The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. Acco...The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. According to the results, a CeO2-TiO2solid solution is formed when the mole ratio of cerium to titanium n（Ce）：n（Ti） is 5：5 or greater, and the most suitable n（Ce）：n（Ti） isdetermined as 7：3, over which the conversion rate of SO2 and the yield of sulfur at 500℃ reach 93% and 99%, respectively.According to the activity testing curve, Ce0.7Ti0.3O2 （n（Ce）：n（Ti）=7：3） without any pretreatment can be gradually activated by reagentgas after about 10 min, and reaches a steady activation status 60 min later. The XPS results of Ce0.7Ti0.3O2 after different time ofSO2＋CO reaction show that CeO2 is the active component that offers the redox couple Ce4＋/Ce3＋ and the labile oxygen vacancies, andTiO2 only functions as a catalyst structure stabilizer during the catalytic reaction process. After 48 h of catalytic reaction at 500℃,Ce0.7Ti0.3O2 still maintains a stable structure without being vulcanized, demonstrating its good anti-sulfur poisoning performance.展开更多
In this work we prepared several CeO2-TiO2 catalysts for the NH3-SCR reactionusing co-precipitation with assistance of microwave irradiation.The catalytic NH3-SCR activities over CeO2-TiO2 catalysts at low temperature...In this work we prepared several CeO2-TiO2 catalysts for the NH3-SCR reactionusing co-precipitation with assistance of microwave irradiation.The catalytic NH3-SCR activities over CeO2-TiO2 catalysts at low temperatures are largely enhanced by the treatment of microwave irradiation,the operation temperature window is also broadened.For better understanding the promotion mechanism,the catalyst prepared by conventional co-precipitation with and without microwave irradiation treatment was characterized with H2-TPR,NH3-TPD,XPS,XRD and BET.Microwave irradiation treatment accelerates the crystallite rate of CeO2-TiO2 catalysts,and greatly enlarges their surface area by adjusting their microstructures.The resistance to SO2 and H2O is also improved via regulating the hierarchical pore structure by the microwave irradiation.Microwave irradiation treatment can also improve the redox property and increase the acid sites over the catalyst surfaces.The result of in situ DRIFTS suggests that the microwave irradiation treatment generates more Br?nsted acid sites on CeO2-TiO2-2 h catalyst,helpful in SCR reactions.XPS results show that after microwave irradiation on the CeO2-TiO2 catalysts,the surface demonstrates an elevated concentration of chemisorbed oxygen,consequently leading to better oxidation of NO to NO2.Additionally,the molar ratio of Ce3+/Ce4+has been elevated after being treated by microwave irradiation,a vital factor in enhancing the NH3-SCR activities.展开更多
Sb-doped SnO2(ATO)-(CeO2-TiO2) thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using lo...Sb-doped SnO2(ATO)-(CeO2-TiO2) thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using low-temperature hydrothermal process.The mixed molar ratio of ATO to(CeO2-TiO2) vs the properties of CeO2-TiO2 thin film was investigated.The optical properties of the films were characterized by UV-visible transmission and infrared reflection spectra,the sheet resistance of ATO particles and films were measured by rubber sheeter(MYI-50) and four-point probe(HisuperGroup Inc,SDY-5),the surface morphology and structure of the films were analyzed using 3D Digitale Mikroskop and X-ray diffraction(XRD),respectively.The results showed that the ATO precursor solution lost weight completely at about 500 oC,and the ATO particles was obtained,which indicated the same rutile lattice structure as SnO2.The glass substrates coated with ATO-(CeO2-TiO2) thin films showed better properties in antistatic electricity(104-106 Ω/),shielding UV(almost 100%),visible light transmission(70%) and infrared reflection(】30%).展开更多
文摘The structure and catalytic desulfurization characteristics of CeO2-TiO2 mixed oxides were investigated by means ofX-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS） and catalytic activity tests. According to the results, a CeO2-TiO2solid solution is formed when the mole ratio of cerium to titanium n（Ce）：n（Ti） is 5：5 or greater, and the most suitable n（Ce）：n（Ti） isdetermined as 7：3, over which the conversion rate of SO2 and the yield of sulfur at 500℃ reach 93% and 99%, respectively.According to the activity testing curve, Ce0.7Ti0.3O2 （n（Ce）：n（Ti）=7：3） without any pretreatment can be gradually activated by reagentgas after about 10 min, and reaches a steady activation status 60 min later. The XPS results of Ce0.7Ti0.3O2 after different time ofSO2＋CO reaction show that CeO2 is the active component that offers the redox couple Ce4＋/Ce3＋ and the labile oxygen vacancies, andTiO2 only functions as a catalyst structure stabilizer during the catalytic reaction process. After 48 h of catalytic reaction at 500℃,Ce0.7Ti0.3O2 still maintains a stable structure without being vulcanized, demonstrating its good anti-sulfur poisoning performance.
基金Project supported by the National Natural Science Foundation of China(21577005)the National Key Research and Development Program of China(2016YFB0600400)
文摘In this work we prepared several CeO2-TiO2 catalysts for the NH3-SCR reactionusing co-precipitation with assistance of microwave irradiation.The catalytic NH3-SCR activities over CeO2-TiO2 catalysts at low temperatures are largely enhanced by the treatment of microwave irradiation,the operation temperature window is also broadened.For better understanding the promotion mechanism,the catalyst prepared by conventional co-precipitation with and without microwave irradiation treatment was characterized with H2-TPR,NH3-TPD,XPS,XRD and BET.Microwave irradiation treatment accelerates the crystallite rate of CeO2-TiO2 catalysts,and greatly enlarges their surface area by adjusting their microstructures.The resistance to SO2 and H2O is also improved via regulating the hierarchical pore structure by the microwave irradiation.Microwave irradiation treatment can also improve the redox property and increase the acid sites over the catalyst surfaces.The result of in situ DRIFTS suggests that the microwave irradiation treatment generates more Br?nsted acid sites on CeO2-TiO2-2 h catalyst,helpful in SCR reactions.XPS results show that after microwave irradiation on the CeO2-TiO2 catalysts,the surface demonstrates an elevated concentration of chemisorbed oxygen,consequently leading to better oxidation of NO to NO2.Additionally,the molar ratio of Ce3+/Ce4+has been elevated after being treated by microwave irradiation,a vital factor in enhancing the NH3-SCR activities.
基金Project supported by the Changjiang Scholars and Innovative Research Team in University
文摘Sb-doped SnO2(ATO)-(CeO2-TiO2) thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using low-temperature hydrothermal process.The mixed molar ratio of ATO to(CeO2-TiO2) vs the properties of CeO2-TiO2 thin film was investigated.The optical properties of the films were characterized by UV-visible transmission and infrared reflection spectra,the sheet resistance of ATO particles and films were measured by rubber sheeter(MYI-50) and four-point probe(HisuperGroup Inc,SDY-5),the surface morphology and structure of the films were analyzed using 3D Digitale Mikroskop and X-ray diffraction(XRD),respectively.The results showed that the ATO precursor solution lost weight completely at about 500 oC,and the ATO particles was obtained,which indicated the same rutile lattice structure as SnO2.The glass substrates coated with ATO-(CeO2-TiO2) thin films showed better properties in antistatic electricity(104-106 Ω/),shielding UV(almost 100%),visible light transmission(70%) and infrared reflection(】30%).