In order to obtain better carbonation effect, extraction behavior of slag batch is necessary to study. Relevant parameters like selective extraction yield were originally discussed. The relationship between selective ...In order to obtain better carbonation effect, extraction behavior of slag batch is necessary to study. Relevant parameters like selective extraction yield were originally discussed. The relationship between selective extraction yield and conversion ratio was systemically focused on. The results show that alkaline earth metal conversion ratio is changed with leaching time and NH4CI concentration by first order exponential, and the maximum conversion for calcium keeps about 68% at 120 min in 0.4 mol/L NH4C1 solution, while leaching temperature and particle size have a linear effect on conversion ratio. Selective extraction yield of calcium is more than 93%, and the value of Mg is less than 5%. Apparent layer bands of silicon and calcium appear in the surface area through morphology detection of slag after leaching, and the case for 38-75 μm slag batch is more obvious than 75 150 μm slag and slag with larger particle size when leaching in 0.4 mol/L NH4Cl solution for 90 rain at 60 ℃.展开更多
Silica sol ceramic mold was made at room temperature with JN-30 silica sol, silica powder and NH4Cl. It is found that the harden time of silica sol ceramic mold is only 0.5 to 1.5 h under the amount of NH4Cl solution ...Silica sol ceramic mold was made at room temperature with JN-30 silica sol, silica powder and NH4Cl. It is found that the harden time of silica sol ceramic mold is only 0.5 to 1.5 h under the amount of NH4Cl solution of 7% to 8% with 15% concentration, and less surface cracks occur by using vacuum drying. The proper vacuum drying process parameters： vacuum drying temperature is 80 to 100℃, drying time is 5 h and vacuum is 0.06 to 0.07MPa. The harden mechanics, vacuum drying mechanics and the reason of less surface cracks of silica sol ceramic mold by vacuum drying： were also analyzed in this paper.展开更多
基金Project(2006BAE03A07)supported by National Key Technology Research and Development Program of 11th Five-year Plan of China
文摘In order to obtain better carbonation effect, extraction behavior of slag batch is necessary to study. Relevant parameters like selective extraction yield were originally discussed. The relationship between selective extraction yield and conversion ratio was systemically focused on. The results show that alkaline earth metal conversion ratio is changed with leaching time and NH4CI concentration by first order exponential, and the maximum conversion for calcium keeps about 68% at 120 min in 0.4 mol/L NH4C1 solution, while leaching temperature and particle size have a linear effect on conversion ratio. Selective extraction yield of calcium is more than 93%, and the value of Mg is less than 5%. Apparent layer bands of silicon and calcium appear in the surface area through morphology detection of slag after leaching, and the case for 38-75 μm slag batch is more obvious than 75 150 μm slag and slag with larger particle size when leaching in 0.4 mol/L NH4Cl solution for 90 rain at 60 ℃.
文摘Silica sol ceramic mold was made at room temperature with JN-30 silica sol, silica powder and NH4Cl. It is found that the harden time of silica sol ceramic mold is only 0.5 to 1.5 h under the amount of NH4Cl solution of 7% to 8% with 15% concentration, and less surface cracks occur by using vacuum drying. The proper vacuum drying process parameters： vacuum drying temperature is 80 to 100℃, drying time is 5 h and vacuum is 0.06 to 0.07MPa. The harden mechanics, vacuum drying mechanics and the reason of less surface cracks of silica sol ceramic mold by vacuum drying： were also analyzed in this paper.