Sulfuric acid immobilized on silica gel is designed as a very useful catalyst for synthesis of 2,3-unsaturated glycopyranosides. This handy,metal-free,environment friendly transformation provides high yields andα-ste...Sulfuric acid immobilized on silica gel is designed as a very useful catalyst for synthesis of 2,3-unsaturated glycopyranosides. This handy,metal-free,environment friendly transformation provides high yields andα-stereoselectivities in a very few amount （0.02 eq.） of catalyst and in short reaction times（10 min）.展开更多
A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acid...A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.展开更多
[ Objective] The aim was to study pretreatment of ultrasound enhancing dilute H2SO4 on cellulase activity of corn straw liquid fermentation and explore the pretretment＇ s optimal conditions. [ Method ] By using ortho...[ Objective] The aim was to study pretreatment of ultrasound enhancing dilute H2SO4 on cellulase activity of corn straw liquid fermentation and explore the pretretment＇ s optimal conditions. [ Method ] By using orthogonal test, the pretretment of ultrasound enhancing dilute H2SO4 on corn straw was studied, then straw was fermented as the sole carbon source. Finally, the cellulase activity in extracellular fermentation broth was determined. [Result] The results showed that cellulase activity in extracellular broth was greatest under the conditions of acid bath time 3 h, acid concentration 3.5%, ultrasonic power 150 W, and ultrasonic time 5 h. They were FPA 15.82 U/ml, Cx 39.9 U/ml, 13-Giu 55.94 U/ml respectively. [ Conclusion] Under the above conditions, extracellular cellulase production has a high stability.展开更多
Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part i...Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.展开更多
A SiC/ZrSiO4？SiO2 （SZS） coating was successfully fabricated on the carbon/carbon （C/C） composites by pack cementation, slurry painting and sintering to improve the anti-oxidation property and thermal shock r...A SiC/ZrSiO4？SiO2 （SZS） coating was successfully fabricated on the carbon/carbon （C/C） composites by pack cementation, slurry painting and sintering to improve the anti-oxidation property and thermal shock resistance. The anti-oxidation properties under different oxygen partial pressures （OPP） and thermal shock resistance of the SZS coating were investigated. The results show that the SZS coated sample under low OPP, corresponding to the ambient air, during isothermal oxidation was 0.54% in mass gain after 111 h oxidation at 1500 ° C and less than 0.03% in mass loss after 50 h oxidation in high OPP, corresponding to the air flow rate of 36 L/h. Additionally, the residual compressive strengths （RCS） of the SZS coated samples after oxidation for 50 h in high OPP and 80 h in low OPP remain about 70% and 72.5% of those of original C/C samples, respectively. Moreover, the mass loss of SZS coated samples subjected to the thermal cycle from 1500 ° C in high OPP to boiling water for 30 times was merely 1.61%.展开更多
基金The project was supported by Shanghai Rising-Star Program(No.06QA14018)University Students Innovative Activities Project of Shanghai Municipal Education Commission(No.KY2008-09S)
文摘Sulfuric acid immobilized on silica gel is designed as a very useful catalyst for synthesis of 2,3-unsaturated glycopyranosides. This handy,metal-free,environment friendly transformation provides high yields andα-stereoselectivities in a very few amount （0.02 eq.） of catalyst and in short reaction times（10 min）.
文摘A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.
基金Supported by the National Key Technology R&D Program during the11~(th)five-year Plan(2007BAD34B03)the Important Project of Ministryof Education(107127)Scientific Research Foundation ofHefei University of Technology(113-036404)~~
文摘[ Objective] The aim was to study pretreatment of ultrasound enhancing dilute H2SO4 on cellulase activity of corn straw liquid fermentation and explore the pretretment＇ s optimal conditions. [ Method ] By using orthogonal test, the pretretment of ultrasound enhancing dilute H2SO4 on corn straw was studied, then straw was fermented as the sole carbon source. Finally, the cellulase activity in extracellular fermentation broth was determined. [Result] The results showed that cellulase activity in extracellular broth was greatest under the conditions of acid bath time 3 h, acid concentration 3.5%, ultrasonic power 150 W, and ultrasonic time 5 h. They were FPA 15.82 U/ml, Cx 39.9 U/ml, 13-Giu 55.94 U/ml respectively. [ Conclusion] Under the above conditions, extracellular cellulase production has a high stability.
文摘Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.
基金Project supported by the Nonferrous Metal Oriented Advanced Structural Materials and Manufacturing Cooperative Innovation Center,ChinaProject(51205417)supported by the National Natural Science Foundation of China
文摘A SiC/ZrSiO4？SiO2 （SZS） coating was successfully fabricated on the carbon/carbon （C/C） composites by pack cementation, slurry painting and sintering to improve the anti-oxidation property and thermal shock resistance. The anti-oxidation properties under different oxygen partial pressures （OPP） and thermal shock resistance of the SZS coating were investigated. The results show that the SZS coated sample under low OPP, corresponding to the ambient air, during isothermal oxidation was 0.54% in mass gain after 111 h oxidation at 1500 ° C and less than 0.03% in mass loss after 50 h oxidation in high OPP, corresponding to the air flow rate of 36 L/h. Additionally, the residual compressive strengths （RCS） of the SZS coated samples after oxidation for 50 h in high OPP and 80 h in low OPP remain about 70% and 72.5% of those of original C/C samples, respectively. Moreover, the mass loss of SZS coated samples subjected to the thermal cycle from 1500 ° C in high OPP to boiling water for 30 times was merely 1.61%.