraction (XRD), atomic force microscopy (AFM) and X-ray photoelectron spectra (XPS), respectively. A scratching test was used to assess the interface adhesive strength between the film and substrate. The corrosion resistance of NiTi alloy coated with oxide films were studied by anodic polarization curves measurement in biological solution. Additionally, a preliminary study of the in vitro bioactivity of the films was conducted. The results indicated that TiO2 and TiO2-SiO2 (Ti/Si=4:1) films have higher electrochemical corrosion resistance and can be used as protective layers on NiTi alloy. In addition, TiO2-SiO2 composite films have better bioactivity than TiO2 film.展开更多
Post-processing can effectively improve the resistance to laser damage in multilayer films used in a high power laser system.In this work,HfO_(2)/SiO_(2)multilayer films are prepared by e-beam evaporation and thenβ-r...Post-processing can effectively improve the resistance to laser damage in multilayer films used in a high power laser system.In this work,HfO_(2)/SiO_(2)multilayer films are prepared by e-beam evaporation and thenβ-ray irradiation is employed as the post-processing method.The particle irradiation affects the laser induced damage threshold(LIDT),which includes defects,surface roughness,packing density and residual stress.The residual stress that is relaxed during irradiation changes from compressive stress into tensile stress.Our results indicate that appropriate tensile stress can improve LIDT remarkably.In view of the fact that LIDT rises from 8 J/cm^(2)to 12 J/cm^(2),i.e.,50%increase,after the film has been irradiated by 2.2×10^(13)/cm^(2)β-ray,the particle irradiation can be used as a controllable and desirable postprocessing method to improve the resistance to laser induced damage.展开更多
In order to prolong the service life of piston rings of heavy vehicle engine and decrease the friction and wear of piston rings and cylinder liner,CrMoN/MoS_2 multilayer films were deposited on the surface of rings by...In order to prolong the service life of piston rings of heavy vehicle engine and decrease the friction and wear of piston rings and cylinder liner,CrMoN/MoS_2 multilayer films were deposited on the surface of rings by magnetron sputtering and low temperature ion sulfuration.FESEM equipped with EDX was adopted to analyze the compositions and morphologies of surface,cross-section,and wear scars of the multilayer films.The nano-hardness and Young＇s modulus of the films were measured by a nano tester.Tribologicalproperties of the films were tested by an SRV~174;4 wear tester.The experimentalresults indicate that the structures of the multilayer films are dense and compact.The films possess nano hardness value of approximately 26.7 GPa and superior ability of plastic deformation resistance.The multilayer films can activate solid lubricating,and possess an excellent antifriction and wear resistance under the conditions of heavy load,high frequency,high temperature,and dynamic load.展开更多
The Sb6 Te4/VO2 multilayer thin films are prepared by magnetron sputtering and the potential application in phase change memory is investigated in detail. Compared with Sb6 Te4, Sb6 Te4/VO2 multilayer composite thin f...The Sb6 Te4/VO2 multilayer thin films are prepared by magnetron sputtering and the potential application in phase change memory is investigated in detail. Compared with Sb6 Te4, Sb6 Te4/VO2 multilayer composite thin films have higher phase change temperature and crystallization resistance, indicating better thermal stability and less power consumption. Also, Sb6 Te4/VO2 has a broader energy band of 1.58 eV and better data retention （125℃ for 103/）. The crystallization is suppressed by the multilayer interfaces in Sbf Te4/VO2 thin film with a smaller rms surface roughness for Sbf Te4/VO2 than monolayer Sb4Te6. The picosecond laser technology is applied to study the phase change speed. A short crystallization time of 5.21 ns is realized for the Sb6Te4 （2nm）/VO2 （8nm） thin film. The Sb6 Te4/VO2 multilayer thin film is a potential and competitive phase change material for its good thermal stability and fast phase change speed.展开更多
TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system.The crystalline structures,morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-r...TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system.The crystalline structures,morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-ray diffraction（XRD）,atomic force microscopy（AFM） and ultraviolet spectrophotometer,respectively.The results indicated that working pressure was the key deposition parameter in？uencing the TiO2 film phase composition at room temperature,which directly affected its photocatalytic activity.With increasing working pressure,the target self-bias decreases monotonously.Therefore,low temperature TiO2 phase（anatase） could be deposited with high working pressure.The anatase TiO2 films deposited with 1.4 Pa working pressure displayed the highest photocatalytic activity by the decomposition of Methyl Orange solution,which the degradation rate reached the maximum（35%） after irradiation by ultraviolet light for 1 h.展开更多
Zn-doped TiO2 (Zn?TiO2) thin films were prepared by the sol?gel method on titanium substrates with heat treatment at different temperatures. The effects of heat treatment temperatures and Zn doping on the structure, p...Zn-doped TiO2 (Zn?TiO2) thin films were prepared by the sol?gel method on titanium substrates with heat treatment at different temperatures. The effects of heat treatment temperatures and Zn doping on the structure, photocathodic protection and photoelectrochemical properties of TiO2 thin films were investigated. It is indicated that the photoelectrical performance of the Zn?TiO2 films is enhanced with the addition of Zn element compared with the pure-TiO2 film and the largest decline by 897 mV in the electrode potential is achieved under 300 °C heat treatment. SEM?EDS analyses show that Zn element is unevenly distributed in Zn?TiO2 films; XRD patterns reveal that the grain size of Zn?TiO2 is smaller than that of pure-TiO2; FTIR results indicate that Zn - O bond forms on Zn?TiO2 surface. Ultraviolet visible absorption spectra prove that Zn?TiO2 shifts to visible light region.Mott?Shottky curves show that the flat-band potential of Zn?TiO2 is more negative and charge carrier density is bigger than that ofpure-TiO2, implying that under the synergy of the width of the space-charge layer, carrier density and flat-band potential, Zn?TiO2 with 300 °C heat treatment displays the best photocathodic protection performance.展开更多
With rapid progressive application of TiO2 thin films, magnetron sputtering becomes a very interesting method to prepare such multi-functional thin films. This paper focuses on influences of various deposition process...With rapid progressive application of TiO2 thin films, magnetron sputtering becomes a very interesting method to prepare such multi-functional thin films. This paper focuses on influences of various deposition processes and deposition rate on the structures and properties of TiO2 thin films. Anatase, rutile or amorphous TiO2 films with various crystalline structures and different photocatalytic, optical and electrical properties can be produced by varying sputtering gases, substrate temperature, annealing process, deposition rate and the characteristics of magnetron sputtering. This may in turn affect the functions of TiO2 films in many applications. Furthermore, TiO2-based composites films can overcome many limitations and improve the properties of TiO2 films.展开更多
Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XR...Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, ultraviolet- visible spectroscopy （UV-Vis） and photoluminescence spectroscopy （PL）. The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange （MO） aqueous solution under visible light irradiation. The results indicate that the Cu2O/TiO2/Pt composite films are made up of three layers which are Pt layer, anatase-TiO2 layer and Cu2O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu2O/TiO2/Pt three-layer film is much higher than that of the Cu2O/TiO2 double-layer film. Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombination, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.展开更多
Anatase TiO2 sol was synthesized under mild conditions （75℃ and ambient pressure） by hydrolysis of titaniumn-butoxide in abundant acidic aqueous solution and subsequent reflux to enhance crystallization. At room te...Anatase TiO2 sol was synthesized under mild conditions （75℃ and ambient pressure） by hydrolysis of titaniumn-butoxide in abundant acidic aqueous solution and subsequent reflux to enhance crystallization. At room temperature and in ambient atmosphere, crystalline TiO2 thin films were deposited on polymethylmethacrylate （PMMA）, SiO2-coated PMMA and SiO2-coated silicone rubber substrates from the as-prepared TiO2 sol by a dip-coating process. SiO2 layers prior to TiO2 thin films on polymer substrates could not only protect the substrates from the photocatalytic decomposition of the TiO2 thin films but also enhance the adhesion of the TiO2 thin films to the substrates. Field-emission type scanning electron microscope （FE-SEM） investigations revealed that the average particle sizes of the nanoparticles composing the TiO2 thin films were about 35-47 nm. The TiO2 thin films exhibited high photocatalytic activities in the degradation of reactive brilliant red dye X-3B in aqueous solution under aerated conditions. The preparation process of photocatalytic TiO2 thin films on the polymer substrates was quite simple and a low temperature route.展开更多
Three thicknesses of TiO2 films, 174, 195, and 229 nm, were deposited onto quartz substrates by sol–gel spin coating method. The as-deposited thin films were characterized by nano-crystallite with different sizes (19...Three thicknesses of TiO2 films, 174, 195, and 229 nm, were deposited onto quartz substrates by sol–gel spin coating method. The as-deposited thin films were characterized by nano-crystallite with different sizes (19–46 nm) and relatively high porous structure. Optical constants were determined and showed the lowest refractive index of 1.66 for the as-prepared films that ever reported till now. Obtained results were discussed through current theoretical ideas.展开更多
Ag TiO 2 thin films were prepared on glasses.The morphology and structure of Ag TiO 2 films were investigated by XRD, SEM and FT IR.The photocatalytic and hydrophilic properties of Ag TiO 2 thin films were also...Ag TiO 2 thin films were prepared on glasses.The morphology and structure of Ag TiO 2 films were investigated by XRD, SEM and FT IR.The photocatalytic and hydrophilic properties of Ag TiO 2 thin films were also evaluated by examining photocatalytic degradation dichlorophos under sunlight illumination and the change of contact angle respectively.The research results show that the Ag TiO 2 thin film is mainly composed of 20-100nm Ag and TiO 2 particles.The Ag TiO 2 thin films possess a super hydrophilic ability and higher photocatalytic activity than that of pure TiO 2 thin film.展开更多
Pb-doped TiO2 photocatalytic thin films were prepared on a soda-lime glass substrate via sol-gel method using TiO2 sol solution containing lead and characterized by X-ray photoelectron spectroscopy (XPS). The results ...Pb-doped TiO2 photocatalytic thin films were prepared on a soda-lime glass substrate via sol-gel method using TiO2 sol solution containing lead and characterized by X-ray photoelectron spectroscopy (XPS). The results showed that besides oxides of Ti(IV) there is a certain amount of oxides of To(?) and Ti(?) and Pb exists in the forms of PbTiO3 and PbO. The photocatalytic activity of the Pb-doped TiO2 films was evaluated by the photocatalytic decolorization of aqueous methyl orange and photocatalytic mechanism mas also analyzed.展开更多
TiO2-SiO2 thin films have been prepared on slide glass substrates by sol-gel method, and the effect of SiO2 additive on photo-generated hydrophilicity of TiO2 thin film was investigated by measuring the contact angle ...TiO2-SiO2 thin films have been prepared on slide glass substrates by sol-gel method, and the effect of SiO2 additive on photo-generated hydrophilicity of TiO2 thin film was investigated by measuring the contact angle of water, the microstructure, the transmittance, the photocatalytic activity and the specific surface area . The results showed that 10mol% of SiO2 additive was the most effective for decreasing contact angle of water. The SiO2 additive of less than 30mol% has a suppressive effect on the crystal growth of anatase in calcinations, resulting in a large surface area. Consequently, the super-hydrophilicity was improved.展开更多
The microstructure properties of the sol-gel derived TiO2 films were studied by the atomic force microscopy (AFM). The films were prepared by dip coating process. The optical properties of the films were explained on ...The microstructure properties of the sol-gel derived TiO2 films were studied by the atomic force microscopy (AFM). The films were prepared by dip coating process. The optical properties of the films were explained on the basis of the microstructure of the films.展开更多
Preparation of TiO<sub>2</sub> thin films by MOCVD method is presented in this paper. A MOCVD system has been designed and built. A wide range of processing conditions are investigated to deposit TiO<su...Preparation of TiO<sub>2</sub> thin films by MOCVD method is presented in this paper. A MOCVD system has been designed and built. A wide range of processing conditions are investigated to deposit TiO<sub>2</sub> films on Si wafers starting from metal-organic precursor tetrabutyl titanate. Activation energy of the film formation （E） is obtained to be 23.6 kJ/mol. Structure of films is pure anatase when deposit temperatures are low, rutile forms at 700℃. The films also exhibit preferred crystallographic orientations which strongly depend on deposit conditions. Refractive index increases with increasing of film thickness and decreasing of deposit temperature.展开更多
The transparent anatase TiO 2 nanometer thin films were prepared by the sol-gel method on soda-lime glass.X-ray diffraction,thermal analysis and UV-visible spectrophotometer were used to analyze the formation of the ...The transparent anatase TiO 2 nanometer thin films were prepared by the sol-gel method on soda-lime glass.X-ray diffraction,thermal analysis and UV-visible spectrophotometer were used to analyze the formation of the phases.Only increasing the heat-treatment time,the average grain size has no obvious change.The mechanism of grain growth in TiO 2 thin film is probably as follows:the grain of coating will become grain core later;TiO 2 sol constantly deposited on the surface of TiO 2 grain and formed membrane with increasing of coating cycle times;TiO 2 grain in the film grow steadily.展开更多
TiO2 is a promising photocatalyst. However, the low photocatalytic efficiency calls for the modification of TiO2. Metal- and nonmetal-doping of TiO2 have been proved to be effective ways to enhance photocatalytic prop...TiO2 is a promising photocatalyst. However, the low photocatalytic efficiency calls for the modification of TiO2. Metal- and nonmetal-doping of TiO2 have been proved to be effective ways to enhance photocatalytic properties. This review provides a deep insight into the understanding of the metal- and nonmetal-doped TiO2 photocatalysts. This article begins with the introduction of the crystal structures of TiO2 and applications of TiO2 materials. We then reviewed the doped-TiO2 system in two categories： （1） metal-doped TiO2 photocatalysts system, and （2） nonmetal-doped TiO2 photocatalysts system. Both experimental results and theoretical analyses are elaborated in this section. In the following part, for the advantages of TiO2 thin films over particles, various preparation methods to obtain TiO2 thin films are briefly discussed. Finally, this review ends with a concise conclusion and outlook of new trends in the development of TiO2-based photocatalysts.展开更多
Co−TiO2 nanocomposite films were prepared via magnetron sputtering at various substrate temperatures.The films comprise Co particles dispersed in an amorphous TiO2 matrix and exhibit coexisting ferromagnetic and super...Co−TiO2 nanocomposite films were prepared via magnetron sputtering at various substrate temperatures.The films comprise Co particles dispersed in an amorphous TiO2 matrix and exhibit coexisting ferromagnetic and superparamagnetic properties.When the substrate temperature increases from room temperature to 400℃,Co particles gradually grow,and the degree of Co oxidation significantly decreases.Consequently,the saturation magnetization increases from 0.13 to 0.43 T at the same Co content by increasing the substrate temperature from room temperature to 400℃.At a high substrate temperature,conductive pathways form among some of the clustered Co particles.Thus,resistivity rapidly declines from 1600 to 76μΩ·m.The magnetoresistive characteristic of Co−TiO2 films is achieved even at resistivity of as low as 76μΩ·m.These results reveal that the obtained nanocomposite films have low Co oxidation,high magnetization and magnetoresistance at room temperature.展开更多
TiO2 thin films were prepared by DC magnetron sputtering with the oxygen flow rate higher than the threshold. The film deposited for 5 h was of anatase phase with a preferred orientation along the <220> directio...TiO2 thin films were prepared by DC magnetron sputtering with the oxygen flow rate higher than the threshold. The film deposited for 5 h was of anatase phase with a preferred orientation along the <220> direction, but the films deposited for 2 and 3 h were amorphous. The transmittance and photocatalytic activity of the TiO2 films increased constantly with increasing film thickness. When the annealing temperature was lower than 700℃, only anatase grew in the TiO2 film. TiO2 phase changed from anatase to rutile when the annealing temperature was above 800℃. The photocatalytic activity decreased with increasing annealing temperature.展开更多
基金Supported by the National Natural Science Foundation of China(Nos.91123029, 61077066 and 50902128)the Natural Science Foundation of Jilin Province, China(No.20101534)
文摘Metallosupramolecular coordination polyelectrolyte, Fe（II）-metalloviologen（FEN）, was prepared by the reaction of Fe（II） with a novel bisterpyridine ligand. As active components, FENs could be assembled into electrochromic multilayer films with negative charged polystyrene sulfate（PSS） by the sequential deposition layer-by-layer technique. Numerous analytical instruments, such as UV-Vis spectroscopy, atomic force microscopy（AFM）, tunneling electron microscopy（TEM）, zeta-potential measurement and electrochemical measurement have been utilized to characterize their morphology, optical and electrochromic properties. It has been observed that as-prepared films exhibited multi-colour changes by triggering with different potentials. However, the low optical contrast of multilayer films would limit their further applications. In order to overcome this problem, semiconductor TiO2 nanoparticles（TiO2） were incorporated into FEN multilayers by layer-by-layer approach. By carefully optimizing the film structure, as-resulted hybrid films containing FEN, TiO2 and PSS exhibited high optical contrast, suitable response time and long-term stability. Such hybrid films should be promising candidates to meet the requirements for developing flexible displays and electrochromic devices.
基金This work was supported by the National Natural Science Foundation of China(No.50081001)the Education Department Project of Liaoning Province(No.202073425).
文摘In order to improve the corrosion resistance and biocompatibility of NiTi surgical alloy, TiO2 and TiO2-SiO2 thin films were prepared by sol-gel method. The surface characteristics of the film, which include surface composition, microstructure and surface morphology, were studied by X-ray diffraction (XRD), atomic force microscopy (AFM) and X-ray photoelectron spectra (XPS), respectively. A scratching test was used to assess the interface adhesive strength between the film and substrate. The corrosion resistance of NiTi alloy coated with oxide films were studied by anodic polarization curves measurement in biological solution. Additionally, a preliminary study of the in vitro bioactivity of the films was conducted. The results indicated that TiO2 and TiO2-SiO2 (Ti/Si=4:1) films have higher electrochemical corrosion resistance and can be used as protective layers on NiTi alloy. In addition, TiO2-SiO2 composite films have better bioactivity than TiO2 film.
基金Project supported by the National Natural Science Foundation of China(Grant No.11405085)the Jiangsu Provincial Natural Science Fund,China(Grant No.BK20130789)
文摘Post-processing can effectively improve the resistance to laser damage in multilayer films used in a high power laser system.In this work,HfO_(2)/SiO_(2)multilayer films are prepared by e-beam evaporation and thenβ-ray irradiation is employed as the post-processing method.The particle irradiation affects the laser induced damage threshold(LIDT),which includes defects,surface roughness,packing density and residual stress.The residual stress that is relaxed during irradiation changes from compressive stress into tensile stress.Our results indicate that appropriate tensile stress can improve LIDT remarkably.In view of the fact that LIDT rises from 8 J/cm^(2)to 12 J/cm^(2),i.e.,50%increase,after the film has been irradiated by 2.2×10^(13)/cm^(2)β-ray,the particle irradiation can be used as a controllable and desirable postprocessing method to improve the resistance to laser induced damage.
基金Funded by the National Natural Science Foundation of China(No.50901089)the Project supported by Army Important Researches(No.2012ZB02)
文摘In order to prolong the service life of piston rings of heavy vehicle engine and decrease the friction and wear of piston rings and cylinder liner,CrMoN/MoS_2 multilayer films were deposited on the surface of rings by magnetron sputtering and low temperature ion sulfuration.FESEM equipped with EDX was adopted to analyze the compositions and morphologies of surface,cross-section,and wear scars of the multilayer films.The nano-hardness and Young＇s modulus of the films were measured by a nano tester.Tribologicalproperties of the films were tested by an SRV~174;4 wear tester.The experimentalresults indicate that the structures of the multilayer films are dense and compact.The films possess nano hardness value of approximately 26.7 GPa and superior ability of plastic deformation resistance.The multilayer films can activate solid lubricating,and possess an excellent antifriction and wear resistance under the conditions of heavy load,high frequency,high temperature,and dynamic load.
基金Supported by the National Natural Science Foundation of China under Grant No 11774438the Natural Science Foundation of Jiangsu Province under Grant No BK20151172+2 种基金the Qing Lan Project,the Opening Project of State Key Laboratory of Silicon Materials under Grant No SKL2017-04the Opening Project of Key Laboratory of Microelectronic Devices and Integrated Technology of Chinese Academy of Sciencesthe Postgraduate Research and Practice Innovation Program of Jiangsu Province under Grant No SJCX18_1024
文摘The Sb6 Te4/VO2 multilayer thin films are prepared by magnetron sputtering and the potential application in phase change memory is investigated in detail. Compared with Sb6 Te4, Sb6 Te4/VO2 multilayer composite thin films have higher phase change temperature and crystallization resistance, indicating better thermal stability and less power consumption. Also, Sb6 Te4/VO2 has a broader energy band of 1.58 eV and better data retention （125℃ for 103/）. The crystallization is suppressed by the multilayer interfaces in Sbf Te4/VO2 thin film with a smaller rms surface roughness for Sbf Te4/VO2 than monolayer Sb4Te6. The picosecond laser technology is applied to study the phase change speed. A short crystallization time of 5.21 ns is realized for the Sb6Te4 （2nm）/VO2 （8nm） thin film. The Sb6 Te4/VO2 multilayer thin film is a potential and competitive phase change material for its good thermal stability and fast phase change speed.
基金supported by the Dalian Foundation for Development of Science and Technology (No.2006A13GX029)
文摘TiO2 films were deposited at room temperature by DC pulse magnetron sputtering system.The crystalline structures,morphological features and photocatalytic activity of TiO2 films were systematically investigated by X-ray diffraction（XRD）,atomic force microscopy（AFM） and ultraviolet spectrophotometer,respectively.The results indicated that working pressure was the key deposition parameter in？uencing the TiO2 film phase composition at room temperature,which directly affected its photocatalytic activity.With increasing working pressure,the target self-bias decreases monotonously.Therefore,low temperature TiO2 phase（anatase） could be deposited with high working pressure.The anatase TiO2 films deposited with 1.4 Pa working pressure displayed the highest photocatalytic activity by the decomposition of Methyl Orange solution,which the degradation rate reached the maximum（35%） after irradiation by ultraviolet light for 1 h.
基金Project(cstc2011jj A50008)supported by the Natural Science Foundation of Chongqing,ChinaProject(14ZB0025)supported by Education Department of Sichuan Province,China
文摘Zn-doped TiO2 (Zn?TiO2) thin films were prepared by the sol?gel method on titanium substrates with heat treatment at different temperatures. The effects of heat treatment temperatures and Zn doping on the structure, photocathodic protection and photoelectrochemical properties of TiO2 thin films were investigated. It is indicated that the photoelectrical performance of the Zn?TiO2 films is enhanced with the addition of Zn element compared with the pure-TiO2 film and the largest decline by 897 mV in the electrode potential is achieved under 300 °C heat treatment. SEM?EDS analyses show that Zn element is unevenly distributed in Zn?TiO2 films; XRD patterns reveal that the grain size of Zn?TiO2 is smaller than that of pure-TiO2; FTIR results indicate that Zn - O bond forms on Zn?TiO2 surface. Ultraviolet visible absorption spectra prove that Zn?TiO2 shifts to visible light region.Mott?Shottky curves show that the flat-band potential of Zn?TiO2 is more negative and charge carrier density is bigger than that ofpure-TiO2, implying that under the synergy of the width of the space-charge layer, carrier density and flat-band potential, Zn?TiO2 with 300 °C heat treatment displays the best photocathodic protection performance.
文摘With rapid progressive application of TiO2 thin films, magnetron sputtering becomes a very interesting method to prepare such multi-functional thin films. This paper focuses on influences of various deposition processes and deposition rate on the structures and properties of TiO2 thin films. Anatase, rutile or amorphous TiO2 films with various crystalline structures and different photocatalytic, optical and electrical properties can be produced by varying sputtering gases, substrate temperature, annealing process, deposition rate and the characteristics of magnetron sputtering. This may in turn affect the functions of TiO2 films in many applications. Furthermore, TiO2-based composites films can overcome many limitations and improve the properties of TiO2 films.
基金financially supported by the National Natural Science Foundation of China (No.51301118)the Projects of International Cooperation in Shanxi (No.2014081002)the Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi (No.2013108)
文摘Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, ultraviolet- visible spectroscopy （UV-Vis） and photoluminescence spectroscopy （PL）. The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange （MO） aqueous solution under visible light irradiation. The results indicate that the Cu2O/TiO2/Pt composite films are made up of three layers which are Pt layer, anatase-TiO2 layer and Cu2O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu2O/TiO2/Pt three-layer film is much higher than that of the Cu2O/TiO2 double-layer film. Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombination, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.
文摘Anatase TiO2 sol was synthesized under mild conditions （75℃ and ambient pressure） by hydrolysis of titaniumn-butoxide in abundant acidic aqueous solution and subsequent reflux to enhance crystallization. At room temperature and in ambient atmosphere, crystalline TiO2 thin films were deposited on polymethylmethacrylate （PMMA）, SiO2-coated PMMA and SiO2-coated silicone rubber substrates from the as-prepared TiO2 sol by a dip-coating process. SiO2 layers prior to TiO2 thin films on polymer substrates could not only protect the substrates from the photocatalytic decomposition of the TiO2 thin films but also enhance the adhesion of the TiO2 thin films to the substrates. Field-emission type scanning electron microscope （FE-SEM） investigations revealed that the average particle sizes of the nanoparticles composing the TiO2 thin films were about 35-47 nm. The TiO2 thin films exhibited high photocatalytic activities in the degradation of reactive brilliant red dye X-3B in aqueous solution under aerated conditions. The preparation process of photocatalytic TiO2 thin films on the polymer substrates was quite simple and a low temperature route.
文摘Three thicknesses of TiO2 films, 174, 195, and 229 nm, were deposited onto quartz substrates by sol–gel spin coating method. The as-deposited thin films were characterized by nano-crystallite with different sizes (19–46 nm) and relatively high porous structure. Optical constants were determined and showed the lowest refractive index of 1.66 for the as-prepared films that ever reported till now. Obtained results were discussed through current theoretical ideas.
文摘Ag TiO 2 thin films were prepared on glasses.The morphology and structure of Ag TiO 2 films were investigated by XRD, SEM and FT IR.The photocatalytic and hydrophilic properties of Ag TiO 2 thin films were also evaluated by examining photocatalytic degradation dichlorophos under sunlight illumination and the change of contact angle respectively.The research results show that the Ag TiO 2 thin film is mainly composed of 20-100nm Ag and TiO 2 particles.The Ag TiO 2 thin films possess a super hydrophilic ability and higher photocatalytic activity than that of pure TiO 2 thin film.
基金Natural Science Foundation of Hubei Province, China (No. 98J029)
文摘Pb-doped TiO2 photocatalytic thin films were prepared on a soda-lime glass substrate via sol-gel method using TiO2 sol solution containing lead and characterized by X-ray photoelectron spectroscopy (XPS). The results showed that besides oxides of Ti(IV) there is a certain amount of oxides of To(?) and Ti(?) and Pb exists in the forms of PbTiO3 and PbO. The photocatalytic activity of the Pb-doped TiO2 films was evaluated by the photocatalytic decolorization of aqueous methyl orange and photocatalytic mechanism mas also analyzed.
基金Funded by Key Scientific and Technological Items of the Ministry of Education (No.99087) .
文摘TiO2-SiO2 thin films have been prepared on slide glass substrates by sol-gel method, and the effect of SiO2 additive on photo-generated hydrophilicity of TiO2 thin film was investigated by measuring the contact angle of water, the microstructure, the transmittance, the photocatalytic activity and the specific surface area . The results showed that 10mol% of SiO2 additive was the most effective for decreasing contact angle of water. The SiO2 additive of less than 30mol% has a suppressive effect on the crystal growth of anatase in calcinations, resulting in a large surface area. Consequently, the super-hydrophilicity was improved.
基金We are very grateful to the National Natural Science of Foundation of China(No.69978017,59802007)Shanghai Education Committee(No JW99-TJ-03)for their help and financial supports
文摘The microstructure properties of the sol-gel derived TiO2 films were studied by the atomic force microscopy (AFM). The films were prepared by dip coating process. The optical properties of the films were explained on the basis of the microstructure of the films.
文摘Preparation of TiO<sub>2</sub> thin films by MOCVD method is presented in this paper. A MOCVD system has been designed and built. A wide range of processing conditions are investigated to deposit TiO<sub>2</sub> films on Si wafers starting from metal-organic precursor tetrabutyl titanate. Activation energy of the film formation （E） is obtained to be 23.6 kJ/mol. Structure of films is pure anatase when deposit temperatures are low, rutile forms at 700℃. The films also exhibit preferred crystallographic orientations which strongly depend on deposit conditions. Refractive index increases with increasing of film thickness and decreasing of deposit temperature.
文摘The transparent anatase TiO 2 nanometer thin films were prepared by the sol-gel method on soda-lime glass.X-ray diffraction,thermal analysis and UV-visible spectrophotometer were used to analyze the formation of the phases.Only increasing the heat-treatment time,the average grain size has no obvious change.The mechanism of grain growth in TiO 2 thin film is probably as follows:the grain of coating will become grain core later;TiO 2 sol constantly deposited on the surface of TiO 2 grain and formed membrane with increasing of coating cycle times;TiO 2 grain in the film grow steadily.
文摘TiO2 is a promising photocatalyst. However, the low photocatalytic efficiency calls for the modification of TiO2. Metal- and nonmetal-doping of TiO2 have been proved to be effective ways to enhance photocatalytic properties. This review provides a deep insight into the understanding of the metal- and nonmetal-doped TiO2 photocatalysts. This article begins with the introduction of the crystal structures of TiO2 and applications of TiO2 materials. We then reviewed the doped-TiO2 system in two categories： （1） metal-doped TiO2 photocatalysts system, and （2） nonmetal-doped TiO2 photocatalysts system. Both experimental results and theoretical analyses are elaborated in this section. In the following part, for the advantages of TiO2 thin films over particles, various preparation methods to obtain TiO2 thin films are briefly discussed. Finally, this review ends with a concise conclusion and outlook of new trends in the development of TiO2-based photocatalysts.
基金Project(2016YFE0205700)supported by the National Key Research and Development Program of ChinaProject(18JCYBJC18000)supported by the Natural Science Foundation of Tianjin City,China。
文摘Co−TiO2 nanocomposite films were prepared via magnetron sputtering at various substrate temperatures.The films comprise Co particles dispersed in an amorphous TiO2 matrix and exhibit coexisting ferromagnetic and superparamagnetic properties.When the substrate temperature increases from room temperature to 400℃,Co particles gradually grow,and the degree of Co oxidation significantly decreases.Consequently,the saturation magnetization increases from 0.13 to 0.43 T at the same Co content by increasing the substrate temperature from room temperature to 400℃.At a high substrate temperature,conductive pathways form among some of the clustered Co particles.Thus,resistivity rapidly declines from 1600 to 76μΩ·m.The magnetoresistive characteristic of Co−TiO2 films is achieved even at resistivity of as low as 76μΩ·m.These results reveal that the obtained nanocomposite films have low Co oxidation,high magnetization and magnetoresistance at room temperature.
基金supported by the National Natural Science Foundation of China(No.50001013)Hundred-Talent Project of CAS and the NSFC for Outstanding Young Scientists(No.59625103).
文摘TiO2 thin films were prepared by DC magnetron sputtering with the oxygen flow rate higher than the threshold. The film deposited for 5 h was of anatase phase with a preferred orientation along the <220> direction, but the films deposited for 2 and 3 h were amorphous. The transmittance and photocatalytic activity of the TiO2 films increased constantly with increasing film thickness. When the annealing temperature was lower than 700℃, only anatase grew in the TiO2 film. TiO2 phase changed from anatase to rutile when the annealing temperature was above 800℃. The photocatalytic activity decreased with increasing annealing temperature.