Pitch and TiB2/C green composite cathode material were respectively analyzed with simultaneous DSC-TGA, and effects of three baking processes of TiB2/C composite cathode material, i.e. K25, K5 and M5, on properties of...Pitch and TiB2/C green composite cathode material were respectively analyzed with simultaneous DSC-TGA, and effects of three baking processes of TiB2/C composite cathode material, i.e. K25, K5 and M5, on properties of TiB2/C composite cathode material were investigated. The results show that thermogravimetrie behavior of pitch and TiB2/C green composite cathode is similar, and appears the largest mass loss rate in the temperature range from 200 to 600 ℃. The bulk density variation of sample K5 before and after baking is the largest （11.9%）, that of sample K25 is the second, and that of sample M5 is the smallest （6.7%）. The crushing strength of sample M5 is the biggest （51.2 MPa）, that of sample K2.5 is the next, and that of sample K5 is the smallest （32.8 MPa）. But, the orders of the electrical resistivity and electrolysis expansion of samples are just opposite with the order of crushing strength. The heating rate has a great impact on the microstructure of sample. The faster the heating rate is, the bigger the pore size and porosity of sample are. Compared with the heating rate between 200 and 600℃ of samples K25 and K5, that of sample M5 is slower and suitable for baking process of TiB2/C composite cathode material.展开更多
Ag/SnO2,as a promising and environment-friendly electrical contact material,is widely applied in low-voltage apparatus.But the properties of Ag/SnO2 composites is difficult to improve due to the poor distribution phas...Ag/SnO2,as a promising and environment-friendly electrical contact material,is widely applied in low-voltage apparatus.But the properties of Ag/SnO2 composites is difficult to improve due to the poor distribution phases and difficult component design.In this work,the Ag/SnO2 composites are prepared by selective laser melting.To get better performance,Ag/SnO2 composites with different energy density were studied.The microstructure was observed by field emission scanning electron microscope.In addition,reinforced SnO2 phase was characterized by X-ray diffraction and transmission electron microscope.The results indicated that the microstructure,relative density and hardness of are influenced by energy density,while Ag/SnO2 composites with homogeneous microstructure,high relative density,higher hardness and lower electrical resistivity can be obtained by proper energy density(E?68 J/mm^3).展开更多
B_(4)C/Al composites are widely utilized as neutron absorbing materials for the storage and transportation of spent nuclear fuel.In order to improve the high-temperature mechanical properties of B_(4)C/Al composites,i...B_(4)C/Al composites are widely utilized as neutron absorbing materials for the storage and transportation of spent nuclear fuel.In order to improve the high-temperature mechanical properties of B_(4)C/Al composites,in-situ nano-Al_(2)O_(3)was introduced utilizing oxide on Al powder surface.In this study,the Al_(2)O_(3)content was adjusted by utilizing spheroid Al powder with varying diameters,thereby investigating the impact of Al_(2)O_(3)content on the tensile properties of(B_(4)C+Al_(2)O_(3))/Al composites.It was found that the pinning effect of Al_(2)O_(3)on the grain boundaries could hinder the recovery of dislocations and lead to dislocation accumulation at high temperature.As the result,with the increase in Al_(2)O_(3)content and the decrease in grain size,the high-temperature strength of the composites increased significantly.The finest Al powder used in this investigation had a diameter of 1.4μm,whereas the resultant composite exhibited a maximum strength of 251 MPa at room temperature and 133 MPa at 350℃,surpassing that of traditional B_(4)C/Al composites.展开更多
Compound Zn2Sn0.8Ti0.2O4 was synthesized by a hydrothermal method in which SnCl4-5H2O,TiCl4,ZnCl2 and N2H4-H2O were used as reactants.The composite Zn2Sn0.8Ti0.2O4/C was then prepared through a carbothermic reduction ...Compound Zn2Sn0.8Ti0.2O4 was synthesized by a hydrothermal method in which SnCl4-5H2O,TiCl4,ZnCl2 and N2H4-H2O were used as reactants.The composite Zn2Sn0.8Ti0.2O4/C was then prepared through a carbothermic reduction process using the as-prepared Zn2Sn0.8Ti0.2O4 and glucose as reactants.The structure,morphology and electrochemical properties of the as-prepared products were investigated by XRD,XPS,TEM and electrochemical measurements.In addition,electrochemical Li insertion/extraction in composite Zn2Sn0.8Ti0.2O4/C were examined by ex situ XRD and SEM.The first discharge capacity of Zn2SnO4 is about 1670.8 mA-h/g,with a capacity retain of 342.7 mA-h/g in the 40th cycle at a constant current density of 100 mA/g in the voltage range of 0.05-3.0 V.Comparing with the Zn2SnO4,some improved electrochemical properties are obtained for Zn2Sn0.8Ti0.2O4,Zn2SnO4/C and Zn2Sn0.8Ti0.2O4/C.The composite Zn2Sn0.8Ti0.2O4/C shows the best electrochemical properties,and its first discharge capacity is about 1530.0 mA-h/g,with a capacity retain of 479.1 mA-h/g the 100th cycle.展开更多
基金Project (2005CB623703) supported by the Major State Basic Research and Development Program of ChinaProject (2008AA030502) supported by the National High-Tech Research and Development Program of China
文摘Pitch and TiB2/C green composite cathode material were respectively analyzed with simultaneous DSC-TGA, and effects of three baking processes of TiB2/C composite cathode material, i.e. K25, K5 and M5, on properties of TiB2/C composite cathode material were investigated. The results show that thermogravimetrie behavior of pitch and TiB2/C green composite cathode is similar, and appears the largest mass loss rate in the temperature range from 200 to 600 ℃. The bulk density variation of sample K5 before and after baking is the largest （11.9%）, that of sample K25 is the second, and that of sample M5 is the smallest （6.7%）. The crushing strength of sample M5 is the biggest （51.2 MPa）, that of sample K2.5 is the next, and that of sample K5 is the smallest （32.8 MPa）. But, the orders of the electrical resistivity and electrolysis expansion of samples are just opposite with the order of crushing strength. The heating rate has a great impact on the microstructure of sample. The faster the heating rate is, the bigger the pore size and porosity of sample are. Compared with the heating rate between 200 and 600℃ of samples K25 and K5, that of sample M5 is slower and suitable for baking process of TiB2/C composite cathode material.
基金sponsored by the Natural Science Foundation of China (Grant nos. 51775208)the Hubei Science Fund for Distinguished Young Scholars (No. 0216110085)+2 种基金the National Key Research and Development Program “Additive Manufacturing and Laser Manufacturing”(No. 2016YFB1100101)Wuhan Morning Light Plan of Youth Science and Technology (No. 0216110066)the Academic frontier youth team at Huazhong University of Science and Technology (HUST)
文摘Ag/SnO2,as a promising and environment-friendly electrical contact material,is widely applied in low-voltage apparatus.But the properties of Ag/SnO2 composites is difficult to improve due to the poor distribution phases and difficult component design.In this work,the Ag/SnO2 composites are prepared by selective laser melting.To get better performance,Ag/SnO2 composites with different energy density were studied.The microstructure was observed by field emission scanning electron microscope.In addition,reinforced SnO2 phase was characterized by X-ray diffraction and transmission electron microscope.The results indicated that the microstructure,relative density and hardness of are influenced by energy density,while Ag/SnO2 composites with homogeneous microstructure,high relative density,higher hardness and lower electrical resistivity can be obtained by proper energy density(E?68 J/mm^3).
基金supported by the National Key R&D Program of China(Grant No.2023YFB3710601)the National Natural Science Foundation of China(Grant Nos.52203385 and 52171056)+2 种基金the CNNC Science Fund for Talented Young Scholars,the Institute of Metal Research(IMR)Innovation Fund(Grant No.2021-ZD02)the Natural Science Foundation of Liaoning Province(Grant No.2022-BS-009)Young Elite Scientists Sponsorship Program by CAST(Grant No.YESS20220225).
文摘B_(4)C/Al composites are widely utilized as neutron absorbing materials for the storage and transportation of spent nuclear fuel.In order to improve the high-temperature mechanical properties of B_(4)C/Al composites,in-situ nano-Al_(2)O_(3)was introduced utilizing oxide on Al powder surface.In this study,the Al_(2)O_(3)content was adjusted by utilizing spheroid Al powder with varying diameters,thereby investigating the impact of Al_(2)O_(3)content on the tensile properties of(B_(4)C+Al_(2)O_(3))/Al composites.It was found that the pinning effect of Al_(2)O_(3)on the grain boundaries could hinder the recovery of dislocations and lead to dislocation accumulation at high temperature.As the result,with the increase in Al_(2)O_(3)content and the decrease in grain size,the high-temperature strength of the composites increased significantly.The finest Al powder used in this investigation had a diameter of 1.4μm,whereas the resultant composite exhibited a maximum strength of 251 MPa at room temperature and 133 MPa at 350℃,surpassing that of traditional B_(4)C/Al composites.
基金Project (51004028) supported by the National Natural Science Foundation of China
文摘Compound Zn2Sn0.8Ti0.2O4 was synthesized by a hydrothermal method in which SnCl4-5H2O,TiCl4,ZnCl2 and N2H4-H2O were used as reactants.The composite Zn2Sn0.8Ti0.2O4/C was then prepared through a carbothermic reduction process using the as-prepared Zn2Sn0.8Ti0.2O4 and glucose as reactants.The structure,morphology and electrochemical properties of the as-prepared products were investigated by XRD,XPS,TEM and electrochemical measurements.In addition,electrochemical Li insertion/extraction in composite Zn2Sn0.8Ti0.2O4/C were examined by ex situ XRD and SEM.The first discharge capacity of Zn2SnO4 is about 1670.8 mA-h/g,with a capacity retain of 342.7 mA-h/g in the 40th cycle at a constant current density of 100 mA/g in the voltage range of 0.05-3.0 V.Comparing with the Zn2SnO4,some improved electrochemical properties are obtained for Zn2Sn0.8Ti0.2O4,Zn2SnO4/C and Zn2Sn0.8Ti0.2O4/C.The composite Zn2Sn0.8Ti0.2O4/C shows the best electrochemical properties,and its first discharge capacity is about 1530.0 mA-h/g,with a capacity retain of 479.1 mA-h/g the 100th cycle.