A new ternary compound La8Al13Sn3 was synthesized and studied by means of X-ray powder diffraction technique. The compound La8Al13Sn3 crystallizes in a hexagonal AlB2-type structure with space group P6/mmm （No. 191）...A new ternary compound La8Al13Sn3 was synthesized and studied by means of X-ray powder diffraction technique. The compound La8Al13Sn3 crystallizes in a hexagonal AlB2-type structure with space group P6/mmm （No. 191） and the lattice parameters a = 0.44919（1） nm and c = 0.43835（1） nm. The Smith and Snyder figure of merit for index, FN, is F30 = 197.3（30）. The Rietveld refinement for the crystal structure of the compound was carried out successfully. The liability R-factors of Rietveld refinement are Rp = 0.114 and Rwp = 0.148. The compound La8Al13Sn3 decomposes into LaAl2 with cubic structure and space group Fd 3m （227）, LaAl3 with hexagonal structure and space group P63/mmc （194）, and Sn at 720°C.展开更多
The new ternary compound Al14NdsSi has been studied by means of the X-ray powder diffraction technique and the Rietveld method. The ternary compound Al14Nd5Si has a hexagonal Ni3Sn-type structure with space group P63/...The new ternary compound Al14NdsSi has been studied by means of the X-ray powder diffraction technique and the Rietveld method. The ternary compound Al14Nd5Si has a hexagonal Ni3Sn-type structure with space group P63/mmc （No.194）, the lattice parameters are a = 0.64470 （2） nm and c = 0.45926 （1） nm. The Smith and Snyder figure of merit for the index, FN, is F30 = 97.8 （30）. The X-ray diffraction data indicated that the crystal structure of the compound Al14Nd5Si has been successfully refined by the Rietveld method. The R-factors of Rietveld refinement are Rp = 0.088 and Rwp = 0.120, respectively. The thermal dependence of magnetization for the compound was measured by a vibrating sample magnetometer. The experimentally determined magnetic effective paramagnetic moment is μeff= 3.60 μB per Nd atom. The paramagnetic Currie temperature θp = -33.7 K was also obtained from the Currie-Weiss law.展开更多
基金supported by the Natural Sci-ence Foundation of Guangxi Province, China (Nos. 0832027 and 0640072)
文摘A new ternary compound La8Al13Sn3 was synthesized and studied by means of X-ray powder diffraction technique. The compound La8Al13Sn3 crystallizes in a hexagonal AlB2-type structure with space group P6/mmm （No. 191） and the lattice parameters a = 0.44919（1） nm and c = 0.43835（1） nm. The Smith and Snyder figure of merit for index, FN, is F30 = 197.3（30）. The Rietveld refinement for the crystal structure of the compound was carried out successfully. The liability R-factors of Rietveld refinement are Rp = 0.114 and Rwp = 0.148. The compound La8Al13Sn3 decomposes into LaAl2 with cubic structure and space group Fd 3m （227）, LaAl3 with hexagonal structure and space group P63/mmc （194）, and Sn at 720°C.
基金financially supported by the Natural Sci-ence Foundation of Guangxi Province, China (No. 0575001)
文摘The new ternary compound Al14NdsSi has been studied by means of the X-ray powder diffraction technique and the Rietveld method. The ternary compound Al14Nd5Si has a hexagonal Ni3Sn-type structure with space group P63/mmc （No.194）, the lattice parameters are a = 0.64470 （2） nm and c = 0.45926 （1） nm. The Smith and Snyder figure of merit for the index, FN, is F30 = 97.8 （30）. The X-ray diffraction data indicated that the crystal structure of the compound Al14Nd5Si has been successfully refined by the Rietveld method. The R-factors of Rietveld refinement are Rp = 0.088 and Rwp = 0.120, respectively. The thermal dependence of magnetization for the compound was measured by a vibrating sample magnetometer. The experimentally determined magnetic effective paramagnetic moment is μeff= 3.60 μB per Nd atom. The paramagnetic Currie temperature θp = -33.7 K was also obtained from the Currie-Weiss law.