Gel polymer electrolytes(GPEs) are promising alternatives to liquid electrolytes applied in high-energydensity batteries.Here superior SiO_(2) nanofiber composite gel polymer electrolytes(SNCGPEs) are developed via in...Gel polymer electrolytes(GPEs) are promising alternatives to liquid electrolytes applied in high-energydensity batteries.Here superior SiO_(2) nanofiber composite gel polymer electrolytes(SNCGPEs) are developed via in-situ ionic ring-opening polymerization of 1,3-dioxolane(DOL) monomers in SiO_(2) nanofiber membrane(PDOL-SiO_(2)) for lithium metal batteries.The oxygen atoms of PDOL together with Si-O of SiO_(2) construct a more efficient channel for Li^(+) migration.Consequently,the lithium ion transference number(t_(Li^(+)) and ionic conductivity(σ) at 30℃ of PDOL-SiO_(2) are 0.80 and 1.68×10^(-4)S/cm separately.PDOL-SiO_(2) manifests the electrochemical decomposition potentials of 4.90 V.At 0.5 mA/cm^(2),Li|PDOL-SiO_(2) |Li cell shows a steady cycling performance for nearly 1400 h.LFP|PDOL-SiO_(2) |Li battery can steadily cycle at 0.5 C with a capacity retention rate of 89% after 200 cycles.While cycling at 2 C,the capacity retention rate can maintain at 78% after 300 cycles.This contribution provides a innovative strategy for accelerating Li^(+)transportation via designing PDOL molecular chains throughout the SiO_(2) nanofiber framework,which is crucial for high-energy-density LMBs.展开更多
[Zn(CH3COO)2 + PVP]/[C2H5O)4Si + PVP]/[SnCl4 + PVP]/[Ti(OC4H9)4 + CH3COOH + PVP] precursor composite fibers have been fabricated through self-made electrospinning equipment via electrospinning tech-nique. ZnO/SiO2/SnO...[Zn(CH3COO)2 + PVP]/[C2H5O)4Si + PVP]/[SnCl4 + PVP]/[Ti(OC4H9)4 + CH3COOH + PVP] precursor composite fibers have been fabricated through self-made electrospinning equipment via electrospinning tech-nique. ZnO/SiO2/SnO2/TiO2 composite nanofibers were obtained by calcination of the relevant precursor composite fibers. The samples were characterized by thermogravimetric-differential thermal analysis (TG-DTA), X-ray diffractometry (XRD), Fourier transform infrared spectroscopy (FTIR), and Scanning electron microscopy (SEM). TG-DTA analysis reveals that solvents, organic compounds and inorganic in the precursor composite fibers are decomposed and volatilized totally, and the mass of the samples kept constant when sintering temperature was above 900?C, and the total mass loss percentage is 88%. XRD results show that the precursor composite fibers are amorphous in structure, and pure phase ZnO/SiO2/SnO2/TiO2 com-posite nanofibers are obtained by calcination of the relevant precursor composite fibers. FTIR analysis manifests that pure inorganic oxides are formed. SEM analysis indicates that the width of the precursor composite fibers is ca. 1.485 ± 0.043 μm. The width of the ZnO/SiO2/SnO2/TiO2 composite nanofibers is ca. 1145.098 ± 68.093 nm.展开更多
Porous TiO2/ZnO composite nanofibers have been successfully prepared by electrospinning technique for the first time.It was generated by calcining TiO2/ZnCl2/PVP[PVP：polyvinyl pyrrolidone）]nanofibers,which were elec...Porous TiO2/ZnO composite nanofibers have been successfully prepared by electrospinning technique for the first time.It was generated by calcining TiO2/ZnCl2/PVP[PVP：polyvinyl pyrrolidone）]nanofibers,which were electrospun from a mixture solution of TiO2,ZnCl2 and PVP.Transmission electron microscopy（TEM） and X-ray diffraction（XRD） analyses were used to identify the morphology of the TiO2/ZnO nanofibers and a formation of inorganic TiO2/ZnO fibers.The porous structure of the TiO2/ZnO fibers was characterized by N2 adsoption/desorption isotherm.Surface photovoltage spectroscopy（SPS） and photocatalytic activity measurements revealed advance properties of the porous TiO2/ZnO composite nanofibers and the results were compared with pure TiO2 nanofibers,pure ZnO nanofibers and TiO2/ZnO nanoparticles.展开更多
We report a facile method for the fabrication of TiO2 nanofiber-nanoparticle composite （FP） via. simulta- neous electrospraying and electrospinning for dye-sensitized solar cell （DSC） applications. The loading of ...We report a facile method for the fabrication of TiO2 nanofiber-nanoparticle composite （FP） via. simulta- neous electrospraying and electrospinning for dye-sensitized solar cell （DSC） applications. The loading of nanoparticles on the fibers is controlled by varying their feed rates during electrospinning. The FP composites having three different particle loading are prepared by the methodology and the FP with the highest particle loading （denoted as FP-3 in the manuscript） showed the best overall efficiency of 9.15% in comparison to the other compositions of the FP （FP-2, 8.15% and FP-1, Z51%, respectively） and nanofibers （F） and nanoparticles （P） separately （7.21 and 7.81, respectively）. All the material systems are characterized by spec- troscopy, microscopy, surface area measurements and the devices are characterized by current-voltage （I-V）, incident photon-to-current conversion efficiency （IPCE）, electrochemical impedance measurements, etc. I-V, dye-loading and reflectance measurements throw light on the overall performance of the DSC devices.展开更多
One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT...One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.展开更多
Silver/titanium dioxide composite nanoparticles imbedded in polyacrylonitrile (PAN) nanofibers and converted into carbon nanofibers by stabilization and calcination was obtained and tested for capacitive deionization ...Silver/titanium dioxide composite nanoparticles imbedded in polyacrylonitrile (PAN) nanofibers and converted into carbon nanofibers by stabilization and calcination was obtained and tested for capacitive deionization technology. First, the silver ions were converted to metallic silver nanoparticles, through reduction of silver nitrate with dilute solution of PAN. Second, the TiO2 precursor (Titanium Isopropoxide) was added to the solution to form Ag/TiO2 composites imbedded in the PAN polymer solution. Last step involves electrospinning of viscous PAN solution containing silver/TiO2 nanoparticles, thus obtaining PAN nanofibers containing silver/TiO2 nanoparticles. Scanning electron microscopy (SEM) revealed that the diameter of the nanofibers ranged between 50 and 300 nm. Transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS) showed silver/TiO2 nanoparticles dispersed on the surface of the carbon nanofibers. The obtained fiber was fully characterized by measuring and comparing the FTIR spectra and thermogravimetric analysis (TGA) diagrams of PAN nanofiber with and without imbedded nanoparticles, in order to show the effect of silver/TiO2 nanoparticles on the electrospun fiber properties.展开更多
The uniform transparent TiO2/SiO2 photocatalytic composite thin films are prepared by sol-gel method on the soda lime glass substrates, and characterized by UV-visible spectroscopy, X-ray diffraction (XRD), transmissi...The uniform transparent TiO2/SiO2 photocatalytic composite thin films are prepared by sol-gel method on the soda lime glass substrates, and characterized by UV-visible spectroscopy, X-ray diffraction (XRD), transmission electron microscopy (TEM), BET surface area, FTIR spectroscopy and X-ray photoelectron spectroscopy (XPS). It was found that the addition of SiO2 to TiO2 thin films can suppress the grain growth of TiO2 crystal, increase the hydroxyl content on the surface of TiO2 films, lower the contact angle for water on TiO, films and enhance the hydrophilic property of TiO2 films. The super-hydrophilic TiO2/SiO2 photocatalytic composite thin films with the contact angle of 0((o) under bar) are obtained by the addition of 10%-20% SiO2 in mole fraction.展开更多
The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The c...The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.展开更多
Hollow B–SiO2@TiO2 composites were prepared by the wet chemical deposition method starting from TiCl4 and hollow B–SiO2 microspheres.TiO2 layers composed of anatase TiO2 nanoparticles were coated on the surfaces of ...Hollow B–SiO2@TiO2 composites were prepared by the wet chemical deposition method starting from TiCl4 and hollow B–SiO2 microspheres.TiO2 layers composed of anatase TiO2 nanoparticles were coated on the surfaces of the hollow B–SiO2 microspheres probably through the formation of Ti—O—Si and Ti—O—B bonds.A great number of—OH groups were also present at the TiO2 coating layers.The presence of Ti—O—Si bonds and Ti—O—B bonds resulted in the formation of defects in the TiO2 coating layers,which decreased the band gap of the TiO2 coating layers to ca.3.0 eV and endowed the TiO2 coating layers with visible light absorption performance.The buoyancy hollow B–SiO2@TiO2 composites exhibited high photocatalytic activities for the degradation of ammonia-nitrogen and green algae.The conversion of ammonia-nitrogen reached 65%when the degradation of ammonia-nitrogen(43 mg·L-1 at pH value of 8)was catalyzed by the B–SiO2@TiO2(100:10)composite under the simulated solar light irradiation at 35°C for 660 min.The green algae(5 mg·L-1)were almost completely degraded over the B–SiO@TiO2(100:20)photocatalyst under the visible light irradiation at 35°C for 510 min.展开更多
Supermacroporous composite cryogels embedded with SiO2 nanoparticles were prepared by radical cryogenic copolymerization of the reactive monomer mixture of acrylamide（AAm） and N,N-methylene-bis-acrylamide（MBAAm） c...Supermacroporous composite cryogels embedded with SiO2 nanoparticles were prepared by radical cryogenic copolymerization of the reactive monomer mixture of acrylamide（AAm） and N,N-methylene-bis-acrylamide（MBAAm） containing SiO2 nanoparticles（mass ratios of nanoparticles to the monomer AAm from 0.01 to 0.08） under the freezing-temperature variation condition in glass columns.The properties of these composite cryogels were measured.The height equivalent to theoretical plate（HETP） of the cryogel beds at different liquid flow rates was determined by residence time distribution（RTD） using tracer pulse-response method.The composite cryogel matrix embedded with the mass fraction of SiO2 nanoparticles of 0.02 presented the best properties and was employed in the following graft polymerization.Chromatographic process of lysozyme in the composite cryogel grafted with 2-acrylamido-2-methyl-1-propanesulfonic acid（AMPSA） was carried out to evaluate the protein breakthrough and elution characteristics.The chromatography can be carried out at relatively high superficial velocity,i.e.,15 cm·min-1,indicating the satisfactory mechanical strength due to the embedded nanoparticles.展开更多
A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion...A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion behavior of the NiP/TiO2 composite film was investigated by polarization resistance measurement, anode polarization, ESEM （environmental scanning electron microscopy） and EIS （electrochemical impedance spectroscopy） measurements. Results showed that the NiP/ TiO2 composite film has a good corrosion resistance in 0.5mol/L H2SO4 solution. The element valence of the composite film was characterized by XPS （X-ray photoelectron spectroscopy） spectrum, and an anticorrosion mechanism of the composite film was discussed.展开更多
A silicon dioxide fiber-reinforced silicon nitride matrix （SiOJSi3N4） composite used for radomes was prepared by chemical vapor infiltration （CVI） process using the SiCl4-NH3-H2 system. The effects of the process ...A silicon dioxide fiber-reinforced silicon nitride matrix （SiOJSi3N4） composite used for radomes was prepared by chemical vapor infiltration （CVI） process using the SiCl4-NH3-H2 system. The effects of the process conditions, including infiltration temperature, infiltration time, and gas flux were investigated. The energy dispersion spectra （EDS） result showed that the main elements of this composite contained Si, N, and O. The X-ray diffraction （XRD） results indicated that phases of the composite before and after treatment at 1350℃ were all amorphous. A little fiber pull-out was observed on the cross section of the composite by scan electron microscope （SEM）. As a result, the composite exhibited good thermal stability, but an appropriate interface was necessary between the fiber and the matrix.展开更多
Total dose effects and single event effects on radiation-hardened power vertical double-diffusion metal oxide semiconductor（VDMOS） devices with composite SiO2-Si3N4 film gates are investigated.The relationships amon...Total dose effects and single event effects on radiation-hardened power vertical double-diffusion metal oxide semiconductor（VDMOS） devices with composite SiO2-Si3N4 film gates are investigated.The relationships among the important electrical parameters of the samples with different thickness SiO2-Si3N4 films,such as threshold voltage,breakdown voltage,and on-state resistance in accumulated dose,are discussed.The total dose experiment results show that the breakdown voltage and the on-state resistance barely change with the accumulated dose.However,the relationships between the threshold voltages of the samples and the accumulated dose are more complex,and not only positively drift,but also negatively drift.At the end of the total dose experiment,we select the group of samples which have the smaller threshold voltage shift to carry out the single event effect studies.We find that the samples with appropriate thickness ratio SiO2-Si3N4 films have a good radiation-hardening ability.This method may be useful in solving both the SEGR and the total dose problems with the composite SiO2-Si3N4 films.展开更多
ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （...ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.展开更多
An ambient pressure synthesis of SiO2/TiO2 binary aerogel was prepared through the low-cost precursors of titanium tetrachloride（TiCl4） and sodium silicate（Na2O·nSiO2）.After gelation,solvent exchange and surf...An ambient pressure synthesis of SiO2/TiO2 binary aerogel was prepared through the low-cost precursors of titanium tetrachloride（TiCl4） and sodium silicate（Na2O·nSiO2）.After gelation,solvent exchange and surface modification were performed simultaneously and the modified gel was finally dried under ambient pressure.Microstructural analyses by transmission electron microscope（TEM） indicate that fabricated SiO2/TiO2 aerogel composite shows similar sponge-like nanostructure as silica aerogel,and the Brunauer-EmmettTeller（BET） analysis shows that the specific surface area of the composite reaches 605 m^2/g,and the average pore size is 9.7 nm.Such binary aerogel exhibits significant photocatalytic performance in this paper for treating model pollutant of methyl orange（MO）,and the decolorizing efficiency of MO is detected as 84.9%after 210 mins exposure to UV light irradiation.Degraded gel suspends in the water so as to separate from solution for reuse,and after 4 times recycling,70%degradation efficiency can be easily reached when composite catalyzed system is exposed for 210 mins under UV irradiation.展开更多
The micro/nano-scale indentation tests were performed to explore the performance of bisphenol-α-glycidyl methacrylate (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) dental resin composites. The effect of the fi...The micro/nano-scale indentation tests were performed to explore the performance of bisphenol-α-glycidyl methacrylate (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) dental resin composites. The effect of the filling content of nano-SiO2 particles on the mechanical properties of the dental composites was studied as well. The experimental results showed that the incorporation of the nano-SiO2 particles at low concentrations (up to 10 wt.%) can apparently increase the hardness and elastic modulus of the dental rein composites. The plasticity index indicates a best elastic recovery capability at a proper amount (4 wt.%) of the nanoparticles. Combined with the infrared spectrum, the mechanical enhancement mechanisms of the dental resin composites were analyzed.展开更多
TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to es...TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to estimate activity of catalysts and determine the kinetics. And the effects of parameters including the initial concentration of AY, light intensity and TiO2 content in catalysts were examined. The results indicate that TAs has a higher efficiency in decomposition of AY than P25, pure TiO2 particles as well as the mixture of TiO2 powder and active carbon. The photocatalytic degradation rate is found to follow the pseudo-first order kinetics with respect to the AY concentration. The new kinetic model fairly resembles the classic Langmuir-Hinshelwood equation, and the rate constant is proportional to the square root of the light intensity in a wide range. However, its absorption performance depends on the surface areas of catalysts. The model fits quite well with the experimental data and elucidates phenomena about the effects of the TiO2 content in TAs on the degradation rate.展开更多
Using low-cost precipitated silica(SiO2) as the carrier,a ternary SiO2-TiO2/g-C3N4 composite photocatalyst was prepared via the sol-gel method associated with a wet-grinding process.The asprepared composite exhibits p...Using low-cost precipitated silica(SiO2) as the carrier,a ternary SiO2-TiO2/g-C3N4 composite photocatalyst was prepared via the sol-gel method associated with a wet-grinding process.The asprepared composite exhibits photocatalytic hydrogen production and pollutant degradation performance under solar-like irradiation.The effect of SiO2 carrier on the properties of the heterostructure between TiO2 and g-C3N4(CN) was systematically studied.It is found that SiO2 has important effects on promoting the interaction between TiO2 and CN.The particle size of TiO2 and CN was obviously reduced during the calcination process due to the effects of SiO2.Especially,the TiO2 particles exhibit monodispersed state with particle size below 10 nm(quantum dots),resulting in the improvement of the contact area and the interaction betweenTiO2 and CN,and leading to the formation of efficient TiO2/CN Zscheme heterostructure in SiO2-TiO2/CN.Besides,the introduction of SiO2 can increase the specific surface area and light absorption of SiO2-TiO2/CN,further promoting the photocatalytic reaction.As expected,the optimum SiO2-TiO2/CN composite exhibits 12.3,3.1 and 2.9 times higher photocatalytic hydrogen production rate than that of SiO2-TiO2,CN and TiO2/CN under solar-like irradiation,while the photocatalytic active component in SiO2-TiO2/CN is only about 60 wt%.Moreover,the rhodamine B degradation rate of SiO2-TiO2/CN is also higher than that of SiO2-TiO2,CN and TiO2/CN.展开更多
In the present work, structure changes during （SiO2） composites have been investigated systematically stretching of isotactic polypropylene （iPP） and iPP/silicon dioxide The or-form crystal structure of both iPP a...In the present work, structure changes during （SiO2） composites have been investigated systematically stretching of isotactic polypropylene （iPP） and iPP/silicon dioxide The or-form crystal structure of both iPP and iPP/SiO2 composites is destroyed and transforms into the mesophase as the samples are stretched at a low temperature （35℃）, while stretching at high temperatures （90℃ and 120℃） can restrain the appearance of defects and keep the perfection of crystal structure. FTIR results reveal that the stretching temperatures show no obvious difference of the effect on the orientation of pure iPP, however, the orientation of iPP/SiO2 composites is greatly changed by the tensile temperature. In the case of micron-sized SiO2 particles （average particle diameter d 〉 1 μm）, the orientation of the composites is lower than that of pure iPP at all stretching temperatures. The above results suggest that the stretching temperature and the SiO2 particle size have great influence on the structure variation and orientation behavior of iPP/SiO2 composites.展开更多
Three-dimensional （3D） five-directional braided （SiO2）/SiO2 composites were prepared by silicasol-infiltration-sintering （SIS） method. The flexural properties and microstructures were studied. The flexural stren...Three-dimensional （3D） five-directional braided （SiO2）/SiO2 composites were prepared by silicasol-infiltration-sintering （SIS） method. The flexural properties and microstructures were studied. The flexural strength and flexural elastic modulus were found to be 73 MPa and 12 GPa, respectively. The results of stress vs deflection curve and SEM examinations revealed that the fracture mechanism of 3D, five-directional braided （SiO2）/SiO2 composite was a mixture mode of ductile and brittle. The ductile mode was attributed to the weak bonding strength of fiber/matrix at low temperature. The brittle fracture might be caused by the propagation of micro defect or crack, which existed in the as-prepared composites for the ten-cycle process.展开更多
基金supported by the Department of Science and Technology of Zhuhai City(No.ZH22017001200059PWC)the Department of Science and Technology of Guangdong Province,China(No.2019A050510043)。
文摘Gel polymer electrolytes(GPEs) are promising alternatives to liquid electrolytes applied in high-energydensity batteries.Here superior SiO_(2) nanofiber composite gel polymer electrolytes(SNCGPEs) are developed via in-situ ionic ring-opening polymerization of 1,3-dioxolane(DOL) monomers in SiO_(2) nanofiber membrane(PDOL-SiO_(2)) for lithium metal batteries.The oxygen atoms of PDOL together with Si-O of SiO_(2) construct a more efficient channel for Li^(+) migration.Consequently,the lithium ion transference number(t_(Li^(+)) and ionic conductivity(σ) at 30℃ of PDOL-SiO_(2) are 0.80 and 1.68×10^(-4)S/cm separately.PDOL-SiO_(2) manifests the electrochemical decomposition potentials of 4.90 V.At 0.5 mA/cm^(2),Li|PDOL-SiO_(2) |Li cell shows a steady cycling performance for nearly 1400 h.LFP|PDOL-SiO_(2) |Li battery can steadily cycle at 0.5 C with a capacity retention rate of 89% after 200 cycles.While cycling at 2 C,the capacity retention rate can maintain at 78% after 300 cycles.This contribution provides a innovative strategy for accelerating Li^(+)transportation via designing PDOL molecular chains throughout the SiO_(2) nanofiber framework,which is crucial for high-energy-density LMBs.
文摘[Zn(CH3COO)2 + PVP]/[C2H5O)4Si + PVP]/[SnCl4 + PVP]/[Ti(OC4H9)4 + CH3COOH + PVP] precursor composite fibers have been fabricated through self-made electrospinning equipment via electrospinning tech-nique. ZnO/SiO2/SnO2/TiO2 composite nanofibers were obtained by calcination of the relevant precursor composite fibers. The samples were characterized by thermogravimetric-differential thermal analysis (TG-DTA), X-ray diffractometry (XRD), Fourier transform infrared spectroscopy (FTIR), and Scanning electron microscopy (SEM). TG-DTA analysis reveals that solvents, organic compounds and inorganic in the precursor composite fibers are decomposed and volatilized totally, and the mass of the samples kept constant when sintering temperature was above 900?C, and the total mass loss percentage is 88%. XRD results show that the precursor composite fibers are amorphous in structure, and pure phase ZnO/SiO2/SnO2/TiO2 com-posite nanofibers are obtained by calcination of the relevant precursor composite fibers. FTIR analysis manifests that pure inorganic oxides are formed. SEM analysis indicates that the width of the precursor composite fibers is ca. 1.485 ± 0.043 μm. The width of the ZnO/SiO2/SnO2/TiO2 composite nanofibers is ca. 1145.098 ± 68.093 nm.
基金supported in part by the National Natural Science Foundation of China(Nos.50473008 and 50673034)by Natural Science Foundation of the Jiangsu Higher Education Institutions of China(No.09KJD 150001)by DuPont Company through a Young Faculty Grant Award to Prof.C.Wang,and by Headwater Nanokinetix,Inc
文摘Porous TiO2/ZnO composite nanofibers have been successfully prepared by electrospinning technique for the first time.It was generated by calcining TiO2/ZnCl2/PVP[PVP：polyvinyl pyrrolidone）]nanofibers,which were electrospun from a mixture solution of TiO2,ZnCl2 and PVP.Transmission electron microscopy（TEM） and X-ray diffraction（XRD） analyses were used to identify the morphology of the TiO2/ZnO nanofibers and a formation of inorganic TiO2/ZnO fibers.The porous structure of the TiO2/ZnO fibers was characterized by N2 adsoption/desorption isotherm.Surface photovoltage spectroscopy（SPS） and photocatalytic activity measurements revealed advance properties of the porous TiO2/ZnO composite nanofibers and the results were compared with pure TiO2 nanofibers,pure ZnO nanofibers and TiO2/ZnO nanoparticles.
基金supported by Ministry of New and Renewable Energy(MNRE)the Solar Energy Research Initiative(SERI),respectively.of Govt.of India
文摘We report a facile method for the fabrication of TiO2 nanofiber-nanoparticle composite （FP） via. simulta- neous electrospraying and electrospinning for dye-sensitized solar cell （DSC） applications. The loading of nanoparticles on the fibers is controlled by varying their feed rates during electrospinning. The FP composites having three different particle loading are prepared by the methodology and the FP with the highest particle loading （denoted as FP-3 in the manuscript） showed the best overall efficiency of 9.15% in comparison to the other compositions of the FP （FP-2, 8.15% and FP-1, Z51%, respectively） and nanofibers （F） and nanoparticles （P） separately （7.21 and 7.81, respectively）. All the material systems are characterized by spec- troscopy, microscopy, surface area measurements and the devices are characterized by current-voltage （I-V）, incident photon-to-current conversion efficiency （IPCE）, electrochemical impedance measurements, etc. I-V, dye-loading and reflectance measurements throw light on the overall performance of the DSC devices.
基金Funded by the National Natural Science Foundation of China (No. 50674048)Research Fund for the Doctoral Program of Higher Education of China(No.20103227110006)
文摘One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.
文摘Silver/titanium dioxide composite nanoparticles imbedded in polyacrylonitrile (PAN) nanofibers and converted into carbon nanofibers by stabilization and calcination was obtained and tested for capacitive deionization technology. First, the silver ions were converted to metallic silver nanoparticles, through reduction of silver nitrate with dilute solution of PAN. Second, the TiO2 precursor (Titanium Isopropoxide) was added to the solution to form Ag/TiO2 composites imbedded in the PAN polymer solution. Last step involves electrospinning of viscous PAN solution containing silver/TiO2 nanoparticles, thus obtaining PAN nanofibers containing silver/TiO2 nanoparticles. Scanning electron microscopy (SEM) revealed that the diameter of the nanofibers ranged between 50 and 300 nm. Transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS) showed silver/TiO2 nanoparticles dispersed on the surface of the carbon nanofibers. The obtained fiber was fully characterized by measuring and comparing the FTIR spectra and thermogravimetric analysis (TGA) diagrams of PAN nanofiber with and without imbedded nanoparticles, in order to show the effect of silver/TiO2 nanoparticles on the electrospun fiber properties.
基金This work was financially supported by the Foundation for University Key Teachers by the Ministry of Education, theKey Resear
文摘The uniform transparent TiO2/SiO2 photocatalytic composite thin films are prepared by sol-gel method on the soda lime glass substrates, and characterized by UV-visible spectroscopy, X-ray diffraction (XRD), transmission electron microscopy (TEM), BET surface area, FTIR spectroscopy and X-ray photoelectron spectroscopy (XPS). It was found that the addition of SiO2 to TiO2 thin films can suppress the grain growth of TiO2 crystal, increase the hydroxyl content on the surface of TiO2 films, lower the contact angle for water on TiO, films and enhance the hydrophilic property of TiO2 films. The super-hydrophilic TiO2/SiO2 photocatalytic composite thin films with the contact angle of 0((o) under bar) are obtained by the addition of 10%-20% SiO2 in mole fraction.
基金Sponsored by Hi-Tech Research and Development Program of China (2003AA305120)
文摘The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.
基金Supported by the National Natural Science Foundation of China(21506078).
文摘Hollow B–SiO2@TiO2 composites were prepared by the wet chemical deposition method starting from TiCl4 and hollow B–SiO2 microspheres.TiO2 layers composed of anatase TiO2 nanoparticles were coated on the surfaces of the hollow B–SiO2 microspheres probably through the formation of Ti—O—Si and Ti—O—B bonds.A great number of—OH groups were also present at the TiO2 coating layers.The presence of Ti—O—Si bonds and Ti—O—B bonds resulted in the formation of defects in the TiO2 coating layers,which decreased the band gap of the TiO2 coating layers to ca.3.0 eV and endowed the TiO2 coating layers with visible light absorption performance.The buoyancy hollow B–SiO2@TiO2 composites exhibited high photocatalytic activities for the degradation of ammonia-nitrogen and green algae.The conversion of ammonia-nitrogen reached 65%when the degradation of ammonia-nitrogen(43 mg·L-1 at pH value of 8)was catalyzed by the B–SiO2@TiO2(100:10)composite under the simulated solar light irradiation at 35°C for 660 min.The green algae(5 mg·L-1)were almost completely degraded over the B–SiO@TiO2(100:20)photocatalyst under the visible light irradiation at 35°C for 510 min.
基金Supported by the National Natural Science Foundation of China（20876145） the Natural Science Foundation of Zhejiang Province（Y4080329）
文摘Supermacroporous composite cryogels embedded with SiO2 nanoparticles were prepared by radical cryogenic copolymerization of the reactive monomer mixture of acrylamide（AAm） and N,N-methylene-bis-acrylamide（MBAAm） containing SiO2 nanoparticles（mass ratios of nanoparticles to the monomer AAm from 0.01 to 0.08） under the freezing-temperature variation condition in glass columns.The properties of these composite cryogels were measured.The height equivalent to theoretical plate（HETP） of the cryogel beds at different liquid flow rates was determined by residence time distribution（RTD） using tracer pulse-response method.The composite cryogel matrix embedded with the mass fraction of SiO2 nanoparticles of 0.02 presented the best properties and was employed in the following graft polymerization.Chromatographic process of lysozyme in the composite cryogel grafted with 2-acrylamido-2-methyl-1-propanesulfonic acid（AMPSA） was carried out to evaluate the protein breakthrough and elution characteristics.The chromatography can be carried out at relatively high superficial velocity,i.e.,15 cm·min-1,indicating the satisfactory mechanical strength due to the embedded nanoparticles.
文摘A NiP/TiO2 composite film on carbon steel was prepared by electroless plating and sol-gel composite process. An artificial neural network was applied to optimize the prepared condition of the composite film. Corrosion behavior of the NiP/TiO2 composite film was investigated by polarization resistance measurement, anode polarization, ESEM （environmental scanning electron microscopy） and EIS （electrochemical impedance spectroscopy） measurements. Results showed that the NiP/ TiO2 composite film has a good corrosion resistance in 0.5mol/L H2SO4 solution. The element valence of the composite film was characterized by XPS （X-ray photoelectron spectroscopy） spectrum, and an anticorrosion mechanism of the composite film was discussed.
基金This study was financially supported by the Key Foundation of National Science in China (No. 90405015), the National Elitist Youth Foundation of China (No. 50425208the Doctorate Foundation of Northwestern Polytechnical University (CX200505).
文摘A silicon dioxide fiber-reinforced silicon nitride matrix （SiOJSi3N4） composite used for radomes was prepared by chemical vapor infiltration （CVI） process using the SiCl4-NH3-H2 system. The effects of the process conditions, including infiltration temperature, infiltration time, and gas flux were investigated. The energy dispersion spectra （EDS） result showed that the main elements of this composite contained Si, N, and O. The X-ray diffraction （XRD） results indicated that phases of the composite before and after treatment at 1350℃ were all amorphous. A little fiber pull-out was observed on the cross section of the composite by scan electron microscope （SEM）. As a result, the composite exhibited good thermal stability, but an appropriate interface was necessary between the fiber and the matrix.
文摘Total dose effects and single event effects on radiation-hardened power vertical double-diffusion metal oxide semiconductor（VDMOS） devices with composite SiO2-Si3N4 film gates are investigated.The relationships among the important electrical parameters of the samples with different thickness SiO2-Si3N4 films,such as threshold voltage,breakdown voltage,and on-state resistance in accumulated dose,are discussed.The total dose experiment results show that the breakdown voltage and the on-state resistance barely change with the accumulated dose.However,the relationships between the threshold voltages of the samples and the accumulated dose are more complex,and not only positively drift,but also negatively drift.At the end of the total dose experiment,we select the group of samples which have the smaller threshold voltage shift to carry out the single event effect studies.We find that the samples with appropriate thickness ratio SiO2-Si3N4 films have a good radiation-hardening ability.This method may be useful in solving both the SEGR and the total dose problems with the composite SiO2-Si3N4 films.
基金Project(gf200901002)supported by the Open Research Fund of National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology of Nanchang Hangkong University,China
文摘ZrO2/TiO2 composite photocatalytic film was produced on the pure titanium substrate using in-situ Zr（OH）4 colloidal particle by the micro-arc oxidation technique and characterized by scanning electron microscope （SEM）, energy dispersive X-ray （EDX）, X-ray diffraction （XRD） and ultraviolet-visible （UV-Vis） spectrophotometer. The composite film shows a lamellar and porous structure which consists of anatase, futile and ZrO2 phases. The optical absorption edge of film is shifted to longer wavelength when ZrO2 is introduced to TiO2. Furthermore, the photocatalytic reaction rate constants of degradation of rhodamine B solution with ZrO2/TiO2 composite film and pure TiO2 film under ultraviolet irradiation are measured as 0.0442 and 0.0186 h 1, respectively.
基金Funded by the National Natural Science Foundation of China(NSFC)(Nos.51278073,51308079 and 51408073)
文摘An ambient pressure synthesis of SiO2/TiO2 binary aerogel was prepared through the low-cost precursors of titanium tetrachloride（TiCl4） and sodium silicate（Na2O·nSiO2）.After gelation,solvent exchange and surface modification were performed simultaneously and the modified gel was finally dried under ambient pressure.Microstructural analyses by transmission electron microscope（TEM） indicate that fabricated SiO2/TiO2 aerogel composite shows similar sponge-like nanostructure as silica aerogel,and the Brunauer-EmmettTeller（BET） analysis shows that the specific surface area of the composite reaches 605 m^2/g,and the average pore size is 9.7 nm.Such binary aerogel exhibits significant photocatalytic performance in this paper for treating model pollutant of methyl orange（MO）,and the decolorizing efficiency of MO is detected as 84.9%after 210 mins exposure to UV light irradiation.Degraded gel suspends in the water so as to separate from solution for reuse,and after 4 times recycling,70%degradation efficiency can be easily reached when composite catalyzed system is exposed for 210 mins under UV irradiation.
文摘The micro/nano-scale indentation tests were performed to explore the performance of bisphenol-α-glycidyl methacrylate (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) dental resin composites. The effect of the filling content of nano-SiO2 particles on the mechanical properties of the dental composites was studied as well. The experimental results showed that the incorporation of the nano-SiO2 particles at low concentrations (up to 10 wt.%) can apparently increase the hardness and elastic modulus of the dental rein composites. The plasticity index indicates a best elastic recovery capability at a proper amount (4 wt.%) of the nanoparticles. Combined with the infrared spectrum, the mechanical enhancement mechanisms of the dental resin composites were analyzed.
基金Project(50802034) supported by the National Natural Science Foundation of ChinaProject(11A093) supported by the Key Project Foundation by the Education Department of Hunan Province,China
文摘TiO2-coated activated carbon surface （TAs） composites were prepared by a sol-gel method with supercritical pretreatment. The photocatalytic degradation of acid yellow （AY） was investigated under UV radiation to estimate activity of catalysts and determine the kinetics. And the effects of parameters including the initial concentration of AY, light intensity and TiO2 content in catalysts were examined. The results indicate that TAs has a higher efficiency in decomposition of AY than P25, pure TiO2 particles as well as the mixture of TiO2 powder and active carbon. The photocatalytic degradation rate is found to follow the pseudo-first order kinetics with respect to the AY concentration. The new kinetic model fairly resembles the classic Langmuir-Hinshelwood equation, and the rate constant is proportional to the square root of the light intensity in a wide range. However, its absorption performance depends on the surface areas of catalysts. The model fits quite well with the experimental data and elucidates phenomena about the effects of the TiO2 content in TAs on the degradation rate.
基金partly supported by the National Natural Science Foundation of China(Nos.21577132,21978276)。
文摘Using low-cost precipitated silica(SiO2) as the carrier,a ternary SiO2-TiO2/g-C3N4 composite photocatalyst was prepared via the sol-gel method associated with a wet-grinding process.The asprepared composite exhibits photocatalytic hydrogen production and pollutant degradation performance under solar-like irradiation.The effect of SiO2 carrier on the properties of the heterostructure between TiO2 and g-C3N4(CN) was systematically studied.It is found that SiO2 has important effects on promoting the interaction between TiO2 and CN.The particle size of TiO2 and CN was obviously reduced during the calcination process due to the effects of SiO2.Especially,the TiO2 particles exhibit monodispersed state with particle size below 10 nm(quantum dots),resulting in the improvement of the contact area and the interaction betweenTiO2 and CN,and leading to the formation of efficient TiO2/CN Zscheme heterostructure in SiO2-TiO2/CN.Besides,the introduction of SiO2 can increase the specific surface area and light absorption of SiO2-TiO2/CN,further promoting the photocatalytic reaction.As expected,the optimum SiO2-TiO2/CN composite exhibits 12.3,3.1 and 2.9 times higher photocatalytic hydrogen production rate than that of SiO2-TiO2,CN and TiO2/CN under solar-like irradiation,while the photocatalytic active component in SiO2-TiO2/CN is only about 60 wt%.Moreover,the rhodamine B degradation rate of SiO2-TiO2/CN is also higher than that of SiO2-TiO2,CN and TiO2/CN.
基金financially supported by the National Natural Science Foundation of China (Nos. 51073004 and 21074141)the China National Funds for Distinguished Young Scientists (No. 50925313)
文摘In the present work, structure changes during （SiO2） composites have been investigated systematically stretching of isotactic polypropylene （iPP） and iPP/silicon dioxide The or-form crystal structure of both iPP and iPP/SiO2 composites is destroyed and transforms into the mesophase as the samples are stretched at a low temperature （35℃）, while stretching at high temperatures （90℃ and 120℃） can restrain the appearance of defects and keep the perfection of crystal structure. FTIR results reveal that the stretching temperatures show no obvious difference of the effect on the orientation of pure iPP, however, the orientation of iPP/SiO2 composites is greatly changed by the tensile temperature. In the case of micron-sized SiO2 particles （average particle diameter d 〉 1 μm）, the orientation of the composites is lower than that of pure iPP at all stretching temperatures. The above results suggest that the stretching temperature and the SiO2 particle size have great influence on the structure variation and orientation behavior of iPP/SiO2 composites.
基金Funded by the Basic Research Project of Science and Technology of Jiangsu Province(No.BK2009002)the National Natural ScienceFoundation of China(No.61176062)the Fundamental Research Funds for the Central Universities(No.NS2013061)
文摘Three-dimensional （3D） five-directional braided （SiO2）/SiO2 composites were prepared by silicasol-infiltration-sintering （SIS） method. The flexural properties and microstructures were studied. The flexural strength and flexural elastic modulus were found to be 73 MPa and 12 GPa, respectively. The results of stress vs deflection curve and SEM examinations revealed that the fracture mechanism of 3D, five-directional braided （SiO2）/SiO2 composite was a mixture mode of ductile and brittle. The ductile mode was attributed to the weak bonding strength of fiber/matrix at low temperature. The brittle fracture might be caused by the propagation of micro defect or crack, which existed in the as-prepared composites for the ten-cycle process.