Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indica...Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indicating high crystalline and phase purity.The SEM and TEM images reveal that diameter of the spherical-like Na2FePO4F/C particles ranges from 50 to 300 nm,and HRTEM image shows that the surface of Na2FePO4F/C composite is uniformly coated by carbon layer with a average thickness of about 3.6 nm.The carbon coating constrains the growth of the particles and effectively reduces the agglomeration of nanoparticles.Using lithium metal as anode,the composite delivers a discharge capacities of 102.8,96.4 and 90.3 mA·h/g at rates of 0.5C,1C and 2C,respectively.After 100 cycles at 0.5C,a discharge capacity of 98.9 mA·h/g is maintained with capacity retention of 96.2%.The Li+diffusion coefficient(D)of Na2FePO4F/C composite is calculated as 1.71×10^–9 cm^2/s.This study reveals that the simple solid state reaction could be a practical and effective synthetic route for the industrial production of Na2FePO4F/C material.展开更多
In this work,the influence of CO2 on the structural variation and catalytic performance of Na2WO4/Mn/Si O2 for oxidative coupling of methane to ethylene was investigated. The catalyst was prepared by impregnation meth...In this work,the influence of CO2 on the structural variation and catalytic performance of Na2WO4/Mn/Si O2 for oxidative coupling of methane to ethylene was investigated. The catalyst was prepared by impregnation method and characterized by XRD,Raman and XPS techniques. Appropriate amount of CO2 in the reactant gases enhanced the formation of surface tetrahedral Na2WO4 species and promoted the migration of O in MOx,Na,W from the catalyst bulk to surface,which were favorable for oxidative coupling of methane. When the molar ratio of CH4/O2/CO2 was 3/1/2,enriched surface tetrahedral Na2WO4 species and high surface concentration of O in MOx,Na,W were detected,and then high CH4 conversion of 33.1% and high C2H4 selectivity of 56.2% were obtained. With further increase of CO2 in the reagent gases,the content of active surface tetrahedral Na2WO4 species and surface concentration of O in MOx,Na,W decreased,while that of inactive species（Mn WO4 and Mn2O3） increased dramatically,leading to low CH4 conversion and low C2H4 selectivity. It could be speculated that Na2WO4 crystal was transformed into Mn WO4 crystal with excessive CO2 added under the reaction conditions. Pretreatment of Na2WO4/Mn/Si O2 catalyst by moderate amount of CO2 before OCM also promoted the formation of Na2WO4 species.展开更多
基金Projects(51472211,51502256)supported by the National Natural Science Foundation of ChinaProjects(2016GK4005,2016GK4030)supported by the Strategic New Industry of Hunan Province,ChinaProject(13C925)supported by the Research Foundation of Education Bureau of Hunan Province,China
文摘Using low-cost FePO4·2H2O as iron source,Na2FePO4F/C composite is prepared by alcohol-assisted ball milling and solid-state reaction method.The XRD pattern of Na2FePO4F/C composite demonstrates sharp peaks,indicating high crystalline and phase purity.The SEM and TEM images reveal that diameter of the spherical-like Na2FePO4F/C particles ranges from 50 to 300 nm,and HRTEM image shows that the surface of Na2FePO4F/C composite is uniformly coated by carbon layer with a average thickness of about 3.6 nm.The carbon coating constrains the growth of the particles and effectively reduces the agglomeration of nanoparticles.Using lithium metal as anode,the composite delivers a discharge capacities of 102.8,96.4 and 90.3 mA·h/g at rates of 0.5C,1C and 2C,respectively.After 100 cycles at 0.5C,a discharge capacity of 98.9 mA·h/g is maintained with capacity retention of 96.2%.The Li+diffusion coefficient(D)of Na2FePO4F/C composite is calculated as 1.71×10^–9 cm^2/s.This study reveals that the simple solid state reaction could be a practical and effective synthetic route for the industrial production of Na2FePO4F/C material.
基金support from the Ministry of Science and Technology (Nos.2012BAC20B10)the National Natural Science Foundation of China (Nos. 21321061 and 20976109)
文摘In this work,the influence of CO2 on the structural variation and catalytic performance of Na2WO4/Mn/Si O2 for oxidative coupling of methane to ethylene was investigated. The catalyst was prepared by impregnation method and characterized by XRD,Raman and XPS techniques. Appropriate amount of CO2 in the reactant gases enhanced the formation of surface tetrahedral Na2WO4 species and promoted the migration of O in MOx,Na,W from the catalyst bulk to surface,which were favorable for oxidative coupling of methane. When the molar ratio of CH4/O2/CO2 was 3/1/2,enriched surface tetrahedral Na2WO4 species and high surface concentration of O in MOx,Na,W were detected,and then high CH4 conversion of 33.1% and high C2H4 selectivity of 56.2% were obtained. With further increase of CO2 in the reagent gases,the content of active surface tetrahedral Na2WO4 species and surface concentration of O in MOx,Na,W decreased,while that of inactive species（Mn WO4 and Mn2O3） increased dramatically,leading to low CH4 conversion and low C2H4 selectivity. It could be speculated that Na2WO4 crystal was transformed into Mn WO4 crystal with excessive CO2 added under the reaction conditions. Pretreatment of Na2WO4/Mn/Si O2 catalyst by moderate amount of CO2 before OCM also promoted the formation of Na2WO4 species.