Some active metal oxides(Al_(2)O_(3),TiO_(2),and Cr_(2)O_(3))were selected as dopants to the Al_(2)O_(3)-based ceramic shells for investment casting of K417G superalloy.The effects of dopant types and contents(0,2,5,a...Some active metal oxides(Al_(2)O_(3),TiO_(2),and Cr_(2)O_(3))were selected as dopants to the Al_(2)O_(3)-based ceramic shells for investment casting of K417G superalloy.The effects of dopant types and contents(0,2,5,and 8 wt.%)on the wettability and interfacial reaction between the alloy and shell were investigated by a sessile-drop experiment.The results show that increasing the Al_(2)O_(3) doping contents(0−8 wt.%)reduces the porosity(21.74%−10.08%)and roughness(3.22−1.34μm)of the shell surface.The increase in Cr_(2)O_(3) dopant content(2−8 wt.%)further exacerbates the interfacial reaction,leading to an increase in the thickness of the reaction layer(2.6−3.1μm)and a decrease in the wetting angle(93.9°−91.0°).The addition of Al_(2)O_(3) and TiO_(2) dopants leads to the formation of Al_(2)TiO_(5) composite oxides in the reaction products,which effectively inhibits the interfacial reaction.The increase in TiO_(2) dopant contents(0−8 wt.%)further promotes the formation of Al_(2)TiO_(5),which decreases the thickness of the interfacial reaction layer(3.9−1.2μm)and increases the wetting angle(95.0°−103.8°).The introduced dopants enhance the packing density of the shell surface,while simultaneously suppress the diffusion of active metal elements from the alloy matrix to the interface.展开更多
ZnAl_(2)O_(4) and ZnAl_(2)O_(4)-based ceramics have attracted much attention from researchers due to their good microwave dielectric,thermal and mechanical properties.In this work,the influence of 5%(in mass)CuO-TiO_(...ZnAl_(2)O_(4) and ZnAl_(2)O_(4)-based ceramics have attracted much attention from researchers due to their good microwave dielectric,thermal and mechanical properties.In this work,the influence of 5%(in mass)CuO-TiO_(2)-Nb_(2)O_(5)(CTN)ternary composite oxide additives with different composition ratios on sintering behavior and properties of ZnAl_(2)O_(4) microwave dielectric ceramics was investigated.When the molar fraction ranges of Cu,Ti and Nb elements in 5%CTN additives are 0.625-0.875,0-0.250 and 0.125-0.625,respectively,sintering temperature of ZnAl_(2)O_(4) ceramics can be reduced from above 1400℃to below 1000℃.The sintering additives CN(Cu:Nb=1:1,molar ratio)and CTN(Cu:Ti:Nb=4:1:3,molar ratio)can reduce sintering temperature of ZnAl_(2)O_(4) ceramics to 975 and 1000℃,respectively,while maintaining good dielectric properties(dielectric constantε_(r)=11.36,quality factor Q׃=8245 GHz andε_(r)=9.52,Q׃=22249 GHz)and flexural strengths(200 and 161 MPa),which are expected to be applied in preparation of low temperature co-fired ceramic(LTCC)materials with copper electrodes.Low-temperature sintering of the ZnAl_(2)O_(4)+CTN system is characterized as activated sintering.Nanometer-level amorphous interfacial films containing Cu,Ti,and Nb elements are observed at the grain boundaries,which may provide fast diffusion pathways for mass transportation during the sintering process.Valence changes of Ti and Cu ions,along with changes of oxygen vacancies,are confirmed,which provides a potential mechanism for reduced sintering temperature of ZnAl_(2)O_(4) ceramics.In addition,a series of reactions occurring at the grain boundaries can activate these boundaries and further promote the sintering densification process.These results suggest a promising way to design a novel LTCC material with excellent properties based on the low temperature sintering of ceramics with the sintering aid of CuO-TiO_(2)-Nb_(2)O_(5) composite oxide.展开更多
Nanostructured Al_(2)O_(3)-10wt.%TiO_(2)-nCeO_(2)ceramic coatings(where n is 0 wt.%,0.2 wt.%,0.5 wt.%,and 0.8 wt.%)were prepared on a 304 stainless steel substrate using atmospheric plasma spraying.The phase compositi...Nanostructured Al_(2)O_(3)-10wt.%TiO_(2)-nCeO_(2)ceramic coatings(where n is 0 wt.%,0.2 wt.%,0.5 wt.%,and 0.8 wt.%)were prepared on a 304 stainless steel substrate using atmospheric plasma spraying.The phase composition and microstructure of the coatings were characterized using an X-ray diffractometer and a scanning electron microscope.The corrosion resistance of the coatings was as-sessed through electrochemical experiments and chloride ion corrosion tests.The results indicated that the coatings comprised both partially and fully melted regions,with spherical particles and pores present on the coating surfaces.The incorporation of CeO_(2)en-hanced the melting of the sprayed powder during the spraying process.When the CeO_(2)content was 0.2 wt.%,the melting of the sprayed powder was optimal.The porosity of the coating was minimized to 2.45%.CeO_(2)also positively influenced the grain refine-ment of the coating;at 0.2 wt.%CeO_(2),the grain size was at its minimum.The grain size of this coating was calculated to be 21.135 nm using the Scherrer formula.This coating demonstrated the best corrosion resistance,with a corrosion potential of-596.31 mV and a corrosion current density of 1.65×10^(-6)A/cm^(2),resulting in a weight loss of 0.0170 g due to chloride ion corrosion.展开更多
The editor regrets that they inadvertently pasted the wrong figure during the production stage.The correct Fig.7 should be as below:The editor would like to apologise for any inconvenience caused.
The Ni-based alloy composite coatings reinforced by nanostructured Al2O3-40%TiO2 multiphase ceramic particles were prepared on the surface of 7005 aluminum alloy by plasma spray technology. The microstructure and trib...The Ni-based alloy composite coatings reinforced by nanostructured Al2O3-40%TiO2 multiphase ceramic particles were prepared on the surface of 7005 aluminum alloy by plasma spray technology. The microstructure and tribological properties of the composite coatings were researched. The results show that the composite coatings mainly consist of γ-Ni, α-Al2O3, γ-Al2O3 and rutile-TiO2 etc, and exhibit lower friction coefficients and wear losses than the Ni-based alloy coatings at different loads and speeds. The composite coating bears low contact stress at 3 N and its wear mechanism is micro-cutting wear. As loads increase to 6-12 N, the contact stress is higher than the elastic limit stress of worn surface, and the wear mechanisms change into multi-plastic deformation wear, micro-brittle fracture wear and abrasive wear. With the increase of speeds, the contact temperature of worn surface increases. The composite coating experiences multi-plastic deformation wear, fatigue wear and adhesive wear.展开更多
Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and cer...Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and ceramic coating were characterized by SEM, XRD and EDS. The results show that two-layer substructure exists in the ceramic coating： one layer evolving from fully melted region where the sintered grains grow fully; another layer resembling the liquid-phase-sintered structure consisting of three-dimensional net where the melted Al2O3 particles are embedded in the TiO2-rich matrix. The mechanism of the two-layer substructure formation is also explained in terms of the melting and flattening behavior of the powders during laser cladding processing. The spinel compounds NiAl2O4 and acicular compounds Cr2O3 are discovered in the interface between bond coating and ceramic coating. It proves that the chemical reactions in the laser cladding process will significantly enhance the coating adhesion.展开更多
The dielectric properties and phase transition characteristics of La2O3- and Sb2O3-doped barium strontium titanate ceramics prepared by solid state route were investigated. The microstructure was identified by X-ray d...The dielectric properties and phase transition characteristics of La2O3- and Sb2O3-doped barium strontium titanate ceramics prepared by solid state route were investigated. The microstructure was identified by X-ray diffraction method and scanning electron microscope was also employed to observe the surface morphologies. It is found that （La,Sb）-codoped barium strontium titanate ceramics exhibit typical perovskite structure and the average grain size decreases dramatically with increasing the content of Sb2O3. Both La3＋ ions and Sb3＋ ions occupy the A-sites in perovskite lattice. The dielectric constant and dielectric loss of barium strontium titanate based ceramics are obviously influenced by La2O3 as well as Sb2O3 addition content. The tetragonal-cubic phase transition of La2O3 modified barium strontium titanate ceramics is of second order and the Curie temperature shifts to lower value with increasing the La2O3 doping content. The phase transition of （La,Sb）-codoped barium strontium titanate ceramics diffuses and the deviation from Curie-Weiss law becomes more obvious with the increase in Sb2O3 concentration. The temperature corresponding to the dielectric constant maximum of （La,Sb）-codoped barium strontium titanate ceramics decreases with increasing the Sb2O3 content, which is attributed to the replacement of host ions by the Sb3＋ ions.展开更多
Sc_(2)O_(3),as a host for solid-state laser gain materials,has advantage of high thermal conductivity and easy matching with activating ions,which is promising in high-power laser applications.Currently,Yb-doped Sc_(2...Sc_(2)O_(3),as a host for solid-state laser gain materials,has advantage of high thermal conductivity and easy matching with activating ions,which is promising in high-power laser applications.Currently,Yb-doped Sc_(2)O_(3) ceramics have been fabricated at very high sintering temperatures,but their optical quality and sintering process still need further improvement.In this work,5%Yb:Sc_(2)O_(3)(in mass)nano-powders were obtained by co-precipitation,and then transparent ceramics were fabricated by vacuum pre-sintering and hot isostatic pressing(HIP)post-treatment.The cubic Yb:Sc_(2)O_(3) nano-powders with good dispersity and an average crystallite of 29 nm were obtained.Influence of pre-sintering temperatures(1500-1700℃)on densification process,microstructure changes,and optical transmittance of Yb:Sc_(2)O_(3) ceramics was detected.Experimental data revealed that all samples have a uniform microstructure,while the average grain sizes increase with the increase of the sintering temperatures.Impressively,the optimum in-line transmittance of Yb:Sc_(2)O_(3) ceramics,pre-sintered at 1550℃after HIP post-treatment,reaches 78.1%(theoretical value of 80%)at 1100 nm.Spectroscopic properties of the Yb:Sc_(2)O_(3) ceramics reveal that the minimum population inversion parameterβ2 and the luminescence decay time of 5%Yb:Sc_(2)O_(3) ceramics are 0.041 and 0.49 ms,respectively,which demonstrate that the optical quality of the Yb:Sc_(2)O_(3) has been improved.Meanwhile,their best vacuum sintering temperature can be controlled down to a lower temperature(1550℃).In conclusion,Yb:Sc_(2)O_(3) nano-powders are successfully synthesized by co-precipitation method,and good optical quality transparent ceramics are fabricated by vacuum pre-sintering at 1550℃and HIP post-treatment.展开更多
As a reliable additive manufacturing technology,the stereolithography(SLA)ceramic core necessitates a tailored sintering process to achieve optimal performance.This study explored the effects of final sintering temper...As a reliable additive manufacturing technology,the stereolithography(SLA)ceramic core necessitates a tailored sintering process to achieve optimal performance.This study explored the effects of final sintering temperatures(specifically 1,150,1,250,and 1,300°C)on the properties of SLA-fabricated SiO_(2)-based ceramic cores reinforced with nano-ZrO_(2)(at concentrations of 1.0wt.%,1.5wt.%,and 2.0wt.%).The results demonstrate that increasing the final sintering temperature and the incorporation of nano-ZrO_(2)enhance the viscous fiow of quartz glass,resulting in a higher sintering degree.As the final sintering temperature rises,the ceramic samples exhibit increased shrinkage rate,decreased apparent porosity,and increased bulk density.Higher final sintering temperatures also promote greater cristobalite precipitation,promoting an increase in the amount and precipitation rate of quartz during investment casting.The formation of a cristobalite and ZrSiO_4 network at elevated temperatures effectively inhibits the viscous flow of quartz glass,thereby significantly improving high-temperature flexural strength and creep resistance of ceramic cores.When the content of nano-ZrO_(2)is between 1.5wt.%and 2.0wt.%,the final sintering temperature of 1,250°C is the best choice.Under these conditions,the shrinkage rate along the Z direction ranges from 3.35%to 3.68%,the porosity lies between 25.57%and 26.03%,the bulk density varies from 1.612 to 1.645 g·cm^(-3),the room temperature fiexural strength is between 26.79 and 27.85 MPa,and the fiexural strength at high temperatures is within the range of 30.77 to 33.02 MPa.The defiection at high-temperatures is 3.37-5.31 mm,while the surface roughness of the upper surface is 3.26-4.79μm,and the surface roughness of the side surface is 4.97-5.79μm.These findings provide valuable guidance for optimizing the sintering processes of SLA ceramic cores,offering potential for industrial applications.展开更多
Full ceramic bearings are mission-critical components in oil-free environments,such as food processing,semiconductor manufacturing,and medical applications.Developing effective fault diagnosis methods for these bearin...Full ceramic bearings are mission-critical components in oil-free environments,such as food processing,semiconductor manufacturing,and medical applications.Developing effective fault diagnosis methods for these bearings is essential to ensuring operational reliability and preventing costly failures.Traditional supervised deep learning approaches have demonstrated promise in fault detection,but their dependence on large labeled datasets poses significant challenges in industrial settings where fault-labeled data is scarce.This paper introduces a few-shot learning approach for full ceramic bearing fault diagnosis by leveraging the pre-trained GPT-2 model.Large language models(LLMs)like GPT-2,pre-trained on diverse textual data,exhibit remarkable transfer learning and few-shot learning capabilities,making them ideal for applications with limited labeled data.In this study,acoustic emission(AE)signals from bearings were processed using empirical mode decomposition(EMD),and the extracted AE features were converted into structured text for fine-tuning GPT-2 as a fault classifier.To enhance its performance,we incorporated a modified loss function and softmax activation with cosine similarity,ensuring better generalization in fault identification.Experimental evaluations on a laboratory-collected full ceramic bearing dataset demonstrated that the proposed approach achieved high diagnostic accuracy with as few as five labeled samples,outperforming conventional methods such as k-nearest neighbor(KNN),large memory storage and retrieval(LAMSTAR)neural network,deep neural network(DNN),recurrent neural network(RNN),long short-term memory(LSTM)network,and model-agnostic meta-learning(MAML).The results highlight LLMs’potential to revolutionize fault diagnosis,enabling faster deployment,reduced reliance on extensive labeled datasets,and improved adaptability in industrial monitoring systems.展开更多
The influence of soaking time on the nonlinear electrical behavior and dielectric properties of TiO2-based varistor ceramics was investigated. Based on single sintering process, six disk samples of （Sr, Bi, Si, Ta）-...The influence of soaking time on the nonlinear electrical behavior and dielectric properties of TiO2-based varistor ceramics was investigated. Based on single sintering process, six disk samples of （Sr, Bi, Si, Ta）-doped TiO2-based varistor ceramics were fabricated by sintering at 1 250 ℃ for 0.5-5.0 h. The samples were characterized by X-ray diffraction, voltage-current characteristics, energy spectra, metallographs, breakdown voltages, and apparent dielectric constant. It is found that the breakdown electrical field intensity at a current density of 10 mA/cma decreases from 5.5 to 4.1 V/mm first and then increases to 7.0 V/mm, the nonlinear coefficient increases from 2.39 to 2.62 first and then decreases to 2.42, and the apparent dielectric constant increases from 98 200 to 1l5 049 first and then decreases to 73 865 with the soaking time increasing from 0.5 to 5.0 h. These indicate that the optimal soaking time is 2.0-3.0 h considering both nonlinear electrical behavior and dielectric properties.展开更多
In this work,the rare-earth doped ternary lead zirconate titanate ceramics with chemical formula of[0.3 Pb(Zn_(1/3)Nb_(2/3))O_(3)-0.7Pb(Zr_(0.52)Ti_(0.48))O_(3)]+x wt%CeO_(2)(x=0-0.5,abbreviated as 0.3PZN-0.7PZT-xCe)w...In this work,the rare-earth doped ternary lead zirconate titanate ceramics with chemical formula of[0.3 Pb(Zn_(1/3)Nb_(2/3))O_(3)-0.7Pb(Zr_(0.52)Ti_(0.48))O_(3)]+x wt%CeO_(2)(x=0-0.5,abbreviated as 0.3PZN-0.7PZT-xCe)were synthesized by a conventional solid-state reaction route,specific attentions was focused on the effects of CeO_(2)dopants on the structures and electrical properties of the 0.3PZN-0.7PZT ceramics,revealing the role conve rsion of CeO_(2)dopants with its doping amount(x).When less CeO_(2)(x≤0.2)is introduced into 0.3PZN-0.7PZT,the prepared ceramics are identified as the coexistence of rhombohedral and tetragonal phases,also involved with an increased grain size and a reduced atomic ratio of Pb/(Zr+Ti+Zn+Nb).The increased remanent polarization(Pr)and deceased coercive filed(Ec),as well as improved dielectric permittivity(er)and piezoelectric coefficient(d_(33))de monstrate the donor substitution of Ce^(3+)for Pb^(2+)at the A-site of perovskite lattice.Conversely,the introduction of excessive CeO_(2)(x>0.2)causes a reversal evolution in the electrical properties of ceramics,suggesting that some of the introduced cerium element tends to become Ce4+,which equivalently substitutes for Zr^(4+)at the B-site.Additionally,the diffused phase transition(DPT)behaviors of the 0.3PZN-0.7PZT-xCe ceramics were investigated by the modified Curie-Weiss Law.The sample with x=0.2 shows reduced DPT character and optimized electrical properties,including TC=297℃,εr=1400,d_(33)=480 pC/N,tanδ=1.6%,kp=65%,d_(33)·g_(33)=16.32×10^(-12)m^(2)/N,Pr=38.3μC/cm^(2)and Ec=1.02 kV/mm.These enhanced electrical properties not only are contributed by the donor substitution effect of Ce^(3+),but also benefit from the optimized morphotropic phase boundary that is close to the tetragonal-rich side.展开更多
Effects of doping CeO2 and Er2O3 on the mechanical strength, thermal expansion coefficient, sintering temperature of TiO2-SiO2 ceramics were investigated. The experimental results and the microscopic analysis of SEM, ...Effects of doping CeO2 and Er2O3 on the mechanical strength, thermal expansion coefficient, sintering temperature of TiO2-SiO2 ceramics were investigated. The experimental results and the microscopic analysis of SEM, XRD, TG-DSC, FT-IR and TEM show that adding CeO2 and Er2O3 into TiO2-SiO2 ceramics can prohibit the growth of its crystal grains, make their size uniform and form them into a dense structure, which finally enhance its mechanical behaviors, and the lower thermal expansion coefficient that leads to an excellent property of thermal shock resistance. After the reforming TiO2-SiO2 ceramics doped by CeO2 was sintered at 1380℃, the bending strength reached to 83 MPa, and the thermal expansion coefficient was 9.8×10-6/℃within the temperature range of 25 ~ 800℃, which provides a promising basis of making equipped honeycomb catalyst of deNOx.展开更多
Composite membranes have attracted increasing attentions owing to their potential applications for CO2 separation. In this work, ceramic supported polydimethylsiloxane （PDMS） and poly （ethylene glycol） diacrylate ...Composite membranes have attracted increasing attentions owing to their potential applications for CO2 separation. In this work, ceramic supported polydimethylsiloxane （PDMS） and poly （ethylene glycol） diacrylate （PEGDA） composite membranes were prepared. The microstructure and physicochemical properties of the compos- ite membranes were characterized. Preparation conditions were systematically optimized. The gas separation performance of the as-prepared membranes was studied by pure gas and binary gas permeation measurement of CO〉 N2 and H〉 Experiments showed that PDMS, as silicone rubber, exhibited larger permeance and lower separation factors. Conversely, PEGDA composite membrane presented smaller gas permeance but higher ideal selectivity for CO2/N2. Compared to the performance of those membranes using polymeric supports or freestanding membranes, the two kinds of ceramic supported composite membranes exhibited higher gas permeance and acceptable selectivity. Therefore, the ceramic supported composite membrane can be expected as a candidate for CO2 separation from light gases.展开更多
We investigated the influence of soaking time on the semi-conductivity and nonlinear electrical properties of TiO2- based varistor ceramic samples. We used a single sintering process and fabricated six disk samples of...We investigated the influence of soaking time on the semi-conductivity and nonlinear electrical properties of TiO2- based varistor ceramic samples. We used a single sintering process and fabricated six disk samples of （Sr, Bi, Si, Ta）-doped TiO2- based varistor ceramics sintered at 1 250℃ for 0.5 h, 1.0 h, 2.0 h, 3.0 h, 4.0 h, and 5.0 h, respectively. The samples were characterized by X-ray diffraction, breakdown voltage, and complex impedance. The results show that as the soaking time increases from 0.5 h to 5.0 h, the breakdown voltage drops before rising while the nonlinear coefficient increases and then decreases. We suggest that, considering both grain semi-conductivity and nonlinear electrical properties of the TiO2-based varistor ceramics, the optimal soaking time is between 2.0 h and 3.0 h.展开更多
Polycrystalline 3Y-TZP/Al2O3 tetragonal zirconia fiber was obtained by the pyrolysis of gel fibers using zirconium oxychloride octahydrate（ZOC） as the raw material. The spinnable zirconia sol was prepared by electro...Polycrystalline 3Y-TZP/Al2O3 tetragonal zirconia fiber was obtained by the pyrolysis of gel fibers using zirconium oxychloride octahydrate（ZOC） as the raw material. The spinnable zirconia sol was prepared by electrolyzing the zirco-nium oxychloride octahydrate（ZOC） solution in the presence of acetic acid and sugar（ sucrose, glucrose or fructose） , in which the molar ratios of CH3 COOH/ZOC and sugar/ZOC were 1.0-4.0 and 0.2-0.4, respectively. The pre- pared tetragonal zireonia fibers sintered at different temperatures showed smooth and crack-free surfaces with diame, ters of 5-10 μm. The addition of Al2O3 enhanced the sintering process and prevented the crystals from growing. Thermogravimetric analysis（TG）, X-ray diffraction （ XRD ）, Fourier transform infrared spectroscopy（FTIR）, and scanning electron microscope（SEM） techniques were used to characterize the prepared fibers.展开更多
The conditions of ZnO-Al2O3 aqueous suspensions and slip casting were optimized to obtain dense green compacts and further to obtain high density ZnO-Al2O3 ceramic composites.The Zeta potential of raw powders was meas...The conditions of ZnO-Al2O3 aqueous suspensions and slip casting were optimized to obtain dense green compacts and further to obtain high density ZnO-Al2O3 ceramic composites.The Zeta potential of raw powders was measured.ZnO and Al2O3 powders have lower Zeta potential than-45 mV commonly at pH 8-10.3 with polyacrylic acid(PAA)added.The influence of pH and the mass fraction of the additives on the stability and fluidity of the suspensions added with PAA and polyethylene glycol(PEG) was investigated by experiments of viscosity and sedimentation.The suspensions have the lowest viscosity and the best stability at pH 9 with 0.2%PAA(mass fraction).The maximum density of green compacts is 66.6%of theoretical density(TD)with compacting and homogeneous green particles.An ultrahigh density sintered compact(>99.6%TD)could be obtained after pressureless sintering at 1 400℃for 2 h.展开更多
Al_(2)O_(3)-based eutectic ceramics are considered as promising candidates for ultra-high-temperature structural materials due to their exceptional thermal stability and mechanical properties.Nonetheless,several chall...Al_(2)O_(3)-based eutectic ceramics are considered as promising candidates for ultra-high-temperature structural materials due to their exceptional thermal stability and mechanical properties.Nonetheless,several challenges must be overcome before they can be widely used.This paper reviews in detail the tailoring of microstructure from the aspect of process parameters,the updated knowledge gained in microstructure(crystallographic orientation,high-resolution interfacial structures)and the latest means of optimizing eutectic microstructure(seed-induced method,introducing low-energy grain boundaries and high-entropy phase).Additionally,the paper explores future techniques for the fabrication of bulk ceramic materials and effective toughening approaches.This review highlights the achievements made especially in the last 15 years,current limitations in Al_(2)O_(3)-based eutectic ceramics,and offers comprehensive insights and strategic guidance for further mechanical breakthroughs.展开更多
The rapid advancement of superalloy melting technology has increased the demands on crucible materials.Y_(2)O_(3) is a promising candidate for nickel-based superalloy melting due to its outstanding high-temperature st...The rapid advancement of superalloy melting technology has increased the demands on crucible materials.Y_(2)O_(3) is a promising candidate for nickel-based superalloy melting due to its outstanding high-temperature stability and non-wetting behavior with various alloys.However,its poor sintering performance limits its development.High-density Y_(2)O_(3) ceramics were successfully prepared via pressureless sintering at 1600℃ in a carbon-embedded atmosphere with talc powder as an additive.The resulting ceramics achieved optimal properties,including a bulk density of 4.27 g cm^(−3),apparent porosity of 1.1%,and cold compressive strength of 311.27 MPa.The talc powder introduced a liquid phase during sintering,which accelerated mass transfer and promoted grain growth and densification.During cooling,this liquid phase remained at the grain boundaries and acted as an intergranular bonding agent,strengthening grain cohesion.Nevertheless,excessive liquid phase hindered grain growth,negatively affecting sintering.Additionally,the extremely low porosity and the formation of the Mg_(2)SiO_(4) phase reduced the residual strength retention ratio of the Y_(2)O_(3) ceramic after thermal shock.展开更多
基金supported by the National Natural Science Foundation of China (No. 52374292)China Baowu Low Carbon Metallurgy Innovation Foundation, China (No. BWLCF202309)the Natural Science Foundation of Changsha City, China (No. KQ2208271)。
文摘Some active metal oxides(Al_(2)O_(3),TiO_(2),and Cr_(2)O_(3))were selected as dopants to the Al_(2)O_(3)-based ceramic shells for investment casting of K417G superalloy.The effects of dopant types and contents(0,2,5,and 8 wt.%)on the wettability and interfacial reaction between the alloy and shell were investigated by a sessile-drop experiment.The results show that increasing the Al_(2)O_(3) doping contents(0−8 wt.%)reduces the porosity(21.74%−10.08%)and roughness(3.22−1.34μm)of the shell surface.The increase in Cr_(2)O_(3) dopant content(2−8 wt.%)further exacerbates the interfacial reaction,leading to an increase in the thickness of the reaction layer(2.6−3.1μm)and a decrease in the wetting angle(93.9°−91.0°).The addition of Al_(2)O_(3) and TiO_(2) dopants leads to the formation of Al_(2)TiO_(5) composite oxides in the reaction products,which effectively inhibits the interfacial reaction.The increase in TiO_(2) dopant contents(0−8 wt.%)further promotes the formation of Al_(2)TiO_(5),which decreases the thickness of the interfacial reaction layer(3.9−1.2μm)and increases the wetting angle(95.0°−103.8°).The introduced dopants enhance the packing density of the shell surface,while simultaneously suppress the diffusion of active metal elements from the alloy matrix to the interface.
基金National Natural Science Foundation of China (U24A2052)Shanghai Eastern Talent Plan。
文摘ZnAl_(2)O_(4) and ZnAl_(2)O_(4)-based ceramics have attracted much attention from researchers due to their good microwave dielectric,thermal and mechanical properties.In this work,the influence of 5%(in mass)CuO-TiO_(2)-Nb_(2)O_(5)(CTN)ternary composite oxide additives with different composition ratios on sintering behavior and properties of ZnAl_(2)O_(4) microwave dielectric ceramics was investigated.When the molar fraction ranges of Cu,Ti and Nb elements in 5%CTN additives are 0.625-0.875,0-0.250 and 0.125-0.625,respectively,sintering temperature of ZnAl_(2)O_(4) ceramics can be reduced from above 1400℃to below 1000℃.The sintering additives CN(Cu:Nb=1:1,molar ratio)and CTN(Cu:Ti:Nb=4:1:3,molar ratio)can reduce sintering temperature of ZnAl_(2)O_(4) ceramics to 975 and 1000℃,respectively,while maintaining good dielectric properties(dielectric constantε_(r)=11.36,quality factor Q׃=8245 GHz andε_(r)=9.52,Q׃=22249 GHz)and flexural strengths(200 and 161 MPa),which are expected to be applied in preparation of low temperature co-fired ceramic(LTCC)materials with copper electrodes.Low-temperature sintering of the ZnAl_(2)O_(4)+CTN system is characterized as activated sintering.Nanometer-level amorphous interfacial films containing Cu,Ti,and Nb elements are observed at the grain boundaries,which may provide fast diffusion pathways for mass transportation during the sintering process.Valence changes of Ti and Cu ions,along with changes of oxygen vacancies,are confirmed,which provides a potential mechanism for reduced sintering temperature of ZnAl_(2)O_(4) ceramics.In addition,a series of reactions occurring at the grain boundaries can activate these boundaries and further promote the sintering densification process.These results suggest a promising way to design a novel LTCC material with excellent properties based on the low temperature sintering of ceramics with the sintering aid of CuO-TiO_(2)-Nb_(2)O_(5) composite oxide.
基金supported by the National Natural Science Foundation of China(Grant No.52375387).
文摘Nanostructured Al_(2)O_(3)-10wt.%TiO_(2)-nCeO_(2)ceramic coatings(where n is 0 wt.%,0.2 wt.%,0.5 wt.%,and 0.8 wt.%)were prepared on a 304 stainless steel substrate using atmospheric plasma spraying.The phase composition and microstructure of the coatings were characterized using an X-ray diffractometer and a scanning electron microscope.The corrosion resistance of the coatings was as-sessed through electrochemical experiments and chloride ion corrosion tests.The results indicated that the coatings comprised both partially and fully melted regions,with spherical particles and pores present on the coating surfaces.The incorporation of CeO_(2)en-hanced the melting of the sprayed powder during the spraying process.When the CeO_(2)content was 0.2 wt.%,the melting of the sprayed powder was optimal.The porosity of the coating was minimized to 2.45%.CeO_(2)also positively influenced the grain refine-ment of the coating;at 0.2 wt.%CeO_(2),the grain size was at its minimum.The grain size of this coating was calculated to be 21.135 nm using the Scherrer formula.This coating demonstrated the best corrosion resistance,with a corrosion potential of-596.31 mV and a corrosion current density of 1.65×10^(-6)A/cm^(2),resulting in a weight loss of 0.0170 g due to chloride ion corrosion.
文摘The editor regrets that they inadvertently pasted the wrong figure during the production stage.The correct Fig.7 should be as below:The editor would like to apologise for any inconvenience caused.
文摘The Ni-based alloy composite coatings reinforced by nanostructured Al2O3-40%TiO2 multiphase ceramic particles were prepared on the surface of 7005 aluminum alloy by plasma spray technology. The microstructure and tribological properties of the composite coatings were researched. The results show that the composite coatings mainly consist of γ-Ni, α-Al2O3, γ-Al2O3 and rutile-TiO2 etc, and exhibit lower friction coefficients and wear losses than the Ni-based alloy coatings at different loads and speeds. The composite coating bears low contact stress at 3 N and its wear mechanism is micro-cutting wear. As loads increase to 6-12 N, the contact stress is higher than the elastic limit stress of worn surface, and the wear mechanisms change into multi-plastic deformation wear, micro-brittle fracture wear and abrasive wear. With the increase of speeds, the contact temperature of worn surface increases. The composite coating experiences multi-plastic deformation wear, fatigue wear and adhesive wear.
基金Project (59975046) supported by the National Natural Science Foundation of China
文摘Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and ceramic coating were characterized by SEM, XRD and EDS. The results show that two-layer substructure exists in the ceramic coating： one layer evolving from fully melted region where the sintered grains grow fully; another layer resembling the liquid-phase-sintered structure consisting of three-dimensional net where the melted Al2O3 particles are embedded in the TiO2-rich matrix. The mechanism of the two-layer substructure formation is also explained in terms of the melting and flattening behavior of the powders during laser cladding processing. The spinel compounds NiAl2O4 and acicular compounds Cr2O3 are discovered in the interface between bond coating and ceramic coating. It proves that the chemical reactions in the laser cladding process will significantly enhance the coating adhesion.
基金Project (11KJB430007) supported by the University Natural Science Research Program of Jiangsu Province, ChinaProject supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions, China
文摘The dielectric properties and phase transition characteristics of La2O3- and Sb2O3-doped barium strontium titanate ceramics prepared by solid state route were investigated. The microstructure was identified by X-ray diffraction method and scanning electron microscope was also employed to observe the surface morphologies. It is found that （La,Sb）-codoped barium strontium titanate ceramics exhibit typical perovskite structure and the average grain size decreases dramatically with increasing the content of Sb2O3. Both La3＋ ions and Sb3＋ ions occupy the A-sites in perovskite lattice. The dielectric constant and dielectric loss of barium strontium titanate based ceramics are obviously influenced by La2O3 as well as Sb2O3 addition content. The tetragonal-cubic phase transition of La2O3 modified barium strontium titanate ceramics is of second order and the Curie temperature shifts to lower value with increasing the La2O3 doping content. The phase transition of （La,Sb）-codoped barium strontium titanate ceramics diffuses and the deviation from Curie-Weiss law becomes more obvious with the increase in Sb2O3 concentration. The temperature corresponding to the dielectric constant maximum of （La,Sb）-codoped barium strontium titanate ceramics decreases with increasing the Sb2O3 content, which is attributed to the replacement of host ions by the Sb3＋ ions.
基金National Key R&D Program of China(2023YFE3812005)International Partnership Program of Chinese Academy of Sciences(121631KYSB20200039)+1 种基金National Center for Research and Development(WPC2/1/SCAPOL/2021)Chinese Academy of Sciences President’s International Fellowship Initiative(2024VEA0005,2024VEA0014)。
文摘Sc_(2)O_(3),as a host for solid-state laser gain materials,has advantage of high thermal conductivity and easy matching with activating ions,which is promising in high-power laser applications.Currently,Yb-doped Sc_(2)O_(3) ceramics have been fabricated at very high sintering temperatures,but their optical quality and sintering process still need further improvement.In this work,5%Yb:Sc_(2)O_(3)(in mass)nano-powders were obtained by co-precipitation,and then transparent ceramics were fabricated by vacuum pre-sintering and hot isostatic pressing(HIP)post-treatment.The cubic Yb:Sc_(2)O_(3) nano-powders with good dispersity and an average crystallite of 29 nm were obtained.Influence of pre-sintering temperatures(1500-1700℃)on densification process,microstructure changes,and optical transmittance of Yb:Sc_(2)O_(3) ceramics was detected.Experimental data revealed that all samples have a uniform microstructure,while the average grain sizes increase with the increase of the sintering temperatures.Impressively,the optimum in-line transmittance of Yb:Sc_(2)O_(3) ceramics,pre-sintered at 1550℃after HIP post-treatment,reaches 78.1%(theoretical value of 80%)at 1100 nm.Spectroscopic properties of the Yb:Sc_(2)O_(3) ceramics reveal that the minimum population inversion parameterβ2 and the luminescence decay time of 5%Yb:Sc_(2)O_(3) ceramics are 0.041 and 0.49 ms,respectively,which demonstrate that the optical quality of the Yb:Sc_(2)O_(3) has been improved.Meanwhile,their best vacuum sintering temperature can be controlled down to a lower temperature(1550℃).In conclusion,Yb:Sc_(2)O_(3) nano-powders are successfully synthesized by co-precipitation method,and good optical quality transparent ceramics are fabricated by vacuum pre-sintering at 1550℃and HIP post-treatment.
基金supported by the Natural Science Foundation of Shanghai(No.23ZR1421500)the National Natural Science Foundation of China(Nos.52474412,52127807,52271035)+3 种基金the Shanghai Municipal Commission of Economy and Informatization(No.GYOJ2022-2-02)the United Innovation Program of Shanghai Commercial Aircraft Engine(No.AR966)the SPMI Project from Shanghai Academy of Spaceflight Technology(No.SPMI2022-06)the Ningbo International Science and Technology Cooperation Program(No.2023H004)。
文摘As a reliable additive manufacturing technology,the stereolithography(SLA)ceramic core necessitates a tailored sintering process to achieve optimal performance.This study explored the effects of final sintering temperatures(specifically 1,150,1,250,and 1,300°C)on the properties of SLA-fabricated SiO_(2)-based ceramic cores reinforced with nano-ZrO_(2)(at concentrations of 1.0wt.%,1.5wt.%,and 2.0wt.%).The results demonstrate that increasing the final sintering temperature and the incorporation of nano-ZrO_(2)enhance the viscous fiow of quartz glass,resulting in a higher sintering degree.As the final sintering temperature rises,the ceramic samples exhibit increased shrinkage rate,decreased apparent porosity,and increased bulk density.Higher final sintering temperatures also promote greater cristobalite precipitation,promoting an increase in the amount and precipitation rate of quartz during investment casting.The formation of a cristobalite and ZrSiO_4 network at elevated temperatures effectively inhibits the viscous flow of quartz glass,thereby significantly improving high-temperature flexural strength and creep resistance of ceramic cores.When the content of nano-ZrO_(2)is between 1.5wt.%and 2.0wt.%,the final sintering temperature of 1,250°C is the best choice.Under these conditions,the shrinkage rate along the Z direction ranges from 3.35%to 3.68%,the porosity lies between 25.57%and 26.03%,the bulk density varies from 1.612 to 1.645 g·cm^(-3),the room temperature fiexural strength is between 26.79 and 27.85 MPa,and the fiexural strength at high temperatures is within the range of 30.77 to 33.02 MPa.The defiection at high-temperatures is 3.37-5.31 mm,while the surface roughness of the upper surface is 3.26-4.79μm,and the surface roughness of the side surface is 4.97-5.79μm.These findings provide valuable guidance for optimizing the sintering processes of SLA ceramic cores,offering potential for industrial applications.
文摘Full ceramic bearings are mission-critical components in oil-free environments,such as food processing,semiconductor manufacturing,and medical applications.Developing effective fault diagnosis methods for these bearings is essential to ensuring operational reliability and preventing costly failures.Traditional supervised deep learning approaches have demonstrated promise in fault detection,but their dependence on large labeled datasets poses significant challenges in industrial settings where fault-labeled data is scarce.This paper introduces a few-shot learning approach for full ceramic bearing fault diagnosis by leveraging the pre-trained GPT-2 model.Large language models(LLMs)like GPT-2,pre-trained on diverse textual data,exhibit remarkable transfer learning and few-shot learning capabilities,making them ideal for applications with limited labeled data.In this study,acoustic emission(AE)signals from bearings were processed using empirical mode decomposition(EMD),and the extracted AE features were converted into structured text for fine-tuning GPT-2 as a fault classifier.To enhance its performance,we incorporated a modified loss function and softmax activation with cosine similarity,ensuring better generalization in fault identification.Experimental evaluations on a laboratory-collected full ceramic bearing dataset demonstrated that the proposed approach achieved high diagnostic accuracy with as few as five labeled samples,outperforming conventional methods such as k-nearest neighbor(KNN),large memory storage and retrieval(LAMSTAR)neural network,deep neural network(DNN),recurrent neural network(RNN),long short-term memory(LSTM)network,and model-agnostic meta-learning(MAML).The results highlight LLMs’potential to revolutionize fault diagnosis,enabling faster deployment,reduced reliance on extensive labeled datasets,and improved adaptability in industrial monitoring systems.
基金Project(50872001) supported by the National Natural Science Foundation of ChinaProjects(KJ2007B132, KJ2009A006Z) supported by the Scientific Research Foundation of Education Department of Anhui Province, ChinaProject(XJ200907) supported by the Foundation of Construction of Quality Project of Anhui University, China
文摘The influence of soaking time on the nonlinear electrical behavior and dielectric properties of TiO2-based varistor ceramics was investigated. Based on single sintering process, six disk samples of （Sr, Bi, Si, Ta）-doped TiO2-based varistor ceramics were fabricated by sintering at 1 250 ℃ for 0.5-5.0 h. The samples were characterized by X-ray diffraction, voltage-current characteristics, energy spectra, metallographs, breakdown voltages, and apparent dielectric constant. It is found that the breakdown electrical field intensity at a current density of 10 mA/cma decreases from 5.5 to 4.1 V/mm first and then increases to 7.0 V/mm, the nonlinear coefficient increases from 2.39 to 2.62 first and then decreases to 2.42, and the apparent dielectric constant increases from 98 200 to 1l5 049 first and then decreases to 73 865 with the soaking time increasing from 0.5 to 5.0 h. These indicate that the optimal soaking time is 2.0-3.0 h considering both nonlinear electrical behavior and dielectric properties.
基金Project supported by the Natural Science Foundation of Sichuan Province(2024NSFSC0219)。
文摘In this work,the rare-earth doped ternary lead zirconate titanate ceramics with chemical formula of[0.3 Pb(Zn_(1/3)Nb_(2/3))O_(3)-0.7Pb(Zr_(0.52)Ti_(0.48))O_(3)]+x wt%CeO_(2)(x=0-0.5,abbreviated as 0.3PZN-0.7PZT-xCe)were synthesized by a conventional solid-state reaction route,specific attentions was focused on the effects of CeO_(2)dopants on the structures and electrical properties of the 0.3PZN-0.7PZT ceramics,revealing the role conve rsion of CeO_(2)dopants with its doping amount(x).When less CeO_(2)(x≤0.2)is introduced into 0.3PZN-0.7PZT,the prepared ceramics are identified as the coexistence of rhombohedral and tetragonal phases,also involved with an increased grain size and a reduced atomic ratio of Pb/(Zr+Ti+Zn+Nb).The increased remanent polarization(Pr)and deceased coercive filed(Ec),as well as improved dielectric permittivity(er)and piezoelectric coefficient(d_(33))de monstrate the donor substitution of Ce^(3+)for Pb^(2+)at the A-site of perovskite lattice.Conversely,the introduction of excessive CeO_(2)(x>0.2)causes a reversal evolution in the electrical properties of ceramics,suggesting that some of the introduced cerium element tends to become Ce4+,which equivalently substitutes for Zr^(4+)at the B-site.Additionally,the diffused phase transition(DPT)behaviors of the 0.3PZN-0.7PZT-xCe ceramics were investigated by the modified Curie-Weiss Law.The sample with x=0.2 shows reduced DPT character and optimized electrical properties,including TC=297℃,εr=1400,d_(33)=480 pC/N,tanδ=1.6%,kp=65%,d_(33)·g_(33)=16.32×10^(-12)m^(2)/N,Pr=38.3μC/cm^(2)and Ec=1.02 kV/mm.These enhanced electrical properties not only are contributed by the donor substitution effect of Ce^(3+),but also benefit from the optimized morphotropic phase boundary that is close to the tetragonal-rich side.
基金Project supported by the National Natural Science Foundation of China (20376034) Social Development Fund of Jiangsu Province (BS2005053)
文摘Effects of doping CeO2 and Er2O3 on the mechanical strength, thermal expansion coefficient, sintering temperature of TiO2-SiO2 ceramics were investigated. The experimental results and the microscopic analysis of SEM, XRD, TG-DSC, FT-IR and TEM show that adding CeO2 and Er2O3 into TiO2-SiO2 ceramics can prohibit the growth of its crystal grains, make their size uniform and form them into a dense structure, which finally enhance its mechanical behaviors, and the lower thermal expansion coefficient that leads to an excellent property of thermal shock resistance. After the reforming TiO2-SiO2 ceramics doped by CeO2 was sintered at 1380℃, the bending strength reached to 83 MPa, and the thermal expansion coefficient was 9.8×10-6/℃within the temperature range of 25 ~ 800℃, which provides a promising basis of making equipped honeycomb catalyst of deNOx.
基金Supported by the National Basic Research Program of China （2009CB623406）, the National Natural Science Foundation of China （20990222） and the Natural Science Foundation of Jiangsu Province （BK2009021, SBK200930313）.
文摘Composite membranes have attracted increasing attentions owing to their potential applications for CO2 separation. In this work, ceramic supported polydimethylsiloxane （PDMS） and poly （ethylene glycol） diacrylate （PEGDA） composite membranes were prepared. The microstructure and physicochemical properties of the compos- ite membranes were characterized. Preparation conditions were systematically optimized. The gas separation performance of the as-prepared membranes was studied by pure gas and binary gas permeation measurement of CO〉 N2 and H〉 Experiments showed that PDMS, as silicone rubber, exhibited larger permeance and lower separation factors. Conversely, PEGDA composite membrane presented smaller gas permeance but higher ideal selectivity for CO2/N2. Compared to the performance of those membranes using polymeric supports or freestanding membranes, the two kinds of ceramic supported composite membranes exhibited higher gas permeance and acceptable selectivity. Therefore, the ceramic supported composite membrane can be expected as a candidate for CO2 separation from light gases.
基金Funded by the Natural Science Foundation of China (No. 50872001 and No. 50642038)the Scientific Research Foundation of Education Ministry of Anhui Province (No. 2005KJ224 and No. KJ2007B132)the Graduate Student Innovation Programs of Anhui University (No. 20072006)
文摘We investigated the influence of soaking time on the semi-conductivity and nonlinear electrical properties of TiO2- based varistor ceramic samples. We used a single sintering process and fabricated six disk samples of （Sr, Bi, Si, Ta）-doped TiO2- based varistor ceramics sintered at 1 250℃ for 0.5 h, 1.0 h, 2.0 h, 3.0 h, 4.0 h, and 5.0 h, respectively. The samples were characterized by X-ray diffraction, breakdown voltage, and complex impedance. The results show that as the soaking time increases from 0.5 h to 5.0 h, the breakdown voltage drops before rising while the nonlinear coefficient increases and then decreases. We suggest that, considering both grain semi-conductivity and nonlinear electrical properties of the TiO2-based varistor ceramics, the optimal soaking time is between 2.0 h and 3.0 h.
基金Supported by National High Technology Research and Development Program of China(No.2002AA2040).
文摘Polycrystalline 3Y-TZP/Al2O3 tetragonal zirconia fiber was obtained by the pyrolysis of gel fibers using zirconium oxychloride octahydrate（ZOC） as the raw material. The spinnable zirconia sol was prepared by electrolyzing the zirco-nium oxychloride octahydrate（ZOC） solution in the presence of acetic acid and sugar（ sucrose, glucrose or fructose） , in which the molar ratios of CH3 COOH/ZOC and sugar/ZOC were 1.0-4.0 and 0.2-0.4, respectively. The pre- pared tetragonal zireonia fibers sintered at different temperatures showed smooth and crack-free surfaces with diame, ters of 5-10 μm. The addition of Al2O3 enhanced the sintering process and prevented the crystals from growing. Thermogravimetric analysis（TG）, X-ray diffraction （ XRD ）, Fourier transform infrared spectroscopy（FTIR）, and scanning electron microscope（SEM） techniques were used to characterize the prepared fibers.
基金Project(50477044)supported by the National Natural Science Foundation of China
文摘The conditions of ZnO-Al2O3 aqueous suspensions and slip casting were optimized to obtain dense green compacts and further to obtain high density ZnO-Al2O3 ceramic composites.The Zeta potential of raw powders was measured.ZnO and Al2O3 powders have lower Zeta potential than-45 mV commonly at pH 8-10.3 with polyacrylic acid(PAA)added.The influence of pH and the mass fraction of the additives on the stability and fluidity of the suspensions added with PAA and polyethylene glycol(PEG) was investigated by experiments of viscosity and sedimentation.The suspensions have the lowest viscosity and the best stability at pH 9 with 0.2%PAA(mass fraction).The maximum density of green compacts is 66.6%of theoretical density(TD)with compacting and homogeneous green particles.An ultrahigh density sintered compact(>99.6%TD)could be obtained after pressureless sintering at 1 400℃for 2 h.
基金financially supported by the National Natural Science Foundation of China(No.52171046)National Natural Science Foundation of China-key programme(No.52234010)the Fundamental Research Funds for the Central Universities and Shaanxi Provincial Key Science and Technology Innovation Team(No.2023-CX-TD-14).
文摘Al_(2)O_(3)-based eutectic ceramics are considered as promising candidates for ultra-high-temperature structural materials due to their exceptional thermal stability and mechanical properties.Nonetheless,several challenges must be overcome before they can be widely used.This paper reviews in detail the tailoring of microstructure from the aspect of process parameters,the updated knowledge gained in microstructure(crystallographic orientation,high-resolution interfacial structures)and the latest means of optimizing eutectic microstructure(seed-induced method,introducing low-energy grain boundaries and high-entropy phase).Additionally,the paper explores future techniques for the fabrication of bulk ceramic materials and effective toughening approaches.This review highlights the achievements made especially in the last 15 years,current limitations in Al_(2)O_(3)-based eutectic ceramics,and offers comprehensive insights and strategic guidance for further mechanical breakthroughs.
基金financially supported by the National Natural Science Foundation of China(No.U21A2057).
文摘The rapid advancement of superalloy melting technology has increased the demands on crucible materials.Y_(2)O_(3) is a promising candidate for nickel-based superalloy melting due to its outstanding high-temperature stability and non-wetting behavior with various alloys.However,its poor sintering performance limits its development.High-density Y_(2)O_(3) ceramics were successfully prepared via pressureless sintering at 1600℃ in a carbon-embedded atmosphere with talc powder as an additive.The resulting ceramics achieved optimal properties,including a bulk density of 4.27 g cm^(−3),apparent porosity of 1.1%,and cold compressive strength of 311.27 MPa.The talc powder introduced a liquid phase during sintering,which accelerated mass transfer and promoted grain growth and densification.During cooling,this liquid phase remained at the grain boundaries and acted as an intergranular bonding agent,strengthening grain cohesion.Nevertheless,excessive liquid phase hindered grain growth,negatively affecting sintering.Additionally,the extremely low porosity and the formation of the Mg_(2)SiO_(4) phase reduced the residual strength retention ratio of the Y_(2)O_(3) ceramic after thermal shock.