Self-designed Al8Si0.4Mg0.4Fe aluminium alloy was modified with Sr,followed by solid solution and aging treatments to regulate its microstructure and mechanical/electrical properties.The results show that after the mo...Self-designed Al8Si0.4Mg0.4Fe aluminium alloy was modified with Sr,followed by solid solution and aging treatments to regulate its microstructure and mechanical/electrical properties.The results show that after the modification treatment,the room-temperature tensile strength of the alloy remains nearly unchanged,the elongation at break slightly increases from 1.82%to 3.34%,and the electrical conductivity significantly increases from 40.1%international annealed copper standard(IACS)to 42.0%IACS.After the modification,the alloy was subjected to solid solution treatment at 515℃for 8 h,followed by aging treatment at 180,200,220 and 240℃for 6 h.With increasing aging temperature,the electrical conductivity increases monotonously from 41.4%IACS to 45.5%IACS,while the room-temperature tensile strength initially increases and then decreases.At 200℃,the alloy achieves an optimal balance between electrical conductivity and room-temperature tensile strength:the electrical conductivity is 42.5%IACS,and the room-temperature tensile strength is 282.9 MPa.When the aging temperature continues to rise,the alloy undergoes overaging.Although the conductivity continues to increase,the room-temperature tensile strength drops sharply,and it is only 177.1 MPa at 240℃.展开更多
Compared with Cu/Al_(2)O_(3)composites,high-strength Cu/Al_(2)O_(3)composites usually exhibit obviously deteriorated electrical conductivity.A chemical and mechanical alloying-based strategy was adopted to fabricate u...Compared with Cu/Al_(2)O_(3)composites,high-strength Cu/Al_(2)O_(3)composites usually exhibit obviously deteriorated electrical conductivity.A chemical and mechanical alloying-based strategy was adopted to fabricate ultrafine composite powders with lowcontent reinforcement and constructed a combined structure of Cu ultrafine powders covered with in-situ Al_(2)O_(3)nanoparticles.After consolidation at a relatively lower sintering temperature of 550℃,high-volume-fraction ultrafine grains were introduced into the Cu/Al_(2)O_(3)composite,and many in-situ Al_(2)O_(3)nanoparticles with an average size of 11.7±7.5 nm were dispersed homogeneously in the Cu grain.Results show that the composite demonstrates an excellent balance of high tensile strength(654±1 MPa)and high electrical conductivity(84.5±0.1%IACS),which is ascribed to the synergistic strengthening effect of ultrafine grains,dislocations,and in-situ Al_(2)O_(3)nanoparticles.This approach,which utilizes ultrafine composite powder with low-content reinforcement as a precursor and employs low-temperature and high-pressure sintering subsequently,may hold promising potential for large-scale industrial production of high-performance oxide dispersion strengthened alloys.展开更多
The effects of forward extrusion as well as extrusion combined with reversible torsion(KoBo extrusion),followed by additional deformation via the MaxStrain module of the Gleeble thermomechanical simulator,on the micro...The effects of forward extrusion as well as extrusion combined with reversible torsion(KoBo extrusion),followed by additional deformation via the MaxStrain module of the Gleeble thermomechanical simulator,on the microstructure,mechanical properties,and electrical conductivity of a Cu−0.7Mg(wt.%)alloy,were investigated.The simulation results highlighted the critical influence of processing history on determining the equivalent strain distribution.The sample subjected to forward extrusion at 400℃and subsequent MaxStrain processing(FM sample),possessed 76%lower grain size compared to the sample processed solely with MaxStrain(AM sample).Likewise,the KoBo-extruded and MaxStrain-processed sample(KM sample)exhibited 66%smaller grain size compared to the AM sample.Tensile test results revealed that the AM,FM,and KM samples,respectively,possessed 251%,288%,and 360%higher yield strength,and 95%,121%,and 169%higher tensile strength compared to the initial annealed alloy,as a result of grain refinement as well as deformation strengthening.Finally,the electrical conductivity measurements revealed that AM,FM,and KM samples,respectively,possessed electrical conductivity values of 37.9,35.6,and 32.0 MS/m,which,by considering their mechanical properties,makes them eligible to be categorized as high-strength and high-conductivity copper alloys.展开更多
The effects of drawing strain during intermediate annealing on the microstructure and properties of Cu-20 wt%Fe alloy wires while maintaining constant total deformation were investigated.Intermediate annealing effecti...The effects of drawing strain during intermediate annealing on the microstructure and properties of Cu-20 wt%Fe alloy wires while maintaining constant total deformation were investigated.Intermediate annealing effectively removes work hardening in both the Cu matrix and Fe fibers,restoring their plastic deformation capacity and preserving fiber continuity during subsequent redrawing.The process also refines the Fe phase,leading to a more uniform size distribution and straighter,better-aligned Cu/Fe phase interfaces,thereby enhancing the comprehensive properties of the alloy.The magnitude of drawing strain during intermediate annealing plays a critical role in balancing the mechanical strength and electrical conductivity of redrawn wires.A lower initial drawing strain requires greater redrawing strain,leading to excessive hardening of the Fe fibers,which negatively impacts the electrical conductivity and tensile plasticity.Conversely,a higher initial drawing strain can result in insufficient work hardening during the redrawing deformation process,yielding minimal strength improvements.Among the tested alloys,H/3.5 wires show a slight reduction in strength and hardness compared to W and H/4.5 wires but exhibit a significant increase in tensile elongation and electrical conductivity.The tensile strength was 755 MPa,and the electrical conductivity was 47%international-annealed copper standard(IACS).The optimal performance is attributed to the formation of a high-density,ultrafine Fe fiber structure-aligned parallel to the drawing direction,which is achieved through a suitable combination of the drawing process and intermediate annealing.展开更多
In thermoelectricity,the inherent coupling between electrical conductivity and Seebeck coefficient represents a fundamental challenge in thermoelectric materials development.Herein,we present a unique pressure-tuning ...In thermoelectricity,the inherent coupling between electrical conductivity and Seebeck coefficient represents a fundamental challenge in thermoelectric materials development.Herein,we present a unique pressure-tuning strategy using compressible layered 2H-MoTe2,achieving an effective decoupling between the electrical conductivity and Seebeck coefficient.The applied pressure simultaneously induces two complementary effects:(1)bandgap reduction that moderately enhances carrier concentration to improve the electrical conductivity,and(2)band convergence that dramatically increases density-of-states effective mass to boost the Seebeck coefficient.This dual mechanism yields an extraordinary 18.5-fold enhancement in the average power factor.First-principles calculations and Boltzmann transport modeling precisely reproduce the experimental observations,validating this pressure-induced decoupling mechanism.The pressure-tuning mechanism provides a feasible and effective strategy for breaking through the optimization limits of the power factor,facilitating the design of high-performance thermoelectric materials.展开更多
Immiscible bimetal systems,of which tungsten–copper(W–Cu)is a typical representative,have crucial applications in fields requiring both mechanical and physical properties.Nevertheless,it is a major challenge to dete...Immiscible bimetal systems,of which tungsten–copper(W–Cu)is a typical representative,have crucial applications in fields requiring both mechanical and physical properties.Nevertheless,it is a major challenge to determine how to give full play to the advantages of the two phases of the bimetal and achieve outstanding comprehensive properties.In this study,an ultrafine-grained W–Cu bimetal with spatially connected Cu and specific Wislands was fabricated through a designed powder-mixing process and subsequent rapid low-temperature sintering.The prepared bimetal concurrently has a high yield strength,large plastic strain,and high electrical conductivity.The stress distribution and strain response of individual phases in different types of W–Cu bimetals under loading were quantified by means of a simulation.The high yield strength of the reported bimetal results from the microstructure refinement and high contiguity of the grains in the W islands,which enhance the contribution of W to the total plastic deformation of the bimetal.The high electrical conductivity is attributed to the increased mean free path of the Cu and the reduced proportion of phase boundaries due to the specific phase combination of W islands and Cu.This work provides new insight into modulating phase configuration in immiscible metallic composites to achieve high-level multi-objective properties.展开更多
The deformation of Cu–20 wt.%Fe alloy wires leads to a significant improvement in mechanical properties and a decrease in electrical conductivity.Simultaneous improvements in strength and conductivity were achieved b...The deformation of Cu–20 wt.%Fe alloy wires leads to a significant improvement in mechanical properties and a decrease in electrical conductivity.Simultaneous improvements in strength and conductivity were achieved by intermediate annealing of drawn Cu–20 wt.%Fe wires.As the annealing temperature increased,the strength of Cu–20 wt.%Fe alloy wire decreased monotonically,but the electrical conductivity first increased and then decreased,reaching its peak value after annealing at 500℃.The decrease in strength is related to dislocation recovery and static recrystallization of Cu and Fe phases,and the increase in electrical conductivity mainly results from the aging precipitation of solid solution Fe.After annealing at 500℃,there was no obvious recrystallization of Cu phase,and many of the nano-Fe particles precipitated from Cu matrix.An annealing temperature of 600℃ induced the recrystallization of Cu matrix and an increase in Fe solid solubility,resulting in a decrease in strength and electrical conductivity.Subsequently,the wires annealed at 500℃ were drawn to 2 mm.Compared with those of the continuously drawn Cu–20 wt.%Fe alloy wires,the deformation ability,strength,and electrical conductivity of Cu–20 wt.%Fe alloy wires subjected to intermediate annealing treatment are significantly greater.This is mainly related to the sufficient precipitation of Fe in Cu matrix and the strengthening of refined Fe fibers parallel to the drawing direction.展开更多
Magnesium(Mg)alloys offer significant potential for conductive applications,thanks to their distinctive attributes,including high specific strength,excellent electrical conductivity(EC),low density,electromagnetic int...Magnesium(Mg)alloys offer significant potential for conductive applications,thanks to their distinctive attributes,including high specific strength,excellent electrical conductivity(EC),low density,electromagnetic interference shielding effectiveness(EMI SE),and recyclability.However,a major challenge in Mg alloy research is balancing high strength with good EC,as strengthening these alloys often compromises their EC.This paper offers an in-depth analysis of the mechanisms,strategies,and applications aimed at improving the EC of Mg alloys.A bibliometric study is performed to uncover the main research trends and emerging hotspots within the field.The review then examines various strategies to improve EC focusing on factors such as solute elements,second phases,grain boundaries,textures,and vacancies.By carefully controlling alloy composition and optimizing heat treatment processes,significant advancements have been achieved by researchers in developing Mg alloys that possess both high strength and high EC,especially in Mg-Al,Mg-Zn,Mg-RE alloy systems and composites.Finally,the paper outlines future research directions,stressing the importance of further exploration into alloying element selection,heat treatment optimization,and other advanced strategies.These efforts are crucial for overcoming current challenges and expanding the application of Mg alloys in EC fields.展开更多
Lightweight aluminum alloy conductor materials(Al-Mg-Si alloys)require not only high electrical conductivity to reduce electrical loss,but also high strength to withstand extreme weather conditions.To improve electric...Lightweight aluminum alloy conductor materials(Al-Mg-Si alloys)require not only high electrical conductivity to reduce electrical loss,but also high strength to withstand extreme weather conditions.To improve electrical conductivity and mechanical properties of Al-Mg-Si alloy simultaneously,the rare earth La was introduced to modify the Al-Mg-Si alloy.The effect of La addition on the microstructure,tensile properties and electrical conductivity of cast Al-Mg-Si alloy was investigated systematically.Results indicate that the appropriate La content is helpful to improve the strength and electrical conductivity of Al-Mg-Si alloys.When the addition of La is 0.2wt.%,theα-Al grains are refined apparently,Mg and Si solute atoms in the Al matrix are reduced by the formation of Mg_(2)Si phase;the distribution of Al_(11)La_(3)phases is uniform,and the morphology of AlFeSi phase transforms from continuous state to discontinuous state.The Al-Mg-Si-0.2La alloy exhibits the optimal tensile properties and electrical conductivity,with an ultimate tensile strength of 170 MPa,a yield strength of 88 MPa,an elongation of 18.9%,and an electrical conductivity of 44.0%IACS.These values represent improvements of 9.0%,15.8%,70.3%,and 17.3%,respectively,compared to the Al-Mg-Si alloy without La addition.However,excessive La deteriorates the properties of Al-Mg-Si-xLa alloys.展开更多
High-performance Ti_(3)C_(2)T_(x)fibers have garnered significant potential for smart fibers enabled fabrics.Nonetheless,a major challenge hindering their widespread use is the lack of strong interlayer interactions b...High-performance Ti_(3)C_(2)T_(x)fibers have garnered significant potential for smart fibers enabled fabrics.Nonetheless,a major challenge hindering their widespread use is the lack of strong interlayer interactions between Ti_(3)C_(2)T_(x)nanosheets within fibers,which restricts their properties.Herein,a versatile strategy is proposed to construct wet-spun Ti_(3)C_(2)T_(x)fibers,in which trace amounts of borate form strong interlayer crosslinking between Ti_(3)C_(2)T_(x)nanosheets to significantly enhance interactions as supported by density functional theory calculations,thereby reducing interlayer spacing,diminishing microscopic voids and promoting orientation of the nanosheets.The resultant Ti_(3)C_(2)T_(x)fibers exhibit exceptional electrical conductivity of 7781 S cm^(-1)and mechanical properties,including tensile strength of 188.72 MPa and Young's modulus of 52.42 GPa.Notably,employing equilibrium molecular dynamics simulations,finite element analysis,and cross-wire geometry method,it is revealed that such crosslinking also effectively lowers interfacial thermal resistance and ultimately elevates thermal conductivity of Ti_(3)C_(2)T_(x)fibers to 13 W m^(-1)K^(-1),marking the first systematic study on thermal conductivity of Ti_(3)C_(2)T_(x)fibers.The simple and efficient interlayer crosslinking enhancement strategy not only enables the construction of thermal conductivity Ti_(3)C_(2)T_(x)fibers with high electrical conductivity for smart textiles,but also offers a scalable approach for assembling other nanomaterials into multifunctional fibers.展开更多
Polymer dielectrics possessing excellent electrical insulation and high thermal conductivity are pivotal for dielectric capacitors at elevated temperatures.However,the integration of electrical insulation and thermal ...Polymer dielectrics possessing excellent electrical insulation and high thermal conductivity are pivotal for dielectric capacitors at elevated temperatures.However,the integration of electrical insulation and thermal conductivity in polymers remains a challenge.In this work,we present a feasible strategy to integrate high electrical insulation and high thermal conductivity by bonding carbon quantum dots(CQDs)with the diamine monomer of polyetherimide(PEI).The CQDs with Coulomb blockade effect serve as traps for the migrating of electrons in the dielectrics,while the bonding networks formed by CQDs and PEI further deepen the traps and augment trap density.As a result,the hybrid dielectrics(PEI-NH_(2)-CQDs)exhibit nearly an order of magnitude higher electrical resistivity than that of pure PEI,leading to an 80%increase in discharge energy density with an energy efficiency of 90%at 200℃ compared to pure counterpart.Additionally,this all-organic dielectric achieves a significantly increased thermal conductivity of 0.65 W m^(-1) K^(-1) compared to 0.26 W m^(-1) K^(-1) of PEI,which supports its cyclic stability at elevated temperatures.We also demonstrate the kilogram-scale production of CQDs,synthesizing over 8 kg in a single batch,paving the way for large-scale production of reliable PEI-NH_(2)-CQDs dielectrics.展开更多
Polyvinyl alcohol(PVA)hydrogels doped with cyclohexane-1,2,3,4,5,6-hexacarboxylic acid(CHA)were successfully prepared during drying and swelling.Structural and morphological characterizations suggest the carboxyl and ...Polyvinyl alcohol(PVA)hydrogels doped with cyclohexane-1,2,3,4,5,6-hexacarboxylic acid(CHA)were successfully prepared during drying and swelling.Structural and morphological characterizations suggest the carboxyl and hydroxyl groups in the material undergo esterification during the preparation of the material,which contributes to the high transparency with 90%transmittance in the 400 to 800 nm range and robust mechanical properties of the material with a tensile strength at a break of 27.55 MPa.It is noteworthy that the bending and torsion angles exhibit a strong linear correlation with electrical resistance,enabling the monitoring of the bending motion state of each human body segment.展开更多
Proton exchange membrane(PEM)is an integral component in fuel cells which enables proton transport for efficient energy conversion.Sulfonated Polyether Ether Ketone(SPEEK)has emerged as a cost-effective option with no...Proton exchange membrane(PEM)is an integral component in fuel cells which enables proton transport for efficient energy conversion.Sulfonated Polyether Ether Ketone(SPEEK)has emerged as a cost-effective option with non-fluorinated aromatic backbones for Proton Exchange Membrane Fuel Cell(PEMFC)applications,even though it exhibits lower proton conductivity compared to Nafion.This work aims to study the influence of Sulfonated Chitosan(SCS)concentrations on proton conductivity of SPEEK-based PEM at room temperature.SPEEK was synthesized using a sulfonation process with concentrated sulfuric acid at room temperature.SCS was synthesized via reflux of CS and 1.2 M H2SO4 with a ratio of 1:35(w/v)at 90℃ for 30 min.The composite membranes of SPEEK-SCS were formed with four different SCS concentrations,using the solution castingmethod,andDimethyl Sulfoxide(DMSO)was used as a solvent.The composite membranes synthesized include pure SPEEK(S0),SPEEK with 1%SCS(S1),SPEEK with 2%SCS(S2),and SPEEK with 3%SCS(S3).Fourier transform infrared spectroscopy(FTIR),X-ray diffraction(XRD),water uptake,degree of swelling,Ionic exchange capacity(IEC)with Electrochemical impedance spectroscopy(EIS)were used to characterize the composite membranes in terms of composition,crystallinity,water absorption,dimensional changes,number of exchangeable ions in membranes,and proton conductivity,respectively.Notably,S3 had the highest water uptake and the lowest degree of swelling.S2 had the highest proton conductivity among the SPEEK-SCS composite membranes at room temperature with 3.44×10^(−2) Scm^(-1).展开更多
With the miniaturization and high-frequency evolution of antennas in 5G/6G communications,aerospace,and transportation,polymer composite papers integrating superior wave-transparent performance and thermal conductivit...With the miniaturization and high-frequency evolution of antennas in 5G/6G communications,aerospace,and transportation,polymer composite papers integrating superior wave-transparent performance and thermal conductivity for radar antenna systems are urgently needed.Herein,a down-top strategy was employed to synthesize poly(p-phenylene benzobisoxazole)precursor nanofibers(prePNF).The prePNF was then uniformly mixed with fluorinated graphene(FG)to fabricate FG/PNF composite papers through consecutively suction filtration,hot-pressing,and thermal annealing.The hydroxyl and amino groups in prePNF enhanced the stability of FG/prePNF dispersion,while the increasedπ-πinteractions between PNF and FG after annealing improved their compatibility.The preparation time and cost of PNF paper was significantly reduced when applying this strategy,which enabled its large-scale production.Furthermore,the prepared FG/PNF composite papers exhibited excellent wave-transparent performance and thermal conductivity.When the mass fraction of FG was 40 wt%,the FG/PNF composite paper prepared via the down-top strategy achieved the wave-transparent coefficient(|T|2)of 96.3%under 10 GHz,in-plane thermal conductivity(λ_(∥))of 7.13 W m^(−1)K^(−1),and through-plane thermal conductivity(λ_(⊥))of 0.67 W m^(−1)K^(−1),outperforming FG/PNF composite paper prepared by the top-down strategy(|T|2=95.9%,λ_(∥)=5.52 W m^(−1)K^(−1),λ_(⊥)=0.52 W m^(−1)K^(−1))and pure PNF paper(|T|2=94.7%,λ_(∥)=3.04 W m^(−1)K^(−1),λ_(⊥)=0.24 W m^(−1)K^(−1)).Meanwhile,FG/PNF composite paper(with 40 wt%FG)through the down-top strategy also demonstrated outstanding mechanical properties with tensile strength and toughness reaching 197.4 MPa and 11.6 MJ m^(−3),respectively.展开更多
The thermal conductivity of nanofluids is an important property that influences the heat transfer capabilities of nanofluids.Researchers rely on experimental investigations to explore nanofluid properties,as it is a n...The thermal conductivity of nanofluids is an important property that influences the heat transfer capabilities of nanofluids.Researchers rely on experimental investigations to explore nanofluid properties,as it is a necessary step before their practical application.As these investigations are time and resource-consuming undertakings,an effective prediction model can significantly improve the efficiency of research operations.In this work,an Artificial Neural Network(ANN)model is developed to predict the thermal conductivity of metal oxide water-based nanofluid.For this,a comprehensive set of 691 data points was collected from the literature.This dataset is split into training(70%),validation(15%),and testing(15%)and used to train the ANN model.The developed model is a backpropagation artificial neural network with a 4–12–1 architecture.The performance of the developed model shows high accuracy with R values above 0.90 and rapid convergence.It shows that the developed ANN model accurately predicts the thermal conductivity of nanofluids.展开更多
Laser-induced aerosols,predominantly submicron in size,pose significant environmental and health risks during the decommissioning of nuclear reactors.This study experimentally investigated the removal of laser-generat...Laser-induced aerosols,predominantly submicron in size,pose significant environmental and health risks during the decommissioning of nuclear reactors.This study experimentally investigated the removal of laser-generated aerosol particles using a water spray system integrated with an innovative system for pre-injecting electrically charged mist in our facility.To simulate aerosol generation in reactor decommissioning,a high-power laser was used to irradiate various materials(including stainless steel,carbon steel,and concrete),generating aerosol particles that were agglomerated with injected water mist and subsequently scavenged by water spray.Experimental results demonstrate enhanced aerosol removal via aerosol-mist agglomeration,with charged mist significantly improving particle capture by increasing wettability and size.The average improvements for the stainless steel,carbon steel,and concrete were 40%,44%,and 21%,respectively.The results of experiments using charged mist with different polarities(both positive and negative)and different surface coatings reveal that the dominant polarity of aerosols varies with the irradiated materials,influenced by their crystal structure and electron emission properties.Notably,surface coatings such as ZrO_(2)and CeO_(2)were found to possibly alter aerosol charging characteristics,thereby affecting aerosol removal efficiency with charged mist configurations.The innovative aerosol-mist agglomeration approach shows promise in mitigating radiation exposure,ensuring environmental safety,and reducing contaminated water during reactor dismantling.This study contributes critical knowledge for the development of advanced aerosol management strategies for nuclear reactor decommissioning.The understanding obtained in this work is also expected to be useful for various environmental and chemical engineering applications such as gas decontamination,air purification,and pollution control.展开更多
Although previous studies have demonstrated that transcranial focused ultrasound stimulation protects the ischemic brain,clear criteria for the stimulation time window and intensity are lacking.Electrical impedance to...Although previous studies have demonstrated that transcranial focused ultrasound stimulation protects the ischemic brain,clear criteria for the stimulation time window and intensity are lacking.Electrical impedance tomography enables real-time monitoring of changes in cerebral blood perfusion within the ischemic brain,but investigating the feasibility of using this method to assess post-stroke rehabilitation in vivo remains critical.In this study,ischemic stroke was induced in rats through middle cerebral artery occlusion surgery.Transcranial focused ultrasound stimulation was used to treat the rat model of ischemia,and electrical impedance tomography was used to measure impedance during both the acute stage of ischemia and the rehabilitation stage following the stimulation.Electrical impedance tomography results indicated that cerebral impedance increased after the onset of ischemia and decreased following transcranial focused ultrasound stimulation.Furthermore,the stimulation promoted motor function recovery,reduced cerebral infarction volume in the rat model of ischemic stroke,and induced the expression of brain-derived neurotrophic factor in the ischemic brain.Our results also revealed a significant correlation between the impedance of the ischemic brain post-intervention and improvements in behavioral scores and infarct volume.This study shows that daily administration of transcranial focused ultrasound stimulation for 20 minutes to the ischemic hemisphere 24 hours after cerebral ischemia enhanced motor recovery in a rat model of ischemia.Additionally,our findings indicate that electrical impedance tomography can serve as a valuable tool for quantitatively evaluating rehabilitation after ischemic stroke in vivo.These findings suggest the feasibility of using impedance data collected via electrical impedance tomography to clinically assess the effects of rehabilitatory interventions for patients with ischemic stroke.展开更多
The mechanism of seeded precipitation of sodium aluminate solution was studied by measuring the seeded-precipitation rate and electrical conductivity online, as well as calculating the activity and fraction of ion pai...The mechanism of seeded precipitation of sodium aluminate solution was studied by measuring the seeded-precipitation rate and electrical conductivity online, as well as calculating the activity and fraction of ion pair. The results show that the electrical conductivity of sodium aluminate slurry linearly decreases with increasing aluminum hydroxide addition. Moreover, both the electrical conductivity of slurry and the difference in electrical conductivity between sodium aluminate solution and slurry remarkably decline in the first 60 min before gradually increasing in the preliminary 10 h and finally reaching almost the same level after 10 h. In low Na2 O concentration solution the activities of Na OH and Na Al（OH）4 in seeded precipitation are high, which can enlarge the difference in conductivity between slurry and solution. Additionally, more ion pairs exist in solution in preliminary seeded precipitation, and the adsorption of Na＋Al（OH）4- on seed surface is likely to break the equilibrium of ion pair formation and to decrease the difference in conductivity in preliminary seeded precipitation.展开更多
The electrical conductivity of NaF-AlF3-CaF2-Al2O3-ZrO2 system was studied by a tube-type cell with fixed cell constant. The results show that the electrical conductivity of NaF-AlF3-3%Al2O3-3%CaF2-ZrO2 molten salt sy...The electrical conductivity of NaF-AlF3-CaF2-Al2O3-ZrO2 system was studied by a tube-type cell with fixed cell constant. The results show that the electrical conductivity of NaF-AlF3-3%Al2O3-3%CaF2-ZrO2 molten salt system decreases with increase of ZrO2 content in an interval of 0-5%. The increase of 1%ZrO2 results in a corresponding electrical conductivity decrease of 0.02 S/cm, and the equivalent conductivity increases with the increase of molar ratio of NaF to AlF3. When the temperature increases by 1 °C, the electrical conductivity increases by 0.004 S/cm. At last, the regression equations of electrical conductivity relative to temperature and ZrO2 are obtained by quadratic regression analysis.展开更多
The ambient electrical conductivity (AEC) of carbon cathode materials was investigated in respect to their open porosity, crystal structure and graphite content using hydrostatic method, four-probe technique and X-ray...The ambient electrical conductivity (AEC) of carbon cathode materials was investigated in respect to their open porosity, crystal structure and graphite content using hydrostatic method, four-probe technique and X-ray diffraction (XRD), respectively. The AEC is proportional to the specific conductivity (σ0) and the exponential of (1?ε) (ε is porosity) by a quasi-uniform formula based on the percolation theory. Theσ0 can reflect the intrinsic conductivity of the carbon cathodes free of pores, and it depends on the mean crystallite size parallel to the layer (002). The exponentn is dependent on the materials nature of the cathode aggregates, while an averaged value, 4.65, can practically work well with 5 types of cathode materials. The calculation ofσ0 can be extended to the graphitic cathodes containing different aggregates using the simple rule of mixture.展开更多
基金Applied Basic Research Program of Liaoning Province(CN)(2022JH2/101300078)。
文摘Self-designed Al8Si0.4Mg0.4Fe aluminium alloy was modified with Sr,followed by solid solution and aging treatments to regulate its microstructure and mechanical/electrical properties.The results show that after the modification treatment,the room-temperature tensile strength of the alloy remains nearly unchanged,the elongation at break slightly increases from 1.82%to 3.34%,and the electrical conductivity significantly increases from 40.1%international annealed copper standard(IACS)to 42.0%IACS.After the modification,the alloy was subjected to solid solution treatment at 515℃for 8 h,followed by aging treatment at 180,200,220 and 240℃for 6 h.With increasing aging temperature,the electrical conductivity increases monotonously from 41.4%IACS to 45.5%IACS,while the room-temperature tensile strength initially increases and then decreases.At 200℃,the alloy achieves an optimal balance between electrical conductivity and room-temperature tensile strength:the electrical conductivity is 42.5%IACS,and the room-temperature tensile strength is 282.9 MPa.When the aging temperature continues to rise,the alloy undergoes overaging.Although the conductivity continues to increase,the room-temperature tensile strength drops sharply,and it is only 177.1 MPa at 240℃.
基金Foundation of Northwest Institute for Non-ferrous Metal Research(YK2020-9,ZZXJ2203)Capital Projects of Financial Department of Shaanxi Province(YK22C-12)+4 种基金National Natural Science Foundation of China(62204207)Innovation Capability Support Plan in Shaanxi Province of China(2022KJXX-82,2023KJXX-083)Natural Science Foundation of Shaanxi Province(2022JQ-332)Shaanxi Innovative Research Team for Key Science and Technology(2023-CX-TD-46)Key Research and Development Projects of Shaanxi Province(2024GX-YBXM-351)。
文摘Compared with Cu/Al_(2)O_(3)composites,high-strength Cu/Al_(2)O_(3)composites usually exhibit obviously deteriorated electrical conductivity.A chemical and mechanical alloying-based strategy was adopted to fabricate ultrafine composite powders with lowcontent reinforcement and constructed a combined structure of Cu ultrafine powders covered with in-situ Al_(2)O_(3)nanoparticles.After consolidation at a relatively lower sintering temperature of 550℃,high-volume-fraction ultrafine grains were introduced into the Cu/Al_(2)O_(3)composite,and many in-situ Al_(2)O_(3)nanoparticles with an average size of 11.7±7.5 nm were dispersed homogeneously in the Cu grain.Results show that the composite demonstrates an excellent balance of high tensile strength(654±1 MPa)and high electrical conductivity(84.5±0.1%IACS),which is ascribed to the synergistic strengthening effect of ultrafine grains,dislocations,and in-situ Al_(2)O_(3)nanoparticles.This approach,which utilizes ultrafine composite powder with low-content reinforcement as a precursor and employs low-temperature and high-pressure sintering subsequently,may hold promising potential for large-scale industrial production of high-performance oxide dispersion strengthened alloys.
基金financially supported by Silesian University of Technology,Poland(No.11/030/BK_23/1127)V?B–Technical University of Ostrava Czech Republic(No.CZ.02.1.01/0.0/0.0/17_049/0008399)。
文摘The effects of forward extrusion as well as extrusion combined with reversible torsion(KoBo extrusion),followed by additional deformation via the MaxStrain module of the Gleeble thermomechanical simulator,on the microstructure,mechanical properties,and electrical conductivity of a Cu−0.7Mg(wt.%)alloy,were investigated.The simulation results highlighted the critical influence of processing history on determining the equivalent strain distribution.The sample subjected to forward extrusion at 400℃and subsequent MaxStrain processing(FM sample),possessed 76%lower grain size compared to the sample processed solely with MaxStrain(AM sample).Likewise,the KoBo-extruded and MaxStrain-processed sample(KM sample)exhibited 66%smaller grain size compared to the AM sample.Tensile test results revealed that the AM,FM,and KM samples,respectively,possessed 251%,288%,and 360%higher yield strength,and 95%,121%,and 169%higher tensile strength compared to the initial annealed alloy,as a result of grain refinement as well as deformation strengthening.Finally,the electrical conductivity measurements revealed that AM,FM,and KM samples,respectively,possessed electrical conductivity values of 37.9,35.6,and 32.0 MS/m,which,by considering their mechanical properties,makes them eligible to be categorized as high-strength and high-conductivity copper alloys.
基金support provided by the National Natural Science Foundation of China(Nos.52405364,and 52171110)the Jiangsu Funding Program for Excellent Postdoctoral Talent.W.Huo acknowledges the support from the European Union Horizon 2020 Research and Innovation Program(No.857470)+1 种基金from the European Regional Development Fund via the Foundation for Polish Science International Research Agenda PLUS Program(No.MAB PLUS/2018/8)The publication was partly created within the framework of the project of the Minister of Science and Higher Education"Support for the activities of Centers of Excellence established in Poland under Horizon 2020"(No.MEiN/2023/DIR/3795).
文摘The effects of drawing strain during intermediate annealing on the microstructure and properties of Cu-20 wt%Fe alloy wires while maintaining constant total deformation were investigated.Intermediate annealing effectively removes work hardening in both the Cu matrix and Fe fibers,restoring their plastic deformation capacity and preserving fiber continuity during subsequent redrawing.The process also refines the Fe phase,leading to a more uniform size distribution and straighter,better-aligned Cu/Fe phase interfaces,thereby enhancing the comprehensive properties of the alloy.The magnitude of drawing strain during intermediate annealing plays a critical role in balancing the mechanical strength and electrical conductivity of redrawn wires.A lower initial drawing strain requires greater redrawing strain,leading to excessive hardening of the Fe fibers,which negatively impacts the electrical conductivity and tensile plasticity.Conversely,a higher initial drawing strain can result in insufficient work hardening during the redrawing deformation process,yielding minimal strength improvements.Among the tested alloys,H/3.5 wires show a slight reduction in strength and hardness compared to W and H/4.5 wires but exhibit a significant increase in tensile elongation and electrical conductivity.The tensile strength was 755 MPa,and the electrical conductivity was 47%international-annealed copper standard(IACS).The optimal performance is attributed to the formation of a high-density,ultrafine Fe fiber structure-aligned parallel to the drawing direction,which is achieved through a suitable combination of the drawing process and intermediate annealing.
基金supported by the Science and Technology Development Project of Jilin Province(Grant No.SKL202402004)the Program for the Development of Science and Technology of Jilin Province(Grant No.YDZJ202201ZYTS308)+1 种基金the Open Research Fund of State Key Laboratory of Inorganic Synthesis and Preparative Chemistry,Jilin University(Grant Nos.202216 and 2022-23)the National Natural Science Foundation of China(Grant No.12350410372)。
文摘In thermoelectricity,the inherent coupling between electrical conductivity and Seebeck coefficient represents a fundamental challenge in thermoelectric materials development.Herein,we present a unique pressure-tuning strategy using compressible layered 2H-MoTe2,achieving an effective decoupling between the electrical conductivity and Seebeck coefficient.The applied pressure simultaneously induces two complementary effects:(1)bandgap reduction that moderately enhances carrier concentration to improve the electrical conductivity,and(2)band convergence that dramatically increases density-of-states effective mass to boost the Seebeck coefficient.This dual mechanism yields an extraordinary 18.5-fold enhancement in the average power factor.First-principles calculations and Boltzmann transport modeling precisely reproduce the experimental observations,validating this pressure-induced decoupling mechanism.The pressure-tuning mechanism provides a feasible and effective strategy for breaking through the optimization limits of the power factor,facilitating the design of high-performance thermoelectric materials.
基金supported by the National Natural Science Foundation of China(92163107,52171061,and 52371128)the National Key Research and Development Program of China(2022YFB3708800 and 2021YFB3501502).
文摘Immiscible bimetal systems,of which tungsten–copper(W–Cu)is a typical representative,have crucial applications in fields requiring both mechanical and physical properties.Nevertheless,it is a major challenge to determine how to give full play to the advantages of the two phases of the bimetal and achieve outstanding comprehensive properties.In this study,an ultrafine-grained W–Cu bimetal with spatially connected Cu and specific Wislands was fabricated through a designed powder-mixing process and subsequent rapid low-temperature sintering.The prepared bimetal concurrently has a high yield strength,large plastic strain,and high electrical conductivity.The stress distribution and strain response of individual phases in different types of W–Cu bimetals under loading were quantified by means of a simulation.The high yield strength of the reported bimetal results from the microstructure refinement and high contiguity of the grains in the W islands,which enhance the contribution of W to the total plastic deformation of the bimetal.The high electrical conductivity is attributed to the increased mean free path of the Cu and the reduced proportion of phase boundaries due to the specific phase combination of W islands and Cu.This work provides new insight into modulating phase configuration in immiscible metallic composites to achieve high-level multi-objective properties.
基金support provided by National Natural Science Foundation of China(Nos.52405364 and 52171110)Jiangsu Funding Program for Excellent Postdoctoral Talent+3 种基金JITRI Advanced Materials R&D Co.Ltdsupport by European Union Horizon 2020 Research and Innovation Program(857470)European Regional Development Fund via the Foundation for Polish Science International Research Agenda PLUS program(MAB PLUS/2018/8)The publication was created within the framework of the project of the Minister of Science and Higher Education,Support for the Activities of Centres of Excellence established in Poland under Horizon 2020,under contract No.MEiN/2023/DIR/3795.
文摘The deformation of Cu–20 wt.%Fe alloy wires leads to a significant improvement in mechanical properties and a decrease in electrical conductivity.Simultaneous improvements in strength and conductivity were achieved by intermediate annealing of drawn Cu–20 wt.%Fe wires.As the annealing temperature increased,the strength of Cu–20 wt.%Fe alloy wire decreased monotonically,but the electrical conductivity first increased and then decreased,reaching its peak value after annealing at 500℃.The decrease in strength is related to dislocation recovery and static recrystallization of Cu and Fe phases,and the increase in electrical conductivity mainly results from the aging precipitation of solid solution Fe.After annealing at 500℃,there was no obvious recrystallization of Cu phase,and many of the nano-Fe particles precipitated from Cu matrix.An annealing temperature of 600℃ induced the recrystallization of Cu matrix and an increase in Fe solid solubility,resulting in a decrease in strength and electrical conductivity.Subsequently,the wires annealed at 500℃ were drawn to 2 mm.Compared with those of the continuously drawn Cu–20 wt.%Fe alloy wires,the deformation ability,strength,and electrical conductivity of Cu–20 wt.%Fe alloy wires subjected to intermediate annealing treatment are significantly greater.This is mainly related to the sufficient precipitation of Fe in Cu matrix and the strengthening of refined Fe fibers parallel to the drawing direction.
基金supported by the National Natural Science Foundation of China(52225101)the Jinhua Science and Technology Program of China(2024A221787)+1 种基金the Sichuan Science and Technology Program of China(2025ZNSFSC0388)the Chongqing Special Project for Science and Technology Innovation of China(CSTB2023YSZX-JCX0006).
文摘Magnesium(Mg)alloys offer significant potential for conductive applications,thanks to their distinctive attributes,including high specific strength,excellent electrical conductivity(EC),low density,electromagnetic interference shielding effectiveness(EMI SE),and recyclability.However,a major challenge in Mg alloy research is balancing high strength with good EC,as strengthening these alloys often compromises their EC.This paper offers an in-depth analysis of the mechanisms,strategies,and applications aimed at improving the EC of Mg alloys.A bibliometric study is performed to uncover the main research trends and emerging hotspots within the field.The review then examines various strategies to improve EC focusing on factors such as solute elements,second phases,grain boundaries,textures,and vacancies.By carefully controlling alloy composition and optimizing heat treatment processes,significant advancements have been achieved by researchers in developing Mg alloys that possess both high strength and high EC,especially in Mg-Al,Mg-Zn,Mg-RE alloy systems and composites.Finally,the paper outlines future research directions,stressing the importance of further exploration into alloying element selection,heat treatment optimization,and other advanced strategies.These efforts are crucial for overcoming current challenges and expanding the application of Mg alloys in EC fields.
基金supported by the National Natural Science Foundation of China(No.51704087)the Natural Science Foundation of Heilongjiang Province(No.LH2020E083).
文摘Lightweight aluminum alloy conductor materials(Al-Mg-Si alloys)require not only high electrical conductivity to reduce electrical loss,but also high strength to withstand extreme weather conditions.To improve electrical conductivity and mechanical properties of Al-Mg-Si alloy simultaneously,the rare earth La was introduced to modify the Al-Mg-Si alloy.The effect of La addition on the microstructure,tensile properties and electrical conductivity of cast Al-Mg-Si alloy was investigated systematically.Results indicate that the appropriate La content is helpful to improve the strength and electrical conductivity of Al-Mg-Si alloys.When the addition of La is 0.2wt.%,theα-Al grains are refined apparently,Mg and Si solute atoms in the Al matrix are reduced by the formation of Mg_(2)Si phase;the distribution of Al_(11)La_(3)phases is uniform,and the morphology of AlFeSi phase transforms from continuous state to discontinuous state.The Al-Mg-Si-0.2La alloy exhibits the optimal tensile properties and electrical conductivity,with an ultimate tensile strength of 170 MPa,a yield strength of 88 MPa,an elongation of 18.9%,and an electrical conductivity of 44.0%IACS.These values represent improvements of 9.0%,15.8%,70.3%,and 17.3%,respectively,compared to the Al-Mg-Si alloy without La addition.However,excessive La deteriorates the properties of Al-Mg-Si-xLa alloys.
基金the support from the National Natural Science Foundation of China(52403112,52473083)Natural Science Basic Research Program of Shaanxi(2024JC-TBZC-04)+2 种基金the Innovation Capability Support Program of Shaanxi(2024RS-CXTD-57)Fundamental Research Funds for the Central Universities(D5000240062,D5000240077)Undergraduate Innovation&Business Program in Northwestern Polytechnical University(202410699041)。
文摘High-performance Ti_(3)C_(2)T_(x)fibers have garnered significant potential for smart fibers enabled fabrics.Nonetheless,a major challenge hindering their widespread use is the lack of strong interlayer interactions between Ti_(3)C_(2)T_(x)nanosheets within fibers,which restricts their properties.Herein,a versatile strategy is proposed to construct wet-spun Ti_(3)C_(2)T_(x)fibers,in which trace amounts of borate form strong interlayer crosslinking between Ti_(3)C_(2)T_(x)nanosheets to significantly enhance interactions as supported by density functional theory calculations,thereby reducing interlayer spacing,diminishing microscopic voids and promoting orientation of the nanosheets.The resultant Ti_(3)C_(2)T_(x)fibers exhibit exceptional electrical conductivity of 7781 S cm^(-1)and mechanical properties,including tensile strength of 188.72 MPa and Young's modulus of 52.42 GPa.Notably,employing equilibrium molecular dynamics simulations,finite element analysis,and cross-wire geometry method,it is revealed that such crosslinking also effectively lowers interfacial thermal resistance and ultimately elevates thermal conductivity of Ti_(3)C_(2)T_(x)fibers to 13 W m^(-1)K^(-1),marking the first systematic study on thermal conductivity of Ti_(3)C_(2)T_(x)fibers.The simple and efficient interlayer crosslinking enhancement strategy not only enables the construction of thermal conductivity Ti_(3)C_(2)T_(x)fibers with high electrical conductivity for smart textiles,but also offers a scalable approach for assembling other nanomaterials into multifunctional fibers.
基金supported by the National Natural Science Foundation of China(52172265)Excellent Youth Science Foundation of Hunan Province(2022JJ20067)+1 种基金The Science and Technology Innovation Program of Hunan Province(2022RC1074)Central South University Innovation-Driven Research Program(2023CXQD010).
文摘Polymer dielectrics possessing excellent electrical insulation and high thermal conductivity are pivotal for dielectric capacitors at elevated temperatures.However,the integration of electrical insulation and thermal conductivity in polymers remains a challenge.In this work,we present a feasible strategy to integrate high electrical insulation and high thermal conductivity by bonding carbon quantum dots(CQDs)with the diamine monomer of polyetherimide(PEI).The CQDs with Coulomb blockade effect serve as traps for the migrating of electrons in the dielectrics,while the bonding networks formed by CQDs and PEI further deepen the traps and augment trap density.As a result,the hybrid dielectrics(PEI-NH_(2)-CQDs)exhibit nearly an order of magnitude higher electrical resistivity than that of pure PEI,leading to an 80%increase in discharge energy density with an energy efficiency of 90%at 200℃ compared to pure counterpart.Additionally,this all-organic dielectric achieves a significantly increased thermal conductivity of 0.65 W m^(-1) K^(-1) compared to 0.26 W m^(-1) K^(-1) of PEI,which supports its cyclic stability at elevated temperatures.We also demonstrate the kilogram-scale production of CQDs,synthesizing over 8 kg in a single batch,paving the way for large-scale production of reliable PEI-NH_(2)-CQDs dielectrics.
基金Funded by the National Natural Science Foundation of China(No.22005151)the Natural Science Foundation of Nanjing University of Posts and Telecommunications(No.NY220127)。
文摘Polyvinyl alcohol(PVA)hydrogels doped with cyclohexane-1,2,3,4,5,6-hexacarboxylic acid(CHA)were successfully prepared during drying and swelling.Structural and morphological characterizations suggest the carboxyl and hydroxyl groups in the material undergo esterification during the preparation of the material,which contributes to the high transparency with 90%transmittance in the 400 to 800 nm range and robust mechanical properties of the material with a tensile strength at a break of 27.55 MPa.It is noteworthy that the bending and torsion angles exhibit a strong linear correlation with electrical resistance,enabling the monitoring of the bending motion state of each human body segment.
文摘Proton exchange membrane(PEM)is an integral component in fuel cells which enables proton transport for efficient energy conversion.Sulfonated Polyether Ether Ketone(SPEEK)has emerged as a cost-effective option with non-fluorinated aromatic backbones for Proton Exchange Membrane Fuel Cell(PEMFC)applications,even though it exhibits lower proton conductivity compared to Nafion.This work aims to study the influence of Sulfonated Chitosan(SCS)concentrations on proton conductivity of SPEEK-based PEM at room temperature.SPEEK was synthesized using a sulfonation process with concentrated sulfuric acid at room temperature.SCS was synthesized via reflux of CS and 1.2 M H2SO4 with a ratio of 1:35(w/v)at 90℃ for 30 min.The composite membranes of SPEEK-SCS were formed with four different SCS concentrations,using the solution castingmethod,andDimethyl Sulfoxide(DMSO)was used as a solvent.The composite membranes synthesized include pure SPEEK(S0),SPEEK with 1%SCS(S1),SPEEK with 2%SCS(S2),and SPEEK with 3%SCS(S3).Fourier transform infrared spectroscopy(FTIR),X-ray diffraction(XRD),water uptake,degree of swelling,Ionic exchange capacity(IEC)with Electrochemical impedance spectroscopy(EIS)were used to characterize the composite membranes in terms of composition,crystallinity,water absorption,dimensional changes,number of exchangeable ions in membranes,and proton conductivity,respectively.Notably,S3 had the highest water uptake and the lowest degree of swelling.S2 had the highest proton conductivity among the SPEEK-SCS composite membranes at room temperature with 3.44×10^(−2) Scm^(-1).
基金the support from the National Natural Science Foundation of China(52473083,52373089,52403085)Natural Science Basic Research Program of Shaanxi(2024JC-TBZC-04)+2 种基金the Innovation Capability Support Program of Shaanxi(2024RS-CXTD-57)Natural Science Basic Research Plan in Shaanxi Province of China(2024JC-YBMS-279)Natural Science Foundation of Chongqing,China(2023NSCQMSX2547)
文摘With the miniaturization and high-frequency evolution of antennas in 5G/6G communications,aerospace,and transportation,polymer composite papers integrating superior wave-transparent performance and thermal conductivity for radar antenna systems are urgently needed.Herein,a down-top strategy was employed to synthesize poly(p-phenylene benzobisoxazole)precursor nanofibers(prePNF).The prePNF was then uniformly mixed with fluorinated graphene(FG)to fabricate FG/PNF composite papers through consecutively suction filtration,hot-pressing,and thermal annealing.The hydroxyl and amino groups in prePNF enhanced the stability of FG/prePNF dispersion,while the increasedπ-πinteractions between PNF and FG after annealing improved their compatibility.The preparation time and cost of PNF paper was significantly reduced when applying this strategy,which enabled its large-scale production.Furthermore,the prepared FG/PNF composite papers exhibited excellent wave-transparent performance and thermal conductivity.When the mass fraction of FG was 40 wt%,the FG/PNF composite paper prepared via the down-top strategy achieved the wave-transparent coefficient(|T|2)of 96.3%under 10 GHz,in-plane thermal conductivity(λ_(∥))of 7.13 W m^(−1)K^(−1),and through-plane thermal conductivity(λ_(⊥))of 0.67 W m^(−1)K^(−1),outperforming FG/PNF composite paper prepared by the top-down strategy(|T|2=95.9%,λ_(∥)=5.52 W m^(−1)K^(−1),λ_(⊥)=0.52 W m^(−1)K^(−1))and pure PNF paper(|T|2=94.7%,λ_(∥)=3.04 W m^(−1)K^(−1),λ_(⊥)=0.24 W m^(−1)K^(−1)).Meanwhile,FG/PNF composite paper(with 40 wt%FG)through the down-top strategy also demonstrated outstanding mechanical properties with tensile strength and toughness reaching 197.4 MPa and 11.6 MJ m^(−3),respectively.
基金supported by Basic Science Research Program through the National Research Foundation of Korea(NRF)funded by the Ministry of Education(2021R1A6A1A10044950).
文摘The thermal conductivity of nanofluids is an important property that influences the heat transfer capabilities of nanofluids.Researchers rely on experimental investigations to explore nanofluid properties,as it is a necessary step before their practical application.As these investigations are time and resource-consuming undertakings,an effective prediction model can significantly improve the efficiency of research operations.In this work,an Artificial Neural Network(ANN)model is developed to predict the thermal conductivity of metal oxide water-based nanofluid.For this,a comprehensive set of 691 data points was collected from the literature.This dataset is split into training(70%),validation(15%),and testing(15%)and used to train the ANN model.The developed model is a backpropagation artificial neural network with a 4–12–1 architecture.The performance of the developed model shows high accuracy with R values above 0.90 and rapid convergence.It shows that the developed ANN model accurately predicts the thermal conductivity of nanofluids.
基金financial support from the Nuclear Energy Science&Technology and Human Resource Development Project of the Japan Atomic Energy Agency/Collaborative Laboratories for Advanced Decommissioning Science(No.R04I034)The author Ruicong Xu appreciates the scholarship(financial support)from the China Scholarship Council(CSC,No.202106380073).
文摘Laser-induced aerosols,predominantly submicron in size,pose significant environmental and health risks during the decommissioning of nuclear reactors.This study experimentally investigated the removal of laser-generated aerosol particles using a water spray system integrated with an innovative system for pre-injecting electrically charged mist in our facility.To simulate aerosol generation in reactor decommissioning,a high-power laser was used to irradiate various materials(including stainless steel,carbon steel,and concrete),generating aerosol particles that were agglomerated with injected water mist and subsequently scavenged by water spray.Experimental results demonstrate enhanced aerosol removal via aerosol-mist agglomeration,with charged mist significantly improving particle capture by increasing wettability and size.The average improvements for the stainless steel,carbon steel,and concrete were 40%,44%,and 21%,respectively.The results of experiments using charged mist with different polarities(both positive and negative)and different surface coatings reveal that the dominant polarity of aerosols varies with the irradiated materials,influenced by their crystal structure and electron emission properties.Notably,surface coatings such as ZrO_(2)and CeO_(2)were found to possibly alter aerosol charging characteristics,thereby affecting aerosol removal efficiency with charged mist configurations.The innovative aerosol-mist agglomeration approach shows promise in mitigating radiation exposure,ensuring environmental safety,and reducing contaminated water during reactor dismantling.This study contributes critical knowledge for the development of advanced aerosol management strategies for nuclear reactor decommissioning.The understanding obtained in this work is also expected to be useful for various environmental and chemical engineering applications such as gas decontamination,air purification,and pollution control.
基金supported by the Fundamental Research Funds for the Central Universities,Nos.G2021KY05107,G2021KY05101the National Natural Science Foundation of China,Nos.32071316,32211530049+1 种基金the Natural Science Foundation of Shaanxi Province,No.2022-JM482the Education and Teaching Reform Funds for the Central Universities,No.23GZ230102(all to LL and HH).
文摘Although previous studies have demonstrated that transcranial focused ultrasound stimulation protects the ischemic brain,clear criteria for the stimulation time window and intensity are lacking.Electrical impedance tomography enables real-time monitoring of changes in cerebral blood perfusion within the ischemic brain,but investigating the feasibility of using this method to assess post-stroke rehabilitation in vivo remains critical.In this study,ischemic stroke was induced in rats through middle cerebral artery occlusion surgery.Transcranial focused ultrasound stimulation was used to treat the rat model of ischemia,and electrical impedance tomography was used to measure impedance during both the acute stage of ischemia and the rehabilitation stage following the stimulation.Electrical impedance tomography results indicated that cerebral impedance increased after the onset of ischemia and decreased following transcranial focused ultrasound stimulation.Furthermore,the stimulation promoted motor function recovery,reduced cerebral infarction volume in the rat model of ischemic stroke,and induced the expression of brain-derived neurotrophic factor in the ischemic brain.Our results also revealed a significant correlation between the impedance of the ischemic brain post-intervention and improvements in behavioral scores and infarct volume.This study shows that daily administration of transcranial focused ultrasound stimulation for 20 minutes to the ischemic hemisphere 24 hours after cerebral ischemia enhanced motor recovery in a rat model of ischemia.Additionally,our findings indicate that electrical impedance tomography can serve as a valuable tool for quantitatively evaluating rehabilitation after ischemic stroke in vivo.These findings suggest the feasibility of using impedance data collected via electrical impedance tomography to clinically assess the effects of rehabilitatory interventions for patients with ischemic stroke.
基金Project(51274242)supported by the National Natural Science Foundation of China
文摘The mechanism of seeded precipitation of sodium aluminate solution was studied by measuring the seeded-precipitation rate and electrical conductivity online, as well as calculating the activity and fraction of ion pair. The results show that the electrical conductivity of sodium aluminate slurry linearly decreases with increasing aluminum hydroxide addition. Moreover, both the electrical conductivity of slurry and the difference in electrical conductivity between sodium aluminate solution and slurry remarkably decline in the first 60 min before gradually increasing in the preliminary 10 h and finally reaching almost the same level after 10 h. In low Na2 O concentration solution the activities of Na OH and Na Al（OH）4 in seeded precipitation are high, which can enlarge the difference in conductivity between slurry and solution. Additionally, more ion pairs exist in solution in preliminary seeded precipitation, and the adsorption of Na＋Al（OH）4- on seed surface is likely to break the equilibrium of ion pair formation and to decrease the difference in conductivity in preliminary seeded precipitation.
基金Project (2007CB210305) supported by the National Basic Research Program of ChinaProject (51074045) supported by the National Natural Science Foundation of China
文摘The electrical conductivity of NaF-AlF3-CaF2-Al2O3-ZrO2 system was studied by a tube-type cell with fixed cell constant. The results show that the electrical conductivity of NaF-AlF3-3%Al2O3-3%CaF2-ZrO2 molten salt system decreases with increase of ZrO2 content in an interval of 0-5%. The increase of 1%ZrO2 results in a corresponding electrical conductivity decrease of 0.02 S/cm, and the equivalent conductivity increases with the increase of molar ratio of NaF to AlF3. When the temperature increases by 1 °C, the electrical conductivity increases by 0.004 S/cm. At last, the regression equations of electrical conductivity relative to temperature and ZrO2 are obtained by quadratic regression analysis.
基金Project(20110006110003)supported by the Research Fund for the Doctoral Program of Higher Education of ChinaProject(51434005)supported by the National Natural Science Foundation of China
文摘The ambient electrical conductivity (AEC) of carbon cathode materials was investigated in respect to their open porosity, crystal structure and graphite content using hydrostatic method, four-probe technique and X-ray diffraction (XRD), respectively. The AEC is proportional to the specific conductivity (σ0) and the exponential of (1?ε) (ε is porosity) by a quasi-uniform formula based on the percolation theory. Theσ0 can reflect the intrinsic conductivity of the carbon cathodes free of pores, and it depends on the mean crystallite size parallel to the layer (002). The exponentn is dependent on the materials nature of the cathode aggregates, while an averaged value, 4.65, can practically work well with 5 types of cathode materials. The calculation ofσ0 can be extended to the graphitic cathodes containing different aggregates using the simple rule of mixture.