The dielectric properties and phase transition characteristics of La2O3- and Sb2O3-doped barium strontium titanate ceramics prepared by solid state route were investigated. The microstructure was identified by X-ray d...The dielectric properties and phase transition characteristics of La2O3- and Sb2O3-doped barium strontium titanate ceramics prepared by solid state route were investigated. The microstructure was identified by X-ray diffraction method and scanning electron microscope was also employed to observe the surface morphologies. It is found that （La,Sb）-codoped barium strontium titanate ceramics exhibit typical perovskite structure and the average grain size decreases dramatically with increasing the content of Sb2O3. Both La3＋ ions and Sb3＋ ions occupy the A-sites in perovskite lattice. The dielectric constant and dielectric loss of barium strontium titanate based ceramics are obviously influenced by La2O3 as well as Sb2O3 addition content. The tetragonal-cubic phase transition of La2O3 modified barium strontium titanate ceramics is of second order and the Curie temperature shifts to lower value with increasing the La2O3 doping content. The phase transition of （La,Sb）-codoped barium strontium titanate ceramics diffuses and the deviation from Curie-Weiss law becomes more obvious with the increase in Sb2O3 concentration. The temperature corresponding to the dielectric constant maximum of （La,Sb）-codoped barium strontium titanate ceramics decreases with increasing the Sb2O3 content, which is attributed to the replacement of host ions by the Sb3＋ ions.展开更多
A near infrared to visible blue, green, and red upconversion luminescence in a Tb^3＋-doped CaO-Al2O3-SiO2 glass was studied, which was excited using 800 nm femtosecond laser irradiation. The upconversion luminescence...A near infrared to visible blue, green, and red upconversion luminescence in a Tb^3＋-doped CaO-Al2O3-SiO2 glass was studied, which was excited using 800 nm femtosecond laser irradiation. The upconversion luminescence was attributed to ^5D3→^7F5, ^5D3→^7F4, ^5D3→^7F3, ^5D4→^7F6, ^5D4→^7F5, ^5D4→^7F4, and ^5D4→^7F3 transitions of Tb^3＋. The relationship between upconversion luminescence intensity and the pump power indicated that a three-photon simultaneous absorption process was dominant in this upconversion luminescence. The intense red, green, and blue upconversion luminescence of Tb^3＋-doped CaO-Al2O3-SiO2 glass may be potentially useful in developing three-dimensional display applications.展开更多
The humidity sensing properties of La^3＋ and K^＋ co-doped Ti0.9Sn0.1O2 thin films were investigated. The humidity sensitive thin films were prepared by sol-gel method on alumina substrates. The sensing behaviors of ...The humidity sensing properties of La^3＋ and K^＋ co-doped Ti0.9Sn0.1O2 thin films were investigated. The humidity sensitive thin films were prepared by sol-gel method on alumina substrates. The sensing behaviors of thin films were inspected at different sintering temperatures by constructing a humidity-impedance measuring system. It was found that the addition of rare earth ion La^3＋ and alkali ion K^＋ was beneficial for improving the humidity sensitive properties of the samples and La0.003K0.5Ti0.9Sn0.1O2 sintered at 500 ℃ for 4 h showed the best humidity sensing properties. The impedance of this thin film decreased from 109 to 104 Ω with excellent linearity in the humidity range of 11%-95%. Narrow hysteresis loop, prominent stability and high sensitivity were obtained. The effects of dopant con-tent and doping mechanism on humidity sensitivity were also discussed in terms of segregation of rare earth ions at grain boundaries and granularity of crystalline and influence of K^＋ on the decrease in the intrinsic resistance of the materials, and increase in the number of wa-ter adsorption sites.展开更多
（Y0.87La0.1Zr0.03）2O3 nanopowders doped with various concentrations of Tm^3＋ and Ho^3＋ were prepared by the citrate method. The standard cubic Y2O3 phase can be matched in the Tm^3＋/Ho^3＋ co-doped（Y0.87La0.1Zr0...（Y0.87La0.1Zr0.03）2O3 nanopowders doped with various concentrations of Tm^3＋ and Ho^3＋ were prepared by the citrate method. The standard cubic Y2O3 phase can be matched in the Tm^3＋/Ho^3＋ co-doped（Y0.87La0.1Zr0.03）2 O3 nanopowders. The nanopowders exhibit average particle sizes of 40,60, 80 and 100 nm after calcinated at 900,1000,1100 and 1200℃,respectively. The energy transfer from Tm^3＋ to Ho^3＋ and the optimum fluorescence emission around 2 μm were investigated. Results indicate that the emission bands at around 1.86 and 1.95 μm correspond to 3 F4→3 H6 transition of Tm^3＋ and 5 I7→5 I8 transition of Ho^3＋, respectively.Better spectral properties were achieved in Tm^3＋/Ho^3＋ co-doped（Y0.87La0.1Zr0.03）2O3 nanopowders with the average size of 100 nm obtained at the conditions of the treatment of precursors calcinated at 1200 ℃ for 2 h doped with 1.5 mol% Tm^3＋ and 1 mol% Ho^3＋.展开更多
采用光电子能谱分析方法对掺杂 L a2 O3的 Mo粉的性能进行了研究。结果表明 :掺杂 L a(NO3) 3的 Mo O2 粉经过还原处理后 ,Mo粉表面的纳米 L a2 O3微粒可以减小 Mo基体的特征能量损失峰 ,增加 Mo3d光电子谱峰强度 ;由于纳米 L a2 O3粒...采用光电子能谱分析方法对掺杂 L a2 O3的 Mo粉的性能进行了研究。结果表明 :掺杂 L a(NO3) 3的 Mo O2 粉经过还原处理后 ,Mo粉表面的纳米 L a2 O3微粒可以减小 Mo基体的特征能量损失峰 ,增加 Mo3d光电子谱峰强度 ;由于纳米 L a2 O3粒子在金属 Mo的表面及周围对 Mo起到包埋效应 ,减小了 Mo与大气的接触面积 ,从而使展开更多
A new stearic acid method(SAM) has been used to prepare ultrafine K2La2Ti3O10 nanocrystalline. Each state of synthesis process was followed by the use of FT IR analysis. The resulting materials have been characterized...A new stearic acid method(SAM) has been used to prepare ultrafine K2La2Ti3O10 nanocrystalline. Each state of synthesis process was followed by the use of FT IR analysis. The resulting materials have been characterized by means of XRD, TEM, BET surface area analysis. The acid exchanging property of the obtained product was also studied. The experimental results showed that comparing with the product of traditional solid state reaction, the particle size of the K2La2Ti3O10 synthesized by SAM is greatly reduced, BET surface area is high(more than 11.83m2· g- 1) and has different acid exchanging properties. It can be easily exfoliated in 2mol· L- 1 HNO3 solution.展开更多
基金Project (11KJB430007) supported by the University Natural Science Research Program of Jiangsu Province, ChinaProject supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions, China
文摘The dielectric properties and phase transition characteristics of La2O3- and Sb2O3-doped barium strontium titanate ceramics prepared by solid state route were investigated. The microstructure was identified by X-ray diffraction method and scanning electron microscope was also employed to observe the surface morphologies. It is found that （La,Sb）-codoped barium strontium titanate ceramics exhibit typical perovskite structure and the average grain size decreases dramatically with increasing the content of Sb2O3. Both La3＋ ions and Sb3＋ ions occupy the A-sites in perovskite lattice. The dielectric constant and dielectric loss of barium strontium titanate based ceramics are obviously influenced by La2O3 as well as Sb2O3 addition content. The tetragonal-cubic phase transition of La2O3 modified barium strontium titanate ceramics is of second order and the Curie temperature shifts to lower value with increasing the La2O3 doping content. The phase transition of （La,Sb）-codoped barium strontium titanate ceramics diffuses and the deviation from Curie-Weiss law becomes more obvious with the increase in Sb2O3 concentration. The temperature corresponding to the dielectric constant maximum of （La,Sb）-codoped barium strontium titanate ceramics decreases with increasing the Sb2O3 content, which is attributed to the replacement of host ions by the Sb3＋ ions.
基金supported by the Education Department of Zhejiang Province (20050359)
文摘A near infrared to visible blue, green, and red upconversion luminescence in a Tb^3＋-doped CaO-Al2O3-SiO2 glass was studied, which was excited using 800 nm femtosecond laser irradiation. The upconversion luminescence was attributed to ^5D3→^7F5, ^5D3→^7F4, ^5D3→^7F3, ^5D4→^7F6, ^5D4→^7F5, ^5D4→^7F4, and ^5D4→^7F3 transitions of Tb^3＋. The relationship between upconversion luminescence intensity and the pump power indicated that a three-photon simultaneous absorption process was dominant in this upconversion luminescence. The intense red, green, and blue upconversion luminescence of Tb^3＋-doped CaO-Al2O3-SiO2 glass may be potentially useful in developing three-dimensional display applications.
文摘The humidity sensing properties of La^3＋ and K^＋ co-doped Ti0.9Sn0.1O2 thin films were investigated. The humidity sensitive thin films were prepared by sol-gel method on alumina substrates. The sensing behaviors of thin films were inspected at different sintering temperatures by constructing a humidity-impedance measuring system. It was found that the addition of rare earth ion La^3＋ and alkali ion K^＋ was beneficial for improving the humidity sensitive properties of the samples and La0.003K0.5Ti0.9Sn0.1O2 sintered at 500 ℃ for 4 h showed the best humidity sensing properties. The impedance of this thin film decreased from 109 to 104 Ω with excellent linearity in the humidity range of 11%-95%. Narrow hysteresis loop, prominent stability and high sensitivity were obtained. The effects of dopant con-tent and doping mechanism on humidity sensitivity were also discussed in terms of segregation of rare earth ions at grain boundaries and granularity of crystalline and influence of K^＋ on the decrease in the intrinsic resistance of the materials, and increase in the number of wa-ter adsorption sites.
基金Project supported by Zhejiang Provincial Natural Science Foundation of China(LZ14B010001)
文摘（Y0.87La0.1Zr0.03）2O3 nanopowders doped with various concentrations of Tm^3＋ and Ho^3＋ were prepared by the citrate method. The standard cubic Y2O3 phase can be matched in the Tm^3＋/Ho^3＋ co-doped（Y0.87La0.1Zr0.03）2 O3 nanopowders. The nanopowders exhibit average particle sizes of 40,60, 80 and 100 nm after calcinated at 900,1000,1100 and 1200℃,respectively. The energy transfer from Tm^3＋ to Ho^3＋ and the optimum fluorescence emission around 2 μm were investigated. Results indicate that the emission bands at around 1.86 and 1.95 μm correspond to 3 F4→3 H6 transition of Tm^3＋ and 5 I7→5 I8 transition of Ho^3＋, respectively.Better spectral properties were achieved in Tm^3＋/Ho^3＋ co-doped（Y0.87La0.1Zr0.03）2O3 nanopowders with the average size of 100 nm obtained at the conditions of the treatment of precursors calcinated at 1200 ℃ for 2 h doped with 1.5 mol% Tm^3＋ and 1 mol% Ho^3＋.
文摘A new stearic acid method(SAM) has been used to prepare ultrafine K2La2Ti3O10 nanocrystalline. Each state of synthesis process was followed by the use of FT IR analysis. The resulting materials have been characterized by means of XRD, TEM, BET surface area analysis. The acid exchanging property of the obtained product was also studied. The experimental results showed that comparing with the product of traditional solid state reaction, the particle size of the K2La2Ti3O10 synthesized by SAM is greatly reduced, BET surface area is high(more than 11.83m2· g- 1) and has different acid exchanging properties. It can be easily exfoliated in 2mol· L- 1 HNO3 solution.