Multiwalled carbon nanotubes (MWNTs) were used as the conductive additive in the electrode materials. The electrochemical properties of supercapacitors based on LiNi0.8Co0.2O2 / MWNTs composite and LiNi0.8Co0.2O2/acet...Multiwalled carbon nanotubes (MWNTs) were used as the conductive additive in the electrode materials. The electrochemical properties of supercapacitors based on LiNi0.8Co0.2O2 / MWNTs composite and LiNi0.8Co0.2O2/acetylene black composite and MWNTs in 1.0 mol·L-1 LiClO4 / EC+DEC [V(EC)∶V(DEC)=1∶1] electrolyte were investigated by means of constant charge/discharge current tests, respectively. The experimental results show that the LiNi0.8Co0.2O2 / MWNTs composite has better performance than that of others, and the maximum specific capacitance of the supercapacitor can reach 271.6 F·g-1, while the energy density is up to 339.5 Wh·kg-1. Furthermore, it is remarkable that the performance of MWNTs is better than that of acetylene black as the conductive additive.展开更多
采用两步干混-球磨方法制备了石墨烯掺杂改性的锂离子电池LiFePO_4/LiNi_(0.8)Co_(0.15)Al_(0.05)O_2复合正极材料,实现LiNi_(0.8)Co_(0.15)Al_(0.05)O_2材料的高容量和高安全性。借助X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、X...采用两步干混-球磨方法制备了石墨烯掺杂改性的锂离子电池LiFePO_4/LiNi_(0.8)Co_(0.15)Al_(0.05)O_2复合正极材料,实现LiNi_(0.8)Co_(0.15)Al_(0.05)O_2材料的高容量和高安全性。借助X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、X射线光电子能谱(XPS)以及电化学测试等表征手段对材料的晶体结构、微观形貌和电化学性能进行了较系统的研究。结果表明,石墨烯的存在实现了Li Fe PO4材料在LiNi_(0.8)Co_(0.15)Al_(0.05)O_2材料表面的完全包覆,形成致密的包覆层,进一步抑制LiNi_(0.8)Co_(0.15)Al_(0.05)O_2与电解液之间的副反应,提高活性材料利用率和循环性能。三者之间构成导电网络,加快电子渗透和传输,提高倍率性能。Li Fe PO4质量分数为20%的Li Fe PO4-Graphene/LiNi_(0.8)Co_(0.15)Al_(0.05)O_2样品具有最佳的容量性能和长循环性能,0.1C时放电容量达到202.5 m Ah·g^(-1),3C时放电容量仍然可保持在160.5 m Ah·g^(-1)。50℃在2.8~4.3 V,0.5C下循环100次后,容量保持率为91.9%,优于LiNi_(0.8)Co_(0.15)Al_(0.05)O_2和LiFePO_4/LiNi_(0.8)Co_(0.15)Al_(0.05)O_2样品的72.9%和82.0%。展开更多
文摘Multiwalled carbon nanotubes (MWNTs) were used as the conductive additive in the electrode materials. The electrochemical properties of supercapacitors based on LiNi0.8Co0.2O2 / MWNTs composite and LiNi0.8Co0.2O2/acetylene black composite and MWNTs in 1.0 mol·L-1 LiClO4 / EC+DEC [V(EC)∶V(DEC)=1∶1] electrolyte were investigated by means of constant charge/discharge current tests, respectively. The experimental results show that the LiNi0.8Co0.2O2 / MWNTs composite has better performance than that of others, and the maximum specific capacitance of the supercapacitor can reach 271.6 F·g-1, while the energy density is up to 339.5 Wh·kg-1. Furthermore, it is remarkable that the performance of MWNTs is better than that of acetylene black as the conductive additive.
文摘采用两步干混-球磨方法制备了石墨烯掺杂改性的锂离子电池LiFePO_4/LiNi_(0.8)Co_(0.15)Al_(0.05)O_2复合正极材料,实现LiNi_(0.8)Co_(0.15)Al_(0.05)O_2材料的高容量和高安全性。借助X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、X射线光电子能谱(XPS)以及电化学测试等表征手段对材料的晶体结构、微观形貌和电化学性能进行了较系统的研究。结果表明,石墨烯的存在实现了Li Fe PO4材料在LiNi_(0.8)Co_(0.15)Al_(0.05)O_2材料表面的完全包覆,形成致密的包覆层,进一步抑制LiNi_(0.8)Co_(0.15)Al_(0.05)O_2与电解液之间的副反应,提高活性材料利用率和循环性能。三者之间构成导电网络,加快电子渗透和传输,提高倍率性能。Li Fe PO4质量分数为20%的Li Fe PO4-Graphene/LiNi_(0.8)Co_(0.15)Al_(0.05)O_2样品具有最佳的容量性能和长循环性能,0.1C时放电容量达到202.5 m Ah·g^(-1),3C时放电容量仍然可保持在160.5 m Ah·g^(-1)。50℃在2.8~4.3 V,0.5C下循环100次后,容量保持率为91.9%,优于LiNi_(0.8)Co_(0.15)Al_(0.05)O_2和LiFePO_4/LiNi_(0.8)Co_(0.15)Al_(0.05)O_2样品的72.9%和82.0%。