A novel Ni-Cr-Si-B filler metal with the cluster formula of[Cr-Ni12]B2Cr+[B-Ni8Cr]BSi Cr based on the cluster-plus-glue-atom model was designed for vacuum brazing GH4169 alloy.The effect of brazing temperature and bra...A novel Ni-Cr-Si-B filler metal with the cluster formula of[Cr-Ni12]B2Cr+[B-Ni8Cr]BSi Cr based on the cluster-plus-glue-atom model was designed for vacuum brazing GH4169 alloy.The effect of brazing temperature and brazing time on microstructure and shear strength of GH4169 alloy joints was investigated.The brazed seam was mainly composed ofγ-Ni solid solution.(Nb,Ti)-rich phase and(Cr,Nb,Mo)-rich borides distributed in diffusion zones.The diffusion and aggregation of B,Cr,Nb,and Mo resulted in the variation of phase contrast and morphology of borides.Coarse precipitations in the joint brazed at1240℃consisted of borides,Laves phase andδphase.The shear strength of joints was principally dominated by the brittle precipitations in diffusion zone,and the homogenization of microstructure improved the room-temperature shear strength to 820 MPa with the high-temperature shear strength of 627 MPa for the joint brazed at 1240℃/20 min.The joint fractured in diffusion zone and brazed seam,and the existence of borides and Laves phase in diffusion zone provide the potential origin for crack growth.展开更多
Composition homogenization in solid solution is important for industrial alloys. In the present work, a solute homogenization model is proposed based on the chemical short-range-order tendency in Mg-Gd- based alloys. ...Composition homogenization in solid solution is important for industrial alloys. In the present work, a solute homogenization model is proposed based on the chemical short-range-order tendency in Mg-Gd- based alloys. After a calculation using the cluster-plus-glue-atom model, the stable Mg-Gd structural unit is derived, [Gd-Mg12 ]Mg6, where one solute Gd is nearest-neighbored with twelve Mg atoms to form the characteristic hcp cluster [Gd-Mg12 ] and this cluster is matched with six Mg glue atoms. Such a local unit is then mixed with [Mg-Mg12 ]Mg3, the stable unit for pure Mg. Assuming that the Gd-containing units are arranged in fcc- or bcc-like lattice points and the Mg units in their octahedral interstices, three proportions between the two units are obtained, 1：1, 2：3, and 1：3, which constitute three solute homogenization modes. The prevailing Mg-Gd-based alloys are consequently classified into three groups, respectively exemplified by GW103 K （Mg-10Gd-3Y-0.4Zr, wt%）, GW83 K （Mg-SGd-3Y-0.4Zr）, and GW63 K （Mg-6Gd- 3Y-0.4Zr）. Mg-Gd-Y-Zr alloys were designed following the model （where Y and Zr were also added in substitution for Gd） and prepared by permanent-mould casting. According to their mechanical properties, the 1：3 alloy （Mg-5.9Gd-1.6Y-0.4Zr） shows the best comprehensive properties （ultimate tensile strength 305 MPa, yield strength 186 MPa, elongation 9.0%） in solution plus ageing state.2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science ＆ Technology.展开更多
基金financially supported by the National Natural Science Foundation of China(51674060)the Fundamental Research Funds for the Central Universities(DUT18LAB01).
文摘A novel Ni-Cr-Si-B filler metal with the cluster formula of[Cr-Ni12]B2Cr+[B-Ni8Cr]BSi Cr based on the cluster-plus-glue-atom model was designed for vacuum brazing GH4169 alloy.The effect of brazing temperature and brazing time on microstructure and shear strength of GH4169 alloy joints was investigated.The brazed seam was mainly composed ofγ-Ni solid solution.(Nb,Ti)-rich phase and(Cr,Nb,Mo)-rich borides distributed in diffusion zones.The diffusion and aggregation of B,Cr,Nb,and Mo resulted in the variation of phase contrast and morphology of borides.Coarse precipitations in the joint brazed at1240℃consisted of borides,Laves phase andδphase.The shear strength of joints was principally dominated by the brittle precipitations in diffusion zone,and the homogenization of microstructure improved the room-temperature shear strength to 820 MPa with the high-temperature shear strength of 627 MPa for the joint brazed at 1240℃/20 min.The joint fractured in diffusion zone and brazed seam,and the existence of borides and Laves phase in diffusion zone provide the potential origin for crack growth.
基金supported financially by the National Key Research and Development Program of China (No. 2016YFB0701201)the Natural Science Foundation of China (No. 11674045)
文摘Composition homogenization in solid solution is important for industrial alloys. In the present work, a solute homogenization model is proposed based on the chemical short-range-order tendency in Mg-Gd- based alloys. After a calculation using the cluster-plus-glue-atom model, the stable Mg-Gd structural unit is derived, [Gd-Mg12 ]Mg6, where one solute Gd is nearest-neighbored with twelve Mg atoms to form the characteristic hcp cluster [Gd-Mg12 ] and this cluster is matched with six Mg glue atoms. Such a local unit is then mixed with [Mg-Mg12 ]Mg3, the stable unit for pure Mg. Assuming that the Gd-containing units are arranged in fcc- or bcc-like lattice points and the Mg units in their octahedral interstices, three proportions between the two units are obtained, 1：1, 2：3, and 1：3, which constitute three solute homogenization modes. The prevailing Mg-Gd-based alloys are consequently classified into three groups, respectively exemplified by GW103 K （Mg-10Gd-3Y-0.4Zr, wt%）, GW83 K （Mg-SGd-3Y-0.4Zr）, and GW63 K （Mg-6Gd- 3Y-0.4Zr）. Mg-Gd-Y-Zr alloys were designed following the model （where Y and Zr were also added in substitution for Gd） and prepared by permanent-mould casting. According to their mechanical properties, the 1：3 alloy （Mg-5.9Gd-1.6Y-0.4Zr） shows the best comprehensive properties （ultimate tensile strength 305 MPa, yield strength 186 MPa, elongation 9.0%） in solution plus ageing state.2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science ＆ Technology.