The effects of Ni addition on solidification micro structure and tensile properties of Ti-48Al-2Cr-2Nb alloy were investigated using differential scanning calorimetry（DSC）,X-ray diffraction（XRD）,scanning electron ...The effects of Ni addition on solidification micro structure and tensile properties of Ti-48Al-2Cr-2Nb alloy were investigated using differential scanning calorimetry（DSC）,X-ray diffraction（XRD）,scanning electron microscopy（SEM） equipped with energy-dispersive spectroscope（EDS） and transmission electron microscopy（TEM）.Results show that with 3 at%Ni addition,the as-cast micro structure is mainly composed of fine lamellar colonies（~50 μm）,γ grains and Ni-ridied τ_3 phase.After heat treatment at 1380℃,the Ni-containing alloy is characterized by fine fully lamellar micro structure（~90 μm）.The heat-treated Ni-containing specimen exhibits superior room temperature tensile properties than other specimens.The tensile properties are discussed in light of the microstructure evolution and role of Ni-riched τ_3 phase.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.51001040,51371064 and 51504075)the Shanghai Aerospace Science and Technology Innovation Fund(No.SAST201428)
文摘The effects of Ni addition on solidification micro structure and tensile properties of Ti-48Al-2Cr-2Nb alloy were investigated using differential scanning calorimetry（DSC）,X-ray diffraction（XRD）,scanning electron microscopy（SEM） equipped with energy-dispersive spectroscope（EDS） and transmission electron microscopy（TEM）.Results show that with 3 at%Ni addition,the as-cast micro structure is mainly composed of fine lamellar colonies（~50 μm）,γ grains and Ni-ridied τ_3 phase.After heat treatment at 1380℃,the Ni-containing alloy is characterized by fine fully lamellar micro structure（~90 μm）.The heat-treated Ni-containing specimen exhibits superior room temperature tensile properties than other specimens.The tensile properties are discussed in light of the microstructure evolution and role of Ni-riched τ_3 phase.