Sb-doped SnO2(ATO)-(CeO2-TiO2)thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using low...Sb-doped SnO2(ATO)-(CeO2-TiO2)thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using low-temperature hydrothermal process.The mixed molar ratio of ATO to(CeO2-TiO2)vs the properties of CeO2-TiO2 thin film was investigated.The optical properties of the films were characterized by UV-visible transmission and infrared reflection spectra,the sheet resistance of ATO particles and films were measured by rubber sheeter(MYI-50)and four-point probe(HisuperGroup Inc,SDY-5),the surface morphology and structure of the films were analyzed using 3D Digitale Mikroskop and X-ray diffraction(XRD),respectively.The results showed that the ATO precursor solution lost weight completely at about 500 oC,and the ATO particles was obtained,which indicated the same rutile lattice structure as SnO2.The glass substrates coated with ATO-(CeO2-TiO2)thin films showed better properties in antistatic electricity(104-106Ω/),shielding UV(almost 100%),visible light transmission(70%)and infrared reflection(】30%).展开更多
(PEO)8LiClO4-SiO2 composite polymer electrolytes(CPEs)were prepared by in-situ reaction,in which ethyl-orthosilicate(TEOS)was catalyzed by HCl and NH3.H2O,respectively.The ionic conductivity,the contact angle and the ...(PEO)8LiClO4-SiO2 composite polymer electrolytes(CPEs)were prepared by in-situ reaction,in which ethyl-orthosilicate(TEOS)was catalyzed by HCl and NH3.H2O,respectively.The ionic conductivity,the contact angle and the morphology of inorganic particles in the CPEs were investigated by AC impedance spectra,contact angle method and TEM.The conductivities of acid-catalyzed CPE and alkali-catalyzed CPE are 2.2×10-5and 1.1×10-5S/cm respectively at 30℃.The results imply that the catalyst plays an important role in the structure of in-situ preparation of SiO2,and influences the surface energy and conductivity of CPE films directly.Meanwhile,the ionic conductivity is related to the surface energy.展开更多
Fe2O3/SiO2 nano-composite films were prepared by sol-gel technique combining heat treatment in the range of 100-900 ℃. The particle size was observed by FE-SEM. Optical properties of the films were investigated by UV...Fe2O3/SiO2 nano-composite films were prepared by sol-gel technique combining heat treatment in the range of 100-900 ℃. The particle size was observed by FE-SEM. Optical properties of the films were investigated by UV-visible spectra. Structural and magnetic characteristics were investigated through FT-IR and VSM. The transparency of the Fe2O3/SiO2 nano-composite films decreased with the content of the Fe2O3. Water and organic solvent in the films were evaporated with heat treatment, so the transparency of the films was enhanced under high temperature. It is also found that the saturation magnetization （Ms） of the films increases with the temperature. As the content of the Fe2O3 increases, when the content of the Fe2O3 is around 30wt%, the Ms of the films has a maximum value.展开更多
Total dose effects and single event effects on radiation-hardened power vertical double-diffusion metal oxide semiconductor（VDMOS） devices with composite SiO2-Si3N4 film gates are investigated.The relationships amon...Total dose effects and single event effects on radiation-hardened power vertical double-diffusion metal oxide semiconductor（VDMOS） devices with composite SiO2-Si3N4 film gates are investigated.The relationships among the important electrical parameters of the samples with different thickness SiO2-Si3N4 films,such as threshold voltage,breakdown voltage,and on-state resistance in accumulated dose,are discussed.The total dose experiment results show that the breakdown voltage and the on-state resistance barely change with the accumulated dose.However,the relationships between the threshold voltages of the samples and the accumulated dose are more complex,and not only positively drift,but also negatively drift.At the end of the total dose experiment,we select the group of samples which have the smaller threshold voltage shift to carry out the single event effect studies.We find that the samples with appropriate thickness ratio SiO2-Si3N4 films have a good radiation-hardening ability.This method may be useful in solving both the SEGR and the total dose problems with the composite SiO2-Si3N4 films.展开更多
This paper reports that single-layer and graded Au-TiO2 granular composite films with Au atom content 15%- 66% were prepared by using reactive co-sputtering technique. The third-order optical nonlinearity of single-la...This paper reports that single-layer and graded Au-TiO2 granular composite films with Au atom content 15%- 66% were prepared by using reactive co-sputtering technique. The third-order optical nonlinearity of single-layer and graded composite films was investigated by using s- and p-polarized Z-scans in femtosecond time scale. The nonlinear absorption coefficient βeff of single-layer Au-TiO2 films is measured to be -2.3×10^3-0.76×10^3 cm/GW with Au atom content 15%-66%. The βeff value of the 10-layer Au-TiO2 graded film is enhanced to be -2.1×10^4cm/GW calculated from p-polarized Z-scans, which is about ten times the maximum βeff of single-layer films. Broadened response in the wavelength region 730-860 nm of the enhanced optical nonlinearity of graded Au-TiO2 composite films was also investigated.展开更多
In the present work, structure changes during （SiO2） composites have been investigated systematically stretching of isotactic polypropylene （iPP） and iPP/silicon dioxide The or-form crystal structure of both iPP a...In the present work, structure changes during （SiO2） composites have been investigated systematically stretching of isotactic polypropylene （iPP） and iPP/silicon dioxide The or-form crystal structure of both iPP and iPP/SiO2 composites is destroyed and transforms into the mesophase as the samples are stretched at a low temperature （35℃）, while stretching at high temperatures （90℃ and 120℃） can restrain the appearance of defects and keep the perfection of crystal structure. FTIR results reveal that the stretching temperatures show no obvious difference of the effect on the orientation of pure iPP, however, the orientation of iPP/SiO2 composites is greatly changed by the tensile temperature. In the case of micron-sized SiO2 particles （average particle diameter d 〉 1 μm）, the orientation of the composites is lower than that of pure iPP at all stretching temperatures. The above results suggest that the stretching temperature and the SiO2 particle size have great influence on the structure variation and orientation behavior of iPP/SiO2 composites.展开更多
Nano metal-particle dispersed glasses are the attractive candidates for nonlinear optical material applications. Au/SiO2 nano-composite thin films with 3 vol% to 65 vol% Au are prepared by inductively coupled plasma s...Nano metal-particle dispersed glasses are the attractive candidates for nonlinear optical material applications. Au/SiO2 nano-composite thin films with 3 vol% to 65 vol% Au are prepared by inductively coupled plasma sputtering. Au particles as perfect spheres with diameters between 10 nm and 30 nm are uniformly dispersed in the SiO2 matrix. Optical absorption peaks due to the surface plasmon resonance of Au particles are observed. The absorption property is enhanced with the increase of Au content, showing a maximum value in the films with 37 vol% Au. The absorption curves of the Au/SiO2 thin films with 3 vol% to 37 vol% Au accord well with the theoretical optical absorption spectra obtained from Mie resonance theory. Increasing Au content over 37 vol% results in the partial connection of Au particles, whereby the intensity of the absorption peak is weakened and ultimately replaced by the optical absorption of the bulk. The band gap decreases with Au content increasing from 3 vol% to 37 vol % but increases as Au content further increases.展开更多
To mitigate secondary electromagnetic pollution,there is an urgent need to develop absorption-dominant electromagnetic interference(EMI)shielding materials with low density,reduced thickness,lightweight construction,f...To mitigate secondary electromagnetic pollution,there is an urgent need to develop absorption-dominant electromagnetic interference(EMI)shielding materials with low density,reduced thickness,lightweight construction,flexibility,exceptional mechanical strength,and superior electrothermal and photothermal properties,particularly for flexible and wearable electronics.In this regard,we designed an absorption-based composite film comprising carbon nanotubes(CNT)and α-Fe_(2)O_(3),featuring a CNT layer sandwiched between twoα-Fe_(2)O_(3)layers on the upper and lower surfaces.This composite film was fabricated through an electrodeposition process followed by a thermal annealing procedure to achieve enhanced EMI shielding performance along with improved electrothermal and photothermal properties.The strategically designed sandwich structure allows the rough surface of the upper α-Fe_(2)O_(3)layer to not only improve the impedance mismatch between free space and the composite film,facilitating the penetration of incident electromagnetic(EM)waves into the film and promoting increased EM absorption rather than reflection,but also to enhance electrical conductivity,thereby improving electron mobility and density.Consequently,the average total shielding effectiveness(SE)of the CNT/Fe_(16)-300 composite demonstrates remarkable EMI shielding effectiveness(EMI SE:56.8 dB).Furthermore,the alteration in the absorption-to-reflection ratio(A/R)signifies a transition in the EMI shielding mechanism from reflection(0.69 for the pristine CNT film)to absorption(1.86 for the CNT/Fe_(16)-300)with the incremental deposition of α-Fe_(2)O_(3)nanoparticles.This work presents a feasible manufacturing approach for developing composite films with a sandwich structure that exhibits absorption-dominant EMI shielding capabilities,contributing to advancements in thermal management and multifunctional electromagnetic shielding applications.展开更多
The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The c...The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.展开更多
Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XR...Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, ultraviolet- visible spectroscopy （UV-Vis） and photoluminescence spectroscopy （PL）. The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange （MO） aqueous solution under visible light irradiation. The results indicate that the Cu2O/TiO2/Pt composite films are made up of three layers which are Pt layer, anatase-TiO2 layer and Cu2O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu2O/TiO2/Pt three-layer film is much higher than that of the Cu2O/TiO2 double-layer film. Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombination, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.展开更多
A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion...A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion behavior of the NiP/TiO2 composite film was investigated by polarization resistance measurement, anode polarization, ESEM （environmental scanning electron microscopy） and EIS （electrochemical impedance spectroscopy） measurements. Results showed that the NiP/ TiO2 composite film has a good corrosion resistance in 0.5mol/L H2SO4 solution. The element valence of the composite film was characterized by XPS （X-ray photoelectron spectroscopy） spectrum, and an anticorrosion mechanism of the composite film was discussed.展开更多
Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire and Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire composite films were successfully prepared using a hydrothermal method.The results show that the light absorption for Bi_(2)WO_(6)/T...Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire and Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire composite films were successfully prepared using a hydrothermal method.The results show that the light absorption for Bi_(2)WO_(6)/TiO_(2) composite films is extended to the visible region after Bi_(2)WO_(6) nanoplates and nanoflowers are assembled onto TiO_(2) nanowires.Furthermore,Bi_(2)WO_(6) nanoflower/TiO_(2) nano wire composite film exhibits a better absorption property compared to Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire film,which is mainly ascribed to the narrower bandgap of Bi_(2)WO_(6) nanoflower compared to that of Bi_(2)WO_(6) nanoplate.The photocurrent density for Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire and Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire composite films can reach 95 and 62.5 μA cm-2,respectively,which are much higher than that obtained for a pure TiO_(2) nanowire film(25 μA cm-2).Meanwhile,under illumination,the pure TiO_(2) nanowire,Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire and Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire films can reduce the potential of the coupled 304 stainless steel in 3.5 wt.%NaCl solution by 299,719 and 739 mV,respectively.Thus,Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire film is found to provide the best effective photocathodic protection for 304 stainless steel.This work not only provides an example of shape-dependent photocathodic protection based on Bi_(2)WO_(6) but also opens up new possibilities to design an ideal microstructure on the basis of semiconductor materials for future applications of photocathodic protection.展开更多
ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （...ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.展开更多
In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performanc...In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performance reliability was examined. The prepared TiO2/Ti composite films showed high photocatalytic activity in the degradation of methylene blue solution. It is obvious that? TiO2/Ti composite films have antibacterial activity under UV irradiation.展开更多
MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage ...MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage on the composite film properties,including adhesion strength,micro-hardness,thickness and tribological properties were investigated.The results showed that proper negative bias voltage could significantly improve the mechanical and tribological properties of composite films.The effects of negative bias voltage on film properties were also put forward.The optimal negative bias voltage was -200 V under this experiment conditions.The obtained composite films were dense,the adhesion strength was about 60 N,the thickness was about 2.4 μm,and the micro-hardness was about 9.0 GPa.The friction coefficient and wear rate was 0.12 and 2.1×10-7 cm3/N·m respectively after 60 m sliding operation against hardened steel under a load of 20 N and a sliding speed of 200 rev·min-1.展开更多
Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO...Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.展开更多
In this work, CaF_2:Ln^(3+)(Ln:Er,Er/Yb)/Nafion composite films were prepared using Nafion as modifications and matrices by dripping method. The composite films were characterized by Fourier transform infrared spectro...In this work, CaF_2:Ln^(3+)(Ln:Er,Er/Yb)/Nafion composite films were prepared using Nafion as modifications and matrices by dripping method. The composite films were characterized by Fourier transform infrared spectroscopy(FT-IR), X-ray diffraction(XRD) and scanning electron microscopy(SEM). Composite films are transparent and CaF_2:Ln^(3+)(Ln:Er,Er/Yb) nanoparticles are well dispersed in Nafion films.The thicknesses of CaF_2:Er^(3+)/Nafion and CaF_2:Er^(3+),Yb^(3+)/Nafion composite film are about 77 and 73 μm,respectively. The nanoparticles in composite film possess cubic phase. CaF_2:Er^(3+),Yb^(3+)/Nafion composite film has stronger characteristic emission of Er^(3+) around 1530 nm with full width at half-maximum(FWHM) of 73 nm and longer luminescence lifetimes of 22.04 μs(25.03%) and 100.77 μs(74.97%).展开更多
The cycling characteristics and low specific capacity of LiMn2O4 have always been the greatest obstacle to its commercialization. For the improvement of cyc le performance,the surface of LiCo0.05Mn1.95O4 was coated wi...The cycling characteristics and low specific capacity of LiMn2O4 have always been the greatest obstacle to its commercialization. For the improvement of cyc le performance,the surface of LiCo0.05Mn1.95O4 was coated with ve ry fine SiO2-TiO2 composite prepared by sol-gel method. The structure and morphology of the coating materials were investigated by X-ray diffraction （XRD ） and scanning electron microscope （SEM）. The electrochemical performances of un coated and SiO2-TiO2 coated LiCo0.05Mn1.95O4 spinel at 25 ℃ and 55 ℃ were studied with a voltage range of 3.04.35V and a current density of 0.1 mA/cm2. There is a slight decrease in the initial discharge ca pacity of coated LiCo0.05Mn1.95O4（119 mA·h/g） compared with that of uncoated （123 mA·h/g）. However the cycle ability of LiCo0.05Mn1. 95O4 coated by SiO2-TiO2 is improved. It is proposed that surface treat ment is an effective method to improve the cycle performance of LiCo0.05Mn 1.95O4. The surface modification is successful in minimizing the harmful side reactions within the batteries by placing a protective barrier layer betwe en the oxidizing cathode material and the liquid electrolyte.展开更多
Nano sized powders of TiO2 （titanium dioxide） and Nb2O5 （Niobium （V） oxide） were used to fabricate TiO2/Nb2O5 composites thin films by EPD （electrophoretic deposition） technique. The metal oxide powders, toget...Nano sized powders of TiO2 （titanium dioxide） and Nb2O5 （Niobium （V） oxide） were used to fabricate TiO2/Nb2O5 composites thin films by EPD （electrophoretic deposition） technique. The metal oxide powders, together with magnesium nitrate hexahydrate pellets, were suspended in propan-2-ol inside an EPD cell. The electrodes, placed 1.2 cm apart, were partially immersed in the suspension and a DC potential applied across them. Key EPD process parameters, which include applied DC electric field, deposition time and solid concentration in suspension, were optimized through visual inspection and from UV-Vis-NIR spectrophotometer spectra. The highest （55%） transmittance was obtained for films with deposition time of 90 s, powder concentration of 0.01 g/40 mL, and 35 V DC （direct current） voltage. XRD micrographs confirmed that TiO2 and Nb2O5 particles were presented in the composite film. SEM （scanning electron microscope） micrographs of the composite electrode thin films showed that porous films of high quality with well controlled morphology were deposited by using the EPD technique.展开更多
基金Project supported by the Changjiang Scholars and Innovative Research Team in University
文摘Sb-doped SnO2(ATO)-(CeO2-TiO2)thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using low-temperature hydrothermal process.The mixed molar ratio of ATO to(CeO2-TiO2)vs the properties of CeO2-TiO2 thin film was investigated.The optical properties of the films were characterized by UV-visible transmission and infrared reflection spectra,the sheet resistance of ATO particles and films were measured by rubber sheeter(MYI-50)and four-point probe(HisuperGroup Inc,SDY-5),the surface morphology and structure of the films were analyzed using 3D Digitale Mikroskop and X-ray diffraction(XRD),respectively.The results showed that the ATO precursor solution lost weight completely at about 500 oC,and the ATO particles was obtained,which indicated the same rutile lattice structure as SnO2.The glass substrates coated with ATO-(CeO2-TiO2)thin films showed better properties in antistatic electricity(104-106Ω/),shielding UV(almost 100%),visible light transmission(70%)and infrared reflection(】30%).
文摘(PEO)8LiClO4-SiO2 composite polymer electrolytes(CPEs)were prepared by in-situ reaction,in which ethyl-orthosilicate(TEOS)was catalyzed by HCl and NH3.H2O,respectively.The ionic conductivity,the contact angle and the morphology of inorganic particles in the CPEs were investigated by AC impedance spectra,contact angle method and TEM.The conductivities of acid-catalyzed CPE and alkali-catalyzed CPE are 2.2×10-5and 1.1×10-5S/cm respectively at 30℃.The results imply that the catalyst plays an important role in the structure of in-situ preparation of SiO2,and influences the surface energy and conductivity of CPE films directly.Meanwhile,the ionic conductivity is related to the surface energy.
基金Funded by the Innovative Program of Shanghai Municipal Education Commission (No.08YZ97)the National Natural Science Foundation of China (No.10704048)
文摘Fe2O3/SiO2 nano-composite films were prepared by sol-gel technique combining heat treatment in the range of 100-900 ℃. The particle size was observed by FE-SEM. Optical properties of the films were investigated by UV-visible spectra. Structural and magnetic characteristics were investigated through FT-IR and VSM. The transparency of the Fe2O3/SiO2 nano-composite films decreased with the content of the Fe2O3. Water and organic solvent in the films were evaporated with heat treatment, so the transparency of the films was enhanced under high temperature. It is also found that the saturation magnetization （Ms） of the films increases with the temperature. As the content of the Fe2O3 increases, when the content of the Fe2O3 is around 30wt%, the Ms of the films has a maximum value.
文摘Total dose effects and single event effects on radiation-hardened power vertical double-diffusion metal oxide semiconductor（VDMOS） devices with composite SiO2-Si3N4 film gates are investigated.The relationships among the important electrical parameters of the samples with different thickness SiO2-Si3N4 films,such as threshold voltage,breakdown voltage,and on-state resistance in accumulated dose,are discussed.The total dose experiment results show that the breakdown voltage and the on-state resistance barely change with the accumulated dose.However,the relationships between the threshold voltages of the samples and the accumulated dose are more complex,and not only positively drift,but also negatively drift.At the end of the total dose experiment,we select the group of samples which have the smaller threshold voltage shift to carry out the single event effect studies.We find that the samples with appropriate thickness ratio SiO2-Si3N4 films have a good radiation-hardening ability.This method may be useful in solving both the SEGR and the total dose problems with the composite SiO2-Si3N4 films.
基金Project supported by the National Natural Science Foundation of China (Grant No 10474075)
文摘This paper reports that single-layer and graded Au-TiO2 granular composite films with Au atom content 15%- 66% were prepared by using reactive co-sputtering technique. The third-order optical nonlinearity of single-layer and graded composite films was investigated by using s- and p-polarized Z-scans in femtosecond time scale. The nonlinear absorption coefficient βeff of single-layer Au-TiO2 films is measured to be -2.3×10^3-0.76×10^3 cm/GW with Au atom content 15%-66%. The βeff value of the 10-layer Au-TiO2 graded film is enhanced to be -2.1×10^4cm/GW calculated from p-polarized Z-scans, which is about ten times the maximum βeff of single-layer films. Broadened response in the wavelength region 730-860 nm of the enhanced optical nonlinearity of graded Au-TiO2 composite films was also investigated.
基金financially supported by the National Natural Science Foundation of China (Nos. 51073004 and 21074141)the China National Funds for Distinguished Young Scientists (No. 50925313)
文摘In the present work, structure changes during （SiO2） composites have been investigated systematically stretching of isotactic polypropylene （iPP） and iPP/silicon dioxide The or-form crystal structure of both iPP and iPP/SiO2 composites is destroyed and transforms into the mesophase as the samples are stretched at a low temperature （35℃）, while stretching at high temperatures （90℃ and 120℃） can restrain the appearance of defects and keep the perfection of crystal structure. FTIR results reveal that the stretching temperatures show no obvious difference of the effect on the orientation of pure iPP, however, the orientation of iPP/SiO2 composites is greatly changed by the tensile temperature. In the case of micron-sized SiO2 particles （average particle diameter d 〉 1 μm）, the orientation of the composites is lower than that of pure iPP at all stretching temperatures. The above results suggest that the stretching temperature and the SiO2 particle size have great influence on the structure variation and orientation behavior of iPP/SiO2 composites.
基金Project supported by the National Natural Science Foundation of China (Grant Nos 50842028 and 50972012)the National Basic Research Program of China (Grant No 2007CB613301)
文摘Nano metal-particle dispersed glasses are the attractive candidates for nonlinear optical material applications. Au/SiO2 nano-composite thin films with 3 vol% to 65 vol% Au are prepared by inductively coupled plasma sputtering. Au particles as perfect spheres with diameters between 10 nm and 30 nm are uniformly dispersed in the SiO2 matrix. Optical absorption peaks due to the surface plasmon resonance of Au particles are observed. The absorption property is enhanced with the increase of Au content, showing a maximum value in the films with 37 vol% Au. The absorption curves of the Au/SiO2 thin films with 3 vol% to 37 vol% Au accord well with the theoretical optical absorption spectra obtained from Mie resonance theory. Increasing Au content over 37 vol% results in the partial connection of Au particles, whereby the intensity of the absorption peak is weakened and ultimately replaced by the optical absorption of the bulk. The band gap decreases with Au content increasing from 3 vol% to 37 vol % but increases as Au content further increases.
基金financially supported by the National Natural Science Foundation of China(Nos.52222202 and 51772310)Chinese Academy of Sciences Key Research Program of Frontier Sciences(No.QYZDY-SSWJSC031)Shanghai Pilot Program for Basic Research-Chinese Academy of Science,Shanghai Branch(No.JCYJ-SHFY-2021-001).
文摘To mitigate secondary electromagnetic pollution,there is an urgent need to develop absorption-dominant electromagnetic interference(EMI)shielding materials with low density,reduced thickness,lightweight construction,flexibility,exceptional mechanical strength,and superior electrothermal and photothermal properties,particularly for flexible and wearable electronics.In this regard,we designed an absorption-based composite film comprising carbon nanotubes(CNT)and α-Fe_(2)O_(3),featuring a CNT layer sandwiched between twoα-Fe_(2)O_(3)layers on the upper and lower surfaces.This composite film was fabricated through an electrodeposition process followed by a thermal annealing procedure to achieve enhanced EMI shielding performance along with improved electrothermal and photothermal properties.The strategically designed sandwich structure allows the rough surface of the upper α-Fe_(2)O_(3)layer to not only improve the impedance mismatch between free space and the composite film,facilitating the penetration of incident electromagnetic(EM)waves into the film and promoting increased EM absorption rather than reflection,but also to enhance electrical conductivity,thereby improving electron mobility and density.Consequently,the average total shielding effectiveness(SE)of the CNT/Fe_(16)-300 composite demonstrates remarkable EMI shielding effectiveness(EMI SE:56.8 dB).Furthermore,the alteration in the absorption-to-reflection ratio(A/R)signifies a transition in the EMI shielding mechanism from reflection(0.69 for the pristine CNT film)to absorption(1.86 for the CNT/Fe_(16)-300)with the incremental deposition of α-Fe_(2)O_(3)nanoparticles.This work presents a feasible manufacturing approach for developing composite films with a sandwich structure that exhibits absorption-dominant EMI shielding capabilities,contributing to advancements in thermal management and multifunctional electromagnetic shielding applications.
基金Sponsored by Hi-Tech Research and Development Program of China (2003AA305120)
文摘The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.
基金financially supported by the National Natural Science Foundation of China (No.51301118)the Projects of International Cooperation in Shanxi (No.2014081002)the Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi (No.2013108)
文摘Cu2O/TiOa/Pt three-layer films were deposited on glass substrates using magnetron sputtering method. The surface morphology and the optical properties of the composite film were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, ultraviolet- visible spectroscopy （UV-Vis） and photoluminescence spectroscopy （PL）. The photocatalytic activity of the samples was evaluated by the photocatalytic degradation of methyl orange （MO） aqueous solution under visible light irradiation. The results indicate that the Cu2O/TiO2/Pt composite films are made up of three layers which are Pt layer, anatase-TiO2 layer and Cu2O layer from bottom to top. The surface of the films is even and composed of regular-shaped spherical particles. The photocatalytic activity of the Cu2O/TiO2/Pt three-layer film is much higher than that of the Cu2O/TiO2 double-layer film. Such enhancement is ascribed to the presence of Pt layer, which further inhibits the photogenerated electron-hole recombination, prolongs the lifetime of the photogenerated carriers, increases the quantum efficiency and hence improves the photocatalytic activity of the film effectively.
文摘A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion behavior of the NiP/TiO2 composite film was investigated by polarization resistance measurement, anode polarization, ESEM （environmental scanning electron microscopy） and EIS （electrochemical impedance spectroscopy） measurements. Results showed that the NiP/ TiO2 composite film has a good corrosion resistance in 0.5mol/L H2SO4 solution. The element valence of the composite film was characterized by XPS （X-ray photoelectron spectroscopy） spectrum, and an anticorrosion mechanism of the composite film was discussed.
基金supported by the National Natural Science Foundation of China(Nos.51822402,51671044 and 52001051)the National Key Research and Development Program of China(Nos.2019YFA0209901 and 2018YFA0702901)+4 种基金the fund of the State Key Laboratory of Solidification Processing in NWPU(Grant No.SKLSP201902)the Liao Ning Revitalization Talents Program(XLYC1807047)the National MCF Energy R&D Program(No.2018YFE0312400)the Fund of Science and Technology on Reactor Fuel and Materials Laboratory(STRFML-2020-04)the China Postdoctoral Science Foundation(No.2020M670747).
文摘Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire and Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire composite films were successfully prepared using a hydrothermal method.The results show that the light absorption for Bi_(2)WO_(6)/TiO_(2) composite films is extended to the visible region after Bi_(2)WO_(6) nanoplates and nanoflowers are assembled onto TiO_(2) nanowires.Furthermore,Bi_(2)WO_(6) nanoflower/TiO_(2) nano wire composite film exhibits a better absorption property compared to Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire film,which is mainly ascribed to the narrower bandgap of Bi_(2)WO_(6) nanoflower compared to that of Bi_(2)WO_(6) nanoplate.The photocurrent density for Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire and Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire composite films can reach 95 and 62.5 μA cm-2,respectively,which are much higher than that obtained for a pure TiO_(2) nanowire film(25 μA cm-2).Meanwhile,under illumination,the pure TiO_(2) nanowire,Bi_(2)WO_(6) nanoplate/TiO_(2) nanowire and Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire films can reduce the potential of the coupled 304 stainless steel in 3.5 wt.%NaCl solution by 299,719 and 739 mV,respectively.Thus,Bi_(2)WO_(6) nanoflower/TiO_(2) nanowire film is found to provide the best effective photocathodic protection for 304 stainless steel.This work not only provides an example of shape-dependent photocathodic protection based on Bi_(2)WO_(6) but also opens up new possibilities to design an ideal microstructure on the basis of semiconductor materials for future applications of photocathodic protection.
基金Project(gf200901002)supported by the Open Research Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang Hangkong University,China
文摘ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.
文摘In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performance reliability was examined. The prepared TiO2/Ti composite films showed high photocatalytic activity in the degradation of methylene blue solution. It is obvious that? TiO2/Ti composite films have antibacterial activity under UV irradiation.
基金Funded by the National Natural Science Foundation of China (No.51075237)the National Basic Research Program of China (No.2009CB724402)+3 种基金the Taishan Scholar Program of Shandong Provincethe Outstanding Young Scholar Science Foundation of Shandong (No.JQ200917)the National Natural Science Foundation of Shandong (No.ZR2010EZ002)National High Technology Research and Development Program (No.2009AA044303)
文摘MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage on the composite film properties,including adhesion strength,micro-hardness,thickness and tribological properties were investigated.The results showed that proper negative bias voltage could significantly improve the mechanical and tribological properties of composite films.The effects of negative bias voltage on film properties were also put forward.The optimal negative bias voltage was -200 V under this experiment conditions.The obtained composite films were dense,the adhesion strength was about 60 N,the thickness was about 2.4 μm,and the micro-hardness was about 9.0 GPa.The friction coefficient and wear rate was 0.12 and 2.1×10-7 cm3/N·m respectively after 60 m sliding operation against hardened steel under a load of 20 N and a sliding speed of 200 rev·min-1.
文摘Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.
基金Project supported by Natural Science Basic Research Plan in Shaanxi Province of China(No.2018JM2021)Xi'an Science and Technology Plan Project(2016CXWL10,CXY1443WL21)Program of Education Department of Shaanxi Provincial Government(15JK2152)
文摘In this work, CaF_2:Ln^(3+)(Ln:Er,Er/Yb)/Nafion composite films were prepared using Nafion as modifications and matrices by dripping method. The composite films were characterized by Fourier transform infrared spectroscopy(FT-IR), X-ray diffraction(XRD) and scanning electron microscopy(SEM). Composite films are transparent and CaF_2:Ln^(3+)(Ln:Er,Er/Yb) nanoparticles are well dispersed in Nafion films.The thicknesses of CaF_2:Er^(3+)/Nafion and CaF_2:Er^(3+),Yb^(3+)/Nafion composite film are about 77 and 73 μm,respectively. The nanoparticles in composite film possess cubic phase. CaF_2:Er^(3+),Yb^(3+)/Nafion composite film has stronger characteristic emission of Er^(3+) around 1530 nm with full width at half-maximum(FWHM) of 73 nm and longer luminescence lifetimes of 22.04 μs(25.03%) and 100.77 μs(74.97%).
文摘The cycling characteristics and low specific capacity of LiMn2O4 have always been the greatest obstacle to its commercialization. For the improvement of cyc le performance,the surface of LiCo0.05Mn1.95O4 was coated with ve ry fine SiO2-TiO2 composite prepared by sol-gel method. The structure and morphology of the coating materials were investigated by X-ray diffraction （XRD ） and scanning electron microscope （SEM）. The electrochemical performances of un coated and SiO2-TiO2 coated LiCo0.05Mn1.95O4 spinel at 25 ℃ and 55 ℃ were studied with a voltage range of 3.04.35V and a current density of 0.1 mA/cm2. There is a slight decrease in the initial discharge ca pacity of coated LiCo0.05Mn1.95O4（119 mA·h/g） compared with that of uncoated （123 mA·h/g）. However the cycle ability of LiCo0.05Mn1. 95O4 coated by SiO2-TiO2 is improved. It is proposed that surface treat ment is an effective method to improve the cycle performance of LiCo0.05Mn 1.95O4. The surface modification is successful in minimizing the harmful side reactions within the batteries by placing a protective barrier layer betwe en the oxidizing cathode material and the liquid electrolyte.
文摘Nano sized powders of TiO2 （titanium dioxide） and Nb2O5 （Niobium （V） oxide） were used to fabricate TiO2/Nb2O5 composites thin films by EPD （electrophoretic deposition） technique. The metal oxide powders, together with magnesium nitrate hexahydrate pellets, were suspended in propan-2-ol inside an EPD cell. The electrodes, placed 1.2 cm apart, were partially immersed in the suspension and a DC potential applied across them. Key EPD process parameters, which include applied DC electric field, deposition time and solid concentration in suspension, were optimized through visual inspection and from UV-Vis-NIR spectrophotometer spectra. The highest （55%） transmittance was obtained for films with deposition time of 90 s, powder concentration of 0.01 g/40 mL, and 35 V DC （direct current） voltage. XRD micrographs confirmed that TiO2 and Nb2O5 particles were presented in the composite film. SEM （scanning electron microscope） micrographs of the composite electrode thin films showed that porous films of high quality with well controlled morphology were deposited by using the EPD technique.