The μi-T curves of the alloy Fe73.5Cu1 Nb3Si13.5B9 in the amorphous state and in the nanocrys-talline state have been investigated. For comparison, μi-T curves of the other two kinds of typical soft magnetic alloys ...The μi-T curves of the alloy Fe73.5Cu1 Nb3Si13.5B9 in the amorphous state and in the nanocrys-talline state have been investigated. For comparison, μi-T curves of the other two kinds of typical soft magnetic alloys also have been measured. It was found that a sharp Hopkinson peak appeared at the Curie point for each amorphous and crystalline alloy but there was no Hopkinson peak for the nanocrystalline alloy at the Curie point of the residual amorphous phase. This phenomenon has been explained in terms of the characteristic temperature dependence of the effective magnetic anisotropy.展开更多
In order to investigate the effect of sample size on the dynamic torsional behaviour of the 2A12 aluminium alloy. In this paper, torsional split Hopkinson bar tests are conducted on this alloy with different sample di...In order to investigate the effect of sample size on the dynamic torsional behaviour of the 2A12 aluminium alloy. In this paper, torsional split Hopkinson bar tests are conducted on this alloy with different sample dimensions. It is found that with the decreasing gauge length and thickness, the tested yield strength increases. However, the sample innerlouter diameter has little effect on the dynamic torsional behaviour. Based on the finite element method, the stress states in the alloy with different sample sizes are analysed. Due to the effect of stress concentration zone （SCZ）, the shorter sample has a higher yield stress. Furthermore, the stress distributes more uniformly in the thinner sample, which leads to the higher tested yield stress. According to the experimental and simulation analysis, some suggestions on choosing the sample size are given as well.展开更多
基金National Natural Science Foundation of China! under grant No. 59871013.
文摘The μi-T curves of the alloy Fe73.5Cu1 Nb3Si13.5B9 in the amorphous state and in the nanocrys-talline state have been investigated. For comparison, μi-T curves of the other two kinds of typical soft magnetic alloys also have been measured. It was found that a sharp Hopkinson peak appeared at the Curie point for each amorphous and crystalline alloy but there was no Hopkinson peak for the nanocrystalline alloy at the Curie point of the residual amorphous phase. This phenomenon has been explained in terms of the characteristic temperature dependence of the effective magnetic anisotropy.
基金Financial support is from the NSFC(Grant Nos.11602257,11472257,11272300,11572299)funded by the key subject"Computational Solid Mechanics"of the China Academy of Engineering Physics
文摘In order to investigate the effect of sample size on the dynamic torsional behaviour of the 2A12 aluminium alloy. In this paper, torsional split Hopkinson bar tests are conducted on this alloy with different sample dimensions. It is found that with the decreasing gauge length and thickness, the tested yield strength increases. However, the sample innerlouter diameter has little effect on the dynamic torsional behaviour. Based on the finite element method, the stress states in the alloy with different sample sizes are analysed. Due to the effect of stress concentration zone （SCZ）, the shorter sample has a higher yield stress. Furthermore, the stress distributes more uniformly in the thinner sample, which leads to the higher tested yield stress. According to the experimental and simulation analysis, some suggestions on choosing the sample size are given as well.