The properties of SiC kiln furniture bonded with fine silicon powderare related to the bonder’s crystal structure. At high temperature, it will crystallize ina-cristobalite with great bulk effect. MnO2 mineralizer ca...The properties of SiC kiln furniture bonded with fine silicon powderare related to the bonder’s crystal structure. At high temperature, it will crystallize ina-cristobalite with great bulk effect. MnO2 mineralizer can make a-cristobalite convertto a-tridymite whose bulk effect is small. The crystal structure and its amount were investigated with XRD technique. The influence of different amounts of MnO2 on thecrystal structure and polycrystal transformation, and that of crystal structure on theproperties of kiln furniture were studied. The best proportion of MnO2 added was determined to be 2.0%.展开更多
研究了水系电解液中Li^+、Zn^(2+)和Mn^(2+)阳离子对具有不同晶型结构和形貌的MnO_2正极电化学性能的影响,探讨其储能机理。结果表明,在不含Mn(Ⅱ)离子的水溶液中,MnO_2电极所表现的电化学性能趋同,容量低,衰减快。含有Zn^(2+)离子的水...研究了水系电解液中Li^+、Zn^(2+)和Mn^(2+)阳离子对具有不同晶型结构和形貌的MnO_2正极电化学性能的影响,探讨其储能机理。结果表明,在不含Mn(Ⅱ)离子的水溶液中,MnO_2电极所表现的电化学性能趋同,容量低,衰减快。含有Zn^(2+)离子的水溶液中,MnO_2电极因二价锌离子的嵌入-脱出,容量明显提升,但衰减严重。当溶液中同时含有Zn^(2+)、Mn^(2+)离子时,基于Mn^(2+)和Zn^(2+)离子之间的协同作用和Mn^(2+)离子氧化/还原反应过程的作用,有效抑制MnO_2颗粒的聚集和结构塌陷,削弱碱式硫酸锌杂质不利的影响,保持了锌离子在MnO_2电极中嵌入-脱出的高容量特性(200 m Ah?g^(-1),电流密度:100m A?g^(-1)),及良好的循环稳定性。展开更多
文摘The properties of SiC kiln furniture bonded with fine silicon powderare related to the bonder’s crystal structure. At high temperature, it will crystallize ina-cristobalite with great bulk effect. MnO2 mineralizer can make a-cristobalite convertto a-tridymite whose bulk effect is small. The crystal structure and its amount were investigated with XRD technique. The influence of different amounts of MnO2 on thecrystal structure and polycrystal transformation, and that of crystal structure on theproperties of kiln furniture were studied. The best proportion of MnO2 added was determined to be 2.0%.
文摘研究了水系电解液中Li^+、Zn^(2+)和Mn^(2+)阳离子对具有不同晶型结构和形貌的MnO_2正极电化学性能的影响,探讨其储能机理。结果表明,在不含Mn(Ⅱ)离子的水溶液中,MnO_2电极所表现的电化学性能趋同,容量低,衰减快。含有Zn^(2+)离子的水溶液中,MnO_2电极因二价锌离子的嵌入-脱出,容量明显提升,但衰减严重。当溶液中同时含有Zn^(2+)、Mn^(2+)离子时,基于Mn^(2+)和Zn^(2+)离子之间的协同作用和Mn^(2+)离子氧化/还原反应过程的作用,有效抑制MnO_2颗粒的聚集和结构塌陷,削弱碱式硫酸锌杂质不利的影响,保持了锌离子在MnO_2电极中嵌入-脱出的高容量特性(200 m Ah?g^(-1),电流密度:100m A?g^(-1)),及良好的循环稳定性。