制备了一种含有胺基官能团的α-二亚胺镍配合物,并将该配合物负载在AlEt_3改性的SiO_2-MgCl_2复合载体上制备负载催化剂,不用昂贵的MAO(甲基铝氧烷)而用AlEt_2Cl作助催化剂,研究了其对乙烯的聚合性能。并采用高温^(13)CNMR、高温GPC、...制备了一种含有胺基官能团的α-二亚胺镍配合物,并将该配合物负载在AlEt_3改性的SiO_2-MgCl_2复合载体上制备负载催化剂,不用昂贵的MAO(甲基铝氧烷)而用AlEt_2Cl作助催化剂,研究了其对乙烯的聚合性能。并采用高温^(13)CNMR、高温GPC、差示扫描量热法(DSC)等对得到的聚合物进行了研究。结果发现,该催化剂具有很高的催化活性(1.89×10~6g of PE/mol of Ni h),得到的聚乙烯产品含有各种短支链(甲基、乙基、丙基、丁基)和长支链,分子量在2.15×10~5～9.27×10~5之间,分子量分布为3.12～4.23。展开更多
A facile and user friendly technique to immobilize the late-transition metal complexes on spherical MgCl2/SiO2/THF support has been developed. The spherical MgCl2/SiO2/THF-supported late-transition metal catalysts 2,6...A facile and user friendly technique to immobilize the late-transition metal complexes on spherical MgCl2/SiO2/THF support has been developed. The spherical MgCl2/SiO2/THF-supported late-transition metal catalysts 2,6-bis-[1-(2,6-dimethylphenylimino)ethyl]pyridine iron(II) dichloride(SC-A) and 1,4-bis(2,6-dimethylphenyl)- acenaphthene diimine nickel(II) dibromide(SC-B) for ethylene polymerization has been prepared by spray-drying technique using tetrahydrofuran suspension containing MgCl2, SiO2 and late-transition metal complexes. The catalysts were characterized by BET, XRD, SEM and the polymers were analyzed using GPC, DSC and 13C-NMR. The test results show that spray-drying is a very effective method for immobilizing late-transition metal catalysts for ethylene polymerization. Among six kinds of cocatalysts for olefin polymerization, TMA and TEA were confirmed to be more effective than other compounds for the ethylene polymerization system using the catalyst SC-A. For the case of the catalyst SC-B, DEAC showed the best performance as cocatalysts in ethylene polymerization. The replication of the catalyst morphology was found in the resultant polyethylene.展开更多
文摘制备了一种含有胺基官能团的α-二亚胺镍配合物,并将该配合物负载在AlEt_3改性的SiO_2-MgCl_2复合载体上制备负载催化剂,不用昂贵的MAO(甲基铝氧烷)而用AlEt_2Cl作助催化剂,研究了其对乙烯的聚合性能。并采用高温^(13)CNMR、高温GPC、差示扫描量热法(DSC)等对得到的聚合物进行了研究。结果发现,该催化剂具有很高的催化活性(1.89×10~6g of PE/mol of Ni h),得到的聚乙烯产品含有各种短支链(甲基、乙基、丙基、丁基)和长支链,分子量在2.15×10~5～9.27×10~5之间,分子量分布为3.12～4.23。
基金supported by the National Natural Science Foundation of China (Grant No.U1162114)the Science Foundation of Tianjin University of Science & Technology (20090420)
文摘A facile and user friendly technique to immobilize the late-transition metal complexes on spherical MgCl2/SiO2/THF support has been developed. The spherical MgCl2/SiO2/THF-supported late-transition metal catalysts 2,6-bis-[1-(2,6-dimethylphenylimino)ethyl]pyridine iron(II) dichloride(SC-A) and 1,4-bis(2,6-dimethylphenyl)- acenaphthene diimine nickel(II) dibromide(SC-B) for ethylene polymerization has been prepared by spray-drying technique using tetrahydrofuran suspension containing MgCl2, SiO2 and late-transition metal complexes. The catalysts were characterized by BET, XRD, SEM and the polymers were analyzed using GPC, DSC and 13C-NMR. The test results show that spray-drying is a very effective method for immobilizing late-transition metal catalysts for ethylene polymerization. Among six kinds of cocatalysts for olefin polymerization, TMA and TEA were confirmed to be more effective than other compounds for the ethylene polymerization system using the catalyst SC-A. For the case of the catalyst SC-B, DEAC showed the best performance as cocatalysts in ethylene polymerization. The replication of the catalyst morphology was found in the resultant polyethylene.
文摘利用溶胶 凝胶技术,控制钛酸四丁酯(TBOT)与硅酸乙酯(TEOS)的水解速度,使其共同水解成溶胶、凝胶,以乙醇为溶剂进行超临界干燥,经过一定温度热处理后,得到暗黄色透明的块体材料·进行了透射电镜观察和X衍射分析,表明锐钛矿结构的纳米TiO2均匀地分散于无定形SiO2基质中·FT IR光谱分析发现纳米TiO2与SiO2基质之间存在着Ti O Si键·在对罗丹明B水溶液的光催化降解中,此块体材料显示较好的光催化活性,在1h内催化降解86%的罗丹明B·此材料克服了粉状TiO2在实际水污染治理应用中的局限性,有着广泛的应用前景·